Bilayer scaffolds/membranes for bone tissue engineering applications: A systematic review

OBJECTIVE

This systematic review evaluates the purpose, materials, physio-mechanical, and biological effects of bilayer scaffolds/membranes used for bone tissue engineering applications.

METHODS

A comprehensive electronic search of English-language literature from 2012 to October 2022 was conducted in PubMed, Scopus, ScienceDirect, and Google Scholar online databases according to the PRISMA 2020 guidelines. The quality of animal studies was evaluated through the SYRCLE's risk of bias tool.

RESULTS

A total of 77 studies were sought for retrieval, and 39 studies met the inclusion criteria. According to the synthesis results, most bilayers had a dense barrier layer that prevented connective tissue penetration and a loose osteogenic layer that supported cell migration and osteogenesis. PLGA, PCL, and chitosan were the most common polymers in the barrier layers, while the most utilized polymers in osteogenic layers were PLGA and gelatin. Electrospinning and solvent casting were the most common fabrication methods to design the bilayer structures. Many studies reported higher biological results for bilayers compared to their single layers. Also, fabricated bilayers' in vitro osteogenesis and in vivo new bone formation were significantly superior or at least comparable to the frequently used commercial membranes.

CONCLUSION

1) Bilayers with two distinct layers and different materials, porosities, mechanical properties, and biological behavior can significantly improve heterogeneous bone regeneration; 2) the addition of ceramics and/or drugs to the osteogenic layer enhances the osteogenic properties of the bilayers; 3) fabrication method and pore size of the layers play an important role in determining the mechanical and biological behavior of them.

Bone Regeneration of Critical-Size Calvarial Defects in Rats Using Highly Pressed Nano-Apatite/Collagen Composites

Osteo-conductive bone substitute materials are required in dentistry. In this study, highly pressed nano-hydroxyapatite/collagen (P-nHAP/COL) composites were formed by a hydraulic press. Critical-size bone defects (Φ = 6 mm) were made in the cranial bones of 10-week-old Wistar rats, in which P-nHAP/COL and pressed collagen (P-COL) specimens were implanted. Defect-only samples (DEF) were also prepared. After the rats had been nourished for 3 days, 4 weeks, or 8 weeks, ossification of the cranial defects of the rats was evaluated by micro-computed tomography (micro-CT) (n = 6 each). Animals were sacrificed at 8 weeks, followed by histological examination. On micro-CT, the opacity of the defect significantly increased with time after P-nHAP/COL implantation (between 3 days and 8 weeks, p < 0.05) due to active bone regeneration. In contrast, with P-COL and DEF, the opacity increased only slightly with time after implantation, indicating sluggish bone regeneration. Histological inspections of the defect zone implanted with P-nHAP/COL indicated the adherence of multinucleated giant cells (osteoclasts) to the implant with phagocytosis and fragmentation of P-nHAP/COL, whereas active bone formation occurred nearby. Fluorescent double staining indicated dynamic bone-formation activities. P-nHAP/COL is strongly osteo-conductive and could serve as a useful novel bone substitute material for future dental implant treatments.

Effectiveness of a Nanohydroxyapatite-Based Hydrogel on Alveolar Bone Regeneration in Post-Extraction Sockets of Dogs with Naturally Occurring Periodontitis

Pathological mandibular fracture after dental extraction usually occurs in dogs with moderate to severe periodontitis. A nanohydroxyapatite-based hydrogel (HAP hydrogel) was developed to diminish the limitations of hydroxyapatite for post-extraction socket preservation (PSP). However, the effect of the HAP hydrogel in dogs has still not been widely investigated. Moreover, there are few studies on PSP in dogs suffering from clinical periodontitis. The purpose of this study was to evaluate the effectiveness of the HAP hydrogel for PSP in dogs with periodontitis. In five dogs with periodontitis, the first molar (309 and 409) of each hemimandible was extracted. Consequently, all the ten sockets were filled with HAP-hydrogel. Intraoral radiography was performed on the day of operation and 2, 4, 8 and 12 weeks post operation. The Kruskal-Wallis test and paired t-test were adopted for alveolar bone regeneration analysis. The results demonstrated that the radiographic grading, bone height measurement, and bone regeneration analysis were positively significant at all follow-up times compared to the day of operation. Moreover, the scanning electron microscopy with energy-dispersive X-ray spectroscopy imaging after immersion showed a homogeneous distribution of apatite formation on the hydrogel surface. Our investigation suggested that the HAP hydrogel effectively enhances socket regeneration in dogs with periodontitis and can be applied as a bone substitute for PSP in veterinary dentistry.

Clinical efficacy of mineralized collagen (MC) versus anorganic bovine bone (Bio-Oss) for immediate implant placement in esthetic area: a single-center retrospective study

BACKGROUND

The purpose of this retrospective study was to evaluate the clinical efficacy of mineralized collagen (MC) versus anorganic bovine bone (Bio-Oss) for immediate implant placement in esthetic area.

METHODS

Medical records of Department of Oral and Maxillofacial Surgery of Shandong Provincial Hospital were screened for patients who had been treated with immediate implant implantation in the esthetic area using either MC (Allgens®, Beijing Allgens Medical Science and Technology Co., Ltd., China) or Bio-Oss (Bio-Oss®, Geistlich Biomaterials, Wolhusen, Switzerland), between January 2018 and December 2019. All patients fulfilling the in-/exclusion criteria and following followed for a minimum period of 1 year after surgery were enrolled into the presented study. Implant survival rate, radiographic, esthetic and patient satisfactory evaluations were performed.

RESULTS

Altogether, 70 patients were included in the study; a total of 80 implants were inserted. All implants had good initial stability. The survival rate of implants was 100% at 1-year follow-up. The differences in horizontal and vertical bone loss between the MC group (0.72 ± 0.26 mm, 1.62 ± 0.84 mm) and the Bio-Oss group (0.70 ± 0.52 mm, 1.57 ± 0.88 mm) were no significant difference statistically no significant 6 months after permanent restoration. Similar results occurred at 12 months after permanent restoration functional loaded. Clinical acceptability defined by pink esthetic score (PES) ≥ 6 (6.07 ± 1.62 vs. 6.13 ± 1.41) was not significantly different between groups. Patient satisfaction estimated by visual analog scale (VAS) was similar (8.56 ± 1.12 vs. 8.27 ± 1.44), and the difference was no significant difference between the two groups.

CONCLUSIONS

The biomimetic MC showed a similar behaviour as Bio-Oss not only in its dimensional tissues changes but also in clinical acceptability and patient satisfaction. Within the limitations of this study, these cases show that MC could be considered as an alternative bone graft in IIP.

In vitro and in vivo study on the osseointegration of magnesium and strontium ion with two different proportions of mineralized collagen and its mechanism

To explore the optimal combination of Mg²⁺, Sr²⁺ and mineralized collagen (nHAC) with two different proportions of hydroxyapatite (HA) and collagen (COL) on differentiation of MC3T3-E1 and the underlying mechanism, as well as achieve bone osseointegration. MC3T3-E1 cells were cultured in a complete medium with Mg²⁺ at the concentration of 0, 4, 8, 12, 16, 20 mmol/L, Sr²⁺ at the concentration of 0, 3, 6, 12 mmol/L, and the impregnation solution of 3:7 and 5:5nHAC. The differentiation of MC3T3-E1 was measured by expression of osteogenic genes and proteins including Runx-2, BMP-2 and OCN and determined the activation of PI3K/AKT/GSK3β/β-catenin signaling pathway in 12 mmol/LMg²⁺+3 mmol/LSr²⁺+3:7nHAC group. Osteoporosis was induced in 18 female rats by means of ovariectomy, the implants were immersed in 60 mmol/LMg²⁺+15 mmol/LSr²⁺+3:7nHAC impregnation solution and implanted into the mesial alveolar fossa for immediate implantation. The osseointegration of the implants was observed by Confocal laser scanning microscopy (CLSM) and histology at 4 and 8 weeks. The groups cultured with 12 mmol/LMg²⁺, 3 mmol/LSr²⁺ and 3:7nHAC impregnation solution showed the osteogenic genes and proteins were significantly higher respectively (P < 0.05), as well as p-Akt, p-GSK3β and β-catenin proteins (P < 0.05). CLSM and histology showed that the implant surface was surrounded by thick lamellar bone plate, and the trabecular bone were dense and continuous in the impregnation solution. These results found that magnesium and strontium ion-loaded mineralized collagen play an critical role in up-regulating the cells activity through PI3K/AKT/GSK3β/β-catenin signaling pathway and could be promote the formation of osseointegration.

Matrix stiffening by self-mineralizable guided bone regeneration

Collagen membranes produced in vitro with different degrees of intrafibrillar mineralization are potentially useful for guided bone regeneration (GBR). However, highly-mineralized collagen membranes are brittle and difficult for clinical manipulation. The present study aimed at developing an intrafibrillar self-mineralization strategy for GBR membrane by covalently conjugating high-molecular weight polyacrylic acid (HPAA) on Bio-Gide® membranes (BG). The properties of the self-mineralizable membranes (HBG) and their potential to induce bone regeneration were investigated. The HBG underwent the progressive intrafibrillar mineralization as well as the increase in stiffness after immersed in supersaturated calcium phosphate solution, osteogenic medium, or after being implanted into a murine calvarial bone defect. The HBG promoted in-situ bone regeneration via stimulating osteogenic differentiation of mesenchymal stromal cells (MSCs). Hippo signaling was inhibited when MSCs were cultured on the self-mineralized HBG, and in HBG-promoted MSC osteogenesis during in-situ bone regeneration. This resulted in translocation of the transcription co-activators Yes-associated protein (YAP) and transcriptional coactivator with PDZ-binding motif (TAZ) into the nucleus to induce transcription of genes promoting osteogenic differentiation of MSCs. Taken together, these findings indicated that HBG possessed the ability to self-mineralize in situ via intrafibrillar mineralization. The increase in stiffness of the extracellular matrix expedited in-situ bone regeneration by inactivating the Hippo-YAP/TAZ signaling cascade. STATEMENT OF SIGNIFICANCE: Guided bone regeneration (GBR) membranes made of naturally derived collagen have been widely used in the bone defect restoration. However, application of collagen GBR membranes run into the bottleneck with the challenges like insufficient stress strength, relatively poor dimensional stability and unsatisfactory osteoinductivity. This study develops a modified GBR membrane that can undergo progressive self-mineralization and matrix stiffening in situ. Increase in extracellular matrix stiffness provides the mechanical cues required for MSCs differentiation and expedites in-situ bone regeneration by inactivating the Hippo-YAP/TAZ signaling cascade.

Biomineralizaion of hydroxyapatite on polyethylene terephthalate artificial ligaments promotes graft-bone healing after anterior cruciate ligament reconstruction: An in vitro and in vivo study

The purpose of the present study is to modify the polyethylene terephthalate ligament with hydroxyapatite via biomineralization and to investigate its effect on graft-bone healing. After biomineralization of hydroxyapatite, the surface characterization of polyethylene terephthalate ligament was examined by scanning electron microscopy, Fourier transform infrared spectroscopy, X-ray diffraction, and water contact angle measurements. The compatibility and osteoinduction, along with the underlying signaling pathway involved of hydroxyapatite-polyethylene terephthalate ligament, were evaluated in vitro. Moreover, a rabbit anterior cruciate ligament reconstruction model was established, and the polyethylene terephthalate or hydroxyapatite-polyethylene terephthalate artificial ligament was implanted into the knee. The micro-computed tomography analysis, histological, and immunohistochemical examination as well as biomechanical test were performed to investigate the effect of hydroxyapatite coating in vivo. The results of scanning electron microscopy, Fourier transform infrared spectroscopy, and X-ray diffraction showed that the hydroxyapatite was successfully deposited on the polyethylene terephthalate ligament. Water contact angle of the hydroxyapatite-polyethylene terephthalate group was significantly smaller than that of the polyethylene terephthalate group. The in vitro study showed that hydroxyapatite coating significantly improved adhesion and proliferation of MC3T3-E1 cells. The osteogenic differentiation of cells was also enhanced through the activation of ERK1/2 pathway. The micro-computed tomography, histological, and immunohistochemical results showed that biomineralization of hydroxyapatite significantly promoted new bone and fibrocartilage tissue formation at 12 weeks postoperatively. Moreover, the failure load and stiffness in the hydroxyapatite-polyethylene terephthalate group were higher than that in the polyethylene terephthalate group. Therefore, biomineralizaion of hydroxyapatite enhances the biocompatibility and osseointegration of the polyethylene terephthalate artificial ligament, thus promoting graft-bone healing for anterior cruciate ligament reconstruction through the activation of ERK1/2 pathway.

Platelet-rich fibrin and collagen membrane in the preservation of the alveolar bone: Feasibility of the elemental inorganic composition and scanning electron microscopy analysis

The success of dental implants is related to the amount, quality, and composition of the alveolar bone. The placement of platelet-rich fibrin (PRF) clot associated with a resorbable collagen membrane (RCM) in a postextraction alveolus is a technique used for ridge preservation. This case report study analyzed the ultrastructural characteristics of cross-sectioned alveolar bone that received PRF and RCM using scanning electron microscopy and the inorganic composition using "energy dispersive X-ray spectrometry," in order to explore the feasibility of this method to clinical studies. Three alveolar bone samples from two male patients (37 and 58 years old), obtained in the procedure of placing the dental implant, were analyzed. Two bone samples previously received PRF and RCM (M37 and M58), the third sample represented a physiological bone formation without treatment (M37-control). The bone sample M37 showed irregularly shaped islets of calcified material intermingled with connective tissue. The other samples, from the 58-year-old patient with PRF and RCM (M58); and the other untreated bone sample from the same 37-year-old patient (M37-control) showed similar ultrastructural morphology with trabecular conformation without islets agglomerations. The inorganic composition analysis showed higher concentrations of calcium and phosphorus in both samples treated with PRF and RCM in comparison to the untreated bone sample. The Ca/P ratio was higher in the M37 sample compared to the others samples. The results showed morphology and inorganic composition differences among the treatments used, suggesting that this method is feasible to analyze parameters of the alveolar bone tissue.