Effect of Ceramic and Dentin Thicknesses and Type of Resin-Based Luting Agents on Intrapulpal Temperature Changes during Luting of Ceramic Inlays

The adhesive cementation of ceramic inlays may increase pulpal temperature (PT) and induce pulpal damage due to heat generated by the curing unit and the exothermic reaction of the luting agent (LA). The aim was to measure the PT rise during ceramic inlay cementation by testing different combinations of dentin and ceramic thicknesses and LAs. The PT changes were detected using a thermocouple sensor positioned in the pulp chamber of a mandibular molar. Gradual occlusal reduction obtained dentin thicknesses of 2.5, 2.0, 1.5, and 1.0 mm. Light-cured (LC) and dual-cured (DC) adhesive cements and preheated restorative resin-based composite (RBC) were applied to luting of 2.0, 2.5, 3.0, and 3.5 mm lithium disilicate ceramic blocks. Differential scanning calorimetry was used to compare the thermal conductivity of dentin and ceramic slices. Although ceramic reduced heat delivered by the curing unit, the exothermic reaction of the LAs significantly increased it in each investigated combination (5.4–7.9 °C). Temperature changes were predominantly influenced by dentin thickness followed by LA and ceramic thickness. Thermal conductivity of dentin was 24% lower than that of ceramic, and its thermal capacity was 86% higher. Regardless of the ceramic thickness, adhesive inlay cementation can significantly increase the PT, especially when the remaining dentin thickness is <2 mm.

The effect of high-irradiance rapid polymerization on degree of conversion, monomer elution, polymerization shrinkage and porosity of bulk-fill resin composites

OBJECTIVE

The purpose was to compare the degree of conversion (DC), monomer elution (ME), polymerization shrinkage (PS) and porosity of two addition-fragmentation chain transfer (AFCT) modified resin-based composites (RBC) light-cured with rapid- (RP), turbo- (TP) or conventional polymerization (CP) settings.

METHODS

Cylindrical samples (6-mm wide, 4-mm thick) were prepared from Tetric PowerFill (TPF) and Filtek One Bulk (FOB). Four groups were established according to the polymerization settings: 3s-RP, 5s-TP, 10s-CP and 20s-CP. Samples in 1 mm thickness with 20s-CP settings served as controls. The DC at the top and bottom surfaces was measured with micro-Raman spectroscopy. ME was detected with high-performance liquid chromatography. PS and porosity were analyzed by micro-computed tomography. ANOVA and Tukey's post-hoc test, multivariate analysis and partial eta-squared statistics were used to analyze the data (p < 0.05).

RESULTS

FOB showed higher DC values (61.5-77.5 %) at the top compared to TPF (43.5-67.8 %). At the bottom TPF samples achieved higher DCs (39.9-58.5 %) than FOB (18.21-66.18 %). Extending the curing time increased DC (except the top of FOB) and decreased ME. BisGMA release was the highest among the detected monomers from both RBCs. The amount was three-fold more from TPF. The factor Material and Exposure significantly influenced DC and ME. PS (1.8-2.5 %) did not differ among the groups and RBCs except for the lowest value of TPF cured with the 3s_RP setting (p = 0.03). FOB showed 4.5-fold lower porosity (p < 0.001). Significantly higher pore volume was detected after polymerization in 3s_RP (p < 0.001).

SIGNIFICANCE

High-irradiance rapid 3-s curing of AFCT modified RBCs resulted in inferior results for some important material properties. A longer exposure time is recommended in a clinical situation.