Mechanism of highly efficient electrochemical degradation of antibiotic sulfadiazine using a layer-by-layer GNPs/PbO2 electrode

A PbO₂ electrode integrating electrocatalytic and adsorptive functions was successfully fabricated by embedding layer-by-layer graphene nanoplatelets (GNPs) into β-PbO₂ active layer (GNPs/PbO₂) and employed as anode for high-efficient removal of sulfadiazine (SDZ). In electrochemical degradation experiments, SDZ was quickly enriched on the surface of GNPs/PbO₂ film via adsorption and then oxidized by ⋅OH in-site. In terms of the electrocatalytic performance and adsorption of electrode, the optimal electrodeposition time for each β-PbO₂ outer layer was 4 min (GNPs/PbO₂-4). Compared with conventional PbO₂ electrode, the layer-by-layer GNPs resulted in the smaller crystal size and denser surface of PbO₂ electrode, thus facilitating the generation of active oxygen species. At the same time, the specific surface area, oxygen evolution potential (OEP) of the anode were enhanced and the charge-transfer resistance was reduced. For GNPs/PbO₂-4 anode, the optimal conditions of electrochemical oxidation of SDZ were identified as initial pH 9, 50 mg/L of SDZ and 20 mA/cm² of current density using response surface methodology (RSM), 98.15% of SDZ could be removed in this case. The contribution of radical oxidation and non-radical oxidation to SDZ removal was about 79% and 21%, respectively. Moreover, the reaction pathways of SDZ on the GNPs/PbO₂-4 electrode involving hydroxylation, radical reaction and ring cleavage were speculated. Finally, the continuous SDZ degradation and accelerated service lifetime test suggested that the GNPs/PbO₂-4 electrode was shown to be stable and repeatable, and the Pb²⁺ concentration was measured to ensure the safety of the treated solution. Consequently, the above findings provide an innovative way to design and prepare an effective and stable PbO₂ electrode for electrochemical degradation of antibiotic wastewater.

When MXene (Ti3C2Tx) meet Ti/PbO2: An improved electrocatalytic activity and stability

Stable electrode materials with high catalytic activity are urgently required for electrochemical degradation of refractory organic pollutants in wastewater treatment. Herein, high conductive MXene (Ti₃C₂T_x) was firstly fabricated by electrophoretic deposition (EPD) as an interlayer for preparing a novel PbO₂ electrode. The well-conducted Ti₃C₂T_x interlayer significantly improved the electrochemical performance of the EPD-2.0/PbO₂ (EPD time was 2.0 min) electrode with the charge transfer resistance decreased by 9.51 times, the inner active sites increased by 5.21 times and the ∙OH radicals generation ability enhanced by 4.07 times than the control EPD-0/PbO₂ anode. Consequently, the EPD-2.0/PbO₂ electrode achieved nearly 100% basic fuchsin (BF) and 86.78% COD removal efficiency after 3.0 h electrolysis. Therefore, this new PbO₂ electrode presented a promising potential for electrochemical degradation of BF and the new Ti₃C₂T_x middle layer could also be used to fabricate other efficient and stable anodes, such as SnO₂, MnO₂, TiO₂, etc.

Fabrication and characterization of porous titanium-based PbO2 electrode through the pulse electrodeposition method: Deposition condition optimization by orthogonal experiment

Porous titanium-based PbO₂ electrodes were successfully fabricated by pulse electrodeposition method. The primary pulse electrodeposition parameters, including pulse frequency (f), duty ratio (γ), average current density (J_a) and electrodeposition time (t) were considered in this study. An orthogonal experiment was designed based on those four factors and in three levels. SEM images and XRD results suggest that the surface morphology and structure of PbO₂ electrodes could be easily changed by varying pulse electrodeposition parameters. Orthogonal analysis reveals that the increase of f and J_a could decrease the average grain size of PbO₂ electrodes, which is conducive to create more active sites and promote the generation of hydroxide radicals. The electrochemical degradation of Azophloxine was carried out to evaluate the electrochemical oxidation performance of pulse electrodeposited electrodes. The results indicate that the influences of four factors can be ranked as follow: J_a >γ≈ t > f. The higher f, larger J_a and longer t could facilitate the optimization of the integrated electrochemical degradation performance of prepared PbO₂ electrode. The accelerated life time is dominated by J_a and t, coincident with the average weight increase of β-PbO₂ layer. The optimal parameters of pulse electrodeposition turn out to be: f = 50 Hz, γ = 30%, J_a = 25 mA cm^-2, t = 60 min. Together, the consequences of the experiments give assistance to uncover and roughly conclude the mechanism of pulse electrodeposition.

Fabrication and characterization of PbO2 electrode modified with [Fe(CN)6](3-) and its application on electrochemical degradation of alkali lignin

PbO2 electrode modified by [Fe(CN)6](3-) (marked as FeCN-PbO2) was prepared by electro-deposition method and used for the electrochemical degradation of alkali lignin (AL). The surface morphology and the structure of the electrodes were characterized by scanning electronic microscopy (SEM) and X-ray diffraction (XRD), respectively. The stability and electrochemical activity of FeCN-PbO2 electrode were characterized by accelerated life test, linear sweep voltammetry, electrochemical impedance spectrum (EIS) and AL degradation. The results showed that [Fe(CN)6](3-) increased the average grain size of PbO2 and formed a compact surface coating. The service lifetime of FeCN-PbO2 electrode was 287.25 h, which was longer than that of the unmodified PbO2 electrode (100.5h). The FeCN-PbO2 electrode showed higher active surface area and higher oxygen evolution potential than that of the unmodified PbO2 electrode. In electrochemical degradation tests, the apparent kinetics coefficient of FeCN-PbO2 electrode was 0.00609 min(-1), which was higher than that of unmodified PbO2 electrode (0.00419 min(-1)). The effects of experimental parameters, such as applied current density, initial AL concentration, initial pH value and solution temperature, on electrochemical degradation of AL by FeCN-PbO2 electrode were evaluated.

Preparation and characterization of PbO₂ electrode and its application in electro-catalytic degradation of o-aminophenol in aqueous solution assisted by CuO-Ce₂O₃/γ-Al₂O₃ catalyst

The electrochemical degradation of o-aminophenol (OAP) in aqueous solution was investigated by galvanostatic electrolysis using PbO₂ electrode as anode. The Ti/SnO₂-Sb₂O₃/PbO₂ anode was prepared by thermal decomposition and electro-deposition method, and was characterized by X-ray diffraction (XRD). The hydroxyl radicals electro-generated on anode were detected by fluorescence spectroscopy. The effects of initial pH and current density on the efficiency of the electrochemical degradation process were also studied. UV spectroscopy and chemical oxygen demand (COD) measurements were conducted to evaluate the removal effects of organic pollutants. The experimental results showed that the refractory organics in wastewater can be removed by pure electrochemical process, COD removal efficiency of 91.6% was obtained in 70 min at initial pH 11.0 and current density was equal to 50 mA cm(-2). In order to improve the efficiency of degradation and accelerate the reaction rate, a novel catalyst, γ-Al₂O₃ supported Ce-doped CuO, was synthesized by impregnating process and was characterized by X-ray photoelectron spectroscopy (XPS). The catalyst exhibited excellent catalytic activity in the electro-catalytic degradation of OAP wastewater and the COD removal efficiency of 91.7% was obtained in 20 min under mild conditions. Finally, a hypothetical mechanism of electro-catalytic degradation was proposed.