Surface Characteristics and Bioactivity of Zirconia (Y-TZP) with Different Surface Treatments

A chlorogenic acid-chitosan complex bifunctional coating for improving osteogenesis differentiation and bactericidal properties of zirconia implants

Poor osteogenesis caused by limited bioactivity and peri-implantitis caused by bacterial colonization are the main challenges affecting the use of zirconia-based materials in dental implants. Accordingly, the development of a surface treatment method with an antibacterial effect and that promotes osteogenesis without damage to cells is crucial for yttrium-stabilized tetragonal zirconia (Y-TZP) implants. Herein, we have developed a functional surface modification strategy whereby a poly (ethylene imine)/hyaluronic acid /chitosan-chlorogenic acid (PEI/HA/CGA-CS) conjugate is deposited on a zirconia surface by the layer-by-layer (LBL) technique, enhancing its osteogenic differentiation and antibacterial activities. The results showed that the PEI/HA/CGA-CS coating improved the wettability of the zirconia surface and maintained stable release of CGA. The PEI/HA/CGA-CS functional coating was found to promote early cell adhesion, proliferation, differentiation, and calcification. The results of bacterial adhesion and activity tests showed that the coating effectively inhibits the proliferation and activity of Porphyromonas gingivalis (P. gingivalis) and Aggregatibacter actinomycetemcomitans (A. actinomycetemcomitans) without impairing the biological activity of osteoblasts. In addition, we found that the PEI/HA/CGA-CS coating enhances the osteogenesis of MC3T3-E1 cells by promoting the protein expression of Nephronectin (NPNT) and activating the Wnt/β-catenin signaling pathway. The above results are of profound significance for the practical application of zirconia-based implants. DATA AVAILABILITY: Data will be made available on request.

Polycrystalline particulates synthesized on zirconia for enhanced bioactivity: An in vitro study

Zirconia is a promising material for dental implant with its excellent biocompatibility, good mechanical properties, and esthetic effect similar to natural teeth. To improve the bioactivity and osteogenic properties of zirconia, pre-sintered zirconia discs were divided into C, T₃ , T₅ , and T₇ group. Group C was as control. T₃ , T₅ , and T₇ groups were soaked in hydrofluoric acid (HF) for 30, 50, and 70 s, respectively. Then, they were placed into CaCl₂ solution and heated in NaOH solution. After sintering, the samples were characterized by scanning electron microscopy, energy dispersive spectrometry, and X-ray diffraction, which confirmed the ZrO₂ polycrystalline particulates in situ synthesized on the treated sample discs. The surface roughness of the treated samples was increased with the prolonged of acid treatment time (p < .05), while the three-point bending strength did not decrease significantly (p > .05). MC3T3-E1 cells were cultured on zirconia discs to evaluate the bioactivity and osteogenic effect of modified zirconia. The living&dead fluorescence staining and CCK-8 assay showed that the specimens were non-toxic and significantly promoted cell proliferation. In addition, the cell proliferation was enhanced with the increase of zirconia surface roughness. Polycrystalline particles modified zirconia were beneficial to cell spreading. After osteogenic induction, MC3T3-E1 cells inoculated on modified zirconia exhibited higher alkaline phosphatase activity, mineralization activity and up-regulated osteogenesis-related gene expression. Above all, in situ synthesized polycrystalline particulates significantly improve the biological activity of zirconia, which will promote the widespread application of zirconia implants.

Pre-cementation procedures' effect on dental zirconias with different yttria content

OBJECTVE

Several pre-cementation procedures have been advocated to enhance adhesion between zirconia and resin-based cement. There is, however, limited documentation on how these pre-treatments affect the strength of zirconia crowns as most tests are performed on discs or bars. The aim was to assess the effect of pre-cementation procedures on fracture mode, fracture strength and cement retention on zirconia.

METHODS

Two dental zirconia materials with different yttria content were assessed (<4 and>5 mol%). Both discs (n = 45) and crown-shaped specimens (n = 30) of the two materials were pretreated with either air-abrasion or hot-etching with KHF₂ and compared with untreated controls with regards to surface roughness, crystallography, wettability, cement adhesion and fracture strength.

RESULTS AND SIGNIFICANCE

Air-abrasion improves adhesion and strength of zirconia with moderate yttria content (<4 mol%). Acid etching with heated KHF₂ showed the best effect on strength and cement retention on zirconia with higher yttria content (>5 mol%). Application of KHF₂ was, however, complicated on crown-shaped specimens. Pre-treatment and cementation protocols should be optimized for different dental zirconias to improve both strength and retention.