Bond strength of self-adhesive resin cement to base metal alloys having different surface treatments

Micro-shear bond strength of a novel resin-modified glass ionomer luting cement (eRMGIC) functionalized with organophosphorus monomer to different dental substrates

Objectives

This study aims to assess and compare the micro-shear bond strength (μSBS) of a novel resin-modified glass-ionomer luting cement functionalized with a methacrylate co-monomer containing a phosphoric acid group, 30 wt% 2-(methacryloxy) ethyl phosphate (2-MEP), with different substrates (dentin, enamel, zirconia, and base metal alloy). This assessment is conducted in comparison with conventional resin-modified glass ionomer cement and self-adhesive resin cement.

Materials and methods

In this in vitro study, ninety-six specimens were prepared and categorized into four groups: enamel (A), dentin (B), zirconia (C), and base metal alloys (D). Enamel (E) and dentin (D) specimens were obtained from 30 human maxillary first premolars extracted during orthodontic treatment. For zirconia and metal alloys, 48 disks were manufactured using IPS e.max ZirCAD through dry milling and Co-Cr powder alloy by selective laser milling. Each group was further subdivided into three subgroups (n = 8) according to the luting cement used: (1) Fuji PLUS resin-modified glass ionomer luting cement (FP) as a control cement, (2) modified control cement (eRMGIC), and (3) RelyX U 200 (RU 200) self-adhesive resin cement. The two-way analysis of variance and Tukey's HSD were used to assess the data obtained from measuring the μSBS of the samples.

Results

The results of this study showed that the mean μSBS values of eRMGIC were statistically higher compared to FP in all tested groups (p < 0.001). The mean μSBS results of eRMGIC were non-significantly different from those recorded by RU 200 for all substrates except for the dentin substrate, where the RU200 cement produced significantly higher strength (p < 0.001). The failure modes were limited to a combination of mixed and adhesive failures without pure cohesive failure.

Significance

The functionalization of FP with an organophosphorus co-monomer (2-MEP) directly affects the adhesion performance of the functionalized cement, which may be utilized to develop a new type of acid-base cement. It exhibited a performance comparable to that of resin-based cement and should serve well under different clinical conditions.

Effect of Surface Textures and Fabrication Methods on Shear Bond Strength Between Titanium Framework and Auto-Polymerizing Acrylic Repair Resin

The aim of the study was to evaluate the effect of airborne particle abrasion (using different sizes of alumina particles) on the shear bond strength (SBS) between cast and milled titanium metal frameworks and auto-polymerizing acrylic repair resin. Forty flat cylindrical titanium disks were divided into two main divisions: cast and milled titanium. The two divisions were further subdivided into four groups based on metal surface treatment. Three particle sizes of aluminum oxide air abrasive powders (50µm, 110µm, and 250µm) were used for metal surface treatment by airborne particle abrasion. One group was the control group with no surface treatment. Auto-polymerizing acrylic repair resin was applied to all titanium disks. The specimens were subjected to SBS testing using a universal testing machine (Instron Corporation, Norwood, Massachusetts, United States). Surface evaluation was performed using a scanning electron microscope. One-way ANOVA was used for statistical analysis. The results showed a significant increase in SBS after airborne particle abrasion of both milled and cast titanium groups (p<0.001). The SBS was directly proportional to the size of the aluminum oxide particles. The milled titanium group showed higher SBS values than the cast group when the surface was not treated with alumina particles (p < 0.001) and when the surface was treated with the smaller particle sizes of 50 µm, whereas the cast group demonstrated higher SBS values than the milled group (p < 0.01) when the particle size was increased to 110 µm and 250 µm. It could be concluded that SBS between titanium metal frameworks and auto-polymerizing repair acrylic resin was directly related to the size of the alumina airborne particle abrasives. The fabrication method of the titanium framework also influenced the SBS as the untreated milled frameworks demonstrated favorable SBS values compared to the untreated cast frameworks.

Evaluation of Bond Strength of Resin and Non-resin Cements to Different Alloys

BACKGROUND

 A strong metal-cement bond is one of the many factors that contribute to the clinical success of a fixed prosthesis. Even though it is crucial to create ideal resistance and retention forms during tooth preparation, dental cement must be strong enough to hold the restoration in place in the mouth. The present study set out to evaluate and compare the binding strength of resin modified glass ionomer cement, resin cement, and glass ionomer cement to four different metal alloys: titanium alloy, cobalt-chromium (Co-Cr) alloy, nickel-chromium (Ni-Cr) alloy, and noble metal alloys (silver palladium based).

METHODS

 Two hundred and forty metal alloy specimens were created; these were fashioned from (i) a noble metal alloy (silver-palladium based), (ii) a titanium alloy, (iii) a cobalt-chromium alloy, and (iv) a nickel-chromium alloy. A universal testing machine was used to perform the shear test, and statistical analysis of the result was done using a two-way analysis of variance (ANOVA) test and Bonferroni test.  Results: The Co-Cr alloy among the cement under investigation had the highest mean value of shear bond strength of 8.06 MPa, whereas a noble metal alloy had the lowest shear strength with a mean value of 5.36 MPa. The resin cement demonstrated the highest shear strength with a mean value that was higher than the other two types of cement. The shear bond strength of the examined samples was significantly affected by the interaction of the alloy and cement, according to the two-way ANOVA test (p=0.001).

CONCLUSION

 The results demonstrate that resin cement offers a stronger bond, followed by resin-modified GIC and GIC. The Co-Cr alloy had the highest shear bond strength, followed by Ni-Cr, titanium, and noble metal alloy which showed significantly lower shear strength than the other three alloys.

Comparison of Bond Strength in the Different Class of Resin Cements to Cast and CAD/CAM Co-Cr Alloys

Objectives

Despite the widespread use of resin cements in cementing dental restorations, their bond strength to CAD/CAM base metal alloys is not widely studied. This study aimed to evaluate the microshear bond strength (μSBS) between cobalt-chrome (Co-Cr) alloys fabricated using casting or CAD/CAM methods with three types of resin cements.

Materials and Methods

Fifty Co-Cr blocks were prepared with CAD/CAM or casting technique. Specimens were divided using primer or not and bonded to three types of resin cements: Panavia F2, RelyX Unicem, and Duo-Link. The differences between the mean μSBS values were analyzed using the two-way ANOVA test and Tukey analysis (α = 0.05). The mode of failure was evaluated using a stereomicroscope. In addition, the specimens were examined by scanning electron microscopy (SEM) based on two received signals: backscattered electrons (SEB) and secondary electrons (SEs). One intact alloy specimen in each group was analyzed by energy-dispersive X-ray spectroscopy (EDX).

Results

Most of the specimens in the no-primer group were prematurely debonded. Statistical analyses showed that the interaction between the alloy substrate and cement type was significant (p=0.001). The bond strength of Panavia F2 was significantly higher than Duo-Link in the CAD/CAM group (p=0.001). SEM evaluation confirmed the difference in grain structures, while EDX showed no remarkable difference in the chemical composition of the alloy substrates.

Conclusion

Alloy fabrication technique may influence the bond strength of resin cements. In the CAD/CAM group, cement containing MDP molecules exhibited higher strength than the etch-and-rinse one.

Surface characterization and bonding properties of milled polyetheretherketone dental posts

PEEK has been used in many dental applications except intra-radicular post. The aim of this study is to test polyetheretherketone (PEEK) as a dental post material through tensile bond strength (TBS) and surface roughness (SR), and to compare it with glass-fiber and cast-metal posts. Thus, 60 human maxillary central incisors with a single root were endodontically treated and divided into three groups (n = 20) according to the type of post (Group P: PEEK, Group F: Glass-fiber, Group M: Cast-metal). Appropriate surface treatment was employed for each group and SR was determined by a three-dimensional non-contact profilometer before cementation. All posts were luted to the canal dentin using self-etch resin cement (Panavia F2.0). Pull-out test was performed on a universal testing machine at a speed of 0.5 mm/min crosshead speed until failure, and TBS were calculated. One-way ANOVA, Tukey's HSD, and Pearson chi-squared tests were performed for statistical analyses (α = 0.05). According to the results, group F demonstrated the highest SR (2.93 ± 0.18 µm) and lowest TBS values (10.05 ± 0.53 MPa), while group P exhibited lowest SR (1.37 ± 0.11 µm) and highest TBS values (14.33 ± 0.58 MPa) (p < 0.001). No significant differences in failure modes were identified among groups, mostly adhesive (p = 0.243). As conclusion, PEEK may be a reliable and contemporary option for dental post systems when used with appropriate surface treatment and luting agent. This high-performance polymer may be a novel candidate as a contemporary dental post system due to its superior mechanical, chemical, thermal, and esthetical properties with low risk of fracture.

Influence of Different Surface Treatments on the Shear Bond Strength of Resin Cement to Base Metal Alloys

Introduction: This study aimed to investigate the effect of different surface treatments on the bond strength of resin cement to nickel-chrome (Ni-Cr) alloy. Methods: Forty disk-shaped specimens of Ni-Cr alloy were prepared and divided into 4 groups. In the first group, the specimens' surface was sandblasted with 50 µ Al2 O3 particles. In the second group, the specimens were prepared with the Er:YAG laser. In the third group, the specimens were prepared using the Er:YAG laser after sandblasting. In the fourth group, the specimens' surface was covered with a thin layer of MKZ metal primer after sandblasting. Then the cylinders of composite resin were bonded to the treated metal surfaces using Panavia F2.0 resin cement. All of the samples were subjected to 2000 thermal cycles. The shear bond strength was tested using a universal testing machine at the crosshead speed of 0.5 mm/min. The failure mode was also observed by a stereomicroscope. Data were analyzed using the one-way ANOVA and the Tukey HSD test at a significance level of 0.05. Results: The shear bond strength from the highest to the lowest were as follows: the Er:YAG laser group, the sandblast and MKZ primer combination group, the sandblast group, and the sandblast and Er:YAG laser combination group. The mean differences of shear bond strength between the Er:YAG laser group and the sandblast group (P=0.047) and also between the Er:YAG laser group and the sandblast and Er:YAG laser combination group (P=0.015) were statistically significant. Conclusion: Among the different surface treatments employed in this study, Er:YAG laser treatment increased the shear bond strength between the metal alloy and the resin cement (Pavnavia F2).