Fracture resistance of Nd:YAG laser-welded cast titanium joints with various clinical thicknesses and welding pulse energies

Applications of Laser Welding in Dentistry: A State-of-the-Art Review

The dental industry without lasers is inconceivable right now. This captivating technology has outlasted other possible alternative technologies applied in dentistry in the past due to its precision, accuracy, minimal invasive effect as well as faster operating time. Other alternatives such as soldering, resistance (spot) welding, plasma (torch) welding, and single pulse tungsten inert gas welding have their pros and cons; nevertheless, laser welding remains the most suitable option so far for dental application. This paper attempts to give an insight into the laser principle and types of lasers used for dental purposes, types of dental alloys used by the dentist, and effect of laser parameters on prosthesis/implants. It is apparent from the literature review that laser assisted dental welding will continue to grow and will become an unparalleled technology for dental arena.

Fatigue limits of titanium-bar joints made with the laser and the electric resistance welding techniques: microstructural characterization and hardness properties

Fatigue behavior of the titanium bars is of utmost importance for the safe and reliable operation of dental implants and prosthetic constructions based on these implants. To date, however, only few data are available on the fatigue strength of dental prostheses made with electric resistance welding and laser welding techniques. This in-vitro study highlighted that although the joints made with the laser welding approach are credited of a superior tensile strength, joints made with electric resistance welding exhibited double the minimum fatigue strength with respect to the joints made with laser welding (120 vs 60 N).

Temporal pulse shaping: a key parameter for the laser welding of dental alloys

This study aims to describe the effect of pulse shaping on the prevention of internal defects during laser welding for two dental alloys mainly used in prosthetic dentistry. Single spot, weld beads, and welds with 80 % overlapping were performed on Co-Cr-Mo and Pd-Ag-Sn cast plates with a pulsed neodymium-doped yttrium aluminum garnet (Nd:YAG) laser. A specific welding procedure using adapted parameters to each alloy was completed. All the possibilities for pulse shaping were tested: (1) the square pulse shape as a default setting, (2) a rising edge slope for gradual heating, (3) a falling edge slope to slow the cooling process, and (4) a combination of rising and falling edges. The optimization of the pulse shape is supposed to produce defect-free welds (crack, pores, voids). Cross-section SEM observations and Vickers microhardness measurements were made. Pd-Ag-Sn was highly sensitive to hot cracking, and Co-Cr-Mo was more sensitive to voids and small porosities (sometimes combined with cracks). Using a slow cooling ramp allowed a better control on the solidification process for those two alloys always preventing internal defects. A rapid slope should be preferred for Co-Cr-Mo alloys due to its low-laser beam reflectivity. On the opposite, for Pd-Ag-Sn alloy, a slow rising slope should be preferred because this alloy has a high-laser beam reflectivity.