Influence of photoirradiation conditions on dentin bond durability and interfacial characteristics of universal adhesives

Effect of air-blowing temperature and water storage time on the bond strength of five universal adhesive systems to dentin

The purpose of this study was to evaluate the air-blowing temperature and water storage time on the micro-tensile bond strength (μTBS) of five universal adhesive systems to dentin. The bond strength with two different air-blowing temperatures (60±2ºC and 23±2ºC) was measured after water storage at 37ºC for 24 h and 100 days respectively. The fracture surface on dentin side was observed by scanning electron microscope (SEM). Three-way ANOVA revealed a significant effect of universal system (p<0.001) and air-blowing temperature (p<0.001) on bond strength to dentin except water-storage time (p=0.145). The interaction within three factors was significantly different (p<0.001). It could be concluded that the μTBS of universal systems to dentin was material-depended. The higher and more stable bonding performance of universal systems on dentin could be achieved by air-blowing at 60±2ºC temperature. In addition, the quantity of voids in the adhesive layer of aceton-based universal adhesive was significantly reduced by higher temperature.

Aged Translucent Aesthetic Zirconia: Bond Strength Analysis

Objective This study evaluates the bond strength of two compositions of aesthetic translucent zirconia (TZ).

Materials and Methods For this evaluation, test specimens were prepared from ICE Zirkon TZ and Prettau Anterior zirconia (PAZ) that were stored in distilled water at 37°C for two time periods: T1 (24 h) and T2 (90 days) to simulate aging. Two factors were evaluated for the samples—ceramic and aging time. The samples were subjected to tests of microshear strength and fracture type and were evaluated using scanning electron microscopy.

Results The results were analyzed using the D'Agostino test, analysis of variance, and Tukey's test ( p < 0.01). Statistically significant differences were observed for ceramic type and aging time.

Conclusion The results showed that PAZ provides significantly superior performance to TZ at the two aging times evaluated.

Universal Adhesives: Setting Characteristics and Reactivity with Dentin

The aim of the study was to evaluate the performance of six commercially available universal dental adhesives: Adhese Universal (ADU), All-Bond Universal (ABU), Clearfil Universal Bond Quick (CBQ), G-Premio Bond (GPB), Prelude One (PRO) and Scotchbond Universal (SBU). The properties tested were: (a) degree of C=C conversion (DC%); (b) Vickers micro-hardness (VHN); (c) extent of oxygen inhibition (OI/μm), all related with the adhesive film properties; (d) extent of dentin demineralisation (DM%), insoluble salt formation (AS%); and (e) shear bond strength (SBS, self-etch mode) related to the adhesive-dentin interactions. Statistical analysis (α = 0.05) was performed by one-way ANOVA and Tukey's test (DC%, VHN, OI, DM% AS%) and Weibull analysis (SBS, σ_0-β). The DC ranged from 67.2-82.5% (all >GPB), OI from 5.6-18.6 μm (SBU > ADU, GPB, ABU > CBQ > PRO), microhardness from 1.1-6.6 VHN (SBU > ADU > ABU > CBQ > PRO > GPB: not measurable), DM from 69.3% (GPB) to 16-12.5% (CBQ, SBU, ADU) and 13.2-10.6% (ABU, ADU, PRO), in homogeneous groups and AS from 26-15.9% (ABU, CBQ > GPB, PRO, ADU, SBU). For SBS the σ₀ (characteristic life) ranged from 29.3-16.6 MPa (CBQ, ADU, ABU, SBU > PRO > GPB), the β (reliability) from 5.1-9.7 (p > 0.05). All failure modes were of mixed type (adhesive and composite cohesive). Although all these adhesives were based on the 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) adhesive monomer, the different co-monomers, solvents and catalysts led to variations in their film properties, reactivity and bonding capacity with dentin.