3-year follow-up of a long-term registry-based multicentre study on vitamin E diffused polyethylene in total hip replacement

Rate of revision and wear penetration in different polyethylene liner compositions in total hip arthroplasty: a Bayesian network meta-analysis

The present Bayesian network meta-analysis compared different types of polyethylene liners in total hip arthroplasty (THA) in terms of wear penetration (mm/year) and rate of revision. The type of liners compared were the crosslinked ultra-high molecular weight polyethylene (CPE/UHMWPE), Vitamin E infused highly cross-linked polyethylene (HXLPE-VEPE), modified cross-linked polyethylene (MXLPE), highly cross-linked polyethylene (HXLPE), Cross-linked polyethylene (XLPE). This study was conducted according to the PRISMA extension statement for reporting systematic reviews incorporating network meta-analyses of healthcare interventions. In June 2024, PubMed, Scopus, Embase, Google Scholar, and Cochrane databases were accessed. A time constraint was set from January 2000. All investigations which compared two or more types of polyethylene liners for THA were accessed. Only studies that clearly stated the nature of the liner were included. Data from 60 studies (37,352 THAs) were collected. 56% of patients were women. The mean age of patients was 60.0 ± 6.6 years, the mean BMI was 27.5 ± 2.0 kg/m2. The mean length of follow-up was 81.6 ± 44.4 months. Comparability was found at baseline between groups. XLPE and HXLPE liners in THA are associated with the lowest wear penetration (mm/year) and the lowest revision rate at approximately 7 years of follow-up.

Application of deep learning for automated diagnosis and classification of hip dysplasia on plain radiographs

BACKGROUND

Hip dysplasia is a condition where the acetabulum is too shallow to support the femoral head and is commonly considered a risk factor for hip osteoarthritis. The objective of this study was to develop a deep learning model to diagnose hip dysplasia from plain radiographs and classify dysplastic hips based on their severity.

METHODS

We collected pelvic radiographs of 571 patients from two single-center cohorts and one multicenter cohort. The radiographs were split in half to create hip radiographs (n = 1022). One orthopaedic surgeon and one resident assessed the radiographs for hip dysplasia on either side. We used the center edge (CE) angle as the primary diagnostic criteria. Hips with a CE angle < 20°, 20° to 25°, and > 25° were labeled as dysplastic, borderline, and normal, respectively. The dysplastic hips were also classified with both Crowe and Hartofilakidis classification of dysplasia. The dataset was divided into train, validation, and test subsets using 80:10:10 split-ratio that were used to train two deep learning models to classify images into normal, borderline and (1) Crowe grade 1-4 or (2) Hartofilakidis grade 1-3. A pre-trained on Imagenet VGG16 convolutional neural network (CNN) was utilized by performing layer-wise fine-turning.

RESULTS

Both models struggled with distinguishing between normal and borderline hips. However, achieved high accuracy (Model 1: 92.2% and Model 2: 83.3%) in distinguishing between normal/borderline vs. dysplastic hips. The overall accuracy of Model 1 was 68% and for Model 2 73.5%. Most misclassifications for the Crowe and Hartofilakidis classifications were +/- 1 class from the correct class.

CONCLUSIONS

This pilot study shows promising results that a deep learning model distinguish between normal and dysplastic hips with high accuracy. Future research and external validation are warranted regarding the ability of deep learning models to perform complex tasks such as identifying and classifying disorders using plain radiographs.

LEVEL OF EVIDENCE

Diagnostic level IV.

Di-cumyl peroxide cross-linked UHMWPE/vitamin-E blend for total joint arthroplasty implants

Majority of ultrahigh molecular weight polyethylene (UHMWPE) medical devices used in total joint arthroplasty are cross-linked using gamma radiation to improve wear resistance. Alternative methods of cross-linking are urgently needed to replace gamma radiation due to rapid decline in its supply. Peroxide cross-linking is a candidate method with widespread industrial applications. Oxidative stability and biocompatibility, which are critical requirements for medical device applications, can be achieved using vitamin-E as an additive and by removing peroxide by-products through high-temperature melting, respectively. We investigated compression molded UHMWPE/vitamin-E/di-cumyl peroxide blends followed by high-temperature melting in inert gas as a material candidate for tibial knee inserts. Wear resistance increased and mechanical properties remained largely unchanged. Oxidation induction time was higher than most of the other clinically available formulations. The material passed the local-end point biocompatibility tests per ISO 10993. Compounds found in exhaustive extraction were of no concern with margin-of-safety values well above the accepted level, indicating a desirable toxicological risk profile. Statement of Clinical Significance: Peroxide cross-linked, vitamin-E stabilized, and high-temperature melted UHMWPE has recently been cleared for clinical use in tibial knee inserts. With all the salient characteristics needed in a material that can provide superior long-term performance in total joint patients, peroxide cross-linking can replace the gamma radiation cross-linking of UHMWPE.

Head, acetabular liner composition, and rate of revision and wear in total hip arthroplasty: a Bayesian network meta-analysis

Total hip arthroplasty (THA) is a common procedure for patients suffering from hip pain e.g. from osteoarthritis, osteonecrosis, or hip fractures. The satisfaction of patients undergoing THA is influenced by the choice of implant type and material, with one key factor being the selection of the appropriate material combination for the bearing surface. In this Bayesian network meta-analysis, we investigated the impact of material combinations for the bearing surface on the longevity of hip implants. The wear penetration rate per year and the total wear penetration in the liner resulting from different material combinations, as well as the survival rate at last follow-up, were examined. We analyzed a total of 663,038 THAs, with 55% of patients being women. Mean patient age was 59.0 ± 8.1 years and mean BMI 27.6 ± 2.6 kg/m2. The combination of an aluminium oxide (Al2O3) head and an Al2O3 liner demonstrated the lowest wear penetration at last follow-up and the lowest rate of wear penetration per year. Additionally, the combination of a crosslinked polyethylene (XLPE) liner and a zircon oxide (ZrO2) head demonstrated the lowest rate of revision at last follow-up. These findings underscore the importance of careful material selection for hip implant bearing surfaces to optimize their longevity and patient satisfaction after THA.

Minimum 7-Year Follow-Up of Vitamin E-Diffused and Highly Cross-Linked Polyethylene Liners in Total Hip Arthroplasty: Findings From a Prospective, International, Multicenter Study of 977 Patients

BACKGROUND

Vitamin E-diffused highly cross-linked polyethylene (VEPE) acetabular liners for total hip arthroplasty (THA) have shown favorable results in small cohort studies. However, larger studies are warranted to compare its performance to highly cross-linked polyethylene (XLPE) and demonstrate clinical significance in 10-year arthroplasty outcomes. This study compared acetabular liner wear and patient-reported outcome measures (PROMs) between patients treated with VEPE and XLPE liners in a prospective, international, multicenter study with minimum 7-year follow-up.

METHODS

A total of 977 patients (17 centers; 8 countries) were enrolled from 2007 to 2012. The centers were randomly assigned to implants. At 1-year, 3-year, 5-year, and 7-year postoperative visits, radiographs, PROMs, and incidence of revision were collected. Acetabular liner wear was calculated using computer-assisted vector analysis of serial radiographs. General health, disease progression, and treatment satisfaction reported by patients were scored using 5 validated surveys and compared using Mann-Whitney U tests. At 7 years, 75.4% of eligible patients submitted data.

RESULTS

The mean acetabular liner wear rate was -0.009 mm/y and 0.024 mm/y for the VEPE and XLPE group, respectively (P = .01). There were no statistically significant differences in PROMs. The overall revision incidence was 1.8% (n = 18). The revision incidence in VEPE and XLPE cohorts were 1.92% (n = 10) versus 1.75% (n = 8), respectively.

CONCLUSION

We found that VEPE acetabular liners in total hip arthroplasty led to no significant clinical difference in 7-year outcomes as measured by acetabular liner wear rate, PROMs, and revision rate. While VEPE liners showed less wear, the wear rate for both the VEPE and XLPE liners was below the threshold for osteolysis. Therefore, the difference in liner wear may indicate comparative clinical performance at 7 years, as further indicated by the lack of difference in PROMs and the low revision incidence.

Risk factors for liner wear and head migration in total hip arthroplasty: a systematic review

Total hip arthroplasty (THA) is a successful orthopaedic surgical procedure, and its longevity depends on bearing components and implant fixation. Optimizing polyethylene and ceramics has led to improved wear parameters and contributed to improved long-term outcomes. The present systematic review investigated whether time span from implantation, patient characteristics and performance status exert an influence on liner wear and head migration in THA. This study was conducted in conformity to the 2020 PRISMA guidelines. All the clinical investigations which reported quantitative data on the amount of liner wear and head migration in THA were considered. Only studies which reported quantitative data at least on one of the following patient characteristics were suitable: mean age, mean BMI (kg/m2), sex, side, time span between the index THA and the last follow-up (months) were eligible. A multiple linear model regression analysis was employed to verify the association between patient characteristics and the amount of liner wear and/or head migration. The Pearson Product-Moment Correlation Coefficient was used to assess the association between variables. Data from 12,629 patients were considered. The mean length of the follow-up was 90.5 ± 50.9 months. The mean age of patients at surgery was 58.4 ± 9.4 years, and the mean BMI was 27.2 ± 2.5 kg/m2. 57% (7199 of 12,629 patients) were women, and in 44% (5557 of 12,629 patients) THAs were performed on the left. The mean pre-operative Harris hip score was 46.5 ± 6.0 points. There was evidence of a moderate positive association between the amount of liner wear and the time elapsed between the index surgery to the follow-up (P = 0.02). There was evidence of a moderate positive association between the amount of head migration and the time elapsed between the index surgery to the follow-up (P = 0.01). No further statistically significant association was found. The time elapsed between the index surgery to the follow-up was the most important factor which influence the head migration and liner wear in THA. Patients' characteristics and preoperative physical activity did not influence the amount of head migration and liner wear.

Cup positioning and its effect on polyethylene wear of vitamin E- and non-vitamin E-supplemented liners in total hip arthroplasty: radiographic outcome at 5-year follow-up

BACKGROUND

Aseptic loosening remains a challenging problem after total hip arthroplasty. Accurate cup placement and supplementation of antioxidants in acetabular liners might reduce material failure rates. The aim of this study is to assess the effect of the cup position on the wear behaviour of UHMWPE-XE and UHMWPE-X liners in vivo using virtual radiographs.

METHODS

We conducted a prospective, randomized, controlled, multicenter trial. Clinical data of 372 probands were analyzed. Anteroposterior pelvic X-rays of 324 patients immediately postoperatively and after 1 and 5 years were evaluated by the RayMatch® analysis software regarding cup position and wear behaviour.

RESULTS

Mean cup anteversion was 20.3° (± 7.4) and inclination was 41.9° (± 7.0) postoperatively. 62.3% of all patients had an anteversion and inclination within the Lewinnek safe zone. Anterior and anterolateral approaches led to significantly higher cup anteversion compared to lateral approaches (27.3° ± 5.5; 20.9° ± 7.2; 17.5° ± 6.6; p < 0.001 and p = 0.001, respectively). Mean anteversion increased to 24.6° (± 8.0) after 1 year (p < 0.001). Only one revision occurred because of implant dislocation. Wear rates from UHMWPE-X and UHMWPE-XE did not differ significantly. Anteversion angles ≥ 25° correlated to increased polyethylene wear (23.7 µm/year ± 12.8 vs. 31.1 µm/year ± 22.8, p = 0.012) and this was amplified when inclination angles were ≥ 50° (23.6 µm/year ± 12.8 vs. 38.0 µm/year ± 22.7, p = 0.062).

CONCLUSION

Anterior approaches lead to the highest inaccuracy of cup placement, but cup positioning outside the Lewinnek safe zone does not necessarily cause higher dislocation rates. Moreover, mean anteversion increased by approximately four degrees within the first year after operation, which is expected to be functional due to a regularization of pelvic tilt after intervention. Mid-term wear rates of UHMWPE-X and UHMWPE-XE liners are comparable, but steep cup positions lead to significantly increased polyethylene wear. In summary, a re-evaluation of target zones for intraoperative cup positioning might be considered. In the long-term reduced oxidative embrittlement could lead to superior wear behaviour of vitamin E-blended liners.

Safety of vitamin E-infused highwall liners for routine use in primary total hip arthroplasty: single centre, short-term follow-up of 1221 cases

BACKGROUND

Introduction of new implants should be monitored closely to capture any signs of compromising patient safety. Vitamin E infused highly-crosslinked polyethylene liners (VEPE) offer the potential for reduced wear. Highwall liners have been hypothesised to result in increased wear and potential liner fractures. The aim of this study was to determine the 3-7-year follow-up of highwall VEPE for primary total hip arthroplasty (THA), focusing on liner-related complications.

METHODS

We included 1221 consecutive THA operations from July 2010 to May 2014 with minimum follow-up of 3 (3.1-6.8) years Data collected included demographics, implant data, complications, reoperations, and deaths. Data were cross-referenced with the Danish Hip Arthroplasty Registry in order to ensure validity and completeness. Acetabular shell position was measured using Martell Hip Analysis Suite in a subgroup of 931 THAs.

RESULTS

Cumulative stem revision and shell revision at 3-year follow-up was 3.4% and 0.4% respectively. There were no revisions due to liner failure. Reason for revision included 11 dislocations, 15 soft-tissue revisions for infection, 44 stem revisions of which 34 were periprosthetic fractures and 13 shell revisions of which 6 were combined shell and stem revisions.

CONCLUSION

Early follow-up of VEPE liners for primary THA have not shown any revisions associated with liner failure. Continued monitoring of new materials are necessary to capture any signs of compromised patient safety.

Vitamin E-Enhanced Liners in Primary Total Hip Arthroplasty: A Systematic Review and Meta-Analysis

Objective

Adding vitamin E to highly cross-linked polyethylene liners is frequently performed in clinical practice, aiming at reducing liner wear, increasing liner survival, and delaying revision surgery. This study is aimed at evaluating the revision rate, total femoral head penetration, and postoperative clinical function of highly cross-linked polyethylene liners with and without vitamin E in total hip arthroplasty.

Methods

We conducted a systematic literature search to identify the use of highly cross-linked vitamin E liners compared to other liners in patients who received total hip arthroplasty (THA) before April 2021. The study quality assessment and data collection were conducted by two independent reviewers. Studies were artificially grouped, and vitamin E-enhanced liners (VE-PE) were compared with vitamin E-free liners (non-VE-PE). Analyses were executed using Review Manager version 5.4.1.

Results

From the preliminary screening of 568 studies, fourteen studies met the research criteria. Compared to non-VE-PE, using VE-PE reduced the all-cause revision rate (odds ratio = 0.54; 95% confidence interval (CI) 0.40, 0.73; P < 0.0001). The total femoral head penetration of the VE-PE was lower than that of the non-VE-PE (mean difference = −0.10; 95% CI -0.17, -0.03; P = 0.007). However, there was no difference in clinical function, including the Harris Hip Score and EuroQol Five-Dimension Questionnaire scores.

Conclusion

Compared to the liners without vitamin E, the addition of vitamin E to liners could reduce the all-cause revision rate by approximately 46% in the short-term follow-up. In addition, even though addition of vitamin E could also slow down femoral head penetration, there is no contribution to clinical function.

Implant survival of 2,723 vitamin E-infused highly crosslinked polyethylene liners in total hip arthroplasty: data from the Finnish Arthroplasty Register

Background and purpose - The use of crosslinked polyethylene in total hip arthroplasty (THA) has decreased wear remarkably. It has been suggested that the antioxidative effects of vitamin E may enhance the wear properties of polyethylene even further. This study evaluates revision rates between vitamin E-infused polyethylene liners (E1 and E-poly, ZimmerBiomet, Warsaw, IN, USA) versus moderately crosslinked polyethylene (ModXLPE) liners from the same manufacturer used in primary THA.Patients and methods - We conducted a study based on data from the Finnish Arthroplasty Register. The study group consisted of 2,723 THAs with a vitamin E-infused liner and a reference group of 2,707 THAs with a moderately crosslinked polyethylene liner. Survivorship, revision risk, and re-revision causes were compared between groups.Results - The 7-year survival of the vitamin E-infused polyethylene liner group and of the reference group with revision for any reason as the endpoint was comparable (94% [95% CI 92.9-94.9] and 93% [CI 91.9-93.9], respectively). The adjusted hazard ratio (HR) for any revision was similar between the groups (0.7 [CI 0.4-1.1]). When revision for aseptic loosening was studied as the endpoint, the survival for the study group was 99% (CI 98.6-99.4) and for the reference group 99% (CI 98.7-99.5), and the risk of revision was comparable between the study groups (HR 1.3 [CI 0.7-2.5]).Interpretation - After an observation period of 7 years vitamin E-infused liners shows results equal to results obtained with crosslinked polyethylene liners.

Current evidence from a worldwide, multicentre, follow-up study of the recalled Articular Surface Replacement Hip System

INTRODUCTION

Our first aim was to report the longitudinal clinical performance of patients treated with the ASR Hip System, a metal-on-metal (MoM) device, in their mid- to late-term follow-up. Secondly, we sought to report on the reasons and risk factors for mid- to late-term implant failure.

METHODS

A total of 1721 ASR patients (1933 hips) from 16 centres in 6 countries were enrolled to a prospective, post-recall study. The average time to enrollment was 7.4 years from index surgery. Data from 3 follow-up visits over 2 years were analysed. Implant performance, based on ion levels and PROMs, was determined at each clinical visit.

RESULTS

The proportion of those exhibiting good performance decreased over time for hip resurfacing (ASR HRA) and total hip arthroplasty (ASR XL) patients. ASR XL patients were likely to exhibit longitudinal blood metal ion increases regardless of symptom state. ASR HRA patients were more likely to present with and maintain good performance over time, especially males with high general health indicators. 6% of ASR HRA and 14% of ASR XL patients were revised throughout the study period.

DISCUSSION

ASR XL THA patients are likely to exhibit blood metal ion increases without accompanying changes in symptom state, and therefore should be followed with annual blood tests at minimum. While appropriately selected ASR HRA patients were the most likely to exhibit low blood metal ion levels and report no symptoms, we recommend vigilant follow-up of all ASR patients to ensure that worsening clinical outcomes and asymptomatic soft tissue damage are not missed.

Reduced wear in vitamin E-infused highly cross-linked polyethylene cups: 5-year results of a randomized controlled trial

Background and purpose - Vitamin E-infused polyethylene is a relatively new material in joint arthroplasty; there are no long-term reports, and only few mid-term results. Using radiostereometric analysis (RSA), we primarily determined whether vitamin E-infused highly cross-linked polyethylene (HXLPE/VitE) acetabular cups show less wear than ultra-high molecular weight polyethylene (UHMWPE) acetabular cups at 5 years after total hip arthroplasty (THA). We also assessed whether wear rates correlate with increasing cup inclination angles or cup sizes.Patients and methods - This is a 5-year follow-up of our previously reported randomized controlled trial of 62 patients with 3 years' follow-up, who received THA with either an HXLPE/VitE or a UHMWPE acetabular cup. At 5 years, 40 patients were analyzed (22 in the HXLPE/VitE and 18 in the UHMWPE group).Results - HXLPE/VitE cups continued to show less cumulative femoral head penetration than UHMWPE cups (HXLPE/VitE: 0.24 mm, UHMWPE: 0.45 mm; p < 0.001). Distribution of wear was also more even with HXLPE/VitE cups than with UHMWPE cups (p = 0.002). Moreover, the difference in PE wear between 1 and 5 years in both groups showed no statistically significant correlation with increasing cup inclination angles or cup sizes. Finally, no osteolysis and implant loosening occurred, and no revision surgeries were required.Interpretation - Wear rates continue to be lower in HXLPE/VitE cups than in UHMWPE cups at 5 years of follow-up without correlation with increasing cup inclination angles or cup sizes. Finally, HXLPE/VitE cups may have the potential to prevent osteolysis and implant loosening.

Vitamin E-blended highly cross-linked polyethylene liners in total hip arthroplasty: a randomized, multicenter trial using virtual CAD-based wear analysis at 5-year follow-up

BACKGROUND

Progressive oxidation of highly cross-linked ultra-high molecular weight (UHMPWE-X) liners is considered to be a risk factor for material failure in THA. Antioxidants such as vitamin E (alpha-tocopherol) (UHMWPE-XE) were supplemented into the latest generation of polyethylene liners. To prevent inhomogenous vitamin E distribution within the polymer, blending was established as an alternative manufacturing process to diffusion. The purpose of the present study was to investigate the in vivo wear behavior of UHMWPE-XE in comparison with conventional UHMWPE-X liners using virtual CAD-based radiographs.

METHODS

Until now, 94 patients from a prospective, randomized, controlled, multicenter study were reviewed at 5-year follow-up. Of these, 51 (54%) received UHMWPE-XE and 43 (46%) UHMWPE-X liners. Anteroposterior pelvic radiographs were made immediately after surgery and at 1 and 5 years postoperatively. The radiographs were analyzed using the observer-independent analysis software RayMatch^® (Raylytic GmbH, Leipzig, Germany).

RESULTS

The mean wear rate was measured to be 23.6 μm/year (SD 13.7; range 0.7-71.8 μm). There were no significant differences between the two cohorts (UHMWPE-X: 23.2 μm/year vs. UHMWPE-XE: 24.0 μm/year, p = 0.73). Cup anteversion significantly changed within the 1st year after implantation independent from the type of polyethylene liner [UHMWPE-X: 18.2-23.9° (p = 0.0001); UHMWPE-XE: 21.0-25.5° (p = 0.002)]. No further significant changes of cup anteversion in both groups were found between year 1 and 5 after implantation [UHMWPE-X (p = 0.46); UHMWPE-XE (p = 0.56)].

CONCLUSION

The present study demonstrates that the addition of vitamin E does not adversely affect the midterm wear behavior of UHMWPE-X. The antioxidative benefit of vitamin E is expected to become evident in long-term follow-up. Cup anteversion increment by 5° within the 1st year is likely a result of the released hip flexion contracture resulting in an enhanced posterior pelvic tilt. Therefore, a reassessment of target values in acetabular cup placement might be considered.

Reasons for Revision, Oxidation, and Damage Mechanisms of Retrieved Vitamin E-Stabilized Highly Crosslinked Polyethylene in Total Knee Arthroplasty

BACKGROUND

In order to improve oxidation resistance, antioxidants such as vitamin-E are added to polyethylene used in the bearing surfaces of orthopedic components. Currently, little is known about the efficacy of this treatment in vivo. This study therefore reports on the reasons for revision, surface damage mechanisms, and oxidation of retrieved vitamin E-stabilized highly crosslinked polyethylene (HXLPE) for total knee arthroplasty.

METHODS

We examined 103 retrieved knee inserts fabricated from vitamin E (VE)-stabilized HXLPE and 67 fabricated from remelted HXLPE as a control. The implantation times were 1.2 ± 1.3 and 1.5 ± 1.3 years for the VE and control cohorts, respectively. The inserts were evaluated for 7 surface damage mechanisms using a semiquantitative scoring method and analyzed for oxidation using Fourier-transform infrared spectroscopy. Reasons for revision were also assessed using operative notes created at time of retrieval.

RESULTS

Both groups were revised primarily for instability, infection, and loosening. Burnishing, pitting, and scratching were the most common damage mechanisms observed, with the VE cohort demonstrating less surface damage than the control. Measured oxidation for the cohort was low, with a median oxidation index of 0.09 ± .05 for the articulating surface, 0.05 ± 0.06 for the backside, 0.08 ± 0.06 for the anterior/posterior surfaces, and 0.08 ± 0.05 for the stabilizing post. As compared to the control cohort, oxidation tended to be less for the VE group at the articulating (P < .001) and backside (P = .003) surfaces, although the median differences were minimal and may not be clinically significant.

CONCLUSION

The results indicate positive fatigue damage resistance and oxidation resistance for the retrieved VE-stabilized total knee arthroplasty inserts.

Longitudinal changes in patient-reported outcome measures following total hip arthroplasty and predictors of deterioration during follow-up

Aims

The primary aim of this study was to quantify the improvement in patient-reported outcome measures (PROMs) following total hip arthroplasty (THA), as well as the extent of any deterioration through the seven-year follow-up. The secondary aim was to identify predictors of PROM improvement and deterioration.

Patients and Methods

A total of 976 patients were enrolled into a prospective, international, multicentre study. Patients completed a battery of PROMs prior to THA, at three months post-THA, and at one, three, five, and seven-years post-THA. The Harris Hip Score (HHS), the 36-Item Short-Form Health Survey (SF-36) Physical Component Summary (PCS), the SF-36 Mental Component Summary (MCS), and the EuroQol five-dimension three-level (EQ-5D) index were the primary outcomes. Longitudinal changes in each PROM were investigated by piece-wise linear mixed effects models. Clinically significant deterioration was defined for each patient as a decrease of one half of a standard deviation (group baseline).

Results

Improvements were noted in each PROM between the preoperative and one-year visits, with one-year values exceeding age-matched population norms. Patients with difficulty in self-care experienced less improvement in HHS (odds ratio (OR) 2.2; p = 0.003). Those with anxiety/depression experienced less improvement in PCS (OR -3.3; p = 0.002) and EQ-5D (OR -0.07; p = 0.005). Between one and seven years, obesity was associated with deterioration in HHS (1.5 points/year; p = 0.006), PCS (0.8 points/year; p < 0.001), and EQ-5D (0.02 points/year; p < 0.001). Preoperative difficulty in self-care was associated with deterioration in HHS (2.2 points/year; p < 0.001). Preoperative pain from other joints was associated with deterioration in MCS (0.8 points/year; p < 0.001). All aforementioned factors were associated with clinically significant deterioration in PROMs (p < 0.035), except anxiety/depression with regard to PCS (p = 0.060).

Conclusion

The present study finds that patient factors affect the improvement and deterioration in PROMs over the medium term following THA. Special attention should be given to patients with risk factors for decreased PROMs, both preoperatively and during follow-up. Cite this article: Bone Joint J 2019;101-B:768–778.

Effects of Vitamin E-Stabilized Ultra High Molecular Weight Polyethylene on Oxidative Stress Response and Osteoimmunological Response in Human Osteoblast

High Crosslink process was introduced in the development of joint prosthetic devices, in order to decrease the wear rate of ultrahigh molecular weight polyethylene (UHMWPE), but it also triggers the formation of free radicals and oxidative stress, which affects the physiological bone remodeling, leading to osteolysis. Vitamin E stabilization of UHMWPE was proposed to provide oxidation resistance without affecting mechanical properties and fatigue strength. The aim of this study is to evaluate the antioxidant effect of vitamin E added to UHMWPE on oxidative stress induced osteolysis, focusing in particular on the oxidative stress response in correlation with the production of osteoimmunological markers, Sclerostin and DKK-1, and the RANKL/OPG ratio compared to conventional UHMWPE wear debris. Human osteoblastic cell line SaOS2 were incubated for 96 h with wear particles derived from crosslinked and not crosslinked Vitamin E-stabilized, UHMWPE without Vitamin E, and growth medium as control. Cellular response to oxidative stress, compared to not treat cells, was evaluated in terms of proteins O-GlcNAcylation, cellular levels of OGA, and OGT proteins by immunoblotting. O-GlcNAcylation and its positive regulator OGT levels are increased in the presence of Vitamin E blended UHMWPE, in particular with not crosslinked Vit E stabilized UHMWPE. Conversely, the negative regulator OGA increased in the presence of UHMWPE not blended with Vitamin E. Vitamin E-stabilized UHMWPE induced a decrease of RANKL/OPG ratio compared to UHMWPE without Vitamin E, and the same effect was observed for Sclerostin, while DKK-1 was not significantly affected. In conclusion, Vitamin E stabilization of UHMWPE increased osteoblast response to oxidative stress, inducing a cellular mechanism aimed at cell survival. Vitamin E antioxidant effect influences the secretion of osteoimmunological factors, shifting the bone turnover balance toward bone protection stimuli. This suggests that Vitamin E-Stabilization of UHMWPE could contribute to reduction of oxidation-induced osteolysis and the consequent loosening of the prosthetic devices, therefore improving the longevity of total joint replacements.

Radiographic and Clinical Outcomes of Porous Titanium-Coated and Plasma-Sprayed Acetabular Shells: A Five-Year Prospective Multicenter Study

BACKGROUND

New materials in cementless total hip arthroplasty are continuously introduced into clinical practice. The objective of this study was to compare the radiographic and clinical performances of acetabular shells made with porous titanium coating (PTC) and plasma-sprayed titanium (PS).

METHODS

Data from a prospective multicenter study monitoring PTC and PS shells were analyzed. Three hundred and eighty patients (191 with PTC and 189 with PS) with postoperative (within 10 months after the operation) and 5-year radiographs were available for assessment of radiographic outcomes and patient-reported outcome measures (PROMs). A radiolucent distance between the cup and acetabulum of ≥0.5 mm was defined as a gap if it was found on a postoperative radiograph and as a radiolucency if it was found on a later follow-up radiograph for the first time.

RESULTS

Postoperative gaps were more common with the PS shell (40% versus 24%, p < 0.001). However, a higher percentage of the gaps in the PTC group persisted at 5 years (56% versus 4%, p < 0.001). At 5 years, 23% of the PTC shells had a radiolucency versus 5% of the PS shells (p < 0.001). Logistic regression revealed a 5.2-fold increase in the odds for radiolucency with the PTC shell (p < 0.001). No patient underwent revision surgery due to acetabular component loosening within the study period. A PTC shell was the only factor associated with the risk of pain in a logistic regression model (odds ratio = 2.0, p = 0.035).

CONCLUSIONS

PTC shells were associated with more patient-reported pain and a higher risk of radiolucency and a persistent gap at 5 years compared with the PS shells, although these outcomes were not related to each other. The clinical relevance of the radiographic findings is unclear as no prostheses were revised because of loosening, but the findings warrant additional follow-up studies.

LEVEL OF EVIDENCE

Therapeutic Level III. See Instructions for Authors for a complete description of levels of evidence.

Catastrophic failure of a dual mobility bearing in a revision total hip arthroplasty

The following case demonstrates an example of a catastrophic failure of a dual mobility (DM) bearing used in the setting of a revision total hip arthroplasty for an acetabular component with an excessive abduction angle. Currently, in the literature, it has been demonstrated that DM bearings have decreased polyethylene wear at abduction angles up to 65°; however, this has only been shown in in vitro studies. To our knowledge, there have been no reports of in vivo DM bearings that have demonstrated these same results. In this case, a DM bearing was used in a revision surgery with a retained acetabular component that had an abduction angle of approximately 70°-75° which ultimately led to catastrophic polyethylene failure.

ARTICULATION AND BACKSIDE WEAR ANALYSIS AFTER LONG-TERM IN VITRO WEAR SIMULATION OF VITAMIN E STABILIZED POLYETHYLENE ACETABULAR LINERS WITH A PRESS-FIT LOCKING MECHANISM

A previous retrieval study analyzed the backside wear of short-term implanted liners against in vitro tested liners of similar life in service and showed comparable results among both groups, with no significant backside wear due to micro-motion.

The purpose — to obtain a picture of the overall wear (articulation and backside surfaces) of 0.1% vitamin e blended polyethylene liners, with a locking mechanism based on a press-fit cone in combination with a rough titanium conical inner surface in the fixation area, under a 20 million cycles hip wear simulation.

Materials and Methods. A semi-quantitative method was used in order to assess the damage on the backside of the liners and a 3d measuring machine to assess the creep and wear at the articulation surface.

Results. The total average backside wear score was 22.00±2.59 from a maximum total score of 147 after 5 million cycles (mc), increased to 31.92±5.57 after 10 mc, but showed no further increment after 15 and 20 mc. The reference liners (subjected only to axial load) showed similar wear scores and modes as the liners under wear simulation (axial load and movement). Small scratches produced during insertion and removal were clearly seen at the rim (fixation) area and no considerable abrasion was observed. The machining marks on the convex surface were always visible. Regarding the articulation surface, a steady state wear rate of 7 µm/year was measured.

Conlusion. These results determined that most of the backside wear produced on the liners occurred during their insertion and removal rather than during their life in service. Moreover, the wear at the articulation surface was similar to that seen in vivo at short- and mid-term on highly cross-linked polyethylene liners with and without vitamin e content.

Superior rim fracture of a vitamin E-infused highly cross-linked polyethylene (HXLPE) liner leading to total hip arthroplasty revision

This case report looks at the failure of a vitamin E-infused highly cross-linked polyethylene acetabular liner that fractured at the superior rim of the locking mechanism. This calls to question whether there is a problem with the vitamin E-infused product or a flaw in the design of the liner or possibly a combination of the 2. Although there has been discussion of a possible minimum rim polyethylene thickness, there has not been a minimum thickness established. In addition, in the case of offset liners, indentations which are a part of a locking mechanism can cause the minimum rim dimension to be much less than the specified nominal thickness. This case serves as an interesting observation and contributes to the discussion of rim liner polyethylene thickness and minimum rim thickness.

Creep and Wear in Vitamin E-Infused Highly Cross-Linked Polyethylene Cups for Total Hip Arthroplasty: A Prospective Randomized Controlled Trial

BACKGROUND

Aseptic loosening, the most common indication for revision surgery in total hip arthroplasty, can result from osteolysis caused by polyethylene (PE) wear particles. PE wear is increased by age-related oxidation of PE and free radicals emerging during irradiation cross-linking. Diffusion of vitamin E into PE stabilizes free radicals to maintain the biomechanical properties of PE. The purpose of this study was to determine whether vitamin E-infused highly cross-linked PE cups could reduce wear rates.

METHODS

We performed a prospective randomized controlled trial, in which 62 patients were allocated to 2 groups: a study group that received a vitamin E-infused highly cross-linked PE (HXLPE/VitE) cup and a control group that received an ultra-high molecular weight PE (UHMWPE) cup. Using radiostereometric analysis, we measured the penetration of the femoral head into the cup 7 days after surgery (baseline) and then again at 6 months and at 1, 2, and 3 years later.

RESULTS

Baseline variables did not differ significantly between the groups. At 1, 2, and 3 years after surgery, the HXLPE/VitE cup showed significantly less cumulative penetration (creep and wear) than the UHMWPE cup (p = 0.004, p < 0.0001, and p < 0.0001, respectively). The cumulative penetration after 3 years was 0.200 mm for the HXLPE/VitE cup versus 0.317 mm for the UHMWPE cup (p < 0.0001). From 1 to 3 years after surgery, after creep had stabilized and further penetration was mainly due to wear, the mean penetration increased only 0.04 mm in the HXLPE/VitE cup and 0.116 mm in the UHMWPE cup.

CONCLUSIONS

Our results confirm that wear rates over the first 3 years following surgery were lower in HXLPE/VitE cups than in UHMWPE cups. This suggests that HXLPE/VitE cups may prevent osteolysis, implant loosening, and eventually revision surgery. Long-term follow-up data continue to be collected to confirm these findings.

LEVEL OF EVIDENCE

Therapeutic Level I. See Instructions for Authors for a complete description of levels of evidence.

Ultra-High Molecular Weight Polyethylene: Influence of the Chemical, Physical and Mechanical Properties on the Wear Behavior. A Review

Ultra-high molecular weight polyethylene (UHMWPE) is the most common bearing material in total joint arthroplasty due to its unique combination of superior mechanical properties and wear resistance over other polymers. A great deal of research in recent decades has focused on further improving its performances, in order to provide durable implants in young and active patients. From "historical", gamma-air sterilized polyethylenes, to the so-called first and second generation of highly crosslinked materials, a variety of different formulations have progressively appeared in the market. This paper reviews the structure-properties relationship of these materials, with a particular emphasis on the in vitro and in vivo wear performances, through an analysis of the existing literature.