One-Pot Synthesis of CoS2 Merged in Polymeric Carbon Nitride Films for Photoelectrochemical Water Splitting

Integrating P-Doped Carbon Nitride Dots as Active Sites on P/Mo Co-Doped BiVO4 Photoanodes Promotes H2O2 Production

The indirect anthraquinone method is currently used to produce H2O2, but it leads to high energy consumption and a large amount of chemical waste. Alternatively, water oxidation reactions offer a potential green approach for H2O2 production, although it is constrained by low selectivity. Herein, the functional photoanodes are rationally designed for H2O2 production via photocatalytic water oxidation. Specifically, P/Mo co-doped BiVO4 films are achieved on a conductive glass to serve as the photocatalytic layer, which is coated with an ultrathin amorphous TiO2 film to achieve good stability. Importantly, metal-free P-doped polymeric carbon nitride dots are deposited on the photoanode, acting as the reaction centres. This innovative approach moves away from the traditional reliance on inorganic materials as co-catalysts in order to suppress the thermodynamically favoured O₂ evolution, which, in turn, significantly enhances the selectivity, efficiency and stability of H₂O₂ production. Consequently, an optimal selectivity of ≈64% for H₂O₂ production is achieved at an applied voltage bias of 1.7 V versus RHE in a 1.0 m KHCO3 solution, achieving a yield of ≈34.2 µmol hr-1 cm-2. This research offers a novel strategy for developing photocatalytic films with optimised co-catalysts for a photoanode in photocatalytic H2O2 synthesis.

An efficient strategy to boost photoelectrochemical water oxidation of g-C3N4 films modified with NiO as cocatalyst

The successful synthesis of carbon nitride films plays a crucial role in photoelectrochemical (PEC) water oxidation reactions. However, a significant technical challenge is that the contact between the g-C3N4 layer and the fluorine-doped tin oxide (FTO) substrate is suboptimal, as well as the recombination of photogenerated electrons and holes is grievous, directly affecting the effective charge transport and the overall photocatalytic efficiency. Herein, we fabricated a g-C3N4 thin photoanode through simple chemical vapor deposition, NiO cocatalyst was modified on the surface of g-C3N4 thin photoanode via electro-deposition and followed by calcination, aiming at improving the transfer of photogenerated charge carriers. As expected, the recombination of photogenerated electrons and holes is effectively suppressed the g-C3N4 thin photoanode after introducing NiO cocatalyst. Moreover, the superior electrical conductivity of NiO reduces charge transport resistance and allows photogenerated holes to be rapid injected into the electrolyte to participate in the water oxidation reaction. As such, the NiO-60s (the deposition time of NiO is 60 s) photoanode exhibits a higher photocurrent density and much negative onset potential than g-C3N4. which is of great benefit to designing effective g-C3N4 based photoanode for PEC water oxidation reaction.

Developing Polymeric Carbon Nitrides for Photocatalytic H2O2 Production

Hydrogen peroxide (H2O2) plays a crucial role in various applications, such as green oxidation processes and the production of high-quality fuels. Currently, H2O2 is primarily manufactured using the indirect anthraquinone method, known for its significant energy consumption and the generation of intensive by-products. Extensive research has been conducted on the photocatalytic production of H2O2 via oxygen reduction reaction (ORR), with polymeric carbon nitride (PCN) emerging as a promising catalyst for this conversion. This review article is organized around two approaches. The first part main consists of the chemical optimization of the PCN structure, while the second focuses on the physical integration of PCN with other functional materials. The objective is to clarify the correlation between the physicochemical properties of PCN photocatalysts and their effectiveness in H2O2 production. Through a thorough review and analysis of the findings, this article seeks to stimulate new insights and achievements, not only in the domain of H2O2 production via ORR but also in other redox reactions.

Films of linear conjugated polymer as photoanodes for oxidation reactions

Photoelectrochemical (PEC) devices hold huge potential to convert solar energy into chemical energy. However, the high cost of raw materials and film processing has hindered its practical use. In this study, we attempt to tackle this issue by fabricating straightforward semiconducting polymer films. These films function as photoanodes for various oxidation reactions, including water oxidation and oxidative organosynthesis. The structures of the polymer were assessed by incorporating electron-rich and electron-deficient co-monomers into dibenzo[b,d]thiophene sulfone materials. Furthermore, to gain comprehensive insight into the performance, we conducted both steady-state and in operando investigations, revealing that the active site on the polymer surface determines the rate of the conversion process. This study marks a significant stride towards leveraging economically viable semiconductors in PEC systems for efficient solar-to-chemical conversions. It addresses the challenges of high material costs and complex film processing, paving the way for the scaled-up application of this burgeoning technology.

Boron and Sodium Doping of Polymeric Carbon Nitride Photoanodes for Photoelectrochemical Water Splitting

Polymeric carbon nitride is a promising photoanode material for water-splitting and organic transformation-based photochemical cells. Despite achieving significant progress in performance, these materials still exhibit low photoactivity compared to inorganic photoanodic materials because of a moderate visible light response, poor charge separation, and slow oxidation kinetics. Here, the synthesis of a sodium- and boron-doped carbon nitride layer with excellent activity as a photoanode in a water-splitting photoelectrochemical cell is reported. The new synthesis consists of the direct growth of carbon nitride (CN) monomers from a hot precursor solution, enabling control over the monomer-to-dopant ratio, thus determining the final CN properties. The introduction of Na and B as dopants results in a dense CN layer with a packed morphology, better charge separation thanks to the in situ formation of an electron density gradient, and an extended visible light response up to 550 nm. The optimized photoanode exhibits state-of-the-art performance: photocurrent densities with and without a hole scavenger of about 1.5 and 0.9 mA cm-2 at 1.23 V versus reversible hydrogen electrode (RHE), and maximal external quantum efficiencies of 56% and 24%, respectively, alongside an onset potential of 0.3 V.

Robust Carbon Nitride Homojunction Photoelectrode for Solar-Driven Water Splitting

Achieving intimate particle-to-particle and particle-to-substrate contacts is the first priority for fabricating high-quality photoelectrodes to ensure sufficient visible light absorption and efficient charge separation/transport. To achieve this goal, a seeding strategy is designed to construct a robust carbon nitride (CN) homojunction photoelectrode, in which vaporized precursors are condensed into a compact seeding layer at low temperatures, inducing the further deposition of the top layer. This optimized photoelectrode displays an excellent photocurrent density of 320 μA cm^-2 in 0.1 M NaOH electrolyte at 1.23 V_RHE (V vs reversible hydrogen electrode) under AM 1.5G illumination, with H₂ and O₂ evolution rates of 2.98 and 1.47 μmol h^-1 cm^-2, respectively. Characterizations show that both the robust contact and the homojunction of the double-layered CN film contribute to enhanced photoelectrochemical performance. This work may provide a new strategy for the design of high-performing CN photoelectrodes.

Rational Design of Carbon Nitride Photoelectrodes with High Activity Toward Organic Oxidations

Carbon nitride (CN_x ) is a light-absorber with excellent performance in photocatalytic suspension systems, but the activity of CN_x photoelectrodes has remained low. Here, cyanamide-functionalized CN_x (^NCN CN_x ) was co-deposited with ITO nanoparticles on a 1.8 Å thick alumina-coated FTO electrode. Transient absorption spectroscopy and impedance measurements support that ITO acts as a conductive binder and improves electron extraction from the ^NCN CN_x , whilst the alumina underlayer reduces recombination losses between the ITO and the FTO glass. The Al₂ O₃ |ITO : ^NCN CN_x film displays a benchmark performance for CN_x -based photoanodes with an onset of -0.4 V vs a reversible hydrogen electrode (RHE), and 1.4±0.2 mA cm^-2 at 1.23 V vs RHE during AM1.5G irradiation for the selective oxidation of 4-methylbenzyl alcohol. This assembly strategy will improve the exploration of CN_x in fundamental and applied photoelectrochemical (PEC) studies.

Designing a 0D/1D S-Scheme Heterojunction of Cadmium Selenide and Polymeric Carbon Nitride for Photocatalytic Water Splitting and Carbon Dioxide Reduction

Constructing photocatalysts to promote hydrogen evolution and carbon dioxide photoreduction into solar fuels is of vital importance. The design and establishment of an S-scheme heterojunction system is one of the most feasible approaches to facilitate the separation and transfer of photogenerated charge carriers and obtain powerful photoredox capabilities for boosting photocatalytic performance. Herein, a zero-dimensional/one-dimensional S-scheme heterojunction composed of CdSe quantum dots and polymeric carbon nitride nanorods (CdSe/CN) is created and constructed via a linker-assisted hybridization approach. The CdSe/CN composites exhibit superior photocatalytic activity in water splitting and promoted carbon dioxide conversion performance compared with CN nanorods and CdSe quantum dots. The best efficiency in photocatalytic water splitting (10.2% apparent quantum yield at 420 nm irradiation, 20.1 mmol g−1 h−1 hydrogen evolution rate) and CO2 reduction (0.77 mmol g−1 h−1 CO production rate) was achieved by 5%CdSe/CN composites. The significantly improved photocatalytic reactivity of CdSe/CN composites primarily originates from the emergence of an internal electric field in the zero-dimensional/one-dimensional S-scheme heterojunction, which could greatly improve the photoinduced charge-carrier separation. This work underlines the possibility of employing polymeric carbon nitride nanostructures as appropriate platforms to establish highly active S-scheme heterojunction photocatalysts for solar fuel production.

Coordination Chemistry Engineered Polymeric Carbon Nitride Photoanode with Ultralow Onset Potential for Water Splitting

Construction of an intimate film/substrate interface is of great importance for a photoelectrode to achieve efficient photoelectrochemical performance. Inspired by coordination chemistry, a polymeric carbon nitride (PCN) film is intimately grown on a Ti-coated substrate by an in situ thermal condensation process. The as-prepared PCN photoanode exhibits a record low onset potential (Eonset ) of -0.38 V versus the reversible hydrogen electrode (RHE) and a decent photocurrent density of 242 μA cm-2 at 1.23 VRHE for water splitting. Detailed characterization confirms that the origin of the ultralow onset potential is mainly attributed to the substantially reduced interfacial resistance between the Ti-coated substrate and the PCN film benefitting from the constructed interfacial sp2 N→Ti coordination bonds. For the first time, the ultralow onset potential enables the PCN photoanode to drive water splitting without external bias with a stable photocurrent density of ≈9 μA cm-2 up to 1 hour.

Recent Progress on Photoelectrochemical Water Splitting of Graphitic Carbon Nitride (g-CN) Electrodes

Graphitic carbon nitride (g-CN), a promising visible-light-responsive semiconductor material, is regarded as a fascinating photocatalyst and heterogeneous catalyst for various reactions due to its non-toxicity, high thermal durability and chemical durability, and "earth-abundant" nature. However, practical applications of g-CN in photoelectrochemical (PEC) and photoelectronic devices are still in the early stages of development due to the difficulties in fabricating high-quality g-CN layers on substrates, wide band gaps, high charge-recombination rates, and low electronic conductivity. Various fabrication and modification strategies of g-CN-based films have been reported. This review summarizes the latest progress related to the growth and modification of high-quality g-CN-based films. Furthermore, (1) the classification of synthetic pathways for the preparation of g-CN films, (2) functionalization of g-CN films at an atomic level (elemental doping) and molecular level (copolymerization), (3) modification of g-CN films with a co-catalyst, and (4) composite films fabricating, will be discussed in detail. Last but not least, this review will conclude with a summary and some invigorating viewpoints on the key challenges and future developments.

Selective Photocatalytic CO2 Reduction to CH4 on Tri-s-triazine-Based Carbon Nitride via Defects and Crystal Regulation: Synergistic Effect of Thermodynamics and Kinetics

Realizing the high selectivity of CH₄ from the photocatalytic CO₂ reduction reaction (CO₂ RR) remains a great challenge owing to the lower efficiency of multi-electron transfer and the similar thermodynamic properties of CH₄ and CO. Herein, nitrogen-deficient carbon nitride two-dimensional (2D) nanosheets were prepared via the high-temperature crystalline phase transformation process. Optimizing crystallinity enhances the in-plane polarization along the a-axis. Owing to the increased electron density of the N defect, the kinetic possibilities of CH₄ production have increased. Furthermore, the potential energy of the mid-gap states introduced by the N defect favors the thermodynamics of CH₄ production. The selectivity values of CH₄ based on yield and electrons are 87.1 and 96.4%. This work unravels the mechanism to selectively produce CH₄ from CO₂ photoreduction through the crystalline phase and defect regulation and provides significant guidance for the rational design of CO₂ reduction photocatalysts for selective CH₄ production.