Pervaporation performance of surface-modified zeolite/PU mixed matrix membranes for separation of phenol from water

Surface-modified silicalite-1-filled PDMS membranes for pervaporation dehydration of trichloroethylene

In this study, the impact of silane coupling agents, namely 3-aminopropyltrimethoxysilane (APTMS), trimethylchlorosilane (TMCS), and 1,1,3,3-tetramethyldisilazane (TMDS), on the hydrophobicity of silicalite-1 zeolite was investigated to enhance the pervaporation separation performance of mixed matrix membranes (MMMs) for trichloroethylene (TCE). The hydrophobicity of TMCS@silicalite-1 and TMDS@silicalite-1 particles exhibited significant improvement, as evidenced by the increase in water contact angle from 96.1° to 101.9° and 109.1°, respectively. Conversely, the water contact angle of APTMS@silicalite-1 particles decreased to 85.2°. Silane-modified silicalite-1 particles were incorporated into polydimethylsiloxane (PDMS) to prepare mixed matrix membranes (MMMs), resulting in a significant enhancement in the adsorption selectivity of trichloroethylene (TCE) on membranes containing TMCS@silicalite-1 and TMDS@silicalite-1 particles. The experimental findings demonstrated that the PDMS membrane with a TMDS@silicalite-1 particle loading of 40 wt% exhibited the most favorable pervaporation performance. Under the conditions of a temperature of 30 °C, a flow rate of 100 mL min-1, and a vacuum degree of 30 kPa, the separation factor and total flux of a 3 × 10-7 wt% TCE aqueous solution were found to be 139 and 242 g m-2 h-1, respectively. In comparison to the unmodified silicalite-1/PDMS, the separation factor exhibited a 44% increase, while the TCE flux increased by 16%. Similarly, when compared to the pure PDMS membrane, the separation factor showed an 83% increase, and the TCE flux increased by 20%. These findings provide evidence that the hydrophobic modification of inorganic fillers can significantly enhance the separation performance of PDMS membranes for TCE.

Improving the Pervaporation Performance of PDMS Membranes for Trichloroethylene by Incorporating Silane-Modified ZSM-5 Zeolite

The hydrophobic nature of inorganic zeolite particles plays a crucial role in the efficacy of mixed matrix membranes (MMMs) for the separation of trichloroethylene (TCE) through pervaporation. This study presents a novel approach to further augment the hydrophobicity of ZSM-5. The ZSM-5 zeolite molecular sieve was subjected to modification using three different silane coupling agents, namely, n-octyltriethoxysilane (OTES), γ-methacryloxypropyltrimethoxysilane (KH-570), and γ-aminopropyltriethoxysilane (KH-550). The water contact angles of the resulting OTES@ZSM-5, KH-570@ZSM-5, and KH-550@ZSM-5 particles exhibited significant increases from 97.2° to 112.8°, 109.1°, and 102.7°, respectively, thereby indicating a notable enhancement in hydrophobicity. Subsequently, mixed matrix membranes (MMMs) were fabricated by incorporating the aforementioned silane-modified ZSM-5 particles into polydimethylsiloxane (PDMS), leading to a considerable improvement in the adsorption selectivity of these membranes towards trichloroethylene (TCE). The findings indicate that the PDMS membrane with a 20 wt.% OTES@ZSM-5 particle loading exhibits superior pervaporation performance. When subjected to a temperature of 30 °C, flow rate of 100 mL/min, and vacuum of 30 Kpa, the separation factor and total flux of a 3 × 10-7 wt.% TCE solution reach 328 and 155 gm-2·h-1, respectively. In comparison to the unmodified ZSM-5/PDMS membrane, the separation factor demonstrates a 41% increase, while the TCE flux experiences a 6% increase. Consequently, this approach effectively enhances the pervaporation separation capabilities of the PDMS membrane for TCE.

Influence of the Zeolite ZSM-22 Precursor on a UF-PES Selective Substrate Layer for Salts Rejection

Fabrication of the ZSM-22/Polyethersulfone (ZSM-22/PES) membranes as selective salt filters represent a growing membrane technological area in separation with the potential of high economic reward based on its low energy requirements. The incorporation of ZSM-22 zeolite material as additives into the PES polymer matrix has the prospective advantage of combining both the zeolite and polymer features while overcoming the limitations associated with both materials. This work investigated the influence of the nature of the silica precursor on ZSM-22 zeolite hydrothermally synthesised using colloidal (C60) and fumed (C60) silica to Si/Al of 60. The successful synthesis of the highly crystalline zeolitic materials was confirmed through XRD, FTIR, and SEM with EDX. The ZSM-22 additives were directly dispersed into a PES polymeric matrix to form a casting solution for the preparation of the ZSM-22/PES selective substrate layers via a phase inversion method for salts rejection. The polymeric PES was selected as an organic network in which the content of the ZSM-22 zeolite (ranging between 0 and 1.0 wt.%), was obtained and characterised by XRD, FTIR, and SEM analysis, as well as water contact angle (WCA) measurement and dead-end filtration cell. The phase inversion preparation method has induced the resulting ZSM-22/PES NF substrates anisotropy, as attributed to a high water flux to the above 700 L·m−2·h−1; high selectivity and rejection of salts to above 80% is revealed by the obtained results. The materials also exhibited improved antifouling behavior to above 70% flux recovery ratios. As such, the nature of the silica precursor influences ZSM-22 zeolite synthesis as a potential additive in the PES polymer matrix and led to the enhanced performance of the pure PES ultrafiltration membrane.