Poly(propylene glycol) and urethane dimethacrylates improve conversion of dental composites and reveal complexity of cytocompatibility testing

Correlating cytotoxicity to elution behaviors of composite resins in term of curing kinetic

Cytotoxicity of photocurable composite resins is a key issue for their safe use in dental restoration. Curing kinetic and elution behaviors of the composite resin would have decisive effects on its cytotoxicity. In this study, composite resins composed of bisphenol-glycidyl dimethacrylate (Bis-GMA), triethyleneglycol dimethacrylate (TEGDMA), camphorquinone (CQ), N,N-dimethylaminoethyl methacrylate (DMAEMA) and barium glass powders were prepared by setting the photoinitiators CQ/DMAEMA at 0.5wt%, 1wt% or 3wt% of the total weight of Bis-GMA/TEGDMA. The ratio of Bis-GMA/TEGDMA was 6:4, the ratio of CQ/DMAEMA was 1:1, and the incorporated inorganic powder was 75wt%. Then, curing kinetics were studied by using real-time Fourier transform infrared spectroscopy (FTIR) and photo-DSC (differential scanning calorimeter). Elution behaviors in both ethanol solution and deionized water were monitored by using liquid chromatogram/mass spectrometry (LC/MS). Cytotoxicity was evaluated by in vitro culture of L929 fibroblasts. Finally, they were all analyzed and correlated in terms of initiator contents. It was found that the commonly used 0.5wt% of photoinitiators was somewhat insufficient in obtaining composite resin with low cytotoxicity.

Own brand label restorative materials-A false bargain?

OBJECTIVES

This study aims at evaluating and comparing mechanical, chemical, and cytotoxicological parameters of a commercial brand name composite material against two 'own brand label' (OBL) composites.

METHODS

Parameters included depth of cure, flexural strength, degree of conversion, polymerization shrinkage, filler particle morphology and elemental analyzes, Vickers hardness, surface roughness parameters after abrasion, monomer elution, and cytotoxicity.

RESULTS

The conventional composite outperformed the OBLS in terms of depth of cure (p<0.001), degree of cure at the first and last time intervals (p<0.001), hardness (p<0.001), and post-abrasion roughness (p<0.05). The polymerization volumetric shrinkage ranged from 2.86% to 4.13%, with the highest shrinkage seen among the OBLs. Both Monomer elution from the OBLs was statistically significantly higher (p<0.001). Statistically significantly higher cytotoxicity combined with altered morphology and loss of confluence was detected in the cells exposed to extracts from the OBLs.

CONCLUSIONS

The OBLs were in general outdone by the conventional composite.

CLINICAL SIGNIFICANCE

OBLs restorative materials have become pervasive in the dental market. Manufacturers often promise equal or better characteristics than existing brand-name composites, but at a lower price. Dentists are highly recommended to reconsider utilization of OBLs lacking sound scientific scrutiny, and our findings underscore this recommendation.

Dental Composites with Calcium / Strontium Phosphates and Polylysine

Purpose

This study developed light cured dental composites with added monocalcium phosphate monohydrate (MCPM), tristrontium phosphate (TSrP) and antimicrobial polylysine (PLS). The aim was to produce composites that have enhanced water sorption induced expansion, can promote apatite precipitation and release polylysine.

Materials and Methods

Experimental composite formulations consisted of light activated dimethacrylate monomers combined with 80 wt% powder. The powder phase contained a dental glass with and without PLS (2.5 wt%) and/or reactive phosphate fillers (15 wt% TSrP and 10 wt% MCPM). The commercial composite, Z250, was used as a control. Monomer conversion and calculated polymerization shrinkage were assessed using FTIR. Subsequent mass or volume changes in water versus simulated body fluid (SBF) were quantified using gravimetric studies. These were used, along with Raman and SEM, to assess apatite precipitation on the composite surface. PLS release was determined using UV spectroscopy. Furthermore, biaxial flexural strengths after 24 hours of SBF immersion were obtained.

Results

Monomer conversion of the composites decreased upon the addition of phosphate fillers (from 76 to 64%) but was always higher than that of Z250 (54%). Phosphate addition increased water sorption induced expansion from 2 to 4% helping to balance the calculated polymerization shrinkage of ~ 3.4%. Phosphate addition promoted apatite precipitation from SBF. Polylysine increased the apatite layer thickness from ~ 10 to 20 μm after 4 weeks. The novel composites showed a burst release of PLS (3.7%) followed by diffusion-controlled release irrespective of phosphate addition. PLS and phosphates decreased strength from 154 MPa on average by 17% and 18%, respectively. All formulations, however, had greater strength than the ISO 4049 requirement of > 80 MPa.

Conclusion

The addition of MCPM with TSrP promoted hygroscopic expansion, and apatite formation. These properties are expected to help compensate polymerization shrinkage and help remineralize demineralized dentin. Polylysine can be released from the composites at early time. This may kill residual bacteria.

Functional dendritic compounds: potential prospective candidates for dental restorative materials and in situ re-mineralization of human tooth enamel

This review provides a snapshot of recent progress in the synthesis and application of dendritic compounds as potential prospective candidates for dental restorative materials andin siture-mineralization of human tooth enamel.