1
|
Bologna FA, Putame G, Audenino AL, Terzini M. Understanding the role of head size and neck length in micromotion generation at the taper junction in total hip arthroplasty. Sci Rep 2024; 14:6397. [PMID: 38493233 PMCID: PMC10944531 DOI: 10.1038/s41598-024-57017-x] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 12/20/2023] [Accepted: 03/13/2024] [Indexed: 03/18/2024] Open
Abstract
Modular hip implants allow intra-operative adjustments for patient-specific customization and targeted replacement of damaged elements without full implant extraction. However, challenges arise from relative micromotions between components, potentially leading to implant failure due to cytotoxic metal debris. In this study magnitude and directions of micromotions at the taper junction were estimated, aiming to understand the effect of variations in head size and neck length. Starting from a reference configuration adhering to the 12/14 taper standard, six additional implant configurations were generated by varying the head size and/or neck length. A musculoskeletal multibody model of a prothesized lower limb was developed to estimate hip contact force and location during a normal walking task. Following the implant assembly, the multibody-derived loads were imposed as boundary conditions in a finite element analysis to compute the taper junction micromotions as the relative slip between the contacting surfaces. Results highlighted the L-size head as the most critical configuration, indicating a 2.81 μm relative slip at the mid-stance phase. The proposed approach enables the investigation of geometric variations in implants under accurate load conditions, providing valuable insights for designing less risky prostheses and informing clinical decision-making processes.
Collapse
Affiliation(s)
- Federico A Bologna
- PolitoBIOMed Lab, Politecnico di Torino, 10129, Turin, Italy
- Department of Mechanical and Aerospace Engineering, Politecnico di Torino, 10129, Turin, Italy
| | - Giovanni Putame
- PolitoBIOMed Lab, Politecnico di Torino, 10129, Turin, Italy
- Department of Mechanical and Aerospace Engineering, Politecnico di Torino, 10129, Turin, Italy
| | - Alberto L Audenino
- PolitoBIOMed Lab, Politecnico di Torino, 10129, Turin, Italy
- Department of Mechanical and Aerospace Engineering, Politecnico di Torino, 10129, Turin, Italy
| | - Mara Terzini
- PolitoBIOMed Lab, Politecnico di Torino, 10129, Turin, Italy.
- Department of Mechanical and Aerospace Engineering, Politecnico di Torino, 10129, Turin, Italy.
| |
Collapse
|
2
|
Diaz-Lopez RA, Wen PH, Shelton JC. Influence of Taper surface topographies on contact deformation and stresses. J Mech Behav Biomed Mater 2023; 148:106213. [PMID: 37952504 DOI: 10.1016/j.jmbbm.2023.106213] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 01/02/2023] [Revised: 10/16/2023] [Accepted: 10/26/2023] [Indexed: 11/14/2023]
Abstract
The role of bore and trunnion surface topography on the failure rate of total hip joint replacements due to trunnionosis is not clear despite significant variations in the design of taper components between manufacturers. Taper surface topography, along with other taper design parameters such as clearance, diameter, and assembly force, determine the initial interlock of the contacting surfaces after assembly; this has been related to relative motions that can cause fretting and corrosion at the taper interface. However, in most in-silico parametrical taper studies associated with taper micromotions, the bore and trunnion surfaces have been simplified using a flat surface and/or sinusoidal functions to mimic the surface roughness. The current study tests the hypothesis that the use of simple geometrical functions for the taper surface topography can predict the surface mechanics developed in assembled tapers. Measured and simulated surfaces of bores and trunnions were characterised using common roughness parameters and spectral density estimations. Using the same characterised surface profiles, 2D Finite Element (FE) models of CoCr alloy femoral heads and Ti alloy trunnions were developed. Models simulated assembly conditions at different resultant forces ranging from 0.5 to 4.0 kN, contact conditions were determined and associated with their topographical characteristics. Measured surfaces of bore and trunnion components comprise up to seven dominant spatial frequencies. Flattening of the trunnion microgrooved peaks was observed during the assembly of the taper. When the femoral head bore and trunnion topography were both considered a reduced number of microgrooved peaks were in contact, from 51 in an idealised taper surfaces to 35 in measured surfaces using an assembly reaction force of 4 kN. The contact points in the models developed high plastic strains, which were greater than that associated with failure of the material. Results showed that line and sine wave functions over estimate contact points at the taper interface compared to those surfaces that consider roughness and peak variation. These findings highlight the important role of modelling the full surface topography on the taper contact mechanics, as surface variations in the roughness and waviness change the performance of tapers.
Collapse
Affiliation(s)
- R A Diaz-Lopez
- School of Engineering and Materials Science, Queen Mary University of London, UK
| | - P H Wen
- School of Engineering and Materials Science, Queen Mary University of London, UK
| | - J C Shelton
- School of Engineering and Materials Science, Queen Mary University of London, UK.
| |
Collapse
|
3
|
McCarty CP, Nazif MA, Sangiorgio SN, Ebramzadeh E, Park SH. Can severity of trunnion damage be estimated by visual inspection alone? Bone Joint Res 2023; 12:155-164. [PMID: 37051817 PMCID: PMC10072233 DOI: 10.1302/2046-3758.123.bjr-2022-0099.r1] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Submit a Manuscript] [Subscribe] [Scholar Register] [Indexed: 04/14/2023] Open
Abstract
Taper corrosion has been widely reported to be problematic for modular total hip arthroplasty implants. A simple and systematic method to evaluate taper damage with sufficient resolution is needed. We introduce a semiquantitative grading system for modular femoral tapers to characterize taper corrosion damage. After examining a unique collection of retrieved cobalt-chromium (CoCr) taper sleeves (n = 465) using the widely-used Goldberg system, we developed an expanded six-point visual grading system intended to characterize the severity, visible material loss, and absence of direct component contact due to corrosion. Female taper sleeve damage was evaluated by three blinded observers using the Goldberg scoring system and the expanded system. A subset (n = 85) was then re-evaluated following destructive cleaning, using both scoring systems. Material loss for this subset was quantified using metrology and correlated with both scoring systems. There was substantial agreement in grading among all three observers with uncleaned (n = 465) and with the subset of cleaned (n = 85) implants. The expanded scoring criteria provided a wider distribution of scores which ultimately correlated well with corrosion material loss. Cleaning changed the average scores marginally using the Goldberg criteria (p = 0.290); however, using the VGS, approximately 40% of the scores for all observers changed, increasing the average score from 4.24 to 4.35 (p = 0.002). There was a strong correlation between measured material loss and new grading scores. The expanded scoring criteria provided a wider distribution of scores which ultimately correlated well with corrosion material loss. This system provides potential advantages for assessing taper damage without requiring specialized imaging devices.
Collapse
Affiliation(s)
- Colin P McCarty
- The J. Vernon Luck, Sr., M.D. Orthopaedic Research Center, Orthopaedic Institute for Children and UCLA Department of Orthopaedic Surgery, Los Angeles, California, USA
| | - Mohammad A Nazif
- The J. Vernon Luck, Sr., M.D. Orthopaedic Research Center, Orthopaedic Institute for Children and UCLA Department of Orthopaedic Surgery, Los Angeles, California, USA
| | - Sophia N Sangiorgio
- The J. Vernon Luck, Sr., M.D. Orthopaedic Research Center, Orthopaedic Institute for Children and UCLA Department of Orthopaedic Surgery, Los Angeles, California, USA
| | - Edward Ebramzadeh
- The J. Vernon Luck, Sr., M.D. Orthopaedic Research Center, Orthopaedic Institute for Children and UCLA Department of Orthopaedic Surgery, Los Angeles, California, USA
| | - Sang-Hyun Park
- The J. Vernon Luck, Sr., M.D. Orthopaedic Research Center, Orthopaedic Institute for Children and UCLA Department of Orthopaedic Surgery, Los Angeles, California, USA
| |
Collapse
|
4
|
Feyzi M, Fallahnezhad K, Taylor M, Hashemi R. An Overview of the Stability and Fretting Corrosion of Microgrooved Necks in the Taper Junction of Hip Implants. MATERIALS (BASEL, SWITZERLAND) 2022; 15:8396. [PMID: 36499893 PMCID: PMC9735617 DOI: 10.3390/ma15238396] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Figures] [Subscribe] [Scholar Register] [Received: 10/14/2022] [Revised: 11/21/2022] [Accepted: 11/22/2022] [Indexed: 06/17/2023]
Abstract
Fretting corrosion at the head-neck interface of modular hip implants, scientifically termed trunnionosis/taperosis, may cause regional inflammation, metallosis, and adverse local tissue reactions. The severity of such a deleterious process depends on various design parameters. In this review, the influence of surface topography (in some cases, called microgrooves/ridges) on the overall performance of the microgrooved head-neck junctions is investigated. The methodologies together with the assumptions and simplifications, as well as the findings from both the experimental observations (retrieval and in vitro) and the numerical approaches used in previous studies, are presented and discussed. The performance of the microgrooved junctions is compared to those with a smooth surface finish in two main categories: stability and integrity; wear, corrosion, and material loss. Existing contradictions and disagreements among the reported results are reported and discussed in order to present a comprehensive picture of the microgrooved junctions. The current research needs and possible future research directions on the microgrooved junctions are also identified and presented.
Collapse
|
5
|
Taper corrosion in total hip arthroplasty – How to assess and which design features are crucial? J Mech Behav Biomed Mater 2022; 133:105307. [DOI: 10.1016/j.jmbbm.2022.105307] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 02/22/2022] [Revised: 05/28/2022] [Accepted: 05/30/2022] [Indexed: 11/21/2022]
|
6
|
Godoy M, Gustafson JA, Hertzler JS, Bischoff JE, Pourzal R, Lundberg HJ. Model validation for estimating taper microgroove deformation during total hip arthroplasty head-neck assembly. J Biomech 2022; 140:111172. [PMID: 35696772 PMCID: PMC9801958 DOI: 10.1016/j.jbiomech.2022.111172] [Citation(s) in RCA: 1] [Impact Index Per Article: 0.5] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 08/26/2021] [Revised: 03/25/2022] [Accepted: 05/31/2022] [Indexed: 01/03/2023]
Abstract
Total hip arthroplasty (THA) failure and the need for revision surgery can result from fretting-corrosion damage of the head-neck modular taper junctions. Prior work has shown that implant geometry, such as microgrooves, influences damage on retrieved implants. Microgroove deformation within the modular taper junction occurs when the female head taper meets the male stem taper during THA surgical procedure. The objective of this work was to validate microgroove deformation after head-neck THA assembly as calculated by finite element analysis (FEA). Four 28 mm CoCrMo head tapers and four Ti6Al4V stem tapers were scanned via white light interferometry. Heads were assembled onto stem tapers until 6kN reaction force was achieved, followed by head removal using a cut-off machine. The stem tapers were then rescanned and analyzed. Simultaneously, a 2D axisymmetric FEA model was developed and assembled per implant geometries and experimental data. For experiments and FEA, the mean change in microgroove height was 1.23 µm and 1.40 µm, respectively. The largest microgroove height change occurred on the proximal stem taper due to the conical angles of the head and stem tapers. FEA showed that the head-stem assembly induced high stresses and microgroove peaks flattening. 76-89% and 91-100% of the microgrooves in the experiments and FEA, respectively, showed height changes along the contact length of the stem taper. A validated FEA model of THA head-neck modular junction contact mechanics is essential to identifying implant geometries and surface topographies that can potentially minimize the risk of fretting and fretting-corrosion at modular junctions.
Collapse
Affiliation(s)
- Michael Godoy
- Department of Orthopedic Surgery, Rush University Medical Center, Chicago, IL, USA
| | | | | | | | - Robin Pourzal
- Department of Orthopedic Surgery, Rush University Medical Center, Chicago, IL, USA
| | - Hannah J. Lundberg
- Department of Orthopedic Surgery, Rush University Medical Center, Chicago, IL, USA
| |
Collapse
|
7
|
Mai PT, Bormann T, Müller U, Kretzer JP, Gibmeier J. Effect of surface topography and residual stress on the taper connection stability in total hip arthroplasty. J Mech Behav Biomed Mater 2022; 128:105119. [DOI: 10.1016/j.jmbbm.2022.105119] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 06/02/2021] [Revised: 01/10/2022] [Accepted: 02/03/2022] [Indexed: 11/26/2022]
|
8
|
Wight CM, Whyne CM, Bogoch ER, Zdero R, Chapman RM, van Citters DW, Walsh WR, Schemitsch E. Effect of head size and rotation on taper corrosion in a hip simulator. Bone Jt Open 2021; 2:1004-1016. [PMID: 34825826 PMCID: PMC8636299 DOI: 10.1302/2633-1462.211.bjo-2021-0147.r1] [Citation(s) in RCA: 4] [Impact Index Per Article: 1.3] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Submit a Manuscript] [Subscribe] [Scholar Register] [Indexed: 01/16/2023] Open
Abstract
AIMS This study investigates head-neck taper corrosion with varying head size in a novel hip simulator instrumented to measure corrosion related electrical activity under torsional loads. METHODS In all, six 28 mm and six 36 mm titanium stem-cobalt chrome head pairs with polyethylene sockets were tested in a novel instrumented hip simulator. Samples were tested using simulated gait data with incremental increasing loads to determine corrosion onset load and electrochemical activity. Half of each head size group were then cycled with simulated gait and the other half with gait compression only. Damage was measured by area and maximum linear wear depth. RESULTS Overall, 36 mm heads had lower corrosion onset load (p = 0.009) and change in open circuit potential (OCP) during simulated gait with (p = 0.006) and without joint movement (p = 0.004). Discontinuing gait's joint movement decreased corrosion currents (p = 0.042); however, wear testing showed no significant effect of joint movement on taper damage. In addition, 36 mm heads had greater corrosion area (p = 0.050), but no significant difference was found for maximum linear wear depth (p = 0.155). CONCLUSION Larger heads are more susceptible to taper corrosion; however, not due to frictional torque as hypothesized. An alternative hypothesis of taper flexural rigidity differential is proposed. Further studies are necessary to investigate the clinical significance and underlying mechanism of this finding. Cite this article: Bone Jt Open 2021;2(11):1004-1016.
Collapse
Affiliation(s)
- Christian M Wight
- Institute of Biomedical Engineering, University of Toronto, Toronto, Ontario, Canada
| | - Cari M Whyne
- Orthopaedic Biomechanics Laboratory, Sunnybrook Research Institute, Toronto, Ontario, Canada
| | - Earl R Bogoch
- Department of Surgery, University of Toronto, Brookfield Chair in Fracture Prevention, Toronto, Ontario, Canada
| | - Radovan Zdero
- London Health Science Centre, Western University, London, Ontario, Canada
| | - Ryan M Chapman
- London Health Science Centre, Western University, London, Ontario, Canada
| | - Douglas W van Citters
- Thayer School of Engineering at Dartmouth College, Western University, Hanover, New Hampshire, USA
| | - William R Walsh
- Surgical and Orthopaedic Research Laboratory, UNSW Prince of Wales Clinical School, Randwick, New South Wales, Australia
| | - Emil Schemitsch
- Division of Orthopaedic Surgery, Department of Surgery, Schulich School of Medicine and Dentistry, University of Western Ontario, London, Ontario, Canada
| |
Collapse
|
9
|
McCarthy SM, Hall DJ, Mathew MT, Jacobs JJ, Lundberg HJ, Pourzal R. Are Damage Modes Related to Microstructure and Material Loss in Severely Damaged CoCrMo Femoral Heads? Clin Orthop Relat Res 2021; 479:2083-2096. [PMID: 34019490 PMCID: PMC8373544 DOI: 10.1097/corr.0000000000001819] [Citation(s) in RCA: 8] [Impact Index Per Article: 2.7] [Reference Citation Analysis] [Abstract] [MESH Headings] [Grants] [Track Full Text] [Journal Information] [Submit a Manuscript] [Subscribe] [Scholar Register] [Received: 09/15/2020] [Accepted: 04/19/2021] [Indexed: 01/31/2023]
Abstract
BACKGROUND Fretting and corrosion in metal-on-polyethylene total hip arthoplasty (THA) modular junctions can cause adverse tissue reactions that are responsible for 2% to 5% of revision surgeries. Damage within cobalt-chromium-molybdenum (CoCrMo) alloy femoral heads can progress chemically and mechanically, leading to damage modes such as column damage, imprinting, and uniform fretting damage. At present, it is unclear which of these damage modes are most detrimental and how they may be linked to implant alloy metallurgy. The alloy microstructure exhibits microstructural features such as grain boundaries, hard phases, and segregation bands, which may enable different damage modes, higher material loss, and the potential risk of adverse local tissue reactions. QUESTIONS/PURPOSES In this study, we asked: (1) How prevalent is chemically dominated column damage compared with mechanically dominated damage modes in severely damaged metal-on-polyethylene THA femoral heads made from wrought CoCrMo alloy? (2) Is material loss greater in femoral heads that underwent column damage? (3) Do material loss and the presence of column damage depend on alloy microstructure as characterized by grain size, hard phase content, and/or banding? METHODS Surgically retrieved wrought CoCrMo modular femoral heads removed between June 2004 and June 2019 were scored using a modified version of the Goldberg visually based scoring system. Of the total 1002 heads retrieved over this period, 19% (190 of 1002) were identified as severely damaged, exhibiting large areas of fretting scars, black debris, pits, and/or etch marks. Of these, 43% (81 of 190) were excluded for metal-on-metal articulations, alternate designs (such as bipolar, dual-mobility, hemiarthroplasty, metal adaptor sleeves), or previous sectioning of the implant for past studies. One sample was excluded retroactively as metallurgical analysis revealed that it was made of cast alloy, yielding a total of 108 for further analysis. Information on patient age (57 ± 11 years) and sex (56% [61 of 108] were males), reason for removal, implant time in situ (99 ± 78 months), implant manufacturer, head size, and the CoCrMo or titanium-based stem alloy pairing were collected. Damage modes and volumetric material loss within the head tapers were identified using an optical coordinate measuring machine. Samples were categorized by damage mode groups by column damage, imprinting, a combination of column damage and imprinting, or uniform fretting. Metallurgical samples were processed to identify microstructural characteristics of grain size, hard phase content, and banding. Nonparametric Mann-Whitney U and Kruskal-Wallis statistical tests were used to examine volumetric material loss compared with damage mode and microstructural features, and linear regression was performed to correlate patient- and manufacturer-specific factors with volumetric material loss. RESULTS Chemically driven column damage was seen in 48% (52 of 108) of femoral heads, with 34% (37 of 108) exhibiting a combination of column damage and imprinting, 12% (13 of 108) of heads displaying column damage and uniform fretting, and 2% (2 of 108) exhibiting such widespread column damage that potentially underlying mechanical damage modes could not be verified. Implants with column damage showed greater material loss than those with mechanically driven damage alone, with median (range) values of 1.2 mm3 (0.2 to 11.7) versus 0.6 mm3 (0 to 20.7; p = 0.03). Median (range) volume loss across all femoral heads was 0.9 mm3 (0 to 20.7). Time in situ, contact area, patient age, sex, head size, manufacturer, and stem alloy type were not associated with volumetric material loss. Banding of the alloy microstructure, with a median (range) material loss of 1.1 mm3 (0 to 20.7), was associated with five times higher material loss compared with those with a homogeneous microstructure, which had a volume loss of 0.2 mm3 (0 to 4.1; p = 0.02). Hard phase content and grain size showed no correlation with material loss. CONCLUSION Chemically dominated column damage was a clear indicator of greater volume loss in this study sample of 108 severely damaged heads. Volumetric material loss strongly depended on banding (microstructural segregations) within the alloy. Banding of the wrought CoCrMo microstructure should be avoided during the manufacturing process to reduce volumetric material loss and the release of corrosion products to the periprosthetic tissue. CLINICAL RELEVANCE Approximately 30% of THAs rely on wrought CoCrMo femoral heads. Most femoral heads in this study exhibited a banded microstructure that was associated with larger material loss and the occurrence of chemically dominated column damage. This study suggests that elimination of banding from the alloy could substantially reduce the release of implant debris in vivo, which could potentially also reduce the risk of adverse local tissue reactions to implant debris.
Collapse
Affiliation(s)
| | - Deborah J. Hall
- Department of Orthopedic Surgery, Rush University Medical Center, Chicago, IL, USA
| | | | - Joshua J. Jacobs
- Department of Orthopedic Surgery, Rush University Medical Center, Chicago, IL, USA
| | - Hannah J. Lundberg
- Department of Orthopedic Surgery, Rush University Medical Center, Chicago, IL, USA
| | - Robin Pourzal
- Department of Orthopedic Surgery, Rush University Medical Center, Chicago, IL, USA
| |
Collapse
|
10
|
Stockhausen KE, Riedel C, Belinski AV, Rothe D, Gehrke T, Klebig F, Gebauer M, Amling M, Citak M, Busse B. Variability in stem taper surface topography affects the degree of corrosion and fretting in total hip arthroplasty. Sci Rep 2021; 11:9348. [PMID: 33931680 PMCID: PMC8087796 DOI: 10.1038/s41598-021-88234-3] [Citation(s) in RCA: 4] [Impact Index Per Article: 1.3] [Reference Citation Analysis] [Abstract] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 06/26/2020] [Accepted: 03/19/2021] [Indexed: 12/29/2022] Open
Abstract
Degradation at the modular head-neck interface in total hip arthroplasty (THA) is predominately expressed in the form of corrosion and fretting, potentially causing peri-prosthetic failure by adverse reactions to metal debris. This retrieval study aimed to quantify variations in stem taper surface topographies and to assess the influence on the formation of corrosion and/or fretting in titanium alloy stem tapers combined with metal and ceramic heads. Four hip stem designs (Alloclassic, CLS, Bicontact and SL-Plus) were characterized using high-resolution 3D microscopy, and corrosion and fretting were rated using the Goldberg scoring scheme. Quantification of the taper surface topographies revealed a high variability in surface characteristics between threaded stem tapers: Alloclassic and CLS tapers feature deeply threaded trapezoid-shaped profiles with thread heights over 65 µm. The sawtooth-shaped Bicontact and triangular SL-Plus taper are characterized by low thread heights below 14 µm. Significantly lower corrosion and fretting scores were observed in lightly threaded compared to deeply threaded tapers in ceramic head combinations. No significant differences in corrosion or fretting scores with thread height were found in pairings with metal heads. Understanding the relationship between stem taper surface topography and the formation of corrosion and fretting could help to improve the performance of modern THAs and lead to longer-lasting clinical results.
Collapse
Affiliation(s)
- Kilian Elia Stockhausen
- Department of Osteology and Biomechanics, University Medical Center Hamburg-Eppendorf, Lottestr. 55a, 22529, Hamburg, Germany
| | - Christoph Riedel
- Department of Osteology and Biomechanics, University Medical Center Hamburg-Eppendorf, Lottestr. 55a, 22529, Hamburg, Germany
| | - Alex Victoria Belinski
- Department of Osteology and Biomechanics, University Medical Center Hamburg-Eppendorf, Lottestr. 55a, 22529, Hamburg, Germany.,Department of Mechanical Engineering, University of California, 6141 Etcheverry Hall, Berkeley, CA, USA
| | - Dorothea Rothe
- Department of Orthopedic Surgery, Helios ENDO-Klinik, Holstenstraße 2, 22767, Hamburg, Germany
| | - Thorsten Gehrke
- Department of Orthopedic Surgery, Helios ENDO-Klinik, Holstenstraße 2, 22767, Hamburg, Germany
| | - Felix Klebig
- Department of Orthopedic Surgery, Helios ENDO-Klinik, Holstenstraße 2, 22767, Hamburg, Germany
| | - Matthias Gebauer
- Department of Orthopedic Surgery, Helios ENDO-Klinik, Holstenstraße 2, 22767, Hamburg, Germany
| | - Michael Amling
- Department of Osteology and Biomechanics, University Medical Center Hamburg-Eppendorf, Lottestr. 55a, 22529, Hamburg, Germany
| | - Mustafa Citak
- Department of Orthopedic Surgery, Helios ENDO-Klinik, Holstenstraße 2, 22767, Hamburg, Germany
| | - Björn Busse
- Department of Osteology and Biomechanics, University Medical Center Hamburg-Eppendorf, Lottestr. 55a, 22529, Hamburg, Germany. .,Interdisciplinary Competence Center for Interface Research (ICCIR), Martinistr. 52, 20251, Hamburg, Germany. .,Forum Medical Technology Health Hamburg (FMTHH), Butenfeld 34, 22529, Hamburg, Germany.
| |
Collapse
|
11
|
Corrosion Concerns? Trends in Metal-on-Polyethylene Total Hip Arthroplasty Revision Rates and Comparisons Against Ceramic-on-Polyethylene up to 10 Years of Follow-Up. J Arthroplasty 2020; 35:2919-2925. [PMID: 32475785 DOI: 10.1016/j.arth.2020.05.007] [Citation(s) in RCA: 2] [Impact Index Per Article: 0.5] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Submit a Manuscript] [Subscribe] [Scholar Register] [Received: 01/11/2020] [Revised: 04/10/2020] [Accepted: 05/02/2020] [Indexed: 02/02/2023] Open
Abstract
BACKGROUND We compared the revision risk between metal-on-polyethylene (MOP) and ceramic-on-polyethylene (COP) total hip arthroplasty patients and evaluated temporal changes in short-term revision risks for MOP patients. METHODS Primary MOP (n = 9480) and COP (n = 3620) total hip arthroplasties were evaluated from the Medicare data set (October 2005 to December 2015) for revision risk, with up to 10 years of follow-up using multivariate analysis. Temporal change in the short-term revision risk for MOP was evaluated (log-rank and Wilcoxon tests). RESULTS Revision incidence was 3.8% for COP and 4.3% for MOP. MOP short-term revision risk did not change over time (P ≥ .844 at 1 year and .627 at 2 years). Dislocation was the most common reason for revision (MOP: 23.5%; COP: 24.8%). Overall adjusted revision risks were not different between MOP and COP up to 10 years of follow-up (P ≥ .181). CONCLUSIONS Concerns with corrosion for metal heads do not appear to result in significantly elevated revision risk for MOP at up to 10 years. Corrosion does not appear as a primary reason for revision compared to other mechanisms.
Collapse
|
12
|
Khullar P, Zhu D, Gilbert JL. Fretting corrosion of Si 3 N 4 vs CoCrMo femoral heads on Ti-6Al-V trunnions. J Orthop Res 2020; 38:1617-1626. [PMID: 32249959 DOI: 10.1002/jor.24681] [Citation(s) in RCA: 5] [Impact Index Per Article: 1.3] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Submit a Manuscript] [Subscribe] [Scholar Register] [Received: 11/18/2019] [Revised: 02/07/2020] [Accepted: 03/25/2020] [Indexed: 02/04/2023]
Abstract
Fretting corrosion at the head-neck taper junction was compared between silicon nitride (Si3 N4 ) and commercially available cobalt chrome (CoCrMo) femoral heads on titanium (Ti-6Al-4V) trunnions. An electrochemical setup was used to capture the fretting currents (characterized by oxide abrasion and repassivation) during cyclic loading. Onset load, pull-off force (disassembly load), short term and long term (1 million cycles) fretting currents were used to compare the fretting corrosion performance between the test group (Si3 N4 /Ti-6Al-4V) and the control group (CoCrMo/Ti-6Al-4V). Incremental cyclic fretting corrosion tests showed that the Si3 N4 /Ti-6Al-4V combination had statistically lower (P < .05) average fretting current of 0.189 µA (SD = 0.114 µA) compared to 0.685 µA (SD = 0.630 µA) for CoCrMo/Ti-6Al-4V for cyclic load of 3200 N. Similarly, for the one million cycle fretting corrosion tests, the Si3 N4 /Ti-6Al-4V couples had statistically lower (P < .05) average current (0.048 µA, SD = 0.025 µA) vs CoCrMo/Ti-6Al-4V couples (0.366 µA, SD = 0.143 µA). The Si3 N4 heads also had higher onset loads (P < .05) for fretting (vs CoCrMo, 2200 N vs 1740 N) indicating a difference in surface contact mechanics between the two groups. Scanning electron microscopy with energy dispersive spectroscopy confirmed material transfer from the trunnions to the heads for both groups tested, and from head to trunnion for the CoCrMo heads. Minimal Si3 N4 transfer was noted. The electrochemical, mechanical, and microscopic inspection data supported the hypothesis that Si3 N4 /Ti-6Al-4Vcombination had better fretting corrosion performance compared to CoCrMo/Ti-6Al-4V.
Collapse
Affiliation(s)
- Piyush Khullar
- Clemson-MUSC Bioengineering Program, Charleston, South Carolina.,Department of Bioengineering, Clemson University, Clemson, South Carolina
| | - Dongkai Zhu
- Clemson-MUSC Bioengineering Program, Charleston, South Carolina.,Department of Bioengineering, Clemson University, Clemson, South Carolina
| | - Jeremy L Gilbert
- Clemson-MUSC Bioengineering Program, Charleston, South Carolina.,Department of Bioengineering, Clemson University, Clemson, South Carolina.,Orthopaedics and Physical Medicine, Medical University of South Carolina, Charleston, South Carolina
| |
Collapse
|
13
|
Rieker CB, Wahl P. What the Surgeon Can Do to Reduce the Risk of Trunnionosis in Hip Arthroplasty: Recommendations from the Literature. MATERIALS 2020; 13:ma13081950. [PMID: 32326259 PMCID: PMC7215371 DOI: 10.3390/ma13081950] [Citation(s) in RCA: 8] [Impact Index Per Article: 2.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 02/29/2020] [Revised: 04/15/2020] [Accepted: 04/17/2020] [Indexed: 01/24/2023]
Abstract
Trunnionosis, defined as wear and corrosion at the head–neck taper connection, is a cause of failure in hip arthroplasty. Trunnionosis is linked to a synergistic combination of factors related to the prosthesis, the patient, and the surgeon. This review presents analytical models that allow for the quantification of the impact of these factors, with the aim of providing practical recommendations to help surgeons minimize the occurrence of this failure mode. A tighter fit reduces micromotion and, consequently, fretting of the taper connection. The paramount parameters controlling the fixation force are the coefficient of friction and the impaction force. The influence of the head diameter, as well as of the diameter and angle of the taper, is comparatively small, but varus alignment of the taper and heads with longer necks are unfavourable under physiologic loads. The trunnion should be rinsed, cleaned, and dried carefully, while avoiding any contamination of the bore—the female counterpart within the head—prior to assembly. Biological debris, and even residual water, might critically reduce the fixation of the taper connection between the head and the neck. The impaction force applied to the components should correspond to at least two strong blows with a 500 g hammer, striking the head with an ad hoc impactor aligned with the axis of the taper. These strong blows should correspond to a minimum impaction force of 4000 N.
Collapse
Affiliation(s)
- Claude B. Rieker
- Scientific Affairs, Zimmer Biomet EMEA (Europa, Middle East and Africa), Sulzerallee 8, 8404 Winterthur, Switzerland
- Correspondence:
| | - Peter Wahl
- Division of Orthopaedics and Traumatology, Cantonal Hospital Winterthur, Brauerstrasse 15, 8400 Winterthur, Switzerland;
| |
Collapse
|
14
|
Taper Design, Head Material, and Manufacturer Affect the Onset of Fretting Under Simulated Corrosion Conditions. J Arthroplasty 2020; 35:1117-1122. [PMID: 31836326 DOI: 10.1016/j.arth.2019.11.005] [Citation(s) in RCA: 1] [Impact Index Per Article: 0.3] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Submit a Manuscript] [Subscribe] [Scholar Register] [Received: 08/16/2019] [Revised: 10/30/2019] [Accepted: 11/05/2019] [Indexed: 02/01/2023] Open
Abstract
BACKGROUND We investigated the effect of taper design, head material, and manufacturer on simulated mechanically assisted crevice corrosion (MACC). METHODS Six pristine C-taper stems coupled with alumina-zirconia or cobalt-chromium (CoCr) heads were tested in a mechanical/electrochemical setup to measure average fretting currents and fretting current onset loads. Outcomes were compared with previous data from V40 tapers from the same manufacturer and 12/14 tapers from another manufacturer. RESULTS Within a single manufacturer, differences in average fretting current between V40 and C-taper designs were dependent on head material. Only with V40 tapers did CoCr heads show higher average fretting currents than ceramic heads. Between manufacturers, differences were found between similar taper designs, as 12/14 taper couples showed higher average fretting currents than C-taper couples, regardless of head material. CONCLUSION Taper design, head material, and factors inherent to different manufacturers influence fretting current in simulated MACC. Unlike clinical and retrieval studies, this experimental design allows for investigations of factors affecting MACC in a controlled environment. Taper design, independent of manufacturer, contributes to the observed differences in average fretting current between head materials. In some taper designs, head composition, specifically ceramic, should not be considered alone to reduce risk of corrosion.
Collapse
|
15
|
Letter to the Editor on "Cobalt and Chromium Ion Release in Metal-on-Polyethylene and Ceramic-on-Polyethylene THA: A Simulator Study With Cellular and Microbiological Correlations". J Arthroplasty 2020; 35:1166-1167. [PMID: 31918986 DOI: 10.1016/j.arth.2019.12.029] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Track Full Text] [Journal Information] [Submit a Manuscript] [Subscribe] [Scholar Register] [Received: 12/01/2019] [Accepted: 12/13/2019] [Indexed: 02/01/2023] Open
|
16
|
Falkenberg A, Biller S, Morlock MM, Huber G. Micromotion at the head-stem taper junction of total hip prostheses is influenced by prosthesis design-, patient- and surgeon-related factors. J Biomech 2020; 98:109424. [DOI: 10.1016/j.jbiomech.2019.109424] [Citation(s) in RCA: 11] [Impact Index Per Article: 2.8] [Reference Citation Analysis] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 07/19/2019] [Revised: 09/25/2019] [Accepted: 10/13/2019] [Indexed: 12/28/2022]
|
17
|
Crackau M, Märtens N, Harnisch K, Berth A, Döring J, Lohmann CH, Halle T, Bertrand J. In vivo corrosion and damages in modular shoulder prostheses. J Biomed Mater Res B Appl Biomater 2019; 108:1764-1778. [PMID: 31763747 DOI: 10.1002/jbm.b.34519] [Citation(s) in RCA: 6] [Impact Index Per Article: 1.2] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 06/17/2019] [Revised: 09/30/2019] [Accepted: 11/04/2019] [Indexed: 11/08/2022]
Abstract
Wear and corrosion at taper junctions of orthopaedic endoprostheses remain of great concern and are associated with adverse clinical reactions. Whereas tribocorrosion of hip tapers was extensively investigated, there is only little knowledge regarding the clinical performance of modular total shoulder prostheses. This retrieval study evaluated 35 modular taper junctions of anatomical shoulder explants using stereomicroscopy, confocal microscopy, as well as optical and scanning electron microscopy to determine the damage modes as well as the effects of taper topography and alloy microstructure. Among all humeral head tapers, 89% exhibited material degradation. Different overlapping wear mechanisms were identified such as plastic deformation, adhesive material transfer, microploughing, and fretting damage. Only CoCrMo cast alloy heads showed a susceptibility to electrochemically dominated fretting in comparison to CoCrMo wrought alloy. Moreover, corundum blasted stem tapers show a significantly increased incidence rate for microploughing. To date, this is the most comprehensive study on the damage types of modular taper junctions of anatomical shoulder arthroplasty proving the existence of fretting even on less weight-bearing implants. This study revealed critical fretting factors, such as the surface finish and the alloy type that are essential for the development of countermeasures that avoid any taper corrosion.
Collapse
Affiliation(s)
- Maria Crackau
- Institute of Materials and Joining Technology, Otto-von-Guericke University, Magdeburg, Germany.,Department of Orthopaedic Surgery, Otto-von-Guericke University, Magdeburg, Germany
| | - Nicole Märtens
- Department of Orthopaedic Surgery, Otto-von-Guericke University, Magdeburg, Germany
| | - Karsten Harnisch
- Institute of Materials and Joining Technology, Otto-von-Guericke University, Magdeburg, Germany
| | - Alexander Berth
- Department of Orthopaedic Surgery, Otto-von-Guericke University, Magdeburg, Germany
| | - Joachim Döring
- Department of Orthopaedic Surgery, Otto-von-Guericke University, Magdeburg, Germany
| | - Christoph H Lohmann
- Department of Orthopaedic Surgery, Otto-von-Guericke University, Magdeburg, Germany
| | - Thorsten Halle
- Institute of Materials and Joining Technology, Otto-von-Guericke University, Magdeburg, Germany
| | - Jessica Bertrand
- Department of Orthopaedic Surgery, Otto-von-Guericke University, Magdeburg, Germany
| |
Collapse
|
18
|
Sivan S, Rahman E, Weaver JD, Di Prima M. Comparison of ASTM F2129 and ASTM F746 for Evaluating Crevice Corrosion. JOURNAL OF TESTING AND EVALUATION 2019; 47:2497-2511. [PMID: 37680964 PMCID: PMC10483512 DOI: 10.1520/jte20180585] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Subscribe] [Scholar Register] [Indexed: 09/09/2023]
Abstract
Crevice corrosion is one of the major mechanisms that drives implant failure in orthopedic devices that have modular interfaces. Despite the prevalence of crevice corrosion in modular interfaces, very little is known with regards to the susceptibility of different material combinations to participate in crevice corrosion. In this study, we compare two electrochemical methods, ASTM F2129, Standard Test Method for Conducting Cyclic Potentiodynamic Polarization Measurements to Determine the Corrosion Susceptibility of Small Implant Devices, and a modified version of ASTM F746, Standard Test Method for Pitting or Crevice Corrosion of Metallic Surgical Implant Materials, in their ability to induce crevice corrosion. Four commonly used metals, 316 stainless steel, commercially pure titanium (Ti grade 2), Ti-6Al-4V (Ti grade 5), and cobalt-chromium-molybdenum per ASTM F1537, Standard Specification for Wrought Cobalt-28Chromium-6Molybdenum Alloys for Surgical Implants (UNSR31537, UNSR31538, and UNSR31539), were used to form crevices with a rod and washer combination. As a control, the metal rod materials were tested alone in the absence of crevices using ASTM F2129 and the modified ASTM F746 method. As another control to determine if crevices formed with polymeric materials would influence crevice corrosion susceptibility, experiments were also conducted with metal rods and polytetrafluorethylene washers. Our results revealed more visible corrosion after ASTM F2129 than ASTM F746. Additionally, ASTM F746 was found to falsely identify crevice corrosion per the critical pitting potential when visual inspection found no evidence of crevice corrosion. Hence, ASTM F2129 was found to be more effective overall at evaluating crevice corrosion compared to ASTM F746.
Collapse
Affiliation(s)
- Shiril Sivan
- Division of Applied Mechanics, Office of Science and Engineering Laboratories, Center for Devices and Radiological Health, U.S Food and Drug Administration, 10903 New Hampshire Ave., Silver Spring, MD 20993, USA
| | - Elnaz Rahman
- Division of Applied Mechanics, Office of Science and Engineering Laboratories, Center for Devices and Radiological Health, U.S Food and Drug Administration, 10903 New Hampshire Ave., Silver Spring, MD 20993, USA
| | - Jason D Weaver
- Division of Applied Mechanics, Office of Science and Engineering Laboratories, Center for Devices and Radiological Health, U.S Food and Drug Administration, 10903 New Hampshire Ave., Silver Spring, MD 20993, USA
| | - Matthew Di Prima
- Division of Applied Mechanics, Office of Science and Engineering Laboratories, Center for Devices and Radiological Health, U.S Food and Drug Administration, 10903 New Hampshire Ave., Silver Spring, MD 20993, USA
| |
Collapse
|
19
|
Lombardo DJ, Siljander MP, Gehrke CK, Moore DD, Karadsheh MS, Baker EA. Fretting and Corrosion Damage of Retrieved Dual-Mobility Total Hip Arthroplasty Systems. J Arthroplasty 2019; 34:1273-1278. [PMID: 30853157 DOI: 10.1016/j.arth.2019.02.008] [Citation(s) in RCA: 21] [Impact Index Per Article: 4.2] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Submit a Manuscript] [Subscribe] [Scholar Register] [Received: 10/01/2018] [Revised: 02/02/2019] [Accepted: 02/07/2019] [Indexed: 02/01/2023] Open
Abstract
BACKGROUND Dual-mobility (DM) total hip arthroplasty (THA) systems are designed to increase stability while potentially avoiding problems associated with large femoral heads. Complications of these systems are not yet fully understood. This study aims at characterizing in vivo performance of DM hip systems and assessing modes of clinical failure. METHODS Under an institutional review board-approved implant retrieval protocol, 18 DM THA systems from 17 patients were included. Implants were graded at the head-neck junction for fretting and corrosion based on the system of Goldberg et al. Components were also macroscopically examined for different damage modes. Demographics and surgical data were collected from medical records, and radiographs were assessed for component positioning. Data were analyzed through Spearman rank-order correlation and Mann-Whitney U-tests, with α = 0.05. RESULTS The average length of implantation was 13.4 months with mild to moderate fretting corrosion damage. Polyethylene (PE) liners exhibited edge deformation, scratching, and pitting damage. Metallic components exhibited burnishing and scratching damage. Summed fretting and corrosion scores were strongly correlated (ρ = 0.967, P < .0001). Summed corrosion score was moderately correlated with presence of embedding on the PE liner (ρ = 0.690, P = .017). PE liner abrasion and edge deformation of the femoral stem taper were moderately positively correlated (ρ = 0.690, P = .017). Fretting and corrosion damage were not significantly correlated with patient demographics or radiographic positioning of implants. There were no differences in scores between modular and monoblock designs. CONCLUSION These findings demonstrate that dual-mobility THA systems may be susceptible to the same fretting and corrosion damage observed in traditional modular THA systems. Future studies are needed to confirm these results and clinical significance.
Collapse
Affiliation(s)
| | | | - Corinn K Gehrke
- Department of Orthopaedic Research, Beaumont Health, Royal Oak, MI
| | - Drew D Moore
- Department of Orthopaedic Surgery, Beaumont Health, Royal Oak, MI; Department of Orthopaedic Surgery, Oakland University-William Beaumont School of Medicine, Rochester, MI
| | - Mark S Karadsheh
- Department of Orthopaedic Surgery, Beaumont Health, Royal Oak, MI; Department of Orthopaedic Surgery, Oakland University-William Beaumont School of Medicine, Rochester, MI
| | - Erin A Baker
- Department of Orthopaedic Research, Beaumont Health, Royal Oak, MI; Department of Orthopaedic Surgery, Oakland University-William Beaumont School of Medicine, Rochester, MI
| |
Collapse
|
20
|
Head Taper Corrosion Causing Head Bottoming Out and Consecutive Gross Stem Taper Failure in Total Hip Arthroplasty. J Arthroplasty 2018; 33:3581-3590. [PMID: 30100136 DOI: 10.1016/j.arth.2018.07.017] [Citation(s) in RCA: 34] [Impact Index Per Article: 5.7] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Submit a Manuscript] [Subscribe] [Scholar Register] [Received: 05/03/2018] [Revised: 07/16/2018] [Accepted: 07/17/2018] [Indexed: 02/01/2023] Open
Abstract
BACKGROUND Taper corrosion in total hip arthroplasty for bearings with metal heads against polyethylene has developed from an anecdotal observation to a clinical problem. Increased taper wear and even gross taper failure have been reported for one particular design. It is hypothesized that corrosion of the female head taper results in taper widening, allowing the cobalt-chromium head to turn on the stem and wear down the softer titanium alloy by abrasive wear, ultimately causing failure. The purpose of this study is to investigate the time course of this process and the general role of taper dimensions and material in this problem. METHODS Retrieved cobalt-chromium alloy heads (n = 30, LFIT; Stryker, Mahwah, NJ) and Ti-12Mo-6Zr-2Fe (TMZF) stems (n = 10, Accolade I; Stryker) were available for analysis. Taper material loss was determined using three-dimensional coordinate measurements and scanning. The pristine tip clearance between head and stem was analytically determined. The influence of taper material and taper size on taper deformation and micromotion was investigated using a finite element model. RESULTS Material loss at the head taper increased with time in situ up to a volume of 20.8 mm3 (P < .001). A mean linear material loss above 76 μm at the head taper was analytically confirmed to result in bottoming out, which was observed in 12 heads. The finite element calculations showed significantly larger deformations and micromotions for a small 11/13 TMZF taper combined with a distinctly different micromotion pattern compared to other materials and taper designs. CONCLUSION A 11/13 TMZF taper design with 36-mm head diameters bears a higher risk for corrosion than larger tapers made from stiffer materials. Failures of this combination are not restricted to the head sizes included in the recall. Patients with this implant combination should be closely monitored.
Collapse
|
21
|
Rowan FE, Wach A, Wright TM, Padgett DE. The onset of fretting at the head-stem connection in hip arthroplasty is affected by head material and trunnion design under simulated corrosion conditions. J Orthop Res 2018; 36:1630-1636. [PMID: 29319895 DOI: 10.1002/jor.23813] [Citation(s) in RCA: 14] [Impact Index Per Article: 2.3] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Submit a Manuscript] [Subscribe] [Scholar Register] [Received: 08/10/2017] [Accepted: 11/11/2017] [Indexed: 02/04/2023]
Abstract
Mechanically assisted crevice corrosion (MACC) is a mechanism for trunnion damage in total hip arthroplasties (THAs). Retrieval studies have shown reduced MACC-related damage for ceramic heads compared with cobalt-chromium (CoCr) heads. We propose that ceramic heads demonstrate fretting at higher cyclic compressive loads than CoCr heads on titanium alloy trunnions in a simulated corrosion model. A closed electrochemical chamber was used to measure fretting current onset loads for two modern titanium alloy trunnions (Zimmer 12/14 and Stryker V-40) in which trunnion failure has been reported. Ceramic and CoCr alloy 36 + 0 mm heads were impacted on each trunnion and cyclically loaded at 3 Hz with increasing magnitude from 100 to 3,400 N for 540 cycles. Onset load was the cyclic compressive load at which the slope of the average fretting current increased significantly. A CoCr head with V40 trunnion demonstrated the lowest onset load (1,400 N), while the V40 trunnion with a ceramic head showed the highest onset load (2,200 N). Significant differences occurred in average fretting current between head materials for V40 trunnions (p < 0.001) at loads over 2,000 N. CoCr-12/14 and ceramic-12/14 couples demonstrated similar onset loads (2,000 N). All head-trunnion combinations showed cyclical fretting response to loading at 100 N. Head material composition was observed to increase fretting at the taper junction but the effect was taper geometry dependent. Using ceramic heads may reduce the phenomena of trunnion fretting and corrosion but the effect of both trunnion geometry and metallurgy warrants further investigation. Statement of clinical significance: Trunnion corrosion may occur with titanium alloy stems regardless of the head material used. © 2017 Orthopaedic Research Society. Published by Wiley Periodicals, Inc. J Orthop Res 36:1630-1636, 2018.
Collapse
Affiliation(s)
- Fiachra E Rowan
- Adult Reconstruction and Joint Replacement, Hospital for Special Surgery, 535 East 70th Street, New York, 10021, New York
| | - Amanda Wach
- Department of Biomechanics, Hospital for Special Surgery, New York, New York
| | - Timothy M Wright
- Department of Biomechanics, Hospital for Special Surgery, New York, New York
| | - Douglas E Padgett
- Adult Reconstruction and Joint Replacement, Hospital for Special Surgery, 535 East 70th Street, New York, 10021, New York
| |
Collapse
|
22
|
Mueller U, Braun S, Schroeder S, Sonntag R, Kretzer JP. Same Same but Different? 12/14 Stem and Head Tapers in Total Hip Arthroplasty. J Arthroplasty 2017; 32:3191-3199. [PMID: 28552447 DOI: 10.1016/j.arth.2017.04.027] [Citation(s) in RCA: 32] [Impact Index Per Article: 4.6] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Submit a Manuscript] [Subscribe] [Scholar Register] [Received: 02/24/2017] [Revised: 03/27/2017] [Accepted: 04/18/2017] [Indexed: 02/01/2023] Open
Abstract
BACKGROUND Taper corrosion has been identified to be a major concern in total hip arthroplasty during the past years. So far, the mechanisms that lead to taper corrosion in modular taper junctions are not fully understood. However, it has been shown that corrosion is also influenced by the geometry and topography of the taper, and these parameters vary among the implant manufacturers. The purpose of this study was to investigate the variations of common stem and head tapers regarding design and surface characteristics. METHODS An analysis of selected commercially available 12/14 stem and head tapers was performed. As geometric parameters, the taper angle, the opening taper diameter, and the taper length were measured using a coordinate measuring machine. Several topographic parameters were determined using a tactile roughness measurement instrument. RESULTS Although all investigated tapers are so-called 12/14 tapers, this study showed that the stem and head tapers differ among the manufacturers. The stem tapers were clearly different in both geometry and topography, and the range in variation of the topographic parameter was greater than it was for the geometric parameter. In contrast, the head tapers were different in their geometry, although not in topography. CONCLUSION Ultimately, this study provides an overview on the characteristics and variations of modular hip taper connections, and in addition, a new classification system regarding the surface finish is presented. These findings could be further considered in experimental corrosion or retrieval studies.
Collapse
Affiliation(s)
- Ulrike Mueller
- Laboratory of Biomechanics and Implant Research, Clinic for Orthopedics and Trauma Surgery, Heidelberg University Hospital, Heidelberg, Germany
| | - Steffen Braun
- Laboratory of Biomechanics and Implant Research, Clinic for Orthopedics and Trauma Surgery, Heidelberg University Hospital, Heidelberg, Germany
| | - Stefan Schroeder
- Laboratory of Biomechanics and Implant Research, Clinic for Orthopedics and Trauma Surgery, Heidelberg University Hospital, Heidelberg, Germany
| | - Robert Sonntag
- Laboratory of Biomechanics and Implant Research, Clinic for Orthopedics and Trauma Surgery, Heidelberg University Hospital, Heidelberg, Germany
| | - J Philippe Kretzer
- Laboratory of Biomechanics and Implant Research, Clinic for Orthopedics and Trauma Surgery, Heidelberg University Hospital, Heidelberg, Germany
| |
Collapse
|
23
|
Affiliation(s)
- Mitchell C Weiser
- 1Department of Orthopaedic Surgery, New York University Langone Medical Center, Hospital for Joint Diseases, and Insall Scott Kelly Institute for Orthopaedics and Sports Medicine, New York, NY 2Department of Orthopedics & Rehabilitation, University of Miami, Coral Gables, Florida 3Department of Mechanical and Materials Engineering and Department of Physical Therapy, Florida International University, Coral Gables, Florida
| | | |
Collapse
|