Immediate and Delayed Effects of Diode Laser on Debonding of Ceramic Brackets: An in vitro Study

Assessment of chemical, ultrasonic, diode laser, and Er:YAG laser application on debonding of ceramic brackets

Background

Risk of enamel damage that often accompanies ceramic brackets debonding raises the demand of finding an optimal method for debonding of them without adverse effects. Different techniques were proposed in an attempt to facilitate their debonding. Comparison of these techniques is crucial. The aim of this study was to evaluate and compare different techniques for debonding of ceramic brackets in terms of shear bond strength and adhesive remnant index.

Materials and methods

A total of 100 extracted premolars were randomly allocated into 5 groups. Ceramic brackets were then bonded to teeth using light cure composite resin. Among test groups; group I: served as control, group II: chemical aided debonding via peppermint oil, group III: ultrasonic aided debonding, group IV: diode laser aided debonding, and group V: Er:YAG laser aided debonding. Brackets were shear tested using universal testing machine followed by ARI assessment and evaluation of enamel microstructure was performed using scanning electron microscopy.

Results

A significantly lower shear bond strength was found in ultrasonic, diode, and Er:YAG laser groups. However, no significant difference was found in the chemical group. A significantly higher adhesive remnant index was found solely in Er:YAG laser group with minimal enamel microstructure alterations.

Conclusions

Er:YAG laser is a promising tool in debonding ceramic brackets. Ultrasonic and diode laser significantly reduced shear bond strength. Yet, adhesive remnant index in both groups revealed no difference. Chemical aided debonding had little effect and hence, it cannot be recommended without further development.

Evaluation of the Shear Bond Strength and Adhesive Remnant Index in Debonding of Stainless Steel Brackets Assisted with Nd:YAG Laser Irradiation

Objectives:

The purpose was to compare shear bond strength (SBS), pulp temperature, and adhesive remnant index (ARI) in debonding of stainless steel brackets from enamel surface using neodymium-doped yttrium aluminum garnet (Nd:YAG) laser versus the conventional debonding method.

Materials and Methods:

Forty-eight extracted premolars were bonded to stainless steel brackets. The samples were divided into three experimental groups and one control group. In the first three groups, Nd:YAG laser was used for debonding with the power of 1, 1.5, and 2 W, respectively, for 10 seconds. The SBS and ARI of the samples were assessed. Pulp temperature was recorded before and after irradiation. Two samples from each group were used for determining enamel morphology after debonding using scanning electron microscopy (SEM).

Results:

The mean SBS in the groups was 33.05, 28.69, 24.37, and 31.53 MPa, respectively, with no statistically significant differences (P=0.205). Significant differences in post-irradiation temperature were noted among the lased groups (P=0.000). Debonding mainly occurred at the adhesive-enamel interface in the 1-W laser and control groups and at the bracket-adhesive interface in the 1.5-W and 2-W laser groups. Enamel structure was amorphous and irregular following laser irradiation.

Conclusion:

Based on the results of this study, the use of Nd:YAG laser could not significantly affect the SBS. Therefore, this laser would not be suitable for debonding of metal brackets. The use of a 2-W laser could significantly raise the pulpal temperature. Nd:YAG laser renders a more heterogeneous enamel morphology compared to conventional debonding methods.