Effect of Styrene Polymerization on the Bondability of Beech and Alder Wood with Different Adhesives

This study aimed to evaluate the bondability of beech and alder wood modified through styrene polymerization within the wood lumen. Unmodified wood samples served as the reference material. Bondability was tested using four adhesive types commonly used in wood technology: polyvinyl acetate (PVAc), urea-formaldehyde (UF), phenol-resorcinol-formaldehyde (PRF), and epoxy resin. In addition to shear strength measurements, the adhesive density profile was also assessed. Results indicated that styrene modification generally reduced wood bondability, with reductions in shear strength ranging from 8% to 23% for beech wood and 1.6% to 29% for alder wood, depending on the adhesive type. The only exception was observed with the epoxy adhesive, which showed a 13% improvement in bonding quality for modified wood. These findings suggest that while styrene modification may enhance specific properties of wood, it can adversely affect its adhesion performance with some adhesive systems, except epoxy, which displayed improved compatibility with styrene-modified wood. The study offers insights for selecting suitable adhesives when using modified wood in structural applications.

Impact of surface delignification on fire retardancy of wood treated with polyelectrolyte complexes

Wood is a natural composite widely employed as a residential building interior finishing. Although wood is readily available and offers benefits to the occupants, such as enhanced well-being, it is rarely employed in commercial construction due, amongst others, to the potential hazard of fire propagation. The application of flame retardant (FR) treatments leads to a reduction of wood flammability and supports wood as interior finishing. Polyelectrolyte complexes (PECs) deposition is an innovative surface treatment that has already proven its efficiency for fabrics. For wood, recent studies have highlighted that the weight gain impacted the fire-retardancy, and a minimum of 2 wt.-% was set to obtain fire protection. This study explored the potential of surface delignification to activate the wood surface and facilitate the PEC impregnation. Yellow birch (Betula alleghaniensis, Britt.) was surface delignified (0.3 mm) using sodium chlorite. The treatment impact on wood was evaluated by spectroscopy analysis (FTIR, Raman), and the increase in wood wettability was demonstrated (contact angle decreases from 50° to 35° after the surface delignification). Then, PECs consisting of polyethyleneimine and sodium phytate were surface impregnated in wood and delignified wood. The flame retardancy was evaluated using a cone calorimeter. Despite the increase in weight gain (1.5 wt.-% ± 0.3 wt.-% to 4.3 wt.-% ± 2.5 wt.-%), fire performance was not improved. This study demonstrates that lignin strongly affects char formation, even in the presence of PECs.

Advances in Sol-Gel-Based Superhydrophobic Coatings for Wood: A Review

As the focus of architecture, furniture, and other fields, wood has attracted extensive attention for its many advantages, such as environmental friendliness and excellent mechanical properties. Inspired by the wetting model of natural lotus leaves, researchers prepared superhydrophobic coatings with strong mechanical properties and good durability on the modified wood surface. The prepared superhydrophobic coating has achieved functions such as oil-water separation and self-cleaning. At present, some methods such as the sol-gel method, the etching method, graft copolymerization, and the layer-by-layer self-assembly method can be used to prepare superhydrophobic surfaces, which are widely used in biology, the textile industry, national defense, the military industry, and many other fields. However, most methods for preparing superhydrophobic coatings on wood surfaces are limited by reaction conditions and process control, with low coating preparation efficiency and insufficiently fine nanostructures. The sol-gel process is suitable for large-scale industrial production due to its simple preparation method, easy process control, and low cost. In this paper, the research progress on wood superhydrophobic coatings is summarized. Taking the sol-gel method with silicide as an example, the preparation methods of superhydrophobic coatings on wood surfaces under different acid-base catalysis processes are discussed in detail. The latest progress in the preparation of superhydrophobic coatings by the sol-gel method at home and abroad is reviewed, and the future development of superhydrophobic surfaces is prospected.

Sustainability in Wood Products: A New Perspective for Handling Natural Diversity

Wood is a renewable resource with excellent qualities and the potential to become a key element of a future bioeconomy. The increasing environmental awareness and drive to achieve sustainability is leading to a resurgence of research on wood materials. Nevertheless, the global climate changes and associated consequences will soon challenge the wood-value chains in several regions (e.g., central Europe). To cope with these challenges, it is necessary to rethink the current practice of wood sourcing and transformation. The goal of this review is to address the intrinsic natural diversity of wood, from its origin to its technological consequences for the present and future manufacturing of wood products. So far, industrial processes have been optimized to repress the variability of wood properties, enabling more efficient processing and production of reliable products. However, the need to preserve biodiversity and the impact of climate change on forests call for new wood processing techniques and green chemistry protocols for wood modification as enabling factors necessary for managing a more diverse wood provision in the future. This article discusses the past developments that have resulted in the current wood value chains and provides a perspective about how natural variability could be turned into an asset for making truly sustainable wood products. After briefly introducing the chemical and structural complexity of wood, the methods conventionally adopted for industrial homogenization and modification of wood are discussed in relation to their evolution toward increased sustainability. Finally, a perspective is given on technological potentials of machine learning techniques and of novel functional wood materials. Here the main message is that through a combination of sustainable forestry, adherence to green chemistry principles and adapted processes based on machine learning, the wood industry could not only overcome current challenges but also thrive in the near future despite the awaiting challenges.

Can Plasma Surface Treatment Replace Traditional Wood Modification Methods?

Wood modification is an excellent and increasingly used method to expand the application of woody materials. Traditional methods, such as chemical or thermal, have been developed for the targeted improvement of some selected properties, unfortunately typically at the expense of others. These methods generally alter the composition of wood, and thus its mechanical properties, and enhance dimensional stability, water resistance, or decrease its susceptibility to microorganisms. Although conventional methods achieve the desired properties, they require a lot of energy and chemicals, therefore research is increasingly moving towards more environmentally friendly processes. The advantage of modern methods is that in most cases, they only modify the surface and do not affect the structure and mechanical properties of the wood, while reducing the amount of chemicals used. Cold plasma surface treatment is one of the cheapest and easiest technologies with a limited burden on the environment. In this review, we focus on cold plasma treatment, the interaction between plasma and wood compounds, the advantages of plasma treatment compared to traditional methods, and perspectives.

Suberin Fatty Acid Hydrolysates from Outer Birch Bark for Hydrophobic Coating on Aspen Wood Surface

Bark extracts are sustainable sources of biopolymers and have great potential to replace fossil-based polymers in wood coating applications. The present study investigated the applicability of suberin fatty acids hydrolysate (SFA) extracted from the outer bark of silver birch (Betula pendula Roth.) for coating of aspen wood (Populus tremula L.). The SFA combined with maleic anhydride (MA) and octadecyltrichlorosilane (OTS) as a curing agent was prepared in ethanol and used in surface coating. The water contact angle, surface reflectance spectra, FTIR, and SEM-EDS were used to characterize the physical and chemical properties of the coated wood samples. Further, the long-term stability of the SFA coating was analyzed via artificial aging. The wood surface became hydrophobic, as the contact angle for the water droplet (WCA) was over ~120°, and was stable for all of the prepared combinations of SFA, MA, and OTS.

Trends in Chemical Wood Surface Improvements and Modifications: A Review of the Last Five Years

Increasing the use of wood in buildings is regarded by many as a key solution to tackle climate change. For this reason, a lot of research is carried out to develop new and innovative wood surface improvements and make wood more appealing through features such as increased durability, fire-retardancy, superhydrophobicity, and self-healing. However, in order to have a positive impact on the society, these surface improvements must be applied in real buildings. In this review, the last five years of research in the domain of wood surface improvements and modifications is first presented by sorting the latest innovations into different trends. Afterward, these trends are correlated to specifications representing different normative, ecologic and economic factors which must be considered when expecting to introduce a wood treatment to the market. With this review, the authors hope to help researchers to take into consideration the different factors influencing whether new innovations can leave the research laboratory or not, and thereby facilitate the introduction of new wood surface treatments in the society.

Innovative Polyelectrolyte Treatment to Flame-Retard Wood

Fire protection has been a major challenge in wood construction for many years, mainly due to the high flame spread risk associated with wood flooring. Wood fire-retardancy is framed by two main axes: coating and bulk impregnation. There is a growing need for economically and environmentally friendly alternatives. The study of polyelectrolyte complexes (PECs) for wood substrates is in its infancy, but PECs’ versatility and eco-friendly character are already recognized for fabric fire-retardancy fabrics. In this study, a new approach to PEC characterization is proposed. First, PECs, which consist of polyethyleneimine and sodium phytate, were chemically and thermally characterized to select the most promising systems. Then, yellow birch (Betula alleghaniensis Britt.) was surface-impregnated under reduced pressure with the two PECs identified as the best options. Overall, wood fire-retardancy was improved with a low weight gain of 2 wt.% without increasing water uptake.

Review of Functional Treatments for Modified Wood

Wood modification is now widely recognized as offering enhanced properties of wood and overcoming issues such as dimensional instability and biodegradability which affect natural wood. Typical wood modification systems use chemical modification, impregnation modification or thermal modification, and these vary in the properties achieved. As control and understanding of the wood modification systems has progressed, further opportunities have arisen to add extra functionalities to the modified wood. These include UV stabilisation, fire retardancy, or enhanced suitability for paints and coatings. Thus, wood may become a multi-functional material through a series of modifications, treatments or reactions, to create a high-performance material with previously impossible properties. In this paper we review systems that combine the well-established wood modification procedures with secondary techniques or modifications to deliver emerging technologies with multi-functionality. The new applications targeted using this additional functionality are diverse and range from increased electrical conductivity, creation of sensors or responsive materials, improvement of wellbeing in the built environment, and enhanced fire and flame protection. We identified two parallel and connected themes: (1) the functionalisation of modified timber and (2) the modification of timber to provide (multi)-functionality. A wide range of nanotechnology concepts have been harnessed by this new generation of wood modifications and wood treatments. As this field is rapidly expanding, we also include within the review trends from current research in order to gauge the state of the art, and likely direction of travel of the industry.

The Impact of a CO2 Laser on the Adhesion and Mold Resistance of a Synthetic Polymer Layer on a Wood Surface

In the wood industry, laser technologies are commonly applied for the sawing, engraving, or perforation of solid wood and wood composites, but less knowledge exists about their effect on the joining and painting of wood materials with synthetic polymer adhesives and coatings. In this work, a CO2 laser with irradiation doses from 2.1 to 18.8 J·cm−2 was used for the modification of European beech (Fagus sylvatica L.) and Norway spruce (Picea abies /L./ Karst) wood surfaces—either in the native state or after covering them with a layer of polyvinyl acetate (PVAc) or polyurethane (PUR) polymer. The adhesion strength of the phase interface “synthetic polymer—wood”, evaluated by the standard EN ISO 4624, decreased significantly and proportionately in all the laser modification modes, with higher irradiation doses leading to a more apparent degradation and carbonization of the wood adherent or the synthetic polymer layer. The mold resistance of the polymers, evaluated by the standard EN 15457, increased significantly for the less mold-resistant PVAc polymer after its irradiation on the wood adherent. However, the more mold-resistant PUR polymer was able to better resist the microscopic fungi Aspergillus niger Tiegh. and Penicillium purpurogenum Stoll. when irradiation doses of higher intensity acted firstly on the wood adherent.

Hydrophobization and Photo-Stabilization of Radiata Pinewood: The Effect of the Esterification on Thermal and Mechanical Properties

Wood protection through chemical modification has received increasing interest over the last decades due to the environmental issues related to conventional biocides or protecting products. Consequently, a wide range of new treatments are developed in laboratories, which are later scaled up in the industrial environment. The main goal of modifying wood for indoor–outdoor application is to change its hydrophilic character, which in turn improves the intrinsic properties of the material and its durability against external factors. Wood can be esterified through its hydroxyl groups to obtain a hydrophobic and photo-stable material. Chemical modifications of Pinus radiata D. Don wood using hexanoyl chloride (P6), dodecanoyl chloride (P12), and stearoyl chloride (P18) were carried out at different concentrations. Esterification was confirmed by Fourier Transform Infrared Spectroscopy (FTIR) technique combined with a discriminatory analysis. Weight percent gain was associated with the number of carbons of the aliphatic chain of the fatty acid (P6 > P12 > P18). Moreover, an increase of wood density as a consequence of modification treatments was observed. A substantial improvement of the hydrophobicity of wood was observed by dynamic contact angle measurements. In addition, the effect of ultraviolet (UV) radiation on color changes was reduced with the treatments. Furthermore, the P6 treatment presented acceptable values of modulus of elasticity (MOE) and modulus of rupture (MOR), being suitable for similar mechanical uses as non-treated pinewood. However, only treatments P12 and P18 enhanced thermal resistance of the pinewood in an oxidative atmosphere.

Improving Fungal Decay Resistance of Less Durable Sapwood by Impregnation with Scots Pine Knotwood and Black Locust Heartwood Hydrophilic Extractives with Antifungal or Antioxidant Properties

Research Highlights: The antifungal assay confirmed that knotwood extractives of Scots pine inhibit the growth of wood decay fungi. Heartwood extracts of black locust were found to be much stronger free radical scavengers than the extracts of Scots pine. The extracts were deposited in the lumina and on the wall surface of cells in the impregnated sapwood. Impregnation of the sapwood blocks with Scots pine and black locust extracts reduced the fungal decay of wood. Objectives: Hydrophilic extracts of Scots pine knotwood and black locust heartwood were chemically analyzed, tested for antifungal and antioxidant properties and used for impregnation of beech and Scots pine sapwood. Materials and Methods: Scots pine knotwood and black locust heartwood were extracted, and obtained hydrophilic extractives were chemically analyzed. Extracts were analyzed for antifungal properties with the in vitro well-diffusion method. The free radical scavenging activity of wood extracts was measured colorimetrically. The retention of the extracts in the impregnated sapwood blocks was evaluated with microscopy and gravimetry. A decay test was performed with the mini block test. Results: Almost half of both Scots pine knotwood and black locust heartwood hydrophilic extracts obtained were described by phenolic compounds. The extracts were deposited in the lumina of cells and on the cell wall surface. Extractives of Scots pine knotwood had good inhibitory properties against white- and brown-rot fungi. On the other hand, extractives of black locust heartwood were found to be good radical scavengers, better than knotwood extractives of Scots pine. The extracts of Scots pine knotwood and black locust reduced the fungal decay of the tested sapwood blocks. Conclusions: The results of this research show that the less-valued knotwood of Scots pine and heartwood of black locust are a potential source of antifungal and antioxidant agents for bio-based wood preservatives.

The Staining Effect of Iron (II) Sulfate on Nine Different Wooden Substrates

Leaving wooden façades uncoated has become popular in modern architecture, especially for large buildings like multi-story houses, in order to circumvent frequent maintenance, particularly repainting. To obtain a quick and even artificial graying of the entire façade that gradually turns into natural graying, a one-off treatment with iron (II) sulfate may be applied. Its mode of action is commonly ascribed to a reaction with phenolic wood extractives, especially hydrolyzable tannins. This does not however sufficiently explain iron (II) sulfate’s ability to color wood species containing only marginal amounts of phenolic extractives; moreover, little is known about the influence of the wooden substrate and light conditions on the color development of façades treated with iron (II) sulfate. In the present study, we investigated the influence of wood extractives, exposure conditions, and nine different wooden substrates on iron (II) sulfate’s staining effect. Spruce specimens with and without extractives were treated with a 4% iron (II) sulfate solution and exposed to sunlight behind window glass. Both wood types darkened slowly but significantly during 51 weeks of exposure. This shows that artificial graying with iron (II) sulfate (1) does not require precipitation unlike natural graying, (2) takes place without initial wood extractives, and (3) proceeds at a slow rate. Specimens protected from sunlight changed their color only slightly, suggesting that photo-induced phenoxyl and ketyl radicals from photolysis of lignin’s ether bonds oxidize iron (II) to iron (III). Specimens made of spruce, pine, larch, and western red cedar (WRC) and exposed outdoors decreased strongly in lightness during the first two months of exposure. In contrast, a staining effect of iron (II) sulfate in terms of artificial graying was not seen on acetylated radiata pine, possibly because iron ions are hindered from entering the cell wall. Specimens partly protected by a roof overhang showed an uneven color development; this is due to the protection from radiation and not from precipitation as is known for natural graying.

Innovative Wood Surface Treatments Based on Nanotechnology

This work reviewed innovative wood surface treatments based on nanotechnology. It is well documented in the literature that the cell walls of wood present significant porosity; this porosity is on a molecular scale. The main reason for the use of nanotechnology in wood science and technology is the unique characteristic of nano-based materials to effectively penetrate deeply into wood substrates, which, in turns, results in the alteration of their surface chemistry. This subsequently causes an improvement in wood properties. Any potential change in the wood properties due to treatment with nanomaterials is based on the higher interfacial area which is developed due to the treatment. This occurs because the number of particles is significantly reduced to the nanoscale. The nanomaterials improve the properties of wood as a raw material and alter its original features to a limited extent. However, their potential impact on both health and the environment should be addressed by applying tools such as life-cycle assessments. This will avoid mistakes being made in which new technologies are released on the market prior to an impact assessment having been carried out.

Visualization of the Stimuli-responsive Surface Behavior of Functionalized Wood Material by Chemical Force Microscopy

The hierarchical and porous wood structure provides a stable scaffold to design functionalized lignocellulosic materials with extended properties by chemical modification techniques. However, proper nanoscale characterization methods for these novel materials are needed to confirm the presence of the added functionality and to locate the introduced functional groups with high spatial resolution. Chemical force microscopy is a suitable characterization method to distinguish chemical surface characteristics by scanning the samples surface with a functionalized tip. We report the application of this nanotechnology method on both, unmodified and functionalized wood samples to confirm the thermo-responsive behavior of poly(N-isopropylacrylamide) (PNIPAM) modified spruce wood. By performing force measurements on ultra-microtomed surfaces, adhesion force differences on the analysed structure are monitored and reveal the location and functionality of introduced functional groups. The modified samples are scanned below and above their lower critical solution temperature with a hydrophobic tip in aqueous media to observe adhesion changes. Additionally, confocal Raman microscopy support the chemical force microscopy measurements by revealing the success of the modification and the distribution of PNIPAM across the sample cross-sections. The results show that PNIPAM is mainly located in wood cell wall areas close to the lumen in early- and transitionwood.