Physical Vapor Deposited [Co:Cd-(dtc)2]/SnO2 Dual Semiconductor Systems: Synthesis, Characterization and Photo-Electrochemistry

Paper-based microfluidic system and chiroptical functionalized gold nano-oval for colorimetric detection of L-Tryptophan

"The development and deployment of a practical and portable technology for on-site chiral identification of enantiomers hold immense significance in the fields of medical and biological sciences. Among the essential amino acids, Tryptophan (Trp) plays a crucial role in human metabolism and serves as a diagnostic marker for various metabolic disorders. In this study, we introduce an innovative approach that combines an enantio-selective ZIF-8-His MOF-MIPs packed-bed centrifugal microfluidic system with an enantioselective colorimetric sensor probe. This system is further integrated with smartphone-based on-site data recording. The basis of this colorimetric sensor's operation lies in the controlled morphology and surface passivation of gold nano-ovals (Au-NOs) through DL-Alanine. To confirm the successful synthesis of the chiral recognition elements, we employed various characterization techniques, including FE-SEM, TEM, FTIR, CD, UV-Vis, zeta potential, DLS, and XRD. Our focus was on optimizing operational parameters for the effective separation and determination of L-chiral tryptophan on-site. The sensor exhibited two linear ranges for L-Trp detection: 0-5.42 and 5.42-80.47 mM, with a detection limit of 0.5 mM. The integrated system possesses advantages such as ease of availability, preparation, high stability, desirable selectivity even in the presence of similar biomolecules, and rapid detection capabilities. Furthermore, our method demonstrated successful enantioselective sensing of L-Trp in various biological samples, including human blood plasma, urine, milk, and bovine serum albumin (BSA), yielding promising results. The integrated microfluidic platform follows a "sample-in and answer-out" approach, making it highly applicable in healthcare, environmental monitoring, food safety analysis, and point-of-care testing. The chiral recognition pretreatment assay and self-contained, automated colorimetric detection on the microfluidic disc represent a promising avenue for cutting-edge research in these domains".

Atmospheric Pressure Solvothermal Synthesis of Nanoscale SnO2 and Its Application in Microextrusion Printing of a Thick-Film Chemosensor Material for Effective Ethanol Detection

The atmospheric pressure solvothermal (APS) synthesis of nanocrystalline SnO₂ (average size of coherent scattering regions (CSR)-7.5 ± 0.6 nm) using tin acetylacetonate as a precursor was studied. The resulting nanopowder was used as a functional ink component in microextrusion printing of a tin dioxide thick film on the surface of a Pt/Al₂O₃/Pt chip. Synchronous thermal analysis shows that the resulting semiproduct is transformed completely into tin dioxide nanopowder at 400 °C within 1 h. The SnO₂ powder and the resulting film were shown to have a cassiterite-type structure according to X-ray diffraction analysis, and IR spectroscopy was used to establish the set of functional groups in the material composition. The microstructural features of the tin dioxide powder were analyzed using scanning (SEM) and transmission (TEM) electron microscopy: the average size of the oxide powder particles was 8.2 ± 0.7 nm. Various atomic force microscopy (AFM) techniques were employed to investigate the topography of the oxide film and to build maps of surface capacitance and potential distribution. The temperature dependence of the electrical conductivity of the printed SnO₂ film was studied using impedance spectroscopy. The chemosensory properties of the formed material when detecting H₂, CO, NH₃, C₆H₆, C₃H₆O and C₂H₅OH, including at varying humidity, were also examined. It was demonstrated that the obtained SnO₂ film has an increased sensitivity (the sensory response value was 1.4-63.5) and selectivity for detection of 4-100 ppm C₂H₅OH at an operating temperature of 200 °C.