Investigation on Synthesis of Hydrogel Starting from Vietnamese Pineapple Leaf Waste-Derived Carboxymethylcellulose

Carboxymethyl cellulose (CMC) is obtained from Vietnamese pineapple leaf waste through etherification. By treating pineapple leaf powder with a solution of NaOH then with HNO₃ at 90°C for an appropriate time, cellulose can be efficiently extracted. To obtain CMC, carboxymethylation was performed by reaction of the pineapple cellulose with chloroacetic acid at 60°C for 1.5 h. The optimal conditions for this reaction were established. The resulting CMC had a degree of substitution (DS) of 0.91. The hydrogel was prepared by graft copolymerization of acrylic acid and acrylamide to the synthesized CMC. During that reaction, N,N'methylenebisacrylamide (MBA) served as the crosslinking agent and ammonium persulfate (APS) as the initiator. The maximum hydrogel absorbencies for distilled water and 0.9 wt.% NaCl solution were relatively high, namely, 588.2 g/g and 79.3 g/g, respectively. Additionally, the water swelling and water retention behaviors of the hydrogel in soil were also investigated. The results showed that this hydrogel can be employed as a suitable moisture-holding additive in soil for cultivation purposes.

Production of biodiesel from Vietnamese Jatropha curcas oil by a co-solvent method

Biodiesel fuels (BDFs) was successfully produced from Vietnamese Jatropha curcas oil with high content of free fatty acids (FFAs) in two stages. In the first stage, the esterification process was carried out with the optimal conditions as follows; a methanol-to-FFAs molar ratio of 6:1, 1 wt% H2SO4, at a temperature of 65 °C, and using 30% (wt/wt) acetonitrile as co-solvent. This step reduced the concentration of FFAs in the reaction mixture from 15.93 to 2 wt% in 60 min. In the second stage, the transesterification process generated fatty acid methyl esters (FAMEs) with 99% efficiency was performed in 30 min with the optimal conditions as follows; a methanol-to-oil molar ratio of 6:1, 1 wt% KOH, at a temperature of 40 °C, and 20% (wt/wt) acetone as co-solvent. The produced biodiesel quality meets the standards JIS K2390 and EN 14214 regarding FAME yield, FFAs and water contents.