Effect of Multiple Enamel Surface Treatments on Micro-Shear Bond Strength

Objectives: The aim of this study was to evaluate the effect of different enamel surface treatments on the micro-shear bond strength. Materials and methods: Sixty-four approximal surfaces from freshly extracted molars were randomly assigned to eight groups, according to combinations of the following enamel surface treatments: ground or unground, 37.5% phosphoric acid etching time of 15 or 30 s, and with or without primer application. The same bonding agent (Optibond FL™ Adhesive, Kerr) was then used for all groups, and a 1.8 mm diameter resin composite (Harmonize™, Kerr) cylinder was built up on the bonded surface. Samples underwent a shear force test at a crosshead speed of 1 mm/min until failure. Bond strength was calculated, and failure modes were inspected under an optical microscope. Results: Bond-strength values ranged from 8.2 MPa for 15 s etched unground enamel with primer application to 19.6 MPa for 30 s etched ground enamel without primer application. ANOVA and Fisher’s LSD post hoc tests revealed significant differences between the groups. Conclusions: Etching time and grinding have a statistically significant effect on the micro-shear bond strength of a three-step etch-and-rinse adhesive system on enamel. Primer application does not seem to be beneficial for enamel adhesion.

A novel non-destructive technique for qualitative and quantitative measurement of dental erosion in its entirety by porosity and bulk tissue-loss

OBJECTIVE

To explore the potential of combining non-contact profilometry (NCP) and confocal laser scanning microscopy (CLSM) data to measure the entire erosive process non-destructively and to validate findings using inductively coupled plasma-atomic emission spectroscopy (ICP-AES), scanning electron microscopy (SEM) and surface microhardness (SMH) using the same samples throughout.

METHODS

Polished bovine enamel samples (n = 35) were divided into groups (7/group) with similar SMH values. Samples underwent individual erosive challenges (1 % citric acid, pH3.8) for 1, 5, 10, 15 or 30 min under stirring and aliquot extracts were analysed for Ca and P by ICP-AES. SMH was used to measure erosive softening. Profilometry was used to assess bulk volume loss (BVL). Images were captured by SEM. Samples were stained with rhodamine-B (0.1 mM, 24 h) and images captured by CLSM. Image processing was used to determine changes in fluorescent volume for the first 10 μm (ΔFV₁₀) for each enamel sample which were combined with BVL to calculate total lesion volume (TLV). ANOVA, linear regression and Pearson correlation analysis were used where applicable.

RESULTS

Surface softening, [Ca], [P], BVL and ΔFV_10μm increased with acid erosion duration which were significant by 10 min (P < .01). The Ca:P ratio increased to 1.57 then decreased after 5 min erosion suggesting a sub/surface phase change, which was observed by SEM and CLSM showing significant changes to the enamel surface and subsurface morphology with time. Combination of BVL and ΔFV₁₀ as TLV strengthened the significant correlations with [Ca], [P], and SMH (P < .01).

CONCLUSION

This novel combination of CLSM and NCP allows for concurrent non-destructive quantification of the entire erosive process by mineral loss, and qualitatively characterise microstructural changes during dental erosion.