Corrosion and adverse tissue reaction after modular unipolar hip hemiarthroplasty

Taper corrosion: a complication of total hip arthroplasty

The focus on taper corrosion in modular hip arthroplasty increased around 2007 as a result of clinical problems with large-head metal-on-metal (MoM) bearings on standard stems. Corrosion problems with bi-modular primary hip stems focused attention on this issue even more.

Factors increasing the risk of taper corrosion were identified in laboratory and retrieval studies: stiffness of the stem neck, taper diameter and design, head diameter, offset, assembly force, head and stem material and loading.

The high variability of the occurrence of corrosion in the clinical application highlights its multi-factorial nature, identifying the implantation procedure and patient-related factors as important additional factors for taper corrosion.

Discontinuing the use of MoM has reduced the revisions due to metal-related pathologies dramatically from 49.7% (MoM > 32 mm), over 9.2% (MoM ⩽ 32 mm) to 0.8% (excluding all MoM).

Further reduction can be achieved by omitting less stiff Ti-alloys and large metal heads (36 mm and above) against polyethylene (PE).

Standardized taper assembly of smaller and ceramic heads will reduce the clinical occurrence of taper corrosion even further. If 36 mm heads are clinically indicated, only ceramic heads should be used.

Taper-related problems will not comprise a major clinical problem anymore if the mentioned factors are respected.

Cite this article: EFORT Open Rev 2020;5:776-784. DOI: 10.1302/2058-5241.5.200013

Atomic Scale Origin of Metal Ion Release from Hip Implant Taper Junctions

Millions worldwide suffer from arthritis of the hips, and total hip replacement is a clinically successful treatment for end-stage arthritis patients. Typical hip implants incorporate a cobalt alloy (Co-Cr-Mo) femoral head fixed on a titanium alloy (Ti-6Al-4V) femoral stem via a Morse taper junction. However, fretting and corrosion at this junction can cause release of wear particles and metal ions from the metallic implant, leading to local and systemic toxicity in patients. This study is a multiscale structural-chemical investigation, ranging from the micrometer down to the atomic scale, of the underlying mechanisms leading to metal ion release from such taper junctions. Correlative transmission electron microscopy and atom probe tomography reveals microstructural and compositional alterations in the subsurface of the titanium alloy subjected to in vitro gross-slip fretting against the cobalt alloy. Even though the cobalt alloy is comparatively more wear-resistant, changes in the titanium alloy promote tribocorrosion and subsequent degradation of the cobalt alloy. These observations regarding the concurrent occurrence of electrochemical and tribological phenomena are vital to further improve the design and performance of taper junctions in similar environments.

Investigation of nano-sized debris released from CoCrMo secondary interfaces in total hip replacements: Digestion of the flakes

The in vivo release of wear debris and corrosion products from the metallic interfaces of total hip replacements is associated with a wide spectrum of adverse body reactions and systemic manifestations. The origin of debris and the electrochemical conditions at the sites of material loss both play a role in determining the physicochemical characteristics of the particles, and thus influence their in vivo reactivity. Debris retrieved from revised CoCrMo tapers and cement-stem interfaces consists of heterogeneous flakes that comprise mechanically mixed metal particles, corrosion products and organic material. Detailed investigation of the size and composition of the metal debris contained within these composites requires the digestion of the flakes to release the small metal particles. Here, we compare alkaline and enzymatic digestion methods that both aim to fragment the flakes and reveal their smallest building blocks. The characterization of debris cleaned with both methods revealed crystalline Cr oxide nanoparticles and clusters. Comparison between the treatments showed that the alkaline method is more efficient in fragmenting the flakes and provided cleaner and generally smaller nanoparticles than exhibited in debris released with the enzymatic treatment. The provision of cleaner nanoparticles from the alkaline method also allows the physicochemical properties of the particles to be more clearly identified. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 107B: 424-434, 2019.