Influence of surface roughening of Titanium substrate in the electrochemical activity of Manganese oxide thin film electrode in anodic oxidation of dye-containing solutions

Copper-Decorated Titanium Electrodes: Impact of Surface Modifications of Substrate on the Morphology and Electrochemical Performance

This study investigates the effect of surface modifications of the titanium substrate on the growth of electrochemically deposited copper. These materials are intended to serve as cathodes in the electroreduction of nitrates in aqueous solutions. Surface modifications included the use of hydrogen fluoride for titanium etching and anodization to promote the growth of a structured titania nanotube array. The effect of an intermediate calcination step for the nanotubes before deposition was assessed along with a comparison to an untreated substrate electrode. The materials were comprehensively characterized by SEM, XRD, contact angle, potentiodynamic tests, EIS, and cyclic voltammetry. Their electrocatalytic ability was tested in the reduction of aqueous solutions containing nitrates. The results reveal that surface finishing impacted the shape and size of the Cu microparticles, as well as the nucleation mechanism enabling a crystal-facet-controllable synthesis. All the materials exhibited microsized copper particles with a spherical shape with some clusters. On the etched titanium surface, a high number of heterogeneous submicroscopic particles were also present. The thermally treated anodized substrate promoted the development of a combination of sparse microparticles corresponding to defect sites in amorphous titanium and the presence of a diffuse coating of octahedral nanosized particles whose growth was promoted by the tetragonal structure of anatase crystals. Electrochemical tests display reduced charge transfer resistance upon copper deposition on the modified substrates, which is indicative of the enhanced conductivity of the coated materials. Additionally, cyclic voltammetry and electrolysis experiments reveal the electrodes' potential for nitrate reduction, showing a better response for the etched titanium substrate (30% nitrate removal, after 2 h at 25 mA cm-2).

Effect of Precursors on the Electrochemical Properties of Mixed RuOx/MnOx Electrodes Prepared by Thermal Decomposition

Growing thin layers of mixed-metal oxides on titanium supports allows for the preparation of versatile electrodes that can be used in many applications. In this work, electrodes coated with thin films of ruthenium (RuOx) and manganese oxide (MnOx) were fabricated via thermal decomposition of a precursor solution deposited on a titanium substrate by spin coating. In particular, we combined different Ru and Mn precursors, either organic or inorganic, and investigated their influence on the morphology and electrochemical properties of the materials. The tested salts were: Ruthenium(III) acetylacetonate (Ru(acac)₃), Ruthenium(III) chloride (RuCl₃·xH₂O), Manganese(II) nitrate (Mn(NO₃)₂·4H₂O), and Manganese(III) acetylacetonate (Mn(acac)₃). After fabrication, the films were subjected to different characterization techniques, including scanning electron microscopy (SEM), polarization analysis, open-circuit potential (OCP) measurements, electrochemical impedance spectroscopy (EIS), linear sweep voltammetry (LSV), cyclic voltammetry (CV), and galvanostatic charge-discharge (GCD) experiments. The results indicate that compared to the others, the combination of RuCl₃ and Mn(acac) produces fewer compact films, which are more susceptible to corrosion, but have outstanding capacitive properties. In particular, this sample exhibits a capacitance of 8.3 mF cm^-2 and a coulombic efficiency of higher than 90% in the entire range of investigated current densities.

Mixed Oxide Electrodes Based on Ruthenium and Copper: Electrochemical Properties as a Function of the Composition and Method of Manufacture

The development of mixed oxide electrodes is being intensively investigated to reduce the high cost associated with the use of noble metals and to obtain versatile and long-lasting devices. To evaluate their use for charge storage or anodic oxidation, in this paper, thin-film electrodes coated with ruthenium (RuOx) and copper oxide (CuOx) are fabricated by thermal decomposition of organic solutions containing the precursors by drop-casting on titanium (Ti) foils. The coating consisted of four layers of metal oxide. To investigate the effect of copper (Cu) on electrochemical performances, different approaches are adopted by varying the ratios of precursors’ concentration and including a RuOx interlayer. A comparison with samples obtained by only RuOx has been also performed. The electrodes are characterized using scanning electron microscopy (SEM), cyclic (CV) and linear sweep (LSV) voltammetry, electrochemical impedance spectroscopy (EIS), and corrosion tests. The addition of Cu enhances the capacitive response of the materials and promotes electron transfer reversibility. The coatings obtained by the highest Ru:Cu ratio (95:5) exhibit a more uniform surface distribution and increased corrosion resistance. The interlayer is beneficial to further reduce the corrosion susceptibility and to promote the oxygen evolution but detrimental in the charge storage power. The results suggest the possibility to enhance the electrochemical performance of expensive RuOx through a combination with a low amount of cheaper and more abundant CuOx.

Effect of Spin Coating Parameters on the Electrochemical Properties of Ruthenium Oxide Thin Films

Ruthenium oxide (RuOx) thin films were spin coated by thermal decomposition of alcoholic solutions of RuCl3 on titanium foils and subsequently annealed at 400 °C. The effect of spin coating parameters, such as spinning speed, volume, and molar concentration of the precursor as well as the number of deposits, on the morphology and electrochemical performance of the electrodes was investigated. The films were characterized by scanning electron microscopy (SEM) equipped with energy-dispersive X-ray spectroscopy (EDX), cyclic voltammetry (CV) with and without chloride, and linear sweep voltammetry (LSV). The prepared materials were also compared to drop cast films and spin-coated films obtained by adopting low-temperature intermediate treatments. The results indicate that even dispersion of the oxide layer was always achieved. By tuning the spin coating parameters, it was possible to obtain different electrochemical responses. The most influential parameter is the number of deposits, while the concentration of the precursor salt and the rotation speed were less relevant, under the adopted conditions.