C60-CN: A bifunctional interface modification material for perovskite solar cells

Titanium dioxide (TiO2) is regularly used as an electron transport material in n-i-p perovskite solar cells (PSCs). However, massive defects exist on the TiO2 surface, which will lead to serious hysteresis and interface charge recombination of the device, thus affecting the device's efficiency. In this study, a cyano fullerene pyrrolidine derivative (C60-CN) was synthesized and applied to PSCs for the first time to modify the TiO2 electron transport layer. Systematic studies have shown that the addition of the C60-CN modification layer on the TiO2 surface will enlargement the perovskite grain size, improve the perovskite film quality, enhance electron transport, and reduce charge recombination. The C60-CN layer can significantly reduce the density of trap states in the perovskite solar cells. As a result, the PSCs based on C60-CN/TiO2 obtained a power conversion efficiency (PCE) of 18.60%, suppressing the hysteresis and improving the stability, whereas the PCE of the control device using the original TiO2 ETL was lower, 17.19%.

Recent Developments in Upscalable Printing Techniques for Perovskite Solar Cells

Just over a decade, perovskite solar cells (PSCs) have been emerged as a next-generation photovoltaic technology due to their skyrocketing power conversion efficiency (PCE), low cost, and easy manufacturing techniques compared to Si solar cells. Several methods and procedures have been developed to fabricate high-quality perovskite films to improve the scalability and commercialize PSCs. Recently, several printing technologies such as blade-coating, slot-die coating, spray coating, flexographic printing, gravure printing, screen printing, and inkjet printing have been found to be very effective in controlling film formation and improving the PCE of over 21%. This review summarizes the intensive research efforts given for these printing techniques to scale up the perovskite films as well as the hole transport layer (HTL), the electron transport layer (ETL), and electrodes for PSCs. In the end, this review presents a description of the future research scope to overcome the challenges being faced in the printing techniques for the commercialization of PSCs.