High pressure CO2 photoreduction using Au/TiO2: unravelling the effect of co-catalysts and of titania polymorphs

A series of Au/TiO₂ based catalysts with low gold loading (0.1–0.5 wt%) were prepared by a modified deposition–precipitation method and their activity was tested for CO₂ photoreduction in the liquid phase at high pressure (7 bar).

Surface Probing by Spectroscopy on Titania-Supported Gold Nanoparticles for a Photoreductive Application

The continuous increase in scientific reports concerning photocatalysis and in particular CO2 photoreduction in recent years reveals the high degree of interest around the topic. However, the adsorption and activation mechanisms of CO2 on TiO2, the most used photocatalyst, are poorly understood and investigated. Gold nanoparticles were prepared by a modified deposition-precipitation method using urea and a chemical reductant. Bare P25 was used as reference. Combined spectroscopic investigations of fresh and spent samples with photoactivity studies reported in this article provide new insights to the role of CO2 adsorption and carbonate formation on Au/TiO2 during CO2 photocatalytic reduction. The key intermediates’ and products’ adsorption (CO, methanol, ethanol) was studied, coupled with X-ray photoelectron microscopy (XPS) and UV-Visible spectroscopy. The adsorption of CO2 on fresh and spent catalysts changes radically considering the carbonate formation and the gold surface presence. Methanol and ethanol revealed new adsorbed species on Au with respect to bare titania. The characterisation of the spent catalysts revealed the good stability of these samples.

High Pressure Photoreduction of CO2: Effect of Catalyst Formulation, Hole Scavenger Addition and Operating Conditions

The photoreduction of CO2 is an intriguing process which allows the synthesis of fuels and chemicals. One of the limitations for CO2 photoreduction in the liquid phase is its low solubility in water. This point has been here addressed by designing a fully innovative pressurized photoreactor, allowing operation up to 20 bar and applied to improve the productivity of this very challenging process. The photoreduction of CO2 in the liquid phase was performed using commercial TiO2 (Evonink P25), TiO2 obtained by flame spray pyrolysis (FSP) and gold doped P25 (0.2 wt% Au-P25) in the presence of Na2SO3 as hole scavenger (HS). The different reaction parameters (catalyst concentration, pH and amount of HS) have been addressed. The products in liquid phase were mainly formic acid and formaldehyde. Moreover, for longer reaction time and with total consumption of HS, gas phase products formed (H2 and CO) after accumulation of significant number of organic compounds in the liquid phase, due to their consecutive photoreforming. Enhanced CO2 solubility in water was achieved by adding a base (pH = 12–14). In basic environment, CO2 formed carbonates which further reduced to formaldehyde and formic acid and consequently formed CO/CO2 + H2 in the gas phase through photoreforming. The deposition of small Au nanoparticles (3–5 nm) (NPs) onto TiO2 was found to quantitatively influence the products distribution and increase the selectivity towards gas phase products. Significant energy storage in form of different products has been achieved with respect to literature results.

Cinnamaldehyde hydrogenation using Au–Pd catalysts prepared by sol immobilisation

We report the catalytic performance of Au–Pd nanoparticles prepared via a sol immobilisation technique for the catalytic hydrogenation of cinnamaldehyde under mild reaction conditions.