Characteristics Analysis of Plasticized Polyvinyl Chloride Gel-Based Microlens at Different Temperatures

Temperature plays a crucial role in the preparation of polyvinyl chloride (PVC) gels for optical applications. Incorrect temperature selection can lead to various issues such as poor surface roughness, inadequate light transmission, and insufficient solution for optical devices. To address this challenge, this study focuses on the preparation of PVC gel samples by combining PVC powder (n = 3000), eco-friendly dibutyl adipate, and tetrahydrofuran at different stirring temperatures ranging from 40 to 70 °C. The PVC gel preparation process is categorized into four groups (T40, T50, T60, and T70) based on the mixing temperatures, employing a controlled test method with specific temperature conditions. The prepared PVC gel samples are then subjected to analysis to evaluate various properties including surface morphology, tensile strength, light transmittance, and electrical response time. Among the samples, the PVC gel prepared at 60 °C (referred to as T60) exhibits excellent optical properties, with a transmittance of 91.2% and a tensile strength of 2.07 MPa. These results indicate that 60 °C is an optimal reaction temperature. Notably, the PVC gel microlenses produced at this temperature achieve their maximum focal length (ranging from -8 to -20 mm) within approximately 60 s, and they recover their initial state within around 80 s after the power is switched off. This focal length achievement is twice as fast as reported in previous studies on microlenses. It is observed that the reaction temperature significantly influences the solubility of the resin-based raw materials and the homogeneity of the gel. Consequently, these findings open up possibilities for utilizing PVC gel microlenses in novel commercial optics applications, thanks to their desirable properties.

Optimal Architecture of a Dual S-Scheme ZnIn2S4-ZnO-Al2O3 Heterosystem with High H2 Evolution Rate under Visible Light

In this study, dual S-scheme ZnIn₂S₄-Al₂O₃-ZnO (ZIS-Al-Zn) heterojunctions were produced by a facile, low cost, and rapid combustion technique. These heterojunctions accelerated the photocatalytic hydrogen production due to the multi-channel-promoted separation of photocarriers. By optimizing the content of the components, the synthesized ZIS-Al-Zn composite with 20 wt% of ZnIn₂S₄ and 30 wt% of Al₂O₃ in the ZIS-Al-Zn composite demonstrated the highest hydrogen production rate of 54.2 mmol g^-1 h^-1, which was nearly 11 and 8.30 times better than ZnO-Al₂O₃ and ZnO-ZnIn₂S₄ composites, respectively. The results of DRS, PL, EIS, LSV, and CV techniques showed the highest shift in the light absorption, rapid interfacial transfer, and quenched recombination of photocarriers over the ternary ZIS-Al-Zn composite than single and binary catalysts. The obtained results revealed the formation of a dual S-scheme mechanism of transfer of photocarriers in ZIS-Al-Zn heterojunctions, contributing to better hydrogen production efficiency. The optimized ZIS-Al-Zn composite also exhibited good stability and reusability.