Scanning electron microscopy observation of dentin bond interfaces in different types of resin luting cements

This study aimed to observe and compare the resin luting cement (RLC)/dentin interfaces of different types of RLC systems with scanning electron microscopy (SEM). This study evaluated six self-adhesive resin luting cement systems (SARLCs), four systems combining a SARLC with a tooth primer (SARLCPs), and six conventional resin luting cement systems (CVRLCs). Cured resin composite rods were bonded to bovine dentin using RLCs in different etching modes. The morphological features at the interfaces were observed using SEM. Although all RLCs in etch-&-rinse (ER) mode showed a clear hybrid layer, most SARLCs had a thinner and more porous hybrid layer than the SARLCPs and CVRLCs. All SARLCPs with primer and CVRLCs showed a thin high-density layer below the primer layer in both etching modes. CVRLCs and SARLCPs with primer treatment systems may be more versatile and reliable when compared to simplified RLC systems.

Prolonged polymerization of a universal adhesive in non-carious cervical lesions: 36-month double-blind randomized clinical trial

OBJECTIVE

To evaluate the effect of prolonged (P) polymerization time of a universal adhesive system applied in etch-and-rinse (ER) or self-etch (SE) strategies on the clinical performance of restorations in non-carious cervical lesions (NCCLs), after 36 months of clinical service.

METHODS

A total of 140 restorations were randomly placed in 35 subjects according to the polymerization time groups: ER (10 s); ER-P (40 s); SE (10 s); and SE-P (40 s) at 1,200 mW/cm2. Composite resin was placed incrementally. The restorations were evaluated immediately and after 6, 12, 18, and 36 months using the FDI criteria. Data were analyzed using the Kaplan-Meier survival test for retention loss, and the Kruskal-Wallis' test for secondary outcomes (α = 0.05).

RESULTS

After 36 months, 19 restorations were lost: ER 6, ER-P 2, SE 9, SE-P 2. The retention rates were 82.3% for ER; 94.1 % for ER-P; 73.5 % for SE; and 94.1 % for SE-P, with a significant difference between ER vs. ER-P and SE vs. SE-P, as well as ER vs. SE-P and ER-P vs. SE (p < 0.0001). Minor defects were observed in 18 restorations for the marginal staining criteria: ER 5, ER-P 2, SE 8, SE-P 3; and in 33 restorations for the marginal adaptation criteria: ER 11, ER-P 4, SE 12, and SE-P 6 (p > 0.05). No restorations showed recurrence of caries or postoperative sensitivity.

CONCLUSIONS

A prolonged polymerization time of 40 s improves the clinical performance of the universal adhesive for both adhesive strategies evaluated, even after 36 months.

CLINICAL SIGNIFICANCE

Prolonging the polymerization time of a universal adhesive from 10 to 40 s has been shown to improve its clinical performance when used in NCCLs.

Comparing Various Resin Luting Cement Systems in Different Etching Modes Through Bond Durability and Morphological Features

OBJECTIVES

This study aimed to investigate bond performance of various resin luting cement (RLC) systems on enamel and dentin in different etching modes and to compare the RLC-tooth interface morphology using scanning electron microscopy (SEM).

METHODS AND MATERIALS

The self-adhesive RLC systems used in combination with universal adhesives were as follows: Scotchbond Universal Adhesive Plus + RelyX Universal (3M Oral Care) and Clearfil Universal Bond Quick ER + SA Luting Multi (Kuraray Noritake Dental). These RLC systems were also used alone as self-adhesive RLC systems without universal adhesives (self-adhesive mode). The conventional RLC systems for comparison materials were as follows: BeautiBond Xtream + ResiCem EX (Shofu) and Tooth Primer + Panavia V5 (Kuraray Noritake Dental). Twelve specimens were prepared for each group to measure shear bond strength (SBS) in different etching modes. A stainless-steel rod was used as a substitute for indirect restorations. Bonded specimens were allocated to baseline (stored for 24 hours) and artificially aged (thermocycling [TC] for 10,000 cycles) groups. Representative treated tooth surfaces and RLC-tooth interfaces were observed using SEM.

RESULTS

Three-way analysis of variance (ANOVA) revealed that all the factors (etching mode, storage period, and RLC system) had a significant influence on the enamel SBS values (p<0.05). Enamel SBS was significantly higher in etch-&-rinse (ER) mode than in self-etch (SE) mode, regardless of RLC system or storage period. Three-way ANOVA showed that all the factors had a significant influence on the dentin SBS values (p<0.001). Most RLC systems showed significantly higher dentin SBS in SE mode than in ER mode, regardless of storage period. However, the combination with Scotchbond Universal Adhesive Plus and RelyX Universal showed no significant difference in SBS values between etching modes at the baseline and showed a significantly higher SBS value in ER mode than in SE mode after TC.

CONCLUSIONS

The self-adhesive RLC systems with universal adhesives tended to show higher enamel and dentin bond performance than the self-adhesive RLC systems alone. The morphology of treated tooth surfaces and resin cement-tooth interfaces were dependent on the RLC system and etching mode used. The RLC systems with primer application showed a thin, high-density layer above the intact dentin in both etching modes, suggesting chemical interaction.

Prolonged application time effects on universal adhesives in non-carious cervical lesions: An 18-month split mouth randomized clinical trial

OBJECTIVE

This double-blind, split mouth randomized clinical trial aimed to assess the clinical performance of Clearfil Universal Bond Quick (CBUq) universal adhesive under different application times (no waiting and waiting) compared to Clearfil SE Bond adhesive in non-carious cervical lesions (NCCLs) over 18 months.

METHODS

One hundred and eighty-three restorations were distributed randomly into three groups based on the adhesive system and waiting time: CUBq without waiting time (CUBq-NW), CUBq with a 20 s waiting time (CUBq-W), and CSE with a 20 s waiting time. After placement, restorations were evaluated after 18 months using the International Dental Federation (FDI) and United States Public Health Service (USPHS) criteria. Statistical analyses involved Friedman repeated measures analysis of variance and Wilcoxon tests, with a significance level set at 5 %.

RESULTS

Over the 18-month period, no restorations were lost across the tested groups. Marginal adaptation evaluation indicated minor discrepancies in 21 restorations (8 CUBq-NW, 6 CUBq-W, and 7 CSE). There were no significant differences observed among the three groups following the 18-month clinical assessment (p > 0.05). Only two restorations showed marginal discoloration after 18 months (1 CUBq-NW and 1 CSE).

CONCLUSIONS

The application of Clearfil Universal Bond Quick using either the "waiting" or "no-waiting" technique exhibited excellent clinical results in NCCLs during the 18-month follow-up period, demonstrating comparable performance to Clearfil SE Bond in all assessed outcomes.

CLINICAL SIGNIFICANCE

The findings suggest that the new universal adhesive applied using the no-waiting technique demonstrates promising clinical performance when compared to conventional application methods.

TRIAL REGISTRATION

ClinicalTrials.gov identifer RBR-69p7mpr.

Effect of the prism-interprisms three-dimension spatial microstructure on the enamel bond strength

The prism-interprisms level of the enamel hierarchical microstructure is the largest degree of structural variation and most sophisticated structural adaptation. We studied the effect of the prism-interprisms three-dimension spatial microstructure on the enamel bond strength. We prepared 11 groups of enamel segments: longitudinally sectioned segments with or without a 45-degree bevel (group = 2), horizontally sectioned segments with or without a 45-degree bevel of three regions (the incisal, middle, and cervical) (group = 6), and tangential (labial) sectioned segments of three regions (the incisal, middle, and cervical) (group = 3). The finished surface of each segment was observed by scanning electric microscopy (SEM) before treatment with four self-etch adhesive systems and applied with four corresponding composite resins. Resin-bonded enamel samples were prepared in beams for microtensile bond strength (MTBS) tests. The results were analyzed with a three-way ANOVA followed by Tukey's post-hoc HSD multiple comparisons procedure. SEM observations revealed complex arrangements of prisms and interprisms. MTBS measurement showed that the longitudinally sectioned group had the lowest value, without significant differences between the groups with or without 45-degree bevel. Combining SEM observations and MTBS measurements, the prism-interprisms microstructure varied with the incisor regions, and different prism-interprisms microstructures allowed diverse sectioned surfaces, which could affect the enamel bonding.

48-month clinical evaluation of a copper-containing universal adhesive in non-carious cervical lesions: A double-blind randomised clinical trial

OBJECTIVES

This study aimed to evaluate the effect of copper nanoparticles (CuNp) on the clinical performance of a universal adhesive system used as an etch-and-rinse or self-etch strategy.

METHODS

A total of 216 class V (non-carious lesions) restorations were randomly placed in 36 subjects according to the following groups: ERcu, adhesive in etch-and-rinse with 0.1% CuNp; ERct, adhesive in etch-and-rinse without CuNp; SEcu, adhesive in self-etch with 0.1% CuNp; and Sect, adhesive in self-etch without CuNp. Restorations were evaluated at baseline and at 6, 12, 18, 36, and 48 months, using the FDI and USPHS criteria. Appropriate statistical analyses were performed (α = 0.05).

RESULTS

After 48 months, 14 restorations were lost (two for ERcu, five for SEcu, and seven for SEct) and the retention rates (95% confidence interval [CI]) were 74.1% for ERcu (95% CI 61.1-83.8); 81.5% for ERct (95% CI 69.2-89.6); 64.8% (95% CI 51.5-76.2) for SEcu; and 64.8% (95% CI 51.5-76.2) for SEct, with statistical differences between SEct vs. ERct and SEcu vs. ERct (p < 0.05). No significant differences between the groups were observed when the secondary parameters were evaluated (p > 0.05). Nineteen restorations (two for ERcu, two for ERct, six for SEcu, and nine for SEct) showed minor marginal staining, and 44 restorations (7 for ERcu, 8 for ERct, 14 for SEcu, and 15 for SEct) presented minimal marginal adaptation defects.

SIGNIFICANCE

This is the first long-term clinical trial to show that the addition of CuNp to a universal adhesive system does not affect clinical performance.

Twenty-month Performance of a Universal Bonding System on Simulated-challenged Dentin Substrates Pretreated with Chlorhexidine

OBJECTIVES

Since the use of dentin antiproteolytic agents with universal adhesives (UAs) can potentially degrade the bonding interface, this study evaluated bond strengths with and without chlorhexidine (CHX) on variously altered dentin surfaces for up to 20 months.

METHODS

Human molar specimens (n=20) were categorized by substrates as S=sound, E=eroded, and C=carious, and by pretreatment as W=water or CHX. These specimens were subjected to micro-tensile bond strength (μTBS) testing at 24 hours, 6 months, and 20 months, after 30 seconds of pretreatment with CHX or W, followed by self-etching and bonding (Adper Single Bond Universal, 3M ESPE). Modes of failure were assessed using optical microscopy (40×) and scanning electron microscopy (SEM), and the results were analyzed by 3-way ANOVA and Tukey's statistical tests (α=0.05).

RESULTS

Substrate (p<0.001), pre-treatment (p=0.0413), and time (p<0.0001) were statistically significant. The sound-dentin group in initial time (W=39.27/CHX=40.55) yielded the higher μTBS values (MPa) in comparison with altered substrates pre-treated with CHX (E-CHX=19.84; C-CHX=18.24) after 20 months, which showed the lowest values. Under SEM analysis, heterogeneous patterns appeared in the hybrid layer of the CHX-treated group, particularly in the altered substrates.

CONCLUSIONS

Bond strength to dentin decreased over a period of 20 months using UA with 10-methacryloyloxydecyl-dihydrogen phosphate (MDP) in self-etching mode. Substrates altered by erosion or caries have impaired adhesion and associated clinical use of UA with MDP and CHX should be avoided.

Effect of Different Application Modalities on the Bonding Performance of Adhesive Systems to Dentin: A Systematic Review and Meta-Analysis

Diverse types of dental adhesives exhibit different cytotoxic outcomes on cells in vitro. Currently, no standard adhesive application technique has so far been decisive for clinicians for better durability of resin-dentin bonds of adhesive systems. The purpose of this study was to systematically review the literature to evaluate the bonding performance of adhesive systems to dentin by using different application modalities. The systematic research strategy was conducted by two reviewers among multiple databases: PubMed, Scopus, Web of Science, Embase, and Scielo. In vitro studies reporting the effects of additional steps for the application of adhesive systems on the bond strength to dentin were selected. Meta-analysis was performed using Review Manager Software version 5.3.5 using the random effects model. The methodological quality of each in vitro study was assessed according to the parameters of a previous systematic review. The electronic research through different databases generated a total of 8318 references. After the examination of titles and abstracts, a total of 106 potentially relevant studies accessed the full-text evaluation phase. After full-text examination, 78 publications were included for the qualitative analysis, and 68 studies were included in the meta-analysis. Regarding the etch-and-rinse adhesive systems, the application modalities that improved the overall bond strength were the application of a hydrophobic resin layer (p = 0.005), an extended application time (p < 0.001), an application assisted by an electric current (p < 0.001), a double-layer application (p = 0.05), the agitation technique (p = 0.02), and the active application of the adhesive (p < 0.001). For self-etch adhesive systems, the techniques that improved the overall bond strength were the application of a hydrophobic resin layer (p < 0.001), an extended application time (p = 0.001), an application assisted by an electric current (p < 0.001), a double-layer application (p < 0.001), the agitation technique (p = 0.01), and the active application of the adhesive (p < 0.001). The in vitro evidence suggests that the application of adhesive systems using alternative techniques or additional strategies may be beneficial for improving their bond strength to dentin. The application modalities that favored the overall bond strength to dentin were an extended application time, a double-layer application, an application assisted by an electric current, the active application of the adhesive, and the application of a hydrophobic resin layer. Worth mentioning is that some techniques are intended to increase the degree of the conversion of the materials, and therefore, improvements in the biocompatibility of the materials can be expected.

Role of the smear layer in adhesive dentistry and the clinical applications to improve bonding performance

Currently, dental adhesives can be divided into two systems; a smear layer-removal approach with etch-and-rinse adhesives or a smear layer-modified approach with self-etching adhesives. After phosphoric acid etching, the smear layer is completely removed. More attention is, however, required when using self-etching adhesives. The smear layer is partially demineralized by the weak acidic monomer and subsequently incorporated into the hybrid layer. Therefore, the characteristics of the smear layer play an important role on the bonding performance of self-etching adhesives. Such characteristics, for instance, smear layer thickness and smear layer density, are influenced by many factors, e.g., instruments used for dentin surface preparation, cutting speed, and the abrasive particle size of the cutting instruments. This review discusses the contributing factors that affect the smear layer characteristics, and the influence of the smear layer on the bonding performance of dental adhesives. Also, the application techniques regarding how to improve the bonding performance of self-etching adhesives – the smear layer removal by using chemical agents, or the modification of the adhesive application procedures – are provided.

Investigation of the Effects of Adhesive Materials of Different Types and Thicknesses on Dental Tissue Stress via FEM Analysis

The aim of this study was to investigate the types and thicknesses of adhesive materials used in restorative treatment in dentistry in class I occlusal and class II disto-occlusal cavities and to examine the effects of stress distribution on enamel, dentin, restoration material, and adhesive material using the finite element stress analysis method. A 3-dimensional geometry of the tooth was obtained by scanning the extracted 26 numbered upper molar tooth with dental tomography. The 3D geometry obtained by using the Geomagic Design X 2020.0 software was divided into surfaces, and necessary arrangements were made. With the Solidworks 2013 software, 2 different cavity modeling, class I occlusal and class II disto-occlusal, with a cavity angle of 95 degrees on the 3D model, as well as 10, 30, and 50 micrometers thick, four types of adhesive materials and the modeling of the bulk-fill composite material on it were made. With finite element stress analysis, the stress distribution was analyzed using the Abaqus software. The materials used in the study are included in the simulation as isotropic linear elastic. Periodontal ligament and jawbone were not included in the analysis. A total of 600 N pressure was applied on the models. In our study, it was observed that the amount of stress on the tooth structures changed when the thickness, elastic modulus, and Poisson ratios of the adhesive material were changed. In addition, when all models are examined, it is seen that when the thickness is increased, more stress is placed on the adhesive material compared to the restoration, while when 50-micrometer-thick adhesive material is used, more stress is placed on the restoration compared to the adhesive material.

Influence of bonding agent application method on the dentin bond durability of a two-step adhesive utilizing a universal-adhesive-derived primer

This study investigated the effect of the bonding agent application method on the dentin bond durability of a two-step adhesive utilizing a universal-adhesive-derived primer. The bonding durability of a universal adhesive was compared with those of two conventional two-step adhesives by shear bond strength testing after thermal cycling. The primer was applied (with or without phosphoric acid pre-etching), and the specimens were divided into three groups based on the bonding agent application method used as follows: (i) strong air-flow application, (ii) gentle air-flow application, and (iii) gentle air-flow + second bonding application. The shear bond strength was determined after thermal cycling. All the factors (bonding agent application method, adhesive system, and storage condition) significantly influenced the dentin shear bond strength both with and without phosphoric acid pre-etching. The specimens exposed to gentle air-flow showed a higher shear bond strength than did those exposed to strong air-flow and gentle air-flow + second bonding. The bond durability of the tested adhesive systems was influenced by the bonding agent application method, and this trend was material dependent. The G2-Bond Universal exhibited the same or greater dentin bond durability to the other two-step adhesive systems.

Effect of Intraoral Humidity on Dentin Bond Strength of Two Universal Adhesives: An In Vitro Preliminary Study

This study investigated the effect of intraoral humidity on microtensile bond strength (μTBS) to dentin of two universal adhesives applied in self-etch (SE) mode. Forty extracted human molars were selected for this study. Dentin specimens were allocated into four groups, standardized and then bonded with two commercial multimode adhesives, according to two humidity conditions (50% relative humidity (RH) and 90% RH). Following composite resin build-up and 24 h of water storage, the μTBS of the bonded interface was analyzed. The 50% RH was higher for Scotchbond Universal (SBU) than Prime&Bond Universal (PBU), while for 90% RH, SBU had significantly lower values than PBU. With PBU, the mean bond strength was not significantly different between both humidity settings tested (p > 0.05), while for SBU, the mean bond strength was significantly different between both conditions tested (p < 0.05); μTBS was significantly higher for 50% RH than for the other group. Within the limitation of this in vitro study, it can be concluded that: 1) the bonding performance of adhesives systems depends on the humidity settings; 2) increased RH exerts a detrimental effect on the bond strength of 2-hydroxyethyl methacrylate (HEMA)-containing adhesive tested. However, this phenomenon was not observed for HEMA-free adhesive tested; 3) further research in this area is needed to investigate different adhesive systems, temperatures and humidity settings.

Effect of Active Bonding Application after Selective Dentin Etching on the Immediate and Long-Term Bond Strength of Two Universal Adhesives to Dentin

The objective was to evaluate the influence of active bonding applications (ABA) for different time intervals after selective dentin etching (SDE) for 3 s on the microtensile bond strength (μTBS) to dentin of two universal adhesive systems (UAs): one containing 2-hydroxyethyl methacrylate (HEMA) (Scotchbond Universal, SBU), and one that was HEMA-free (Prime&Bond Universal, PBU). Dentin bovine specimens were divided into four groups: self-etch as control (SE), SDE + ABA for 15 s (SDE15), SDE + ABA for 20 s (SDE20), and SDE + ABA for 25 s (SDE25). The μTBS test was performed after a water storage of 24 h and 6 months. Scanning electron microscopy (SEM) was used in order to examine the resin−dentin interface. For the PBU, the µTBS was significantly influenced only by the aging factor (p < 0.026). A statistically significant decrease in the µTBS after 6 months of aging was observed only for the SDE15 group. For SBU, µTBS was significantly influenced by the protocol application and the aging time (p ≤ 0.041). The groups SDE15, SDE20, and SDE25 achieved statistically significant higher values (after 24 h and 6 months). No considerable variances were noticed in the homogeneity and continuity of the hybrid layer (HL) among the groups. In conclusion, SDE and ABA improved the µTBS only of a HEMA-containing universal adhesive.

Dentin contamination during repair procedures: A threat to universal adhesives?

Objective

This study examined the influence of surface contamination during repair procedures with hydrofluoric acid, silane, or ammonium polyfluoride on the bond strength of universal adhesives to dentin using different etching modes before and after thermocycling.

Materials and Methods

Dentin surfaces of human molars were contaminated in different ways (silane, hydrofluoric acid, ammonium polyfluoride, and no pretreatment as control) followed by application of a universal adhesive (etch & rinse or self‐etch mode). After a composite build‐up was placed onto each tooth, sticks for the microtensile bond strength (MTBS) test were sectioned. Half of the sticks were tested after water storage for 24 h, the other half after thermocycling (15,000 cycles, 5/55°C). The MTBS data were analyzed statistically by using the Kolmogorov–Smirnov test, one‐way analysis of variance, and Tukey HSD test (p < 0.05). The fracture patterns of all specimens were evaluated and analyzed using a χ² test.

Results

Dentin contamination with a multifunctional silane does not influence microtensile bond strength irrespective of aging. Contamination with hydrofluoric acid or an ammonium polyfluoride primer leads to a significantly lower bond strength after aging, irrespective of the etch mode.

Conclusion

Dentin contamination with hydrofluoric acid or ammonium polyfluorides during repair procedures should be avoided, as they appear to decrease the bond strength of universal adhesives.

Effect of Adhesive Application Method on the Enamel Bond Durability of a Two-Step Adhesive System Utilizing a Universal Adhesive-Derived Primer

This study aimed to evaluate the effect of the adhesive application method on the durability of the enamel bond and the thickness of the adhesive layer. A new-generation two-step universal adhesive system, G2-Bond Universal, and two conventional two-step adhesive systems were utilized. The shear bond strength to bovine enamel was measured after thermal cycling in both etch-and-rinse and self-etch modes. Fifteen specimens were divided into three groups as follows: Group I, wherein a strong air stream was applied over the bonding agent for 5 s; Group II, wherein a gentle air stream was applied over the bonding agent for 5 s; and Group III, which was prepared as in Group II, followed by the application of a second layer of the bonding agent and a gentle air stream for 5 s. The durability of the enamel bond and thickness of the tested adhesives were influenced by the application method in both etching modes. The application method used in Group II appeared to be most suitable in terms of the bonding of the adhesives to the enamel. The new-generation two-step self-etch adhesive, comprising a universal adhesive-derived primer and a hydrophobic bonding agent, showed superior bond performance to the conventional two-step adhesive systems.

Bond Strength of Universal Adhesives to Dentin: A Systematic Review and Meta-Analysis

Currently, the availability of a wide variety of universal adhesives makes it difficult for clinicians to choose the correct system for specific bonding situations to dentin substrate. This study aimed to determine whether there are any alternative techniques or additional strategies available to enhance the bond strength of universal adhesives to dentin through a systematic review and meta-analysis. Two reviewers executed a literature search up to September 2020 in four electronic databases: PubMed, ISI Web of Science, Scopus, and EMBASE. Only in vitro studies that reported the dentin bond strength of universal adhesives using additional strategies were included. An analysis was carried out using Review Manager Software version 5.3.5 (The Nordic Cochrane Centre, The Cochrane Collaboration, Copenhagen, Denmark). The methodological quality of each in vitro study was assessed according to the parameters of a previous systematic. A total of 5671 potentially relevant studies were identified. After title and abstract examination, 74 studies remained in systematic review. From these, a total of 61 studies were included in the meta-analysis. The bond strength of universal adhesives to dentin was improved by the use of one of the following techniques: Previous application of matrix metalloproteinases (MMP) inhibitors (p < 0.001), prolonged application time (p = 0.007), scrubbing technique (p < 0.001), selective dentin etching (p < 0.001), non-atmospheric plasma (p = 0.01), ethanol-wet bonding (p < 0.01), prolonged blowing time (p = 0.02), multiple layer application (p = 0.005), prolonged curing time (p = 0.006), and hydrophobic layer coating (p < 0.001). On the other hand, the use of a shortened application time (p = 0.006), and dentin desensitizers (p = 0.01) impaired the bond strength of universal adhesives to dentin. Most of the analyses performed showed a high heterogenicity. The in vitro evidence suggests that the application of universal adhesives using some alternative techniques or additional strategies may be beneficial for improving their bonding performance to dentin. This research received no external funding. Considering that this systematic review was carried out only with in vitro studies, registration was not performed.

Evaluation of gap formation at the composite resin-tooth interface after using universal adhesives: In vitro SEM study using the replica technique

The aim of this study was to evaluate gap formation after using two universal adhesives, Peak Universal Bond (P), which contains chlorhexidine and Adhese Universal (A), which contains 10-MDP monomer, and to compare them with two gold standard adhesives. The adhesives were tested in different etching modes, etch-and-rinse (ER) or self-etch (SE), and under thermomechanical loading (TML). Two identical Class V cavities were prepared in each of 30 human third molar teeth, and resin-composite restorations were made. Before and after TML, replicas of the restorations were prepared. Gap formation and their frequency according to the modified classification of Blunck and Zaslansky and the width of the maximum marginal gap (MG) were separately evaluated in enamel and dentin. Gap frequency did not differ significantly only in the enamel before TML, despite the use of different adhesives or etching modes. At both timepoints, the highest MG values were obtained with the Peak Universal Bond self-etch (PSE) group in enamel (6.2 μm before TML, 12.2 μm after TML) and the Peak Universal Bond etch-and-rinse (PER) group in dentine (21.3 μm before TML, 35.5 μm after TML). After TML, there was a significant increase of gap frequency for Adhese universal self-etch (ASE) group and MG values for PER, PSE, ASE groups at the resin-enamel interface, and gap frequency and MG values for all groups at the resin-dentin interface. Universal adhesive with 10-MDP monomer have beneficial effect on the resin-dentin interface, while chlorhexidine may reduce the resistance of the universal adhesive system to oral cavity conditions.

Influence of Application Time on Dentin Bond Performance in Different Etching Modes of Universal Adhesives

We attempted to determine the effect of universal adhesive application time on dentin bond performance in different etching modes based on shear bond strength (SBS) tests and surface free energy (SFE) measurements. The five universal adhesives used were Adhese Universal (AU), Clearfil Universal Bond Quick (CQ), G-Premio Bond (GP), Scotchbond Universal (SU), and Tokuyama Universal Bond (TU). Bovine dentin specimens were divided into four groups of 10 for each adhesive. SBS and SFE were determined after applying the following surface treatments: 1) self-etch (SE) mode with immediate air blowing after adhesive application (IA treatment), 2) SE mode with prolonged application time (PA treatment), 3) etch-and-rinse (ER) mode with IA treatment, and 4) ER mode with PA treatment. Bonded specimens were subjected to SBS testing. The SFE of adhesive-treated dentin surfaces was measured after rinsing with acetone and water. Three-way analysis of variance revealed that dentin SBS values (p<0.001) were significantly influenced by the factors of adhesive type and application duration, but the factor of pre-etching was not significant (p=0.985). The manufacturer's instructions require longer application times for AU and SU, which showed significantly lower SBS values in IA than in PA treatment in both etching modes. However, the difference in the other adhesives was not significant between the IA and PA treatments in either etching mode. The total SFE (γ_S) was dependent on the adhesive and etching mode. The γ_S value of the initial group (SiC paper ground group) at baseline was 69.5 (mN·m^-1) and that of the pre-etching group at baseline was 30.6 (mN·m^-1). For all the adhesives, γ_S in SE mode showed significantly higher values than in ER mode, regardless of the application time. In SE mode, almost all universal adhesives tested showed lower γ_S values in PA treatment than in IA treatment. For ER mode, all the adhesives showed significantly higher γ_S values than those of the pre-etching baseline, regardless of the application time. Most adhesives did not show any significant differences in γ_S values between IA and PA treatments, regardless of etching mode.

The Effect of Diode and Er,Cr:YSGG Lasers on the Bond Strength of Fiber Posts

Background: Laser irradiation modifies the topography and composition of dentin surface aiming to increase the retention of bonded posts. Objective: To assess the effect of dentin irradiation with Er,Cr:YSGG or diode lasers on the bond strength of fiber posts using self-adhesive resin cement. Materials and methods: Sixty bovine root canals were root-canal treated, post spaces were prepared, and subsequently fiber posts were cemented. The samples were distributed according to the surface treatment: distilled water (control), Er,Cr:YSGG (1.5 W, 20 sec), or diode (1.5 W, 20 sec) lasers. Bond strengths were assessed by pull-out (n = 10) or push-out testing (n = 10). Pearson's correlation was calculated. Failure mode after testing and the depth of tags in the dentinal tubules were analyzed by confocal laser microscopy. Data were submitted to analysis of variance and Tukey's test. A p < 0.05 was considered significant. Results: In the push-out test, Er,Cr:YSGG laser had significantly different higher values (5.43 ± 0.10 MPa) compared to the control (4.79 ± 0.05 MPa). Diode laser values were not significantly different from the other groups (5.12 ± 0.27 MPa). In the pull-out test, there were no significant differences between Er,Cr:YSGG (6.86 ± 2.16 MPa) and diode (8.43 ± 1.77 MPa) lasers, and both had significant differences compared to the control (4.18 ± 1.29 MPa). No correlation was found. Adhesive failures were predominant in all groups, and no significant differences in tag penetration among the groups were found. Conclusions: The Er,Cr:YSGG laser increases the bond strength of resin cement and fiber post to dentin in both tests, compared to control group without laser treatment. Diode laser only enhanced bonding for pull-out test.

Universal dental adhesives: Current status, laboratory testing, and clinical performance

Increasing demand for simplified and user-friendly adhesive systems has led to the development of a new class of adhesives termed as Universal Adhesives (UAs). The term "Universal" reflects manufacturers' claims that these adhesives can be applied with any adhesion strategy and offer the versatility of use with a variety of direct and indirect restorative materials. The aim of this review was to synthesize the literature regarding the current status of UAs, their adhesion potential to various substrates and their performance in different restorative situations. In vitro studies, clinical trials and systematic reviews were identified utilizing controlled vocabulary and keyword searches in Medline and EMBASE databases. About 282 studies (272 in vitro studies; 11 clinical studies) were included. Available laboratory and clinical evidence does not support the claim that UAs can be used with any adhesive strategy. Although, they can chemically bond to various tooth and direct/indirect restorative substrates, the stability of this bond is material-dependent and subject to hydrolytic degradation. Hence, additional measures are still needed to ensure long-term durability. which undermines the versatility of UAs. The lack of long-term data regarding the clinical performance of UAs further complicates clinical decision-making. © 2019 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 107B: 2121-2131, 2019.