Mechanical Properties' Strengthening of Photosensitive 3D Resin in Lithography Technology Using Acrylated Natural Rubber

Digital Light Processing Route for 3D Printing of Acrylate-Modified PLA/Lignin Blends: Microstructure and Mechanical Performance

In this study, digital light processing (DLP) was utilized to generate 3D-printed blends composed of photosensitive acrylate-modified polylactic acid (PLA) resin mixed with varying weight ratios of lignin extracted from softwood, typically ranging from 5 wt% to 30 wt%. The microstructure of these 3D-printed blends was examined through X-ray microtomography. Additionally, the tensile mechanical properties of all blends were assessed in relation to the weight ratio and post-curing treatment. The results suggest that post-curing significantly influences the tensile properties of the 3D-printed composites, especially in modulating the brittleness of the prints. Furthermore, an optimal weight ratio was identified to be around 5 wt%, beyond which UV light photopolymerization experiences compromises. These findings regarding acrylate-modified PLA/lignin blends offer a cost-effective alternative for producing 3D-printed bio-sourced components, maintaining technical performance in reasonable-cost, low-temperature 3D printing, and with a low environmental footprint.

Sustainable Materials with Improved Biodegradability and Toughness from Blends of Poly(Lactic Acid), Pineapple Stem Starch and Modified Natural Rubber

Poly(lactic acid) (PLA), derived from renewable resources, plays a significant role in the global biodegradable plastic market. However, its widespread adoption faces challenges, including high brittleness, hydrophobicity, limited biodegradability, and higher costs compared to traditional petroleum-based plastics. This study addresses these challenges by incorporating thermoplastic pineapple stem starch (TPSS) and modified natural rubber (MNR) into PLA blends. TPSS, derived from pineapple stem waste, is employed to enhance hydrophilicity, biodegradability, and reduce costs. While the addition of TPSS (10 to 40 wt.%) marginally lowered mechanical properties due to poor interfacial interaction with PLA, the inclusion of MNR (1 to 10 wt.%) in the PLA/20TPSS blend significantly improved stretchability and impact strength, resulting in suitable modulus (1.3 to 1.7 GPa) and mechanical strength (32 to 52 MPa) for diverse applications. The presence of 7 wt.% MNR increased impact strength by 90% compared to neat PLA. The ternary blend exhibited a heterogeneous morphology with enhanced interfacial adhesion, confirmed by microfibrils and a rough texture on the fracture surface. Additionally, a downward shift in PLA's glass transition temperature (Tg) by 5-6 °C indicated improved compatibility between components. Remarkably, the PLA ternary blends demonstrated superior water resistance and proper biodegradability compared to binary blends. These findings highlight the potential of bio-based plastics, such as PLA blends with TPSS and MNR, to contribute to sustainable economic models and reduce environmental impact for using in plastic packaging applications.

Influence of Post-Processing on the Degree of Conversion and Mechanical Properties of 3D-Printed Polyurethane Aligners

BACKGROUND

This study explores how different post-processing methods affect the mechanical properties and degree of conversion of 3d-printed polyurethane aligners made from Tera Harz TC-85 resin.

METHODS

Using Fourier-transform infrared (FTIR) spectroscopy, the degree of conversion of liquid resin and post-processed materials was analyzed. This investigation focused on the effects of various post-curing environments (nitrogen vs. air) and rinsing protocols (centrifuge, ethanol, isopropanol, and isopropanol + water). The assessed mechanical properties were flexural modulus and hardness.

RESULTS

The degree of conversion showed no significant variance across different groups, though the polymerization environment influenced the results, accounting for 24.0% of the variance. The flexural modulus varied considerably, depending on both the rinsing protocol and the polymerization environment. The standard protocol (centrifugation followed by nitrogen polymerization) exhibited the highest flexural modulus of 1881.22 MPa. Hardness testing revealed significant differences, with isopropanol treatments showing increased resistance to wear in comparison to the centrifuge and ethanol rinse treatments.

CONCLUSIONS

This study conclusively demonstrates the adverse effects of oxygen on the polymerization process, underscoring the critical need for an oxygen-free environment to optimize material properties. Notably, the ethanol rinse followed by nitrogen polymerization protocol emerged as a viable alternative to the conventional centrifuge plus nitrogen method.