Smokeless tobacco contains an inhibitor of prolyl hydroxylase activity

Comparison of growth and metabolism of avian osteoblasts on polished disks versus thin films of titanium alloy

The purpose of this study was to evaluate the efficacy of using high vacuum, thermal evaporation to deposit thin films of Ti-6Al-4V onto plates for subsequent cell culture investigations. Osteoblastic response to thin-film coated plates was compared to that of cells grown on Ti alloy disk inserts and uncoated culture plates. The Ti alloy disks were polished, cleaned, and passivated following a commercial protocol for orthopedic implants. Mean surface roughness was 262 nm for the Ti alloy disks and 4.756 nm for the coated culture plates. Osteoblasts isolated from 16-day chick embryo calvariae were cultured on polystyrene, thin films, and disks. At confluence, the cells were cultured an additional 48 h and were evaluated for cell number (DNA content), rate of glycolysis (lactate production), alkaline phosphatase activity (ALPase), and collagenous (3H-proline hydroxylation) and noncollagenous protein synthesis. Cell morphology was similar for the controls, disks, and thin-film groups. DNA, lactate, cell layer ALPase, 3H-hydroxyproline, and noncollagenous protein were not different (p > 0.05) among the control, thin-film, and disk groups. Medium ALPase was lower (p < 0.05) in the thin-film group compared to the control group. Although aluminum and vanadium percentages varied from nominal in the thin-film groups (11Al-2V as opposed to 6Al-4V), avian osteoblasts responded similarly to the Ti alloy thin films, disks, and uncoated culture plates for the smooth surfaces tested. The thin-film cell culture system used for elemental material studies appears to offer a promising method for the investigation of cellular response to alloyed biomaterials as well. Proper adjustments in alloy percentages before deposition, however, need to be made if thermal evaporation is utilized.

The effects of smokeless tobacco extract on bone nodule formation and mineralization by chick osteoblasts in vitro

Short-term exposure to smokeless tobacco extracts (STE) reportedly inhibits osteoblast metabolism. The objective of this study was to determine the effects of serial dilutions of a water-soluble extract of smokeless tobacco on osteoblast proliferation and their potential to form and mineralize bone nodules. STE significantly stimulated cell proliferation when diluted 10(2)-10(4) times; 10(3) and 10(4) dilutions produced the greatest effect. 10(2)-10(4) STE dilutions significantly increased alkaline phosphatase activity at day 7 but 10(6) STE dilutions significantly decreased it. 10(3) and 10(4) dilutions significantly increased bone nodule formation, but inhibited their mineralization. In contrast, 10(5) and 10(6) dilutions significantly decreased bone nodule formation, but increased their mineralization. Stimulation of in vitro bone nodule formation by STE was similar to that produced by 10(-7) M insulin-like growth factor 1 (IGF-1) in vivo. Heat and acid treatment of STE significantly reduced its beneficial effect on cell proliferation, suggesting that a peptide within STE may be responsible for enhancement of osteogenic cell proliferation. Thus, STE may contain a peptide capable of significantly stimulating osteoblast proliferation, differentiation and metabolism, similar to the effects of IGF-1. This peptide could have potential therapeutic benefits.