Effect of Chlorhexidine and Ethanol Application on Long-term Push-out Bond Strength of Fiber Posts to Dentin

Effect of chlorhexidine and benzalkonium chloride on the long-term push-out bond strength of fiber posts

Background and Aim

Fiber posts are widely used in endodontically treated teeth with extensive loss of coronal structure. The purpose of this study was to investigate immediate and the long-term effects of chlorhexidine (CHX) and benzalkonium chloride (BAC) application, on the push-out bond strength of fiber posts.

Material and Methods

Sixty mandibular premolars were decoronated, and root canal treatment was performed. After post space preparation, the specimens were divided into three groups according to the post space-surface pretreatment (n = 20); no surface treatment (control group-Group 1), 2% CHX application (Group 2), and 1% BAC application (Group 3). A self-curing adhesive cement and an etch and rinse adhesive were used for the cementation of posts. Three sections (one cervical, one middle, and one apical) of 1 mm thickness were prepared from each specimen. A push-out test was performed immediately on the half of the specimen sections (n = 10). The other half of the specimen sections were subjected to 20.000 thermal cycles before applying the push-out test (n = 10). The failure mode of each specimen was observed under a stereomicroscope at ×40 magnification.

Results

The data were analyzed by one-way analysis of variance (ANOVA), Tukey Honestly significant difference (HSD), and Tamhane tests (P = 0.05). The cervical thirds displayed the highest, and the apical thirds showed the lowest values in all groups (P < 0.05), except the control-aged group (P = 0.554). The aged control groups' values were found to be significantly lower than the aged CHX and BAC groups (P < 0.001). Aging significantly reduced the bond strength values of specimens in control groups (P < 0.001). However, aging did not significantly affect the push-out bond strength values of CHX and BAC groups (P > 0.050). The failure types were adhesive between the post and cement (type 1) in all groups, except control-aged group (type 2).

Conclusion

The application of 2% chlorhexidine or 1% BAC may be an essential step that can be taken to preserve the bond strength of fiber posts.

Influence of different intraradicular chemical pretreatments on the bond strength of adhesive interface between dentine and fiber post cements: A systematic review and network meta-analysis

Systematic review and network meta-analyses were performed to answer the question: Do intraradicular chemical pretreatments affect the bond strength of the adhesive interface between dentine and fiber post cements? A literature search was performed in PubMed, Scopus, Web of Science, LILACS, BBO, and Cochrane Library in October 2018 (updated September 2021). In vitro studies that compared the bond strength assessed by push-out tests following at least two dentine chemical treatments prior to fiber post cementation were included. Risk of bias was evaluated. A random-effects Bayesian-mixed treatment comparison model was used to compare push-out bond strength of different chemical pretreatments. SUCRA (surface area under the cumulative ranking) analysis was performed to rank the pretreatments. After removing duplicates and screening titles and abstracts, 61 studies remained. SUCRA analysis showed that the best bond strength values for self-etch, etch-and-rinse, and self-adhesive cements were ethyl acetate (SUCRA: 99.8%), low concentration NaOCl (SUCRA: 83.4%), and grape seed extract (SUCRA: 97.6%), respectively. According to the SUCRA rankings, ethanol was in a good position for all adhesive strategies (SUCRA: 78.6%). The use of chemical pretreatments in intraradicular dentine of endodontically treated teeth depends on the adhesive and cementation strategy. The pretreatment generally associated with the highest bond strength was ethanol.

Post-Space Treatment Influences the Bond Strength In Endodontically Treated Teeth: A Systematic Review and Meta-Analysis of In Vitro Studies

OBJECTIVES

This systematic review of in vitro studies investigated the influence of the post-space treatment used to remove the smear layer on the bond strength of the post to root canal dentin.

METHODS AND MATERIALS

In vitro studies included in this study were identified from PubMed/MEDLINE, Lilacs, and Scopus databases up until March 2019, without limits on publication year or language. Two reviewers independently selected the studies based on the inclusion and exclusion criteria, extracted the data, and evaluated the risk of bias of all studies. A random effects model was used for pairwise meta-analyses (control vs. post-space preparation groups) at a significance level of p<0.05.

RESULTS

Of the 2,832 potentially eligible studies, 453 studies were selected for full-text analysis, and 75 were included in this systematic review. Only one study was considered to have a low risk of bias. Overall, post-space treatment significantly improves the bond strength to root canal dentin (p<0.00001).

CONCLUSION

Post-space treatment has a positive influence on the bond strength of the post to root canal dentin. In this review, the post-space treatments that improve the adhesive resistance of the post were ethanol, sodium hypochlorite, and ethylene diamine tetra-acetic acid (NaOCl + EDTA), NaOCl + EDTA + ultrasound, erbium-doped yttrium aluminium garnet laser (Er:YAG laser), neodymium-doped yttrium aluminium garnet laser (Nd:YAG laser), and diode laser.

Recent Advances in Adhesive Bonding - The Role of Biomolecules, Nanocompounds, and Bonding Strategies in Enhancing Resin Bonding to Dental Substrates

PURPOSE OF REVIEW

To present an overview on the main agents (i.e., biomolecules and nanocompounds) and/or strategies currently available to amplify or stabilize resin-dentin bonding.

RECENT FINDINGS

According to studies retrieved for full text reading (2014-2017), there are currently six major strategies available to overcome resin-dentin bond degradation: (i) use of collagen crosslinking agents, which may form stable covalent bonds with collagen fibrils, thus strengthening the hybrid layer; (ii) use of antioxidants, which may allow further polymerization reactions over time; (iii) use of protease inhibitors, which may inhibit or inactivate metalloproteinases; (iv) modification of the bonding procedure, which may be performed by using the ethanol wet-bonding technique or by applying an additional adhesive (hydrophobic) coating, thereby strengthening the hybrid layer; (v) laser treatment of the substrate prior to bonding, which may cause specific topographic changes in the surface of dental substrates, increasing bonding efficacy; and (vi) reinforcement of the resin matrix with inorganic fillers and/or remineralizing agents, which may positively enhance physico-mechanical properties of the hybrid layer.

SUMMARY

With the present review, we contributed to the better understanding of adhesion concepts and mechanisms of resin-dentin bond degradation, showing the current prospects available to solve that problematic. Also, adhesively-bonded restorations may be benefited by the use of some biomolecules, nanocompounds or alternative bonding strategies in order to minimize bond strength degradation.

Evaluation of different surface treatments on fiber post cemented with a self-adhesive system

Surface treatment of fiber-reinforced posts can increase adhesion, especially on the post/resin cement interface. The purpose of this in vitro study was to evaluate the effect of different surface treatments on fiber post cemented with a self-adhesive system. Sixty fiberglass epoxy resin posts were cleaned, dried and divided into 6 groups (n=10): Control (no surface treatment), silane (silane coupling agent was applied homogeneously on surface), 24% hydrogen peroxide (H₂O₂) (immersion during 1min), blasting (blasting with aluminum oxide for 30s), NH₃ plasma (plasma treatment for 3min) and HMDSO plasma (plasma treatment for 15min). After the treatments, posts were inserted into a silicon matrix that was filled with the resin cement RelyX U200. Afterwards, the post/cement specimens were cut perpendicularly to the long axis of the posts into six 1.0mm thick discs and submitted to a push-out bond strength (POBS) test. Failure pattern was classified in 5 types: type I: cohesive in post; type II: cohesive in cement; type III: cohesive post and cement; type IV: adhesive post/cement; and type V: mixed (association between cohesive and adhesive). Data were analyzed by one-way ANOVA and Tukey HSD post hoc test (α=0.05). Silane (15.94±6.5), blasting (13.13±3.6), NH₃ plasma (14.44±4.0) and HMDSO plasma (13.23±5.3) showed higher POBS when compared to control (p<0.05) and similar among them. H₂O₂ (9.40±4.0) treatment showed POBS values statistically similar to control (9.65±3.6). Failures were predominantly cohesive post and cement, type III, in all groups. In conclusion, surface treatments influenced in the adhesion of fiberglass post with the self-adhesive cement RelyX U200. Silane, blasting with aluminum oxide and plasmas (NH₃ and HMDSO) showed results superior to 24% hydrogen peroxide.