Is the dentifrice containing calcium silicate, sodium phosphate, and fluoride able to protect enamel against chemical mechanical wear? An in situ/ex vivo study

Effect of the calcium silicate and sodium phosphate remineralizing products on bleached enamel

Context and Aims

This study evaluated the effect of calcium silicate and sodium phosphate (CSSP) dentifrice and serum on the surface of enamel bleached with hydrogen peroxide (H2O2).

Materials and Methods

A total of 160 bovine enamel slabs were bleached with 35% H2O2 and treated with sodium fluoride (NaF) dentifrice-GI, CSSP dentifrice-GII; CSSP dentifrice + CSSP serum-GIII, or NaF dentifrice + NaF gel-GIV. The dentifrices were applied using a brushing machine three times daily for 7 days. After brushing, sodium phosphate gel and CSSP serum were applied. The microhardness (KNH, n = 14), surface roughness (Ra, n = 14), energy dispersive spectroscopy (n = 6), and scanning electron microscopy (n = 6) were assessed at t0 (before bleaching), t1 (after bleaching), and t2 (after postbleaching treatments).

Statistical Analysis Used

The data were subjected to a two-way analysis of variance and Bonferroni's test.

Results

The KNH decreased at t1 (P < 0.001) but recovered at t2 for all treatments, although only GII showed restored baseline values (P = 0.0109). The surface roughness increased at t1 (P < 0.001) and reduced at t2 (P < 0.001) for all groups, with no significant differences among groups. Enamel composition and morphology did not differ after the treatments, except for silicon accumulation in GIII.

Conclusions

Postbleaching treatment with CSSP dentifrice and serum yielded superior remineralizing effects on bleached enamel.

The role of calcium in the prevention of erosive tooth wear: a systematic review and meta-analysis

OBJECTIVES

The loss of hard dental tissue due to recurrent acid challenges and mechanical stresses without bacterial involvement is known as erosive tooth wear (ETW). Many studies in the literature have concentrated on variables that may affect the ETW process and prevent its occurrence or reduce its advancement. However, to date, no previous systematic review has evaluated the role of calcium in preventing ETW. Therefore, the purpose of the present systematic review was to review and critically appraise the scientific evidence regarding the role of calcium formulations in the prevention of ETW.

METHODS

The review protocol was registered in the PROSPERO international prospective register of systematic reviews (Ref: CRD42021229819). A literature search was conducted in electronic databases to identify in situ randomized controlled trials evaluating the prevention of ETW following the application of calcium formulations. The outcomes studied included mean enamel loss, surface microhardness, surface roughness, mean erosion/softening depth, mineral loss/precipitation and remineralization. Study characteristics and outcomes of included studies were summarized. Cochrane's risk-of-bias tool 2.0 was used to assess the quality of eligible studies, and meta-analysis using a random effects model was performed.

RESULTS

The search retrieved 869 studies of which 21 were considered eligible. Regarding the results of the quality assessment for potential risk of bias in all included studies, overall, 5 studies were considered as being at low risk, another 12 at unclear risk and 4 at high risk of bias. The findings of the studies showed that the addition of calcium in juice drinks led to reduced enamel loss, with blackcurrant juice presenting 2.6 times statistically significant less enamel loss compared to orange juice (p = 0.0001, I2 = 89%). No statistically significant difference in mean surface microhardness of eroded enamel was recorded between chewing gum with or without casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) (p = 0.31, I2 = 71%). Contradictory were the results regarding the effect of milk and CPP-ACP pastes on prevention of ETW.

CONCLUSIONS

Calcium formulations play an important role in ETW prevention, mainly through their addition to acidic drinks.

Fluorotic Enamel Susceptibility to Dental Erosion and Fluoride Treatment

The purpose of this in vitro study was to test the hypothesis that fluoride treatment can prevent dental erosion on fluorotic enamel of different severities. It followed a 3×2 factorial design, considering a) fluorosis severity: sound (TF0, Thylstrup-Fejerskov Index), mild (TF1-2), moderate (TF3-4); and b) fluoride treatment: 0 (negative control) and 1150ppmF. Human molars with the three fluorosis severities (n=16, each) were selected and randomly assigned to the two fluoride treatments (n=8). Enamel blocks (4×4mm) were prepared from each tooth and subjected to a dental erosion cycling model, for 10 days. The daily cycling protocol consisted of erosive challenges (1% citric acid, pH 2.4), interspersed by periods of immersion in artificial saliva, and three 2-minute treatments with either 0 or 1150ppm F. The enamel volume loss (mm3) was calculated by subtracting values obtained by microtomography before and after cycling. Two-Way ANOVA showed no significant interaction between fluorosis severity and fluoride treatment (p=0.691), and no significant effect for either fluorosis severity (TF0 mean±standard-deviation: 13.5(10-2±0.42(10-2, TF1-2: 1.50(10-2±0.52(10-2, TF3-4: 1.24(10-2±0.52(10-2, p=0.416) or treatment (0ppmF: 1.49(10-2±0.53(10-2; 1150ppmF: 1.21(10-2±0.42(10-2; p=0.093), when evaluated independently. Considering the limitations of this in vitro study, the presence and severity of fluorosis in enamel do not appear to affect its susceptibility to dental erosion. Fluoride treatment was not effective in preventing the development of dental erosion in both sound and fluorotic enamel substrates under our experimental conditions.

Combined use of stannous fluoride-containing mouth rinse and toothpaste prevents enamel erosion in vitro

OBJECTIVE

To compare the protective effect of commercial stannous-containing mouth rinses on enamel erosion in a simulated 5-day in vitro cycling model.

MATERIALS AND METHODS

81 human enamel specimens were embedded in resin blocks and divided into nine groups as follows; group 1: stannous fluoride (1000SnF2) toothpaste; groups 2,3, and 4 were the same as group 1 plus Elmex®, PerioMed™, and Meridol®, respectively, group 5: stannous fluoride (1450SnF2) toothpaste, groups 6, 7, and 8 were the same as group 5 plus Elmex®, PerioMed™, and Meridol®, respectively, group 9: negative control. An erosive challenge was induced with a 1 min hydrochloric acid (0.01 M, pH 2.2) treatment 3 times per day. Each cycle included immersing in the toothpaste slurry twice for two minutes and a one-minute rinse. The enamel slabs were immersed in artificial saliva between each erosive cycle and incubated overnight at 37 °C. Surface hardness loss and enamel loss were determined by Knoop surface hardness and non-contact profilometry, respectively. Finally, enamel surfaces were analyzed by scanning electron microscopy and X-ray energy dispersive spectroscopy (SEM/EDS).

RESULTS

All three mouth rinses had similar protective effects against erosion when using adjunct with 1000 SnF2 toothpaste (p > 0.05). With 1450 SnF2 toothpaste, Elmex® presented significantly lower surface hardness loss than Meridol® (p < 0.05). The combined use of Elmex® or PerioMed™ with toothpaste provided significantly better erosion protection than toothpaste alone, either 1000 or 1450 SnF2. In addition, 1000SnF2 toothpaste adjunct with mouth rinse is comparable to 1450 SnF2 toothpaste alone in preventing enamel erosion.

CONCLUSION

All three mouth rinses reduced enamel erosion. The additional use of a high concentration stannous containing mouth rinse with 1450 SnF2 toothpaste increases the protective effect against enamel erosion in vitro.

CLINICAL SIGNIFICANCE

To date, no standard protocol for preventing dental erosion is available. There are three stannous-containing mouth rinses on the market; however, no study compared their efficacy or indicated whether using adjuncts with anti-erosion toothpaste provides additional benefits. This study found that adding stannous mouth rinse to twice-daily toothpaste increases erosion protection.

Treatment for dental erosion: a systematic review of in vitro studies

Background

Dental erosion is a chemical loss of the mineralized dental tissue caused by exposure to nonbacterial acids. Different treatment protocols have been adopted with the use of fluoride compounds to promote the formation of a layer of mineral precipitation in eroded lesions.

Aim

This systematic review aimed to evaluate the main treatments for dental erosion.

Methodology

This study followed the Preferred Reporting Items for Systematic Reviews and Meta-Analyses (PRISMA) guidelines and recorded in the Open Science Framework database (OSF) under DOI 10.17605/OSF.IO/XMFNZ. The searches were conducted in six electronic databases (Pubmed, Embase, Web of Science, Cochrane, Scopus, Lilacs) and two grey literature sources (Google Scholar and OpenGrey). The eligibility criteria included in vitro studies that evaluated eroded teeth under treatment with some topical agent. Risk of bias assessment and qualitative synthesis were performed using the Cochrane collaboration's tool for assessing risk of bias modified for in vitro studies.

Results

A total of 522 studies were identified, and only four studies that fulfilled our eligibility criteria were included in this review. Among these studies, three were considered to have a low risk of bias, and one to have a high risk of bias. Two studies evaluated the anti-erosion effect of fluoride toothpaste, and the other two assessed the action of casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) on the surface of human teeth. Among the products analyzed, CPP-ACP was the only one that promoted a significant increase in enamel microhardness and reduced tooth wear.

Conclusion

Based on the in vitro studies included in this review, there was no anti-erosion effect after using different fluoride toothpaste. However, it should be considered that one of these studies presented a high risk of bias. On the other hand, studies with CPP-ACP showed anti-erosion efficacy when applied before or after erosive wear.

Topical Agents for Nonrestorative Management of Dental Erosion: A Narrative Review

A nonrestorative approach to the management of dental erosion is the foremost option: controlling dental erosion. The objectives of this study are to provide an overview and to summarise the effects and properties of topical anti-erosive agents as a nonrestorative treatment of dental erosion. A literature search was conducted on five databases of peer-reviewed literature—Cochrane Library, EMBASE, PubMed, Scopus and Web of Science—to recruit articles published between 1 January 2000 and 31 December 2021. The literature search identified 812 studies; 95 studies were included. Topical anti-erosive agents can be broadly categorised as fluorides, calcium phosphate-based agents, organic compounds and other anti-erosive agents. In the presence of saliva, fluorides promote the formation of fluorapatite on teeth through remineralisation. Calcium phosphate-based agents supply the necessary minerals that are lost due to the acid challenge of erosion. Some organic compounds and other anti-erosive agents prevent or control dental erosion by forming a protective layer on the tooth surface, by modifying salivary pellicle or by inhibiting the proteolytic activity of dentine collagenases. Topical anti-erosive agents are promising in managing dental erosion. However, current evidence shows inconsistent or limited results for supporting the use of these agents in clinical settings.

Advanced non-fluoride approaches to dental enamel remineralization: The next level in enamel repair management

In modern dentistry, a minimally invasive management of early caries lesions or early-stage erosive tooth wear (ETW) with synthetic remineralization systems has become indispensable. In addition to fluoride, which is still the non-plus-ultra in these early caries/ETW treatments, a number of new developments are in the test phase or have already been commercialized. Some of these systems claim that they are comparable or even superior to fluoride in terms of their ability to remineralize enamel. Besides, their use can help avoid some of the risks associated with fluoride and support treatments of patients with a high risk of caries. Two individual non-fluoride systems can be distinguished; intrinsic and extrinsic remineralization approaches. Intrinsic (protein/peptide) systems adsorb to hydroxyapatite crystals/organics located within enamel prisms and accumulate endogenous calcium and phosphate ions from saliva, which ultimately leads to the re-growth of enamel crystals. Extrinsic remineralization systems function on the basis of the external (non-saliva) supply of calcium and phosphate to the crystals to be re-grown. This article, following an introduction into enamel (re)mineralization and fluoride-assisted remineralization, discusses the requirements for non-fluoride remineralization systems, particularly their mechanisms and challenges, and summarizes the findings that underpin the most promising advances in enamel remineralization therapy.

Protection of calcium silicate/sodium phosphate/fluoride toothpaste with serum on enamel and dentin erosive wear

Objective

To evaluate the effect of a toothpaste containing calcium silicate/sodium phosphate/fluoride associated or not to the boost serum (BS) against erosive tooth wear (ETW) on enamel and dentin.

Methodology

Bovine enamel and dentin specimens were subjected to an erosion-abrasion cycling model (1% citric acid - pH 3.6 -2 min / artificial saliva – 60 min, 4×/day, 5 days). Toothbrushing was performed for 15 s (2 min exposed to slurry), 2×/day, with the toothpastes (n=10): control without fluoride (Weleda), Arg/Ca/MFP (Colgate Pro-Relief), Si/PO₄/MFP (Regenerate-Unilever), and Si/PO₄/MFP/BS (Si/PO₄/MFP with dual BS – Advanced Enamel Serum-Unilever). The effect of treatments on the eroded tissues was assessed by surface microhardness in the first day, and surface loss (SL) resulting from ETW was evaluated by profilometry (μm) after three and five days. Additional dentin specimens (n=5/group) were subjected to 20,000 brushing cycles to verify the abrasivity of the toothpastes. Data were subjected to ANOVA and correlation tests (5%).

Results

For enamel, no difference in microhardness was observed among the treated groups, and similar SL was obtained after 5 days. For dentin, Si/PO₄/MFP/BS resulted in higher microhardness values, but none of the groups presented significantly lower SL than the control. There was no significant correlation between SL and abrasiveness.

Conclusion

The calcium silicate/sodium phosphate toothpaste and serum increased microhardness of eroded dentin, but they did not significantly reduce enamel and dentin loss compared to the non-fluoride control toothpaste. The abrasiveness of the toothpastes could not predict their effect on ETW.

Enamel erosion control by strontium-containing TiO2- and/or MgO-doped phosphate bioactive glass

OBJECTIVES

To evaluate the effect of strontium-containing titanium- and/or magnesium-doped phosphate bioactive glass on the control of dental erosion.

MATERIALS AND METHODS

Fifty fragments of human enamel were divided into five groups: negative control, 45S5 bioglass, strontium-containing Ti-doped phosphate bioactive glass (PBG-Ti), strontium-containing Mg-doped phosphate bioactive glass (PBG-Mg), and strontium-containing Ti- and Mg-doped phosphate bioactive glass (PBG-TiMg). The specimens underwent cycles of erosive challenge twice daily for 5 days with 1 mL of citric acid for 2 min followed by 1 mL of the suspension with bioactive substances for 3 min. After the cycles, profilometry, roughness and microhardness testing, and scanning electron microscopy (SEM) were performed. The following statistical tests were used: one-way ANOVA (profile, roughness, and surface microhardness (%VMS) data variation), Tukey's HSD (%VMS), Games-Howell test (profilometry), Student's t test (roughness), and Pearson's correlation between the variables.

RESULTS

The lower loss of enamel surface and lower %VMS was observed in the PBG-Mg and PBG-TiMg groups, and only the PBG-Mg group showed similar roughness between baseline and eroded areas (p > 0.05). On SEM micrographs, PBG-Ti and PBG-Mg groups showed lower apparent demineralization.

CONCLUSION

All bioactive materials protected the enamel against erosion. However, strontium-containing phosphate bioactive glasses showed lower enamel loss, and the presence of Mg in these bioactive glasses provided a greater protective effect.

CLINICAL RELEVANCE

Experimental strontium-containing phosphate bioactive glasses are effective in controlling enamel erosion. The results obtained in this study will guide the development of new dental products.

Toothbrushing Wear Resistance of Stained CAD/CAM Ceramics

Aim: To investigate the effect of toothbrushing on different stained Computerd Aided Design/Computer Aided Manufacturing CAD/CAM ceramics. Materials and Methods: Fifty specimens (high translucency zirconia, YZHT; zirconia-reinforced lithium silicate, ZLS; feldspathic, FDL; hybrid ceramic, HC; all from Vita Zahnfabrik) were divided into five groups according to their staining technique. ZLS allowed the composition of two groups: ZLS1 with crystallization and staining together; ZLS2, with the stain firing after the crystallization. YZHT received a stain firing after the sintering process, and FDL received stain firing directly. The HC was stained with acrylic staining, and was light-cured on its surface. The specimens were brushed in total for 150,000 cycles at 2.45 N with 180 strokes/min. Surface measurements to obtain Rz were performed after 50,000, 100,000 and 150,000 cycles, with five evaluation lines (5 mm) per specimen orthogonal to the brushing direction, covering brushed and unbrushed areas. The wear was analyzed using two-way ANOVA and Tukey tests (α = 5%). Scanning electron microscopy (SEM) was performed to access the surface profile. The wear was affected by material (p < 0.001) and time (p = 0.139). Superior wear (µm) was observed for HC (6.6 ± 4.4; 6.8 ± 4.0; 9.2 ± 3.5) compared to ZLS2 (1.0 ± 0.3; 1.2 ± 2.2; 1.3 ± 0.3), YZHT (1.0 ± 0.1; 1.2 ± 0.3; 1.2 ± 0.3), ZLS1 (0.9 ± 0.1; 1.1 ± 0.5; 1.2 ± 0.3) and FDL (0.9 ± 0.1; 0.9 ± 0.1; 1.0 ± 0.2) after 5, 10 and 15 years of simulation, respectively. SEM showed different wear patters for HC with the removal of the glaze layer. HC showed a higher staining wear rate compared to the glass-based and polycrystalline ceramics after 15 years. The extrinsic characterization of feldspathic ceramic showed its superior longevity compared to the evaluated high-translucency zirconia, zirconia-reinforced lithium silicate, and hybrid ceramic.

Effectiveness of a toothpaste and a serum containing calcium silicate on protecting the enamel after interproximal reduction against demineralization

To evaluate the effectiveness of a calcium silicate/phosphate fluoridated tooth paste and a serum compared with a toothpaste containing hydroxyapatite on protecting the enamel after interproximal reduction against demineralization. 3 sets of eleven incisors were created. The teeth underwent interproximal enamel reduction (IER) of 0.5 mm. Each set was allocated to one of three groups: (1) Brushing without toothpaste (control group); (2) Vitis toothpaste + Remin Pro; (3) Regenerate toothpaste + Regenerate Serum. The agents were applied three times a day and specimens subjected to demineralization cycles for 30 days. The weight percentages of calcium (Ca) and phosphorous (P) were quantified by X-ray microfluorescence spectroscopy. Surface microhardness measurements and electron scanning microscopy (SEM) observations were made. Ca data and the Ca/P ratio were significantly higher in Group 3 than the other groups (p < 0.017), while P was significantly lower in Group 3 (p < 0.017). No significant differences were found between Groups 1 and 2 (p > 0.017). Group 3 showed significantly higher microhardness values (p < 0.05) than Group 1. No significant differences were found for other comparisons between groups (p < 0.05). SEM images showed less demineralization in Group 3. The application of a calcium silicate/phosphate fluoridated tooth paste (Regenerate advance) and a dual serum (Regenerate advance enamel serum) protect the enamel with interproximal reduction against demineralization. Therefore, this treatment could be used to prevent the dissolution of hydroxyapatite after IER.

Stannous Fluoride Effects on Enamel: A Systematic Review

In recent years there has been a lot of talk about toothpastes with a particular chemical compound: stannous fluoride (SnF2). Its presence is currently still highly controversial, as the latter could have negative health effects. The different companies that produce toothpastes express its dosage in ppm. The purpose of this systematic literature review is to analyze all randomized clinical trials in the literature over the last 10 years and to draw clear results on the function of stannous fluoride, for this purpose the authors performed a Mann-Whitney U Test.

MATERIALS

The first analysis of the literature produced a number greater than 800 results, subsequently applying the inclusion and exclusion criteria, and following a manual analysis of the results, 26 manuscripts have been obtained.

RESULTS

From the results analyzed in this review, it could be shown that stannous fluoride does not present important contraindications, if not those commonly reported for fluorine. A meta-analysis on enamel loss has been conducted, it shows that SnF2 products provide better results with a p < 0.05 value.

CONCLUSION

This compound could have significant effects in favor of erosion and recalcification of the enamel, on the biofilm formation, gingival inflammation, and in addition, it could be an important aid in the removal of tooth stains and halitosis.

Whitening Dentifrices Effect on Enamel with Orthodontic Braces after Simulated Brushing

Objective  This study aimed to evaluate in vitro the effects of whitening dentifrices on enamel color, the shear bond strength of orthodontic brackets and adhesive remnant index (ARI).

Materials and Methods  Eighty bovine teeth with brackets were randomly divided into four groups ( n = 20): control group (GC)–water, test group 1 (GT1)–Colgate Total 12, test group 2 (GT2)–Curaprox Black Is White, and group test 3 (GT3)–Luminous White. All groups were submitted to brushing, simulating 12 months. The specimens were exposed to spectrophotometer color evaluation and to a shear strength test in a universal test machine using a 300 kN load with a crosshead speed of 0.5 mm/min. The ARI was evaluated with a stereoscopic magnifying glass.

Statistical Analysis  Nonparametric Kruskal–Wallis and Dunn’s tests were used for the color analysis, and Friedman and Nemenyi tests were used to compare the times in the variable. To compare the shear force between the groups, the data were evaluated by one-way analysis of variance and Tukey’s test, and ARI was analyzed using Fisher’s exact test, always with a significance level of 5%.

Results  In the color analysis, GT3 presented the greatest progression in whitening effect. GT1 had greater shear strength than GT3 did ( p ≤ 0.05). For ARI, the score 1 was predominant in the GC and GT1. The GT2 and GT3 groups had scores of 3.

Conclusion  The whitening dentifrices promoted significant color change over the 12-month brushing time and may have interfered in the resistance to shear bond strength and ARI.