Shear bond strength and SEM morphology evaluation of different dental adhesives to enamel prepared with ER:YAG laser

Impact of acid and laser etching of enamel on microleakage in different adhesive systems

This study aimed to evaluate the microleakage of light-cured and self-cured adhesives on enamel surfaces selectively etched with Er, Cr: YSGG laser or 35% phosphoric acid. A total of 60 class V cavities were prepared 1 mm above the cemento-enamel junction (CEJ). The specimens were randomly divided into six groups. Group 1: Clearfil SE Bond with no conditioning, Group 2: Tokuyama Universal Bond with no conditioning, Group 3: Clearfil SE Bond conditioned with 35% phosphoric acid, Group 4: Tokuyama Universal Bond conditioned with 35% phosphoric acid, Group 5: Clearfil SE Bond conditioned with Er, Cr: YSGG laser and Group 6: Tokuyama Universal Bond conditioned with Er, Cr: YSGG laser. Microleakage was evaluated qualitatively (visually) and quantitatively (ImageJ). The data were analyzed using IBM SPSS V23 and submitted to Kruskal-Wallis and Wilcoxon tests. The significance level was set at p < 0.05. In all evaluation methods, the microleakage scores exhibit significant differences (p*<0.001). Group 1 and Group 3 exhibited similar and lower microleakage values than the Group 5. In the occlusal margin, the microleakage values were similar in Group 2, Group 4, and Group 6, whereas in the gingival margin Group 4 showed significantly lower leakage compared to Group 2. Regardless of the etching protocols and adhesive systems used, less microleakage was observed on the occlusal surface than on the gingival surface. Phosphoric acid etching provides better results than laser etching for enamel surface treatment on both occlusal and gingival surfaces.

Effects of Er, Cr: YSGG Laser on Shear Bond Strength of the Orthodontic Brackets for 5 and 10 Seconds: An In Vitro Study

Objectives. The study designed to compare the effect of erbium, chromium: yttrium-scandium-gallium-garnet (Er, Cr: YSGG) laser at different power outputs and short periods of time (5 and 10 s) and acid etching on the shear bond strength (SBS) and failure mode of metallic orthodontic brackets. Material and methods. A total of sixty-nine human premolars extracted for orthodontic purposes were used. 60 teeth were randomly assigned to one of the five treatment groups. (n = 12): group 1: 37% phosphoric acid etching and groups 2–5: the enamel surface irradiated by the Er, Cr: YSGG laser operated at different power outputs (1 W, 1.5 W, 2 W, and 2.5 W), each laser group was divided into two subgroups (n = 6) according to exposure time (5 s and 10 s). Nine teeth were not subjected to SBS testing but were prepared for scanning electron microscopy (SEM). The nonparametric Kruskal–Wallis test was used to evaluate the data; the SBS and adhesive remanent index (ADI) were evaluated. Results. The mean SBS for all laser groups and the acid-etched group were comparable, with no significant differences except for the 1 W group for 5 and 10 s and the 1.5 W group for 5 s. For the ARI scores, no statistically significant difference was found among the groups ( $P=0.059$ ), and the majority of the samples had ARI type 2 or 3. Conclusion. The laser irradiation at 2 and 2.5 W for 5 s was similar to that produced by acid etching, whereas the laser irradiation at 2 and 2.5 W at 10 s was higher compared with that obtained with acid etching and adequate to etch the enamel.

Does laser etching have an effect on application mode of a universal adhesive?-A microleakage and scanning electron microscopy evaluation

This study aimed to evaluate the microleakage of a universal adhesive's different application modes incorporated with Er,Cr:YSGG laser on Class V resin composite restorations. Sound human molar teeth (n = 30) were used for microleakage evaluations. Specimens with 60 standardized Class V cavities were divided into five groups according to the adhesive modes of universal adhesive, Adhese Universal (n = 12). Group 1-etch-and-rinse mode with phosphoric acid; Group 2-etch-and-rinse mode with Er,Cr:YSGG laser; Group 3-selective-etch mode with phosphoric acid; Group 4-selective-etch mode with Er,Cr:YSGG laser; Group 5-self-etch. After restorations were performed with a resin composite, Tetric N-Ceram, the specimens were polished and subjected to thermocycling (10,000X). Following immersion in 0.5% basic fuschin for a day, the teeth were sectioned and the degree of microleakage was determined along the tooth-resin composite interface using a light microscopy(40X). Five specimens from each group were examined by scanning electron microscopy. The Kruskal-Wallis, Siegel Castello, and Wilcoxon tests were used for statistical analyses (α = .05). At the enamel margins, significant differences were obtained among the groups (p < .05). Significantly higher microleakage scores were detected in Group 5 in comparison with Groups 1, 2, and 3. There were no significant differences between different adhesive strategies at the dentin margins (p > .05). While analyzing enamel and dentin microleakage scores, no statistically significant differences were observed in Groups 4 and 5 (p > .05). The laser application time and the adhesive modes of universal adhesives could affect the microleakage at the enamel margins. Different adhesive modes of universal adhesives combined with laser etching had no influence on the microleakage scores of dentin margins.

Effect of Erbium Laser on Microtensile Bond Strength of Fissure Sealant in Primary Teeth: An in vitro Study

Background:

Laser etching has several advantages as compared with conventional acid etching. However, results of earlier studies on conditioning surfaces with erbium, chromium:yttrium–scandium–gallium–garnet (Er, Cr:YSGG) before application of the fissure sealant have been inconclusive.

Aim:

The study aimed to evaluate the microtensile strength of resin-based fissure sealant bonded to primary enamel conditioned by Er, Cr:YSGG laser with varying power outputs.

Materials and Methods:

Fifty sound primary first molars were randomized into the following five groups based on pretreatment choice: Group 1: 3.5 W laser etching + acid etching; Group 2: 2.5 W laser etching + acid etching; Group 3: 3.5 W laser etching with no acid; Group 4: 2.5 W laser etching with no acid and Group 5: acid etching with no laser. Acid etch was performed with 35% orthophosphoric acid for 30 s. Laser etching was performed with Er, Cr:YSGG (2780 nm) laser using G6 tips and 600 μm diameter, 2.5 W or 3.5 W power outputs, pulse duration of 140 μs and a repetition rate of 20 Hz. Sealant was applied on the buccal surface followed by an incremental buildup with composite resin. Microtensile bond strength was assessed and compared among the five groups using one- and two-way ANOVA.

Results:

There was no statistical difference in the mean bond strength between groups except in Group 4 (9.66 MPa) (Group 1: 15.57 MPa; Group 2: 14.18 MPa; Group 3: 14.78 MPa; Group 5: 14.63 MPa).

Conclusion:

Pretreatment with 3.5 W Er, Cr:YSGG laser alone results in microtensile bond strengths similar to that produced by acid etching, indicating that enamel etching using 3.5 W Er, Cr:YSGG laser would result in the long-term success of pit and fissure sealants in primary teeth.

Dental Adhesion to Erbium-Lased Tooth Structure: A Review of the Literature

OBJECTIVE

The aim of the present study was to conduct a review of the literature about adhesion on erbium laser prepared cavities, related to the specific conditions of the irradiated dentin substrate and the effects on bond strength values.

BACKGROUND DATA

Advances in adhesive restorative techniques significantly influenced modern restorative dentistry. The concept of "minimally invasive dentistry" aims to perform more conservative treatment of cavities in which the removal of sound dentin is no longer necessary. This approach, which relies on the concept of adhesion of restorative materials to the mineralized dental tissues, is considered to be a contemporary outcome in dentistry. Similarly, laser technology in restorative dentistry opened new possibilities and strategies as alternatives to conventional treatment. Considering the clinical aspects of the use of erbium lasers for caries removal, cavity preparations, and substrate conditioning, treatment with lasers can be considered to be an efficient technique with wide acceptance by patients.

METHODS

Computerized and manual searches were conducted for studies through 2015 that addressed the topic.

RESULTS

According to the literature, there is no defined standard protocol concerning the information that articles must provide, making a definitive protocol very difficult to establish. Data varied from the type of adhesive and resin composite used, substrate, and parameters (power, energy density, pulse duration, irradiation time, distance, cooling system) to the bond strength test methodology used.

CONCLUSIONS

Further studies are necessary in order to define a standard protocol with positive results and higher bond strength values when using erbium lasers. Detailed information concerning laser parameters should be implemented. Also, longitudinal clinical studies should be developed in the search for new parameters that behave favorably in the irradiated substrate.

The Effect of Energy Densities on the Shear Bond Strength of Self-Adhering Flowable Composite to Er:YAG Pretreated Dentin

Objective. To investigate the shear bond strength of self-adhering flowable resin composite, to dentin, after exposing it to Er:YAG laser radiation, at different energy densities. Materials and Methods. Sixty freshly extracted human third molars were randomly divided into five groups (n = 12). In the control group, dentin was left unirradiated, whereas, in the other four groups, dentin was irradiated with Er:YAG laser in noncontact mode (MSP mode = 100 µs; 10 Hz; beam diameter: 1.3 mm; speed of 1 mm/second; air 6 mL/min; and water 4 mL/min), and respectively, with the following level of energy (50 mJ, 60 mJ, 80 mJ, and 100 mJ). Then, self-adhering flowable resin composite was bonded to all prepared dentin surfaces. Shear bond strength (SBS) was applied and fractured surfaces were examined using scanning electron microscopy. Results. SBS values showed significant differences in 60 mJ (P < 0.05) compared to other groups. Morphological evaluation revealed tags or plugs in dentinal tubules, especially when 60 mJ and 80 mJ were used. All four groups tended to leave more residues on the dentin surface, than the control group. Conclusion. Er:YAG dentin irradiation may enhance SBS of the self-adhering flowable resin composite when it is used at the appropriate low level of energy density.

Microshear Bond Strength of OptiBond All-in-One Self-adhesive Agent to Er:YAG Laser Treated Enamel After Thermocycling and Water Storage

Introduction: This study aimed to compare the microshear bond strength of composite to enamel treated with Erbium-Doped Yttrium Aluminum Garnet (Er:YAG) laser using a self-etch one step bonding agent. Methods: Seventy-six enamel surfaces were prepared from 38 sound human third molar teeth. Specimens were randomly divided into four groups of 18. The enamel surface in half the specimens was irradiated with Er:YAG laser. One extra specimen from each group was evaluated under a scanning electron microscope (SEM). Composite micro-cylinders were bonded to the specimen surfaces using OptiBond All-In-One (OB) adhesive agent and stored in distilled water for 24 hours. Half the specimens were thermocycled (2000 cycles) and stored in distilled water at 37°C for three months (TW). The microshear bond strength of composite to enamel was measured using a universal testing machine at a crosshead speed of 1 mm/min. The fractured surfaces were evaluated under a stereomicroscope at ×40 magnification to determine the mode of failure. Data were analyzed using repeated measures analysis of variance (ANOVA) and t test. Results: The mean values (±standard deviation) were 17.96 ± 2.92 MPa in OB group, 22.29 ± 4.25 MPa in laser + OB group, 18.11 ± 3.52 MPa in laser + OB + TW group and 9.42 ± 2.47 MPa in OB + TW group. Repeated measures ANOVA showed that laser irradiation increased the microshear bond strength (P < 0.001). Bond strength decreased when the samples were thermocycled and stored for three months (P < 0.001). The interaction effect of water storage and laser treatment on bond strength was significant (P < 0.05). Conclusion: Enamel surface preparation with Er:YAG laser is recommended to enhance the durability of the bond of self-etch bonding systems to enamel.

Comparative Evaluation of the Etching Pattern of Er,Cr:YSGG & Acid Etching on Extracted Human Teeth-An ESEM Analysis

INTRODUCTION

Etching of enamel and dentin surfaces increases the surface area of the substrate for better bonding of the tooth colored restorative materials. Acid etching is the most commonly used method. Recently, hard tissue lasers have been used for this purpose.

AIM

The aim of the present study was to evaluate and compare the etching pattern of Er,Cr:YSGG and conventional etching on extracted human enamel and dentin specimens.

MATERIALS AND METHODS

Total 40 extracted non-diseased teeth were selected, 20 anterior and 20 posterior teeth each for enamel and dentin specimens respectively. The sectioned samples were polished by 400 grit Silicon Carbide (SiC) paper to a thickness of 1.0 ± 0.5 mm. The enamel and dentin specimens were grouped as: GrE1 & GrD1 as control specimens, GrE2 & GrD2 were acid etched and GrE3 & GrD3 were lased. Acid etching was done using Conditioner 36 (37 % phosphoric acid) according to manufacturer instructions. Laser etching was done using Er,Cr:YSGG (Erbium, Chromium : Ytrium Scandium Gallium Garnet) at power settings of 3W, air 70% and water 20%. After surface treatment with assigned agents the specimens were analyzed under ESEM (Environmental Scanning Electron Microscope) at X1000 and X5000 magnification.

RESULTS

Chi Square and Student "t" statistical analysis was used to compare smear layer removal and etching patterns between GrE2-GrE3. GrD2 and GrD3 were compared for smear layer removal and diameter of dentinal tubule opening using the same statistical analysis. Chi-square test for removal of smear layer in any of the treated surfaces i.e., GrE2-E3 and GrD2-D3 did not differ significantly (p>0.05). While GrE2 showed predominantly type I etching pattern (Chi-square=2.78, 0.05<p>0.10) and GrE3 showed type III etching (Chi-square=4.50, p<0.05). The tubule diameters were measured using GSA (Gesellschaft fur Softwareentwicklung und Analytik, Germany) image analyzer and the 't' value of student 't' test was 18.10 which was a highly significant result (p<.001). GrD2 had a mean dentinal tubule diameter of 2.78μm and GrD3 of 1.09μm.

CONCLUSION

The present study revealed type I etching pattern after acid etching, while type III etching pattern in enamel after laser etching. The lased dentin showed preferential removal of intertubular dentin while acid etching had more effect on the peritubular dentin. No significant differences was observed in removal of smear layer between the acid etched and lased groups. Although diameter of the exposed dentinal tubules was lesser after lased treatment in comparison to acid etching, further long term in vivo studies are needed with different parameters to establish the usage of Er,Cr:YSGG as a sole etching agent.

Microtensile bond strength of a resin-based fissure sealant to Er,Cr:YSGG laser-etched primary enamel

The aim of this study was to evaluate the effect of Er,Cr:YSGG laser pre-treatment alone, or associated with acid-etching, on the microtensile bond strength of a resin-based fissure sealant to primary enamel. Twenty-five human primary molars were randomly divided into five groups including (1) 35 % acid etching, (2) 2.5-W laser etching, (3) 3.5-W laser etching, (4) 2.5-W laser etching + acid etching, and (5) 3.5-W laser etching + acid etching. Er,Cr:YSGG laser was used at a wavelength of 2.780 nm and pulse duration of 140-200 μs with a repetition rate of 20 Hz. Following surface pre-treatment, the fissure sealant (ClinPro™, 3M Dental Products) was applied. Each tooth was sectioned and subjected to microtensile testing. Kruskal-Wallis test was used for statistical analysis. The level of significance was set at p < 0.05. The microtensile bond strength values of group 1 were significantly higher than those of group 2, while no statistically significant difference was detected between groups 1, 3, 4, and 5. It was concluded that 3.5-W laser etching produced results comparable to conventional acid etching technique, whereas 2.5-W laser etching was not able to yield adequate bonding performance.