Oxidative Dehydrogenation of Ethanol over Vanadium- and Molybdenum-modified Mg-Al Mixed Oxide Derived from Hydrotalcite

Comparative Study of Physicochemical Characteristics and Catalytic Activity of Copper Oxide over Synthetic Silicon Oxide and Silicon Oxide from Rice Husk in Non-Oxidative Dehydrogenation of Ethanol

The article presents the results of comparative research on the physicochemical characteristics and catalytic activity of copper oxide supported on synthetic SiO2 and SiO2 (RH) from rice husk. SiO2 (RH) is more hydrophobic compared to SiO2, which leads to the concentration of copper oxide on its surface in the form of a “crust”, which is very important in the synthesis of low-percentage catalysts. According to SEM, XRD, and TPR-H2, the use of SiO2 (RH) as a carrier leads to an increase in the dispersion of copper oxide particles, which is the active center of ethanol dehydrogenation.

Optimal Conditions for Butanol Production from Ethanol over MgAlO Catalyst Derived from Mg-Al Layer Double Hydroxides

The MgAlO catalyst was obtained from thermal decomposition of the MgAl-LDH catalyst having Mg/Al molar ratio of 5. The catalytic Guerbet reaction of ethanol was investigated to determine the effect of WHSV and nitrogen flow rate on butanol production and product distribution. It was performed in a fixed-bed microreactor under continuous flow of vaporized ethanol mixed with N₂. The MgAlO catalyst had high total basic sites and high total acid sites that were crucial for ethanol Guerbet reaction. The MgAlO catalyst showed the highest butanol selectivity at 300℃ under WHSV = 3.10 h^-1 and nitrogen flow rate = 3,600 mL/h, and the highest butanol yield at 400℃ under WHSV = 3.10 h^-1 and nitrogen flow rate = 900 mL/h. It can be summarized that in order to enhance the butanol yield, the low WHSV is preferred to increase the contact time of ethanol and catalyst under moderate temperature.

Ethanol Dehydrogenation: A Reaction Path Study by Means of Temporal Analysis of Products

Conventional fossil fuels such as gasoline or diesel should be substituted in the future by environmentally-friendly alternatives in order to reduce emissions in the transport sector and thus mitigate global warming. In this regard, iso-butanol is very promising as its chemical and physical properties are very similar to those of gasoline. Therefore, ongoing research deals with the development of catalytically-supported synthesis routes to iso-butanol, starting from renewably-generated methanol. This research has already revealed that the dehydrogenation of ethanol plays an important role in the reaction sequence from methanol to iso-butanol. To improve the fundamental understanding of the ethanol dehydrogenation step, the Temporal Analysis of Products (TAP) methodology was applied to illuminate that the catalysts used, Pt/C, Ir/C and Cu/C, are very active in ethanol adsorption. H2 and acetaldehyde are formed on the catalyst surfaces, with the latter quickly decomposing into CO and CH4 under the given reaction conditions. Based on the TAP results, this paper proposes a reaction scheme for ethanol dehydrogenation and acetaldehyde decomposition on the respective catalysts. The samples are characterized by means of N2 sorption and Scanning Transmission Electron Microscopy (STEM).