Adsorption and photocatalytic-conjugated activity of a chitosan-functionalized titanate coating for the removal of the drug clonazepam from drinking water

This research evaluated H2TiO7 nanotubes (TiNTs) functionalized with 1 (1TiCN), 5 (2TiCN), and 10 (3TiCN) wt.% of chitosan for the removal of clonazepam by an adsorption/photocatalysis-conjugated method. The samples were immobilized on glass, and their mechanical stability was tested by washings. The functionalization of the samples was verified by the FTIR and DRS techniques. SEM images displayed nanotubes in the samples and thickness of 4.24 μm for the 2TiCN coating. The chemical composition of the 2TiCN coating was obtained by EDS. The XRD patterns evidenced chitosan and titanate phases in the functionalized samples. Furthermore, the 2TiCN coating was evaluated in the removal of clonazepam, reaching 80.79% (4.38 and 49.64% more than the TiNT and commercial TiO2 powders, respectively) after 240 min and being 6.88% more efficient after 4 reuses than the 2TiCN powders. OH- ions were the main oxidizing species found by scavenger tests. The surface area of 2TiCN (168.6 m2/g) was 2 times higher than that of TiNTs, and its bandgap (2.95 eV) was the lowest. Therefore, the 2TiCN coating is an excellent alternative to remove clonazepam.

Enhancing the eosin-yellowish dye degradation in drinking water by using TiO2 coatings co-doped with Ni and In

This work reports on the structural, morphological, and photocatalytic properties of titanium dioxide (TiO₂) and TiO₂:NiIn (T-NiIn) coatings fabricated by spin coating. The SEM images revealed coatings with average thicknesses of 3.59 and 3.37 μm for the TiO₂ and T-NiIn, respectively. EDS spectra and Raman studies confirmed the presence of TiO₂ co-doped with nickel (Ni) and indium (In) in the coatings. XRD analysis showed the anatase and rutile phases for the TiO₂ coatings, while the T-NiIn coatings presented the rutile and brookite phases. These samples were evaluated in the photocatalytic degradation of the eosin-yellowish (EY) dye. The T-NiIn coatings showed 9.1% higher effectiveness than the undoped TiO₂ coatings after 300 min under UV irradiation. Meanwhile, the T-NiIn coatings exposed to solar light removed 40% more dye than the TiO₂ coatings. Furthermore, T-NiIn coating was the most stable because its effectiveness was reduced by only 1.4% after 4 cycles of reuse. Additionally, the scavenger tests confirmed that the main oxidizing sites were the •OH^- radicals and the superoxides •O₂^-. Thus, the use of coatings based on TiO₂ co-doped with Ni and In is a feasible strategy to increase the degradation of the EY dye in drinking water.