Calcined Co(II)-Chelated Polyazomethine as Cathode Catalyst of Anion Exchange Membrane Fuel Cells

Co(II)-Chelated Polyimines as Oxygen Reduction Reaction Catalysts in Anion Exchange Membrane Fuel Cells

In this paper, a cobalt (Co)-chelated polynaphthalene imine (Co-PNIM) was calcined to become an oxygen reduction reaction (ORR) electrocatalyst (Co-N-C) as the cathode catalyst (CC) of an anion exchange membrane fuel cell (AEMFC). The X-ray diffraction pattern of CoNC-1000A900 illustrated that the carbon matrix develops clear C(002) and Co(111) planes after calcination, which was confirmed using high-resolution TEM pictures. Co-N-Cs also demonstrated a significant ORR peak at 0.8 V in a C-V (current vs. voltage) curve and produced an extremely limited reduction current density (5.46 mA cm-2) comparable to commercial Pt/C catalysts (5.26 mA cm-2). The measured halfway potential of Co-N-C (0.82 V) was even higher than that of Pt/C (0.81 V). The maximum power density (Pmax) of the AEM single cell upon applying Co-N-C as the CC was 243 mW cm-2, only slightly lower than that of Pt/C (280 mW cm-2). The Tafel slope of CoNC-1000A900 (33.3 mV dec-1) was lower than that of Pt/C (43.3 mV dec-1). The limited reduction current density only decayed by 7.9% for CoNC-1000A900, compared to 22.7% for Pt/C, after 10,000 redox cycles.

2,6-Diaminopyridine-Based Polyurea as an ORR Electrocatalyst of an Anion Exchange Membrane Fuel Cell

In order to yield more Co(II), 2,6-diaminopyridine (DAP) was polymerized with 4,4-methylene diphenyl diisocyanates (MDI) in the presence of Co(II) to obtain a Co-complexed polyurea (Co-PUr). The obtained Co-PUr was calcined to become Co, N-doped carbon (Co-N-C) as the cathode catalyst of an anion exchange membrane fuel cell (AEMFC). High-resolution transmission electron microscopy (HR-TEM) of Co-N-C indicated many Co-Nx (Co covalent bonding with several nitrogen) units in the Co-N-C matrix. X-ray diffraction patterns showed that carbon and cobalt crystallized in the Co-N-C catalysts. The Raman spectra showed that the carbon matrix of Co-N-C became ordered with increased calcination temperature. The surface area (dominated by micropores) of Co-N-Cs also increased with the calcination temperature. The non-precious Co-N-C demonstrated comparable electrochemical properties (oxygen reduction reaction: ORR) to commercial precious Pt/C, such as high on-set and half-wave voltages, high limited reduction current density, and lower Tafel slope. The number of electrons transferred in the cathode was close to four, indicating complete ORR. The max. power density (P_max) of the single cell with the Co-N-C cathode catalyst demonstrated a high value of 227.7 mWcm^-2.

Recent advances in transition metal nitrides for hydrogen electrocatalysis in alkaline media: From catalyst design to application

Hydrogen (H2) has been considered an ideal alternative energy source for solving energy supply security and greenhouse gas reduction. Although platinum group metal (PGM) catalysts have excellent performance in hydrogen electrocatalysis, their scarcity and high cost limit their industrial application. Therefore, it is necessary to develop low-cost and efficient non-PGM catalysts. Transition metal nitrides (TMNs) have attracted much attention because of their excellent catalytic performance in hydrogen electrochemistry, including hydrogen evolution reaction (HER)/hydrogen oxidation reaction (HOR). In this paper, we review and discuss the mechanism of HER/HOR in alkaline media. We compare and evaluate electrocatalytic performance for the HER/HOR TMN catalysts recently reported. Finally, we propose the prospects and research trends in sustainable alkaline hydrogen electrocatalysis.

Synthesis and Characterization of Schiff Base Polymers via Metal Coordination and Its Application in Infrared Stealth Coating

In order to reduce the infrared emissivity to meet the requirements of modern warfare for infrared stealth materials, we prepared the polymers containing Schiff base moieties using polyetheramine and 2,6-pyridinedicarboxaldehyde by solution polycondensation and coordinated with Ni2+, Cu2+, and Sm3+ ions to prepare organic coatings. The structure and the thermal and mechanical properties of the coatings were studied in detail. Meanwhile, the effect of the conductivity change of coordination polymers on infrared emissivity was studied systematically. The results showed the polymer coordinated with Sm3+ ions had the lowest energy band gap, which was 2.99 eV, and the best electrical conductivity of 3.54 × 10−4 S/cm compared with Ni2+ and Cu2+ coordination polymers. The infrared emissivity was the lowest in the 2–22 μm infrared waveband range, which reached 0.58, suggesting the polymers containing Schiff base moieties and their coordination polymers may have a great potential to be applied as infrared stealth materials in military applications.

Cobalt-Based Cathode Catalysts for Oxygen-Reduction Reaction in an Anion Exchange Membrane Fuel Cell

A novel cobalt-chelating polyimine (Co-PIM) containing an additional amine group is prepared from the condensation polymerization of diethylene triamine (DETA) and terephthalalehyde (PTAl) by the Schiff reaction. A Co, N-co-doped carbon material (Co-N-C), obtained from two-stage calcination in different gas atmospheres is used as the cathode catalyst of an anion exchange membrane fuel cell (AEMFC). The Co-N-C catalyst demonstrates a CoNx-type single-atom structure seen under high-resolution transmission electron microscopy (HRTEM). The Co-N-C catalysts are characterized by FTIR, XRD, and Raman spectroscopy as well. Their morphologies are also illustrated by SEM and TEM micrographs, respectively. Surface area and pore size distribution are found by BET analysis. Co-N-C catalysts exhibit a remarkable oxygen reduction reaction (ORR) at 0.8 V in the KOH(aq). From the LSV (linear-sweeping voltammetry) curves, the onset potential relative to RHE is 1.19–1.37 V, the half wave potential is 0.73–0.78 V, the Tafel slopes are 76.9–93.6 mV dec⁻¹, and the average number of exchange electrons is 3.81. The limiting reduction current of CoNC-1000A-900 is almost the same as that of commercial 20 wt% Pt-deposited carbon particles (Pt/C), and the max power density (P_max) of the single cell using CoNC-1000A-900 as the cathode catalyst reaches 361 mW cm⁻², which is higher than Pt/C (284 mW cm⁻²).