Polymer Composites Based on Glycol-Modified Poly(Ethylene Terephthalate) Applied to Additive Manufacturing Using Melted and Extruded Manufacturing Technology

The Influence of Selected Fillers on the Functional Properties of Polycarbonate Dedicated to 3D Printing Applications

Additive manufacturing is still the fastest-developing technology in the modern world. Three-dimensional printing has become popular due to the method's numerous advantages, such as its short time and low cost, compared to conventional methods such as injection molding. Therefore, the demand for new materials and material systems that will be characterized by the desired functional properties is clearly growing. As part of this work, work was carried out on the development and preparation of new polymer composites dedicated to 3D printing applications, especially in FDM/FFF/MEM technologies. The influence of the content and amount of fillers, such as silica modified with alumina (S) and bentonite modified with a quaternary ammonium salt (B), on the functional properties of a commercially available fiber made of traditional plastic, such as polycarbonate, obtained in the form of a filament (PCF), was determined. It was found that the addition of B significantly increased the fluidity of the polymer, the introduction of a filler in the amount of 1.5% allowed to obtain a result that was 6% higher compared to PCF (16.8 g/10 min), while the amount of 3% was 20% higher. The obtained mass melt flow rate (MFR) results were confirmed by determining the viscosity of the produced polymer composites. Satisfactory results of mechanical properties were obtained, including the following: it was found that the introduced modified fillers increased the elasticity of the material. The introduction of modified silica resulted in a reduction in Young's modulus by 10.02% at the content of 0.5% S and at 1% S by 8.64% compared to the polymer. The introduced modified filler S significantly increased the thermostability of polycarbonate (T5% equal to 449 °C) by 23 °C for PCF/0.5% S and 14 °C for PCF/1% S, respectively. The SEM and WAXS results confirmed the appropriate dispersion of the fillers in the polymer matrix, which indicates well-selected conditions for the homogenization process of the components and the subsequent production of samples. Detailed characterization of the influence of selected fillers on the functional properties of the polymer matrix-polycarbonate allowed for an increase in the range of polymer composites and their use in rapid prototyping technologies, as well as supplementing the literature on databases regarding the characteristics of the obtained materials.

Hybrid Composite Materials Made of Recycled PET and Standard Polymer Blends Used in Civil Engineering

This paper presents an investigation of the tensile properties of two composites made from recycled polyethylene tetraphthalate, cement-concrete mix and standard polymer-based adhesive mixes, used in the construction industry. To describe tensile behavior, experimental measurements of each component of the resulting composite materials were processed in detail. It presents the possibilities of modifying materials suitable for building structures and at the same time provides an opportunity to get rid of polyethylene tetraphthalate (PET), which has already been recycled several times. Because the resulting composite contains a majority of the composite composition on a fragile basis, its use in practice depends on its simple thrust properties. In this paper, a study of the most important mechanical properties of a previously unused composite is presented. These properties were obtained experimentally using an innovative tensile test method.

Polymer Composites Based on Polycarbonate/Acrylonitrile-Butadiene-Styrene Used in Rapid Prototyping Technology

As part of this work, polymer composites based on polycarbonate/acrylonitrile-butadiene-styrene (PC/ABS) were obtained and used in 3D printing technology, particularly Melted Extrusion Modeling (MEM) technology. The influence of selected fillers on the properties of the obtained composites was investigated. For this purpose, modified fillers such as silica modified with alumina, bentonite modified with a quaternary ammonium salt, and hybrid lignin/silicon dioxide filler were introduced into the PC/ABS matrix. In the first part of this work, polymer blends and their composites containing 1.5-3 wt. of the filler were used to obtain the filament using the proprietary technological line. Moldings for testing the performance properties were obtained using additive manufacturing techniques and injection molding. In the subsequent part of this work, rheological properties (mass flow rate (MFR) and viscosity curves) and mechanical properties (Rockwell hardness and static tensile strength with Young's modulus) were examined. The structures of the obtained composites were also determined by scanning electron microscopy (SEM/EDS). The obtained results confirmed the results obtained from a wide-angle X-ray scattering analysis (WAXS). In turn, the physicochemical properties were characterized on the basis of the results of tests using thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). Based on the obtained results, it was found that the introduced modified additives had a significant impact on the processing and functional properties of the tested composites.

Hybrid Polymer Composites Based on Polystyrene (PS) Used in the Melted and Extruded Manufacturing Technology

As part of the work, innovative hybrid polymer composites dedicated to rapid prototyping, especially for 3D printing with the melted and extruded manufacturing (MEM) technique, were developed. For this purpose, the influence of modified fillers, such as alumina-modified silica, bentonite modified with quaternary ammonium salt, and lignin/silicon dioxide hybrid filler, on the functional properties of polystyrene-based composites was investigated. The introduced additives were selected to improve the processing properties of polystyrene (PS), in particular its thermal stability, while maintaining good mechanical properties. In the first part of the work, using the proprietary technological line, filaments from unfilled PS and its composites were obtained, which contain modified fillers in the amount of 1.5% to 3.0% by weight. Samples for testing functional properties were obtained by 3D printing in MEM technology and injection technique. The rheological properties-mass melt flow rate (MFR), viscosity, and mechanical properties-are presented in the further part of the work. The size and the respective dispersion in the polystyrene polymer matrix of the fillers used were determined by scanning electron microscopy with energy dispersion spectroscopy (SEM/EDS). The correct dispersion of additives in PS was also confirmed by wide-angle X-ray analysis (WAXS). A significant improvement in the thermal stability of the obtained composites after the introduction of fillers into the polymer matrix was confirmed on the basis of thermogravimetric analysis (TGA). The remaining tests of physicochemical properties, differential scanning calorimetry (DSC), and infrared spectroscopy with Fourier transform (FT-IR) allowed us to state no significant changes in relation to polystyrene. The obtained test results allowed us to conclude that the amount and type of fillers used in the PS polymer matrix significantly affect the performance properties of the tested hybrid composites. The composites obtained as part of the work can be successfully used in rapid prototyping technologies, especially for the production of details originally designed from PS, which are required to have higher thermal stability than is guaranteed only by the polymer matrix.