Ag Catalysts Supported on CeO2, MnO2 and CeMnOx Mixed Oxides for Selective Catalytic Reduction of NO by C3H6

In the present study CeO₂, MnO₂ and CeMnO_x mixed oxide (with molar ratio Ce/Mn = 1) were prepared by sol-gel method using citric acid as a chelating agent and calcined at 500 °C. The silver catalysts (1 wt.% Ag) over the obtained supports were synthesized by the incipient wetness impregnation method with [Ag(NH₃)₂]NO₃ aqueous solution. The selective catalytic reduction of NO by C₃H₆ was investigated in a fixed-bed quartz reactor using a reaction mixture composed of 1000 ppm NO, 3600 ppm C₃H₆, 10 vol.% O₂, 2.9 vol.% H₂ and He as a balance gas, at WHSV of 25,000 mL g^-1 h^-1.The physical-chemical properties of the as-prepared catalysts were studied by several characterization techniques, such as X-ray fluorescence analysis, nitrogen adsorption/desorption, X-ray analysis, Raman spectroscopy, transmission electron microscopy with analysis of the surface composition by X-ray energy dispersive spectroscopy and X-ray photo-electron spectroscopy. Silver oxidation state and its distribution on the catalysts surface as well as the support microstructure are the main factors determining the low temperature activity in NO selective catalytic reduction. The most active Ag/CeMnO_x catalyst (NO conversion at 300 °C is 44% and N₂ selectivity is ~90%) is characterized by the presence of the fluorite-type phase with high dispersion and distortion. The characteristic "patchwork" domain microstructure of the mixed oxide along with the presence of dispersed Ag⁺/Ag_n^δ+ species improve the low-temperature catalyst of NO reduction by C₃H₆ performance compared to Ag/CeO₂ and Ag/MnO_x systems.

Unraveling the low-temperature activity of Rh-CeO2 catalysts in CO oxidation: probing the local structure and Red-Ox transformation of Rh3+ species

The local structure of the active sites is one of the key aspects of establishing the nature of the catalytic activity of the systems. In this work, a detailed structural investigation of the Rh-CeO₂ catalysts prepared by the co-precipitation method was carried out. The application of a variety of physicochemical methods such as XRD, Raman spectroscopy, XPS, TEM, TPR-H₂, and XAS revealed the presence of highly dispersed Rh³⁺ species in the catalysts: Rh³⁺ single ions and RhO_x clusters. The substitution of Ce⁴⁺ ions by Rh³⁺ species, which provided a strong distortion of the CeO₂ lattice, is shown. XAS data ensured the refinement of the Rh local structure. It was shown that single Rh³⁺ sites located next to each other can merge the formation of RhO_x clusters with Rh local environment close to the one in Rh₂O₃ and CeRh₂O₅ oxides. The distortion of the CeO₂ lattice around single and cluster rhodium species had a beneficial effect on the catalytic activity of the samples in low-temperature CO oxidation (LTO-CO). TEM, XAS, and in situ XRD data allowed establishing the structural transformations of the catalysts under Red-Ox treatments. The reduction treatment led to Rhn metallic cluster formation localized on defects of the reduced CeO_2-δ. The reduced sample demonstrated efficient CO conversion at 0 °C. However, this system was not stable: its contact with air led to ceria reoxidation and partial reoxidation of Rh to highly dispersed Rh³⁺ species at room temperature, while heating in an oxidizing atmosphere resulted in the complete reoxidation of metallic rhodium species. The results of the work shed light on the structural aspects of the reversibility of the Rh-CeO₂ catalysts based on the highly dispersed Rh³⁺ species under treatment in the reaction conditions.

In situ probing of Pt/TiO2 activity in low-temperature ammonia oxidation

NAP-XPS and operando XAS study of Pt/TiO₂ catalysts shows that Pt⁰ species stabilized on TiO₂ surface have the highest activity at low-temperature NH₃ oxidation.

Pt-Decorated Boron Nitride Nanosheets as Artificial Nanozyme for Detection of Dopamine

Over the past decade, nanosized metal oxides, metals, and bimetallic particles have been actively researched as enzyme mimetic nanomaterials. However, the common issues with individual nanoparticles (NPs) are stabilization, reproducibility, and blocking of active sites by surfactants. These problems promote further studies of composite materials, where NPs are spread on supports, such as graphene derivatives or dichalcogenide nanosheets. Another promising type of support for NPs is the few-layered hexagonal boron nitride (hBN). In this study, we develop surfactant-free nanocomposites containing Pt NPs dispersed on chemically modified hydrophilic hBN nanosheets (hBNNSs). Ascorbic acid was used as a reducing agent for the chemical reduction of the Pt salt in the presence of hBNNS aqueous colloid, resulting in Pt/hBNNS nanocomposites, which were thoroughly characterized with X-ray diffraction, transmission electron microscopy, dynamic light scattering, and X-ray photoelectron and infrared spectroscopies. Similar to graphene oxide binding the metal NPs more efficiently than pure graphene, hydrophilic hBNNSs well stabilize Pt NPs, with particle size down to around 8 nm. We further demonstrate for the first time that Pt/hBNNS nanocomposites exhibit peroxidase-like catalytic activity, accelerating the oxidation of the classical colorless peroxidase substrate 3,3',5,5'-tetramethylbenzidine (TMB) to its corresponding blue-colored oxidized product in the presence of H₂O₂. Kinetic and mechanism studies involving terephthalic acid and isopropanol as a fluorescent probe and an ^•OH radical scavenger, respectively, proved that Pt/hBNNSs assist H₂O₂ decomposition to active oxygen species (^•OH), which are responsible for TMB oxidation. The Pt/hBNNS nanocomposite-assisted oxidation of TMB provides an effective platform for the colorimetric detection of dopamine, an important biomolecule. The presence of increased amounts of dopamine gradually inhibits the catalytic activity of Pt/hBNNSs for the oxidation of TMB by H₂O₂, thus enabling selective sensing of dopamine down to 0.76 μM, even in the presence of common interfering molecules and on real blood serum samples. The present investigation on Pt/hBNNSs contributes to the knowledge of hBN-based nanocomposites and discovers their new usage as nanomaterials with good enzyme-mimicking activity and dopamine-sensing properties.