Rapid Nitriding of Titanium Alloy with Fine Grains at Room Temperature

Tribocorrosion and Surface Protection Technology of Titanium Alloys: A Review

Titanium alloy has the advantages of high specific strength, good corrosion resistance, and biocompatibility and is widely used in marine equipment, biomedicine, aerospace, and other fields. However, the application of titanium alloy in special working conditions shows some shortcomings, such as low hardness and poor wear resistance, which seriously affect the long life and safe and reliable service of the structural parts. Tribocorrosion has been one of the research hotspots in the field of tribology in recent years, and it is one of the essential factors affecting the application of passivated metal in corrosive environments. In this work, the characteristics of the marine and human environments and their critical tribological problems are analyzed, and the research connotation of tribocorrosion of titanium alloy is expounded. The research status of surface protection technology for titanium alloy in marine and biological environments is reviewed, and the development direction and trends in surface engineering of titanium alloy are prospected.

Corrosion Behavior of Nitrided Layer of Ti6Al4V Titanium Alloy by Hollow Cathodic Plasma Source Nitriding

Ti6Al4V titanium alloys, with high specific strength and good biological compatibility with the human body, are ideal materials for medical surgical implants. However, Ti6Al4V titanium alloys are prone to corrosion in the human environment, which affects the service life of implants and harms human health. In this work, hollow cathode plasm source nitriding (HCPSN) was used to generate nitrided layers on the surfaces of Ti6Al4V titanium alloys to improve their corrosion resistance. Ti6Al4V titanium alloys were nitrided in NH₃ at 510 °C for 0, 1, 2, and 4 h. The microstructure and phase composition of the Ti-N nitriding layer was characterized by high-resolution transmission electron microscopy, atomic force microscopy, scanning electron microscopy, X-ray diffraction, and X-ray photoelectron spectroscopy. This modified layer was identified to be composed of TiN, Ti₂N, and α-Ti (N) phase. To study the corrosion properties of different phases, the nitriding 4 h samples were mechanically ground and polished to obtain the various surfaces of Ti₂N and α-Ti (N) phases. The potentiodynamic polarization and electrochemical impedance measurements were conducted in Hank's solution to characterize the corrosion resistance of Ti-N nitriding layers in the human environment. The relationship between corrosion resistance and the microstructure of the Ti-N nitriding layer was discussed. The new Ti-N nitriding layer that can improve corrosion resistance provides a broader prospect for applying Ti6Al4V titanium alloy in the medical field.

Effect of Nano Nd2O3 on the Microstructure and High-Temperature Resistance of G@Ni Laser Alloying Coatings on Ti-6Al-4V Alloy

Titanium and its alloys are widely used in high-end manufacturing fields. However, their low high-temperature oxidation resistance has limited their further application. Recently, laser alloying processing has attracted researchers to improve the surface properties of Ti, for which Ni coated graphite system is an excellent prospect due to its outstanding properties and metallurgical bonding between coating and substrate. In this paper, nanoscaled rare earth oxide Nd₂O₃ addition was added to Ni coated graphite laser alloying materials to research its influence on the microstructure and high-temperature oxidation resistance of the coating. The results proved that nano-Nd₂O₃ has an outstanding effect on refining coating microstructures, thus the high-temperature oxidation resistance was improved. Furthermore, with the addition of 1. 5 wt.% nano-Nd₂O₃, more NiO formed in the oxide film, which effectively strengthened the protective effect of the film. After 100 h of 800 °C oxidation, the oxidation weight gain per unit area of the normal coating was 14.571 mg/cm², while that of the coating with nano-Nd₂O₃ addition was 6.244 mg/cm², further proving that the addition of nano-Nd₂O₃ substantially improved the high-temperature oxidation properties of the coating.