Flame Retardancy and Thermal Degradation Behaviors of Thiol-Ene Composites Containing a Novel Phosphorus and Silicon-Containing Flame Retardant

A New Phosphorous/Nitrogen-Containing Flame-Retardant Film with High Adhesion for Jute Fiber Composites

In this work, a novel P/N flame-retardant monomer (PDHAA) was synthesized through reacting phenyl dichlorophosphate (PDCP) with N-hydroxyethyl acrylamide (HEAA). The structure of PDHAA was confirmed using Fourier transform infrared (FTIR) spectroscopy and proton nuclear magnetic resonance (NMR) spectroscopy. PDHAA monomer and 2-hydroxyethyl methacrylate phosphate (PM-2) monomer were mixed at different mass ratios, to prepare UV-curable coatings, and then applied to the surface of fiber needled felts (FNFs), to improve their flame retardancy. PM-2 was introduced to reduce the curing time of the flame-retardant coatings and improve the adhesion between the coating and the fiber needled felts (FNFs). The research results indicated that the surface flame-retardant FNFs had a high limiting oxygen index (LOI) and rapidly self-extinguished in a horizontal combustion test and passed a UL-94 V-0 test. At the same time, the CO and CO₂ emissions were greatly reduced, and the carbon residue rate was increased. In addition, the introduction of the coating improved the mechanical properties of the FNFs. Therefore, this simple and efficient UV-curable surface flame-retardant strategy has broad application prospects in the field of fire protection.