Could light-curing time, post-space region and cyclic fatigue affect the nanomechanical behavior of a dual-curing cement for fiber post luting?

OBJECTIVE

To evaluate the effects of curing time, post-space region and cyclic fatigue on the micromechanical properties of a fiber-post luting cement. The null hypotheses were that (1) curing time, (2) fatigue and (3) post-space region does not affect the nanoindentation modulus and hardness of the dual-curing cement.

MATERIALS AND METHODS

48 premolars were endodontically treated and a class I cavity and 8 mm deep post space was prepared. Fiber posts were luted with a universal, dualized adhesive system and a dual-curing cement following manufacturer's instructions. Specimens were divided into three groups (16 specimens for each group) according to light-curing time (no light-curing, 20 s light-curing and 120 s light-curing), which was performed with a LED lamp at 1000 mW/cm 2. The coronal part of the cavity was restored using a nano-filled resin composite. After 24 h, 8 specimens for each group were randomly extract in order to undergo to fatigue test in wet condition through a chewing simulator, while the other specimens were kept in distilled water as benchmark. All the restored teeth were then sectioned in 1 mm thick slices perpendicularly to the fiber post axis. Specimen slices were classified in coronal and apical to be tested through a nanoindenter. Data were analyzed through Kruskal-Wallis test with a significance level of 1%, in order to evaluate the influence of treatments (i.e., curing time and cyclic loading) on the micromechanical properties of the tested luting cement.

RESULTS

Both fatigue and curing time significantly influenced nanoindentation modulus and hardness of dual-curing cement (p < 0.01). No significant differences were reported for post space region. A significant interaction was found among the analyzed factors (p < 0.01).

SIGNIFICANCE

120 s light-curing time is recommended in order to achieve optimal mechanical proprieties, independently from post space region and cyclic fatigue. As matter of fact, 120 s light-curing allowed to prevent strain hardening induced by the fatigue simulation.

Influence of polymerization time on properties of dual-curing cements in combination with high translucency monolithic zirconia

PURPOSE

The aim of this in vitro study was to assess conversion degree (DC), micro-hardness (MH) and bond strength of two dual-curing resin cements employed under translucent monolithic zirconia irradiated with different time protocols.

METHODS

84 square shaped samples of 1mm thickness were prepared from high translucency zirconia blocks and divided into two groups (n=24) according to the cement employed: (1) Rely-X Ultimate; (2) Panavia SA. Each group was further divided into 3 subgroups (n=8) according to the irradiation time: (a) no light; (b) 20s; (c) 120s. Light curing was performed 60s after the sample was placed on the diamond support of a FT-IR spectrophotometer with a high power multiLED lamp. Final DC% were calculated after 10min. After 24h, Vickers Test on the cement layer was performed. The same protocol was used to lute composite cylinders in order to evaluate microshear bond-strength test. ANOVA and Bonferroni tests were performed to find differences between MH and bond-strength to zirconia, while for DC% the Scheirer-Ray-Hare two-way test was used.

RESULTS

The two cements reached higher DC% in subgroup (b) and (c). As concern MH, statistics showed an increase in curing time was able to improve MH significantly. Bond-strength was not affected by irradiation time only for Panavia SA.

CONCLUSIONS

The first null hypothesis has to be rejected since DC% and MH of the dual-cements tested were influenced by the curing time. The second null hypothesis is partially rejected since the bond strength was influenced by the curing time only for Rely-X Ultimate.

Correlation between flexural and indirect tensile strength of resin composite cements

Background

To evaluate a potential correlation between flexural strength and indirect tensile strength in assessing the mechanical strength of resin composite cements.

Methods

Flexural strength (n = 5) and indirect tensile strength (n = 5) of 7 resin composite cements (RelyX Unicem 2 Automix [RXU], Panavia SA [PSA], Clearfil SA [CSA], Panavia F2.0 [PF2], Multilink Implant [MLI], DuoCem [DCM], Panavia 21 [P21]) were determined. Specimens were either auto-polymerized or dual-cured (except P21) and stored in water at 37 °C for 1 day prior to measurement. Flexural and indirect tensile strength of 4 cements (RXU, PSA, PF2, MLI) was additionally measured directly after curing and after 96 h water storage at 37 °C.

Results

Except for PF2, dual-cured specimens achieved higher flexural strength than auto-polymerized specimens. In the indirect tensile strength test differences in auto-polymerized and dual-cured specimens were only detected for RXU and DCM. A general non-linear correlation was found between flexural and indirect tensile strength values. However, strength values of auto-polymerized and dual-cured specimens did not generally correlate.

Conclusions

Flexural strength and indirect tensile strength of resin composite cements are correlated. At high strength values the indirect tensile test is less sensitive than the flexural test. The results suggest that the indirect tensile test may only be recommended as a screening test especially for low or medium strength resin composite cements.