The Re-/Up-Cycling of Wood Waste in Wood-Polymer Composites (WPCs) for Common Applications

Injection Molding Condition Effects on the Mechanical Properties of Coconut-Wood-Powder-Based Polymer Composite

This study investigates the mechanical properties of coconut sawdust powder combined with polypropylene (PP). The effect of compatibility content, wood powder (WP) content, and injection molding parameters on the properties of coconut wood powder composite (WPC) is evaluated. The results could be used to figure out the optimal mechanical properties such as tensile strength, elongation, elastic modulus, and flexural strength by selecting suitable parameters and composition. The bonding between the WP particles and the PP matrix is good, and the WP is uniformly distributed across the composite matrix, as indicated in the scanning electron microscopy (SEM) results. Interestingly, with the presence of the compatibilizer oleamide, increasing the WP content from 20 wt.% to 40 wt.% did not result in WP accumulation in the composite matrix. Notably, at 20 wt.% WP, the elongation is the highest (at 7.40 wt.%), while at 30 wt.% WP, the elastic modulus reaches the highest value. The maximum ultimate tensile strength (UTS) value is obtained at 35 wt.% WP. Higher WP mostly results in greater flexural strength and shore D hardness. At 40 wt.% WP, the WPC achieves its peak shore D hardness of 77.6. The Taguchi results suggest that WP content is the most critical factor in the UTS value of coconut WPCs. The filling pressure ranks second, followed by the packing pressure. Finally, unlike the other characteristics, the melt temperature has a minimal impact on the UTS value.

Evaluation of Starch-Garlic Husk Polymeric Composites through Mechanical, Thermal, and Thermo-Mechanical Tests

The present work evaluates the influence of different properties of composite materials from natural sources. Films were prepared using the evaporative casting technique from corn starch reinforced with a waste material such as garlic husk (GH), using glycerin as a plasticizer. The results of the syntheses carried out demonstrated the synergy between these materials. In the morphological analysis, the compatibility and adequate dispersion of the reinforcer in the matrix were confirmed. Using Fourier transform infrared spectroscopy (FTIR), the interaction and formation of bonds between the matrix and the reinforcer were confirmed by the presence of some signals such as S-S and C-S. Similarly, thermogravimetric analysis (TGA) revealed that even at low concentrations, GH can slightly increase the decomposition temperature. Finally, from the results of dynamic mechanical analysis (DMA), it was possible to identify that the storage modulus increases significantly, up to 115%, compared to pure starch, especially at low concentrations of the reinforcer.