Giemsa as a fluorescent dye for mineralizing bone-like nodules in vitro

Giemsa was first used as a fluorescent dye for mineralized bone and cartilage in tissue sections. The aim of this study was to establish the use of Giemsa as a fluorescent dye for mineralizing bone-like nodules produced in cell cultures. Osteoblasts were grown under mineralizing conditions for 14 days, producing typical bone-like nodules. Upon staining with Giemsa stock solution for 1 min, the mineralizing nodules could be selectively visualized emitting intense green and red fluorescence when observed under blue and green illumination, respectively. The textural details of the nodules were clearly observed under fluorescence microscopy, allowing to identify regions with different degrees of mineralization. The mineralized nature of the nodules was confirmed using von Kossa's method, Alizarin Red S staining and x-ray mapping for Ca and P in a scanning electron microscope, showing a strong correlation between the mineralizing and the fluorescent nodules. The selective fluorescence was related to the mineral phase, being absent in decalcified samples. The use of Giemsa as a fluorescent dye for mineralizing bone-like nodules presents a simple alternative method to quickly analyze biomineralization assays in vitro under fluorescence microscopy, particularly in the biological evaluation of biomaterials.

Ultrastructural and mineral phase characterization of the bone-like matrix assembled in F-OST osteoblast cultures

Cell cultures are often used to study bone mineralization; however, not all systems achieve a bone-like matrix formation. In this study, the mineralized matrix assembled in F-OST osteoblast cultures was analyzed, with the aim of establishing a novel model for bone mineralization. The ultrastructure of the cultures was investigated using scanning electron microscopy, atomic force microscopy, and transmission electron microscopy (TEM). The mineral phase was characterized using conventional and high-resolution TEM, energy-dispersive X-ray spectroscopy, X-ray diffraction, Fourier transform infrared spectroscopy, and solid-state (31)P and (1)H nuclear magnetic resonance. F-OST osteoblast cultures presented a clear nodular mineralization pattern. The chief features of the mineralizing nodules were globular accretions ranging from about 100 nm to 1.5 μm in diameter, loaded with needle-shaped crystallites. Accretions seemed to bud from the cell membrane, increase in size, and coalesce into larger ones. Arrays of loosely packed, randomly oriented collagen fibrils were seen along with the accretions. Mineralized fibrils were often observed, sometimes in close association with accretions. The mineral phase was characterized as a poorly crystalline hydroxyapatite. The Ca/P atomic ratio was 1.49 ± 0.06. The presence of OH was evident. The lattice parameters were a = 9.435 Å and c = 6.860 Å. The average crystallite size was 20 nm long and 10 nm wide. Carbonate substitutions were seen in phosphate and OH sites. Water was also found within the apatitic core. In conclusion, F-OST osteoblast cultures produce a bone-like matrix and may provide a good model for bone mineralization studies.

Osteoblast proliferation on hydroxyapatite thin coatings produced by right angle magnetron sputtering

Right angle magnetron sputtering (RAMS) was used to produce hydroxyapatite (HA) film coatings on pure titanium substrates and oriented silicon wafer (Si(0 0 1)) substrates with flat surfaces as well as engineered surfaces having different forms. Analyses using synchrotron XRD, AFM, XPS, FTIR and SEM with EDS showed that as-sputtered thin coatings consist of highly crystalline hydroxyapatite. The HA coatings induced calcium phosphate precipitation when immersed in simulated body fluid, suggesting in vivo bioactive behavior. In vitro experiments, using murine osteoblasts, showed that cells rapidly adhere, spread and proliferate over the thin coating surface, while simultaneously generating strong in-plane stresses, as observed on SEM images. Human osteoblasts were seeded at a density of 2500 cells cm(-2) on silicon and titanium HA coated substrates by RAMS. Uncoated glass was used as a reference substrate for further counting of cells. The highest proliferation of human osteoblasts was achieved on HA RAMS-coated titanium substrates. These experiments demonstrate that RAMS is a promising coating technique for biomedical applications.