In vitro effect of nanoleakage expression on resin-dentin bond strengths analyzed by microtensile bond test, SEM/EDX and TEM

The Effect of an Extra Hydrophobic Resin Layer on the Bond Strength and Durability of One-Step Universal Adhesives Used as a Primer

OBJECTIVES

To determine the effect of an extra hydrophobic resin layer (EHL) on the bond strength and durability of three different pH one-step universal adhesives (UAs) utilized in self-etch (SE) mode, and to explore whether UAs can be used as a primer in two-step bonding system.

METHODS

Three different pH UAs were utilized: G-Premio Bond (GPB), Scotchbond Universal (SBU), All-Bond Universal (ABU), while the bonding agent of Clearfil SE Bond 2 (SE2) was selected as the EHL. For the EHL groups, EHL was applied after the air blow of each UA and before light curing. The microtensile bond strength (μTBS), fracture modes, interfacial structures and nanoleakage (NL) were evaluated after 24 h water storage and after 15,000 thermal cycling (TC). Elastic modulus (EM) and hardness (H) was tested by a nanoindenter after 24 h.

RESULTS

Significantly higher μTBS was achieved in the GPB+EHL group compared with GPB both at 24 h and after 15,000 TC, while the additional use of EHL did not improve the μTBS of SBU and ABU significantly both at 24 h and after 15,000 TC. GPB+EHL demonstrated lower NL than GPB. The mean EM and H of the adhesive layer in GPB+EHL was significantly decreased compared with GPB.

CONCLUSIONS

The results indicated that the bond strength and durability of low pH one-step UA (GPB) were significantly improved by additional application of EHL both at 24 h and after 15,000 TC, while no significant improvement was observed for ultra-mild one-step UAs (SBU and ABU).

CLINICAL SIGNIFICANCE

This study indicates that GPB can be used as a primer in a two-step bonding system, while SBU and ABU may not be as effective. These findings may help guide clinicians in selecting the appropriate UAs and bonding techniques for different clinical scenarios.

Effect of Different Application Modalities on the Bonding Performance of Adhesive Systems to Dentin: A Systematic Review and Meta-Analysis

Diverse types of dental adhesives exhibit different cytotoxic outcomes on cells in vitro. Currently, no standard adhesive application technique has so far been decisive for clinicians for better durability of resin-dentin bonds of adhesive systems. The purpose of this study was to systematically review the literature to evaluate the bonding performance of adhesive systems to dentin by using different application modalities. The systematic research strategy was conducted by two reviewers among multiple databases: PubMed, Scopus, Web of Science, Embase, and Scielo. In vitro studies reporting the effects of additional steps for the application of adhesive systems on the bond strength to dentin were selected. Meta-analysis was performed using Review Manager Software version 5.3.5 using the random effects model. The methodological quality of each in vitro study was assessed according to the parameters of a previous systematic review. The electronic research through different databases generated a total of 8318 references. After the examination of titles and abstracts, a total of 106 potentially relevant studies accessed the full-text evaluation phase. After full-text examination, 78 publications were included for the qualitative analysis, and 68 studies were included in the meta-analysis. Regarding the etch-and-rinse adhesive systems, the application modalities that improved the overall bond strength were the application of a hydrophobic resin layer (p = 0.005), an extended application time (p < 0.001), an application assisted by an electric current (p < 0.001), a double-layer application (p = 0.05), the agitation technique (p = 0.02), and the active application of the adhesive (p < 0.001). For self-etch adhesive systems, the techniques that improved the overall bond strength were the application of a hydrophobic resin layer (p < 0.001), an extended application time (p = 0.001), an application assisted by an electric current (p < 0.001), a double-layer application (p < 0.001), the agitation technique (p = 0.01), and the active application of the adhesive (p < 0.001). The in vitro evidence suggests that the application of adhesive systems using alternative techniques or additional strategies may be beneficial for improving their bond strength to dentin. The application modalities that favored the overall bond strength to dentin were an extended application time, a double-layer application, an application assisted by an electric current, the active application of the adhesive, and the application of a hydrophobic resin layer. Worth mentioning is that some techniques are intended to increase the degree of the conversion of the materials, and therefore, improvements in the biocompatibility of the materials can be expected.

Effect of phytic acid on bond strength and interfacial integrity of universal adhesive to deep dentin

Abstract This study investigated the effect of phytic acid (IP6) in different concentrations and application times on microtensile bond strength (µTBS) and interfacial integrity of universal adhesive to deep dentin. Flat deep dentin surfaces of 48 human molars were either etched with 37% phosphoric acid (PA) for 15 sec (control); or received no acid treatment and universal adhesive was applied directly in a self-etch mode (SE); or divided according to IP6 concentration (C) into two main groups: C1, 0.5%, and C2, 1%. Specimens of IP6 groups were further subdivided into three subgroups according to application time of IP6 (T) where; T1, 15 sec; T2, 30 sec and T3, 60 sec. Single Bond Universal Adhesive was then applied and resin composite blocks were built-up. Forty Specimens were then sectioned to produce resin/dentin beams that were used for µTBS testing using a universal testing machine. The remaining eight specimens were sectioned into slabs that were immersed into ammonical silver nitrate solution and nanoleakage was observed using a field emission scanning electron microscope (FE-SEM). The results showed that the application of IP6 in 0.5% and 1% produced significantly higher µTBS and less nanoleakage compared to PA and SE groups. Also, the application of IP6 for 60 sec recorded the highest µTBS and the lowest nanoleakage followed by 30 sec, and 15 sec respectively. Therefore, conditioning of deep dentin with IP6 enhances µTBS and interfacial integrity of universal adhesive to deep dentin in comparison to PA etching or using the universal adhesive in SE mode.

Comparative Sample Preparation Using Focused Ion Beam and Ultramicrotomy of Human Dental Enamel and Dentine for Multimicroscopic Imaging at Micro- and Nanoscale

(1) Background: The aim of this study was to systematically compare TEM sections of mineralized human enamel and dentine prepared by focused ion beam (in situ lift-out) technique and ultramicrotomy through a combination of microscopic examination methods (scanning electron microscopy and transmission electron microscopy). In contrast with published studies, we compared the TEM preparation methods using the same specimen blocks as those for the ultramicrotomy and FIB technique. (2) Methods: A further evaluation of TEM sample preparation was obtained by confocal laser scanning microscopy and atomic force microscopy. In addition, ultramicrotome- and focused ion beam-induced artefacts are illustrated. (3) Results: The FIB technique exposed a major difference between non-decalcified enamel and dentine concerning the ultrastructural morphology compared to ultramicrotome-prepared sections. We found that ultramicrotomy was useful for cutting mineralized dentine, with the possibility of mechanical artefacts, but offers limited options for the preparation of mineralized enamel. FIB preparation produced high-quality TEM sections, showing the anisotropic ultrastructural morphology in detail, with minor structural artefacts. Our results show that the solution of artificial saliva and glutardialdehyde (2.5% by volume) is a very suitable fixative for human mineralized tissue. (4) Conclusions: The protocol that we developed has strong potential for the preparation of mineralized biomaterials for TEM imaging and analysis.

Application Modes Affect Two Universal Adhesive Systems' Nanoleakage Expression and Shear Bond Strength

Objectives

The aim of this study was to evaluate the shear bond strength and the nanoleakage expression of CLEARFIL Universal Bond Quick and Tetric N-Bond adhesive systems bonded to dentin.

Materials and Methods

100 freshly extracted human premolar teeth were utilized. The teeth were sectioned to expose dentin. All dentin specimens were assigned into 4 experimental groups; 2 groups had Universal Bond Quick (Universal_self group) and Tetric N-Bond (Tetric_self group) applied in the self-etch mode, while 2 groups had Universal Bond Quick (Universal_total group) and Tetric N-Bond (Tetric_total group) applied in the total-etch mode. n = 15 for shear bond strength and n = 10 for nanoleakage experiment. One-way ANOVA and Kruskal-Wallis test were utilized to analyze the shear bond strength test and the nanoleakage expression, respectively.

Results

The highest significant bond strength value was recorded by the Tetric_self specimens (p < 0.05) when compared to the remaining three groups. There were no statistically significant differences between the shear bond strength values recorded in the Tetric_total, Universal_self, and Universal_total groups (p < 0.05). Both bonding systems applied in the self-etch mode (Universal_self, Tetric_self) had no silver nitrate deposits in the hybrid layer and the hybrid layer-adhesive interface (p < 0.001); however, both bonding systems applied in the total-etch mode (Universal_total, Tetric_total) had silver nitrate deposits in the hybrid layer, the hybrid layer-adhesive interface, and the bonding layer (p < 0.001).

Conclusion

Applying the Universal Bond Quick and Tetric N-Bond in the self-etch mode exhibited better results in terms of nanoleakage expression. Universal Bond Quick showed the stability of the shear bond strength to dentin when applied using the total-etch or self-etch modes. Tetric N-Bond showed significant deterioration in bond strength when applied in the total-etch mode and exhibited the highest bond strength when applied in the self-etch mode.

Evaluation of resveratrol-doped adhesive with advanced dentin bond durability

OBJECTIVES

This paper aimed to evaluate the influence of resveratrol-doped adhesive on the durability and antibiofilm capability of dentin bonding.

METHODS

Experimental adhesives were prepared by incorporating resveratrol into a universal adhesive at concentrations of 0 (control), 0.1, 1, and 10 mg/mL. The microtensile bond strength, fracture modes, and adhesive-dentin interface nanoleakage were assessed after 24 h of water storage, 10,000 times of thermocycling or 1-month of collagenase ageing. Relevant antibiofilm capability on Streptococcus mutans (S. mutans), in situ zymography, degree of conversion, and cytotoxicity of resveratrol-doped adhesives were also determined.

RESULTS

Irrespective of thermocycled or collagenase ageing, the resveratrol-doped adhesive (1 mg/mL) maintained the bond strength and reduced the nanoleakage expression. Meanwhile, the inhibitory ability on endogenous protease activity and S. mutans biofilm formation with acceptable biocompatibility were obtained.

CONCLUSIONS

This study suggested that the resveratrol-doped adhesive achieved effective improvement on dentin bond durability and secondary caries management.

CLINICAL SIGNIFICANCE

The application of the resveratrol-doped adhesive indicates promising benefits to increase the lifetime of composite restorations.

Update on Enamel Bonding Strategies

Optimal strategies for the application of an adhesive differ between enamel and dentin because of the differences in their composition. The development of adhesive systems has mainly focused on the bonding of dentin, rather than on the enamel, by etching with phosphoric acid (PA). Dental adhesive technologies continue to rapidly advance, and various adhesive systems have been developed since the study of Buonocore in 1955. He introduced the enamel acid-etch technique. Then, the etch-and-rinse (ER) system was developed, and subsequently, the self-etch (SE) system. Universal adhesives are a new generation of one-bottle SE adhesives that can be applied with either ER mode or SE mode, or a combined system involving selective enamel etching mode. Since the combination of PA etching and the SE system differs from conventional ER systems, the enamel bonding strategy should be carefully considered. This concise review of the literature on reliable enamel bonding strategies should prove helpful to clinicians to choose an appropriate adhesive system to achieve optimal clinical outcomes.

Detection of the hybrid layer biodegradation initiation factor with a scanning electron microscope

The purpose of this study was to elucidate the origin of initiation of hybrid layer biodegradation. Ninety caries-free human third molars were divided into three surface groups: enamel, dentin, and NaOCl-treated dentin. (n = 30/group) Each group was divided into three subgroups (n = 10/group) of luting resin materials with etch-and-rinse; self-etch and self-adhesive systems. Resin composite blocks and sticks were fabricated and adhered onto dentin and enamel surfaces. The bond strength values were evaluated with micro shear test and statistical analysis were made. On the other hand, teeth were sectioned with a slow-speed saw into multiple beams. After thermocycling, samples were kept in 50% silver nitrate solution. Samples were analyzed with SEM in back-scattered mode. According to the micro-shear bond tests, higher bond strength values were observed in etch-and-rinse system. Bond strength values in self-adhesive and etch-and-rinse groups were significantly higher than self-etch groups in dentin surface and dentin surface treatment with NaOCl. Back-scattered scanning electron microscope results showed that, different degradation mechanism was observed. The present study indicates that, due to the acid etching in dentin, collagen biodegradation was observed within the hybrid layer. On the enamel surfaces, resin degradation was related with resin monomers in adhesive systems.

Bonding Effectiveness of Contemporary Materials in Luting Glass-Ceramic to Dentine: An In Vitro Study

Aim:

To evaluate the shear bond strength (SBS) of resin cements, flowable composites, and a preheated composite in luting glass-ceramic to dentin.

Materials and Methods:

In total, 108 noncaries human third molar teeth embedded in acrylic blocks, grinded from the occlusal surfaces until dentin was exposed, and divided into 9 randomized groups ( n = 12). In total, 108 ceramic samples prepared in disc shape (3mm × 3mm) from IPS e. max CAD (Ivoclar Vivadent) blocks. Four adhesive resin cements: Variolink Esthetic DC (Ivoclar Vivadent), G-CEM LinkForce (GC), Panavia V5 (Kuraray Noritake), Maxcem Elite Chroma (Kerr), and three flowable composites: G-ænial Universal Flo (GC), Herculite XRV Ultra Flow (Kerr), Vertise Flow (Kerr), and one preheated composite: Enamel Plus HRI (Micerium) luted to the prepared occlusal surfaces of the teeth with total-etch, self-etch, and self-adhesive protocols. Then samples were thermocyled (5,000 cycles, 5–55°C, dwell time 20 s). SBS test was performed in a universal testing machine (at 0.5 mm/min). Failure modes were examined under a stereomicroscope at ×25 magnification. Data were analyzed using Kruskal–Wallis and Dunn–Bonferroni tests ( α = 0.05).

Results:

There were statistically significant differences among material types ( P < .05). Highest SBS values found in G-ænial Universal Flo (15.43 ± 5.67), and the lowest values obtained in Maxcem Elite Choroma (SA) (1.25 ± 1.47). There were no significant differences between self-etch (Panavia V5, Maxcem Elite Choroma [SE]) and self-adhesive (Maxcem Elite Choroma [SA], Vertise Flow) protocols ( P > .05).

Conclusion:

Flowable composites can be alternatives to resin cements when bonded with total-etch procedures. Bond strength of self-etch and self-adhesive applications is still to be developed.

New perspective to improve dentin-adhesive interface stability by using dimethyl sulfoxide wet-bonding and epigallocatechin-3-gallate

OBJECTIVES

To determine whether dentin-adhesive interface stability would be improved by dimethyl sulfoxide (DMSO) wet-bonding and epigallocatechin-3-gallate (EGCG).

METHODS

Etched dentin surfaces from sound third molars were randomly assigned to five groups according to different pretreatments: group 1, water wet-bonding (WWB); group 2, 50% (v/v) DMSO wet-bonding (DWB); groups 3-5, 0.01, 0.1, and 1 wt% EGCG-incorporated 50% (v/v) DMSO wet-bonding (0.01%, 0.1%, and 1%EGCG/DWB). Singlebond universal adhesive was applied to the pretreated dentin surfaces, and composite buildups were constructed. Microtensile bond strength (μTBS) and interfacial nanoleakage were respectively examined after 24 h water storage or 1-month collagenase ageing. In situ zymography andStreptococcus mutans (S. mutans) biofilm formation were also investigated.

RESULTS

After collagenase ageing, μTBS of groups 4 (0.1%EGCG/DWB) and 5 (1%EGCG/DWB) did not decrease (p > 0.05) and was higher than that of the other three groups (p < 0.05). Nanoleakage expression of groups 4 and 5 was less than that of the other three groups (p < 0.05), regardless of collagenase ageing. Metalloproteinase activities within the hybrid layer in groups 4 and 5 were suppressed. Furthermore, pretreatment with 1%EGCG/DWB (group 5) efficiently inhibited S. mutans biofilm formation along the dentin-adhesive interface.

SIGNIFICANCE

This study suggested that the synergistic action of DMSO wet-bonding and EGCG can effectively improve dentin-adhesive interface stability. This strategy provides clinicians with promising benefits to achieve desirable dentin bonding performance and to prevent secondary caries, thereby extending the longevity of adhesive restorations.

Effect of the double application of universal adhesives on the dentine bond strength after radiotherapy

BACKGROUND

This study aimed to evaluate the effect of double application of universal adhesives on bond strength to dentine after ionizing radiation.

METHODS

One hundred and forty caries-free human third molars were used. Half of the teeth were irradiated (IR) (70.2 Gy). The IR and non-IR teeth were assigned into seven groups (n = 10). Universal adhesives Single Bond Universal (3M Oral Care), Gluma Bond Universal (Heraeus Kulzer) and Prime&Bond Elect (Dentsply) were employed (following manufacturer's instructions and double application). Two-step self-etch adhesive Clearfil SE Bond (Kuraray Noritake) was used as control. After composite build-ups were bonded to mid-coronal occlusal dentine surfaces, the specimens were stored in water (37°C/24 h) and sectioned into microspecimens. The specimens were subjected to μTBS testing (1.0 mm/min). Failure analysis was performed using stereomicroscope and scanning electron microscopy. Data were analysed with two-way ANOVA and Tukey's test (P = 0.05).

RESULTS

The radiotherapy caused reduction in the bond strength of universal adhesives when the adhesives were used with single application after radiotherapy (P < 0.05). The double application resulted in increased bond strength of the universal adhesives to IR dentine (P < 0.05).

CONCLUSIONS

The double application was beneficial in improving the dentine bond strength of universal adhesives affected by radiotherapy after ionizing radiation.

Combination of baicalein and ethanol-wet-bonding improves dentin bonding durability

OBJECTIVES

This study aimed to investigate the potential of baicalein combined with ethanol-wet bonding (EWB) in improving dentin bonding durability.

METHODS

Sixty caries-free human third molars were randomly allocated into four groups and pretreated with solutions after sectioning and polishing. The pretreatments were prepared via dissolving baicalein in ethanol at concentrations of 0, 0.01%, 0.05% and 0.1% (w/v). Microtensile bond strength (MTBS) test, failure mode analysis and interfacial nanoleakage evaluation were conducted immediately or after thermocycling or 1 month of collagenase aging. In situ zymography, contact angle, antibacterial activity and bioactivity were comprehensively assessed.

RESULTS

Results demonstrated that the three experimental groups exhibited higher MTBS and lower nanoleakage expression regardless of aging. MMP activity within hybrid layer and Streptococcus. mutans biofilm formation were inhibited in the experimental groups in a dose-dependent manner. Baicalein also reduced reactive oxygen species (ROS) expression in human dental pulp cells and resisted adhesive-induced cytotoxicity. Baicalein exhibited remarkable capabilities at concentrations higher than 0.05% (w/v).

CONCLUSION

Baicalein is a prospective candidate as bioactive dentin bonding agent. Combined with EWB, baicalein may form a functional bonding interface, thereby enhancing dentin bond strength and durability.

SIGNIFICANCE

Joint efforts by baicalein and EWB provides a novel therapeutic strategy for obtaining ideal adhesive-dentin interface and prolonging the longevity of restorations.

Bond strength and elemental analysis of oxidized dentin bonded to resin modified glass ionomer based restorative material

Background

This study aimed to investigate the influence of hesperidin application on the bonding of resin-modified glass ionomer-based restorative material to dentin treated with oxygen-induced endodontic irrigants.

Material and Methods

One hundred human permanent molars were categorized into five groups (n= 20/group), treated with various irrigants as follows: Group C; distilled water (control group), Group SH; 5.25% NaOCl, Group SH+H; 5.25% NaOCl + 5 % hesperidin, Group HP; 10% H2O2, Group HP+H; 10% H2O2 + 5 % hesperidin. Specimens were bonded with RMGI based restorative material. For each group, half of the specimens were evaluated for µSBS by a universal testing machine and the other half for dentin ion uptake by EDX. Additional ten specimens (n=2/per group) were prepared for the micro-morphological analysis under SEM.

Results

Hesperidin groups improved the µSBS, with a significant effect for HP+H group (p<. 05). Dentin ion uptake was significantly (p<. 05) improved in hesperidin groups.

Conclusions

In conclusion, Application of hesperidin in conjunction with RMGI based restorative material improved the dentin bond strength and ion uptake; this could be a promising approach to aid dental practitioners in their decisions, regarding which restorative material to use especially in caries susceptible patients. Key words:Hesperidin, elemental analysis, bond strength.

A Randomized Double-blind Clinical Trial of Dentin Surface Treatments for Composite Restorations in Noncarious Cervical Lesions: A 36-month Evaluation

OBJECTIVE:

This randomized, double-blind clinical trial aimed to evaluate the influence of different dentin surface treatments in noncarious cervical lesions (NCCLs).

METHODS AND MATERIALS:

Twenty-nine patients participated in this study. One hundred sixty-five NCCLs were selected and randomly assigned to three groups: G0 (control group) with phosphoric acid etching for 15 seconds; G1: phosphoric acid etching for 30 seconds; and G2: ultrasound probe applied for 30 seconds on the dentin surface. Class V composite resin restorations were performed (Z350, 3M ESPE, St Paul, MN, USA). The restorations were evaluated at baseline and at six, 12, 24, and 36 months according to the World Dental Federation criteria. Survival curves were obtained using the Kaplan-Meier method and the log-rank test. Comparisons between groups and times were performed using the McNemar and Chi-square tests (α =0.05).

RESULTS:

The presence of failures due to retention was statistically different among the groups ( p=0.012), and G0 and G2 showed better clinical performance than did G1. Sensitivity decreased over time in all groups. Marginal discoloration, postoperative sensitivity, and marginal adaptation were not different among the groups ( p>0.05).

CONCLUSIONS:

The studied dentin surface treatments showed similar clinical performance to the conventional technique at 36 months in terms of marginal discoloration, marginal adaptation, and postoperative sensitivity. In contrast, increased acid-etching time resulted in a higher risk of failure due to retention over time in composite Class V restorations.

The effect of warm air-blowing on the microtensile bond strength of one-step self-etch adhesives to root canal dentin

PURPOSE

The use of warm air-blowing to evaporate solvents of one-step self-etch adhesive systems (1-SEAs) has been reported to be a useful method. The purpose of this study was to evaluate the effect of warm air-blowing on root canal dentin.

METHODS

Four 1-SEAs (Clearfil Bond SE ONE, Unifil Core EM self-etch bond, Estelink, BeautiDualbond EX) were used. Each 1-SEA was applied to root canal dentin according to the manufacturers' instructions. After the adhesives were applied, solvent was evaporated using either normal air (23±1°C) or warm air (80±1°C) for 20s, and resin composite was placed in the post spaces. The air from the dryer, which could be used in normal- or hot-air-mode, was applied at a distance of 5cm above the root canal cavity in the direction of tooth axis. The temperature of the stream of air from the dryer in the hot-air-mode was 80±1°C, and in the normal mode, 23±1°C. After water storage of the specimens for 24h, the μTBS were evaluated at the coronal and apical regions. The μTBSs were statistically analyzed using three-way ANOVA and Student's t-test with Bonferroni correction (α=0.05).

RESULTS

The warm air-blowing significantly increased the μTBS of all 1-SEAs at the apical regions, and also significantly increased the μTBS of two adhesives (Estelink and BeautiDualBond EX) at coronal regions.

CONCLUSIONS

The μTBS of 1-SEAs to root canal dentin was improved by using warm air-blowing.

Microtensile bond strength, 4-point bending and nanoleakage of resin-dentin interfaces: Effects of two matrix metalloproteinase inhibitors

Chronic degradation of hybrid layer collagen by matrix metalloproteinases (MMPs) jeopardizes resin-dentin interfacial integrity and limits the durability of dental restorations. The 4-point bending strength (BS) is a valid but uncommon method of testing the mechanical behavior of resin-dentin interfaces. The present study aims to analyze the influence of two matrix metalloproteinase inhibitors on microtensile bond strength (µTBS), BS and nanoleakage. A total of 48M were divided into three groups according to bonding procedure. Teeth were horizontally sectioned to produce a flat dentin surface. In the control group, etch-and-rinse Prime&Bond One (Dentsply) bonding was used; in the self-etch group, methacryloyloxydodecylpyridinium bromide (MDPB)-containing Clearfil SE Protect (Kuraray) was used; and in the benzalkonium chloride (BAC)-etch group, BAC-etchant (Bisco) was used. A Ceram.X-One (Dentsply) composite was built as three successive layers and was light-cured. Samples were sectioned to produce microrods that were randomly divided into two groups for analysis at baseline and after 6 months of water immersion (n = 32), plus one slab for nanoleakage analysis (n = 8) via scanning electron microscopy (SEM) and digital image analysis (Fiji). Data were analyzed using the Weibull distribution and a mixed-model ANOVA with a post hoc Tukey test. All groups showed deterioration of the initial bonds. The self-etch group had a worse baseline µTBS than the control but had the best BS after aging. BAC-etch did not improve bond stability of etch-and-rinse adhesive. The µTBS and BS test results after aging were moderately correlated. Mixed fractures prevailed with regard to µTBS, whereas adhesive fractures dominated with regard to BS. Nanoleakage was not eliminated in any group and increased after aging. MDPB self-etch resisted bond degradation better than etch-and-rinse adhesives, even after BAC-etching. Integrating BS in studies of µTBS and nanoleakage might provide more clinically relevant outcomes for predicting the performance of dental adhesives.

Interfacial microscopic examination and chemical analysis of resin-dentin interface of self-adhering flowable resin composite

Background: The newly introduced self-adhering flowable resin-composites decrease the required time for application by incorporation of an acidic adhesive monomer, thus reducing the number of steps, but its bonding is still uncertain. The aim of this study was to evaluate the interfacial microscopic examination and chemical analysis at the resin-dentin interface of a self-adhering flowable resin composite (Vertise™Flow Self-Adhering Flowable Composite, Kerr Dental, USA) versus a total-etch (Te-Econom Plus) resin composite, using an etching agent (Eco-Etch gel) and bonding agent (Single Bond Universal). Methods: Sixteen freshly extracted sound human posterior teeth were used. The teeth were randomly divided into two groups: 8 specimens per type of composite. Standard-shaped class V cavities were prepared on the buccal surface. One group was restored by Te-Econom Plus resin composite by total-etch technique using Eco-Etch gel, which was applied to dentine for 15 seconds, followed by rinsing, drying and bonding agent application (Single Bond Universal). The other group restored directly with self-adhering resin composite (Vertise-Flow) without application of etch or bond. Curing was done for 20 seconds using a light emitting diode light curing unit. Evaluation of the resin-dentin interface was done microscopically by examination of marginal gap distance in μm using scanning electron microscope (SEM), and chemical analysis of silver particles was observed using SEM with energy-dispersive X-ray spectrometry after 24 hours of specimen storage in ammoniacal silver nitrate. Results: Regarding marginal gap distance (µm) and silver atomic % mean values, teeth restored with self-adhering resin composite (Vertise-Flow) showed significantly higher mean values than the multi-step etch and rinse resin composite group (5.2 vs 0; 12.2 vs 8.2, respectively). Conclusions: Resin-dentin bonding using total-etch resin composite technique was more effective than self-adhering flowable resin composite (Vertise-Flow) regarding marginal gap formation and penetration of silver particles. Further studies for bond strength could be performed.

Interfacial microscopic examination and chemical analysis of resin-dentin interface of self-adhering flowable resin composite

Background: The newly introduced self-adhering flowable resin-composites decrease the required time for application by incorporation of an acidic adhesive monomer, thus reducing the number of steps, but its bonding is still uncertain. The aim of this study was to evaluate the interfacial microscopic examination and chemical analysis at the resin-dentin interface of a self-adhering flowable resin composite (Vertise™Flow Self-Adhering Flowable Composite, Kerr Dental, USA) versus a total-etch (Te-Econom Plus) resin composite, using an etching agent (Eco-Etch gel) and bonding agent (Single Bond Universal). Methods: Sixteen freshly extracted sound human posterior teeth were used. The teeth were randomly divided into two groups: 8 specimens per type of composite. Standard-shaped class V cavities were prepared on the buccal surface. One group was restored by Te-Econom Plus resin composite by total-etch technique using Eco-Etch gel, which was applied to dentine for 15 seconds, followed by rinsing, drying and bonding agent application (Single Bond Universal). The other group restored directly with self-adhering resin composite (Vertise-Flow) without application of etch or bond. Curing was done for 20 seconds using a light emitting diode light curing unit. Evaluation of the resin-dentin interface was done microscopically by examination of marginal gap distance in μm using scanning electron microscope (SEM), and chemical analysis of silver particles was observed using SEM with energy-dispersive X-ray spectrometry after 24 hours of specimen storage in ammoniacal silver nitrate. Results: Regarding marginal gap distance (µm) and silver atomic % mean values, teeth restored with self-adhering resin composite (Vertise-Flow) showed significantly higher mean values than the multi-step etch and rinse resin composite group (5.2 vs 0; 12.2 vs 8.2, respectively). Conclusions: Resin-dentin bonding using total-etch resin composite technique was more effective than self-adhering flowable resin composite (Vertise-Flow) regarding marginal gap formation and penetration of silver particles. Further studies for bond strength could be performed.

Nanoleakage evaluation at adhesive-dentin interfaces by different observation methods

The purpose of this study was to evaluate the capability and characteristics of different nanoleakage observation methods, including light microscope (LM), field-emission scanning electron microscope (FESEM), transmission electron microscope (TEM), and confocal laser scanning microscope (CLSM). Dentin specimens were bonded with either an etch-and-rinse adhesive (SBMP) or a self-etch adhesive (GB), and prepared for nanoleakge evaluation according to different observation methods. LM, FESEM and CLSM results demonstrated that the SBMP group showed more interfacial nanoleakage than the GB group (p<0.05); by contrast, no significant difference was found in TEM results (p>0.05), however, TEM illustrated concrete nanoleakage forms or patterns. The results suggested that different observation methods might exhibit distinct images and a certain degree of variations in nanoleakage statistical results. Researchers should carefully design and calculate the optimum assembly in combination with qualitative and quantitative approaches to obtain objective and accurate nanoleakage evaluation.

Quercetin as a simple but versatile primer in dentin bonding

A quercetin/ethanol solution may serve as a simple but versatile primer to obtain desirable bonding stability and prevent secondary caries.

Effects of Dentin Characteristics on Interfacial Nanoleakage

Water emanating from dentinal tubules during air-drying and light-curing of adhesives leads to entrapment of droplets at the resin-dentin interface and contributes to nanoleakage. This study tested the null hypothesis that characteristics of substrate dentin and type of adhesive used for bonding would not affect the occurrence of nanoleakage. Three self-etch adhesives were used to bond to 4 types of dentin with different characteristics in 12 groups. After silver challenge, nanoleakage percentage was measured within the hybrid layer of each sample. The deep dentin cut perpendicular to tubules always showed a significantly higher nanoleakage percentage compared with that of the other 3 types of dentin. The percentages of nanoleakage within the hybrid layers were not statistically different among adhesives. However, when bonding to deep perpendicular dentin, both all-in-one adhesives revealed more distinct nanoleakage within the adhesive layer compared with that achieved with Clearfil SE Bond, a two-step self-etch adhesive. The results did not support the null hypothesis.

Tubular Occlusion Prevents Water-treeing and Through-and-Through Fluid Movement in a Single-bottle, One-step Self-etch Adhesive Model

Water entrapment occurs at resin-dentin interfaces of one-step self-etch adhesives. We hypothesized that by preventing water fluxes from dentin, any water entrapment would be attributed to incomplete removal of adhesive solvents. We tested this hypothesis by bonding to transparent carious dentin containing occluded dentinal tubules. An experimental single-bottle, one-step self-etch adhesive was applied to flat surfaces of caries-affected dentin surrounded by sound dentin, with or without pulpal pressure. Resin-dentin interfaces were examined with TEM after silver-impregnation. Although caries-affected dentin was highly porous, adhesive layers were devoid of silver deposits when tubules were occluded. Conversely, variable extents of water-treeing and water-droplets were identified from adhesive layers in bonded sound dentin. Water-treeing and water-droplet formation, being manifestations of evaporative and convective water fluxes, can be eliminated during bonding to occluded transparent carious dentin. However, the highly porous nature of this clinically relevant substrate after bonding may lead to potentially undesirable consequences.

Comparative evaluation of shear bond strength and nanoleakage of conventional and self-adhering flowable composites to primary teeth dentin

Background:

The latest advancement in adhesive dentistry is the development of self adhering flowable composite resin which incorporates the self-etch adhesion technology to eliminate the steps of etching, rinsing, priming and bonding. Few studies have addressed resin bonding to primary teeth.

Aim:

The aim of this study was to compare the shear bond strength and nanoleakage of conventional and self adhering flowable composites to primary teeth dentin.

Settings and Design:

This study was conducted in the Department of Pedodontics and Preventive Dentistry, I.T.S Dental College, Hospital and Research Centre, Greater Noida; in association with the Department of Mechanical Engineering, I.T.S Engineering College, Greater Noida; and the Advanced Instrumentation Research Facility (AIRF), Jawaharlal Nehru University, New Delhi.

Materials and Methods:

Sixty of the ninety primary teeth were evaluated for shear bond strength and thirty for nanoleakage. The samples were divided into three groups; Group I – Dyad Flow (Kerr), Group II – Fusio Liquid Dentin (Pentron Clinical Technologies) and Group III – G-aenial Universal Flo (GC). Shear bond strength was determined using a universal testing machine. Nanoleakage pattern was observed under scanning electron microscope.

Results:

The shear bond strength of conventional flowable composite was significantly greater than self adhering flowable composite (p<0.05). Nanoleakage scores of both conventional and self adhering flowable composites were comparable.

Conclusions:

Self adhering flowable composites combine properties of composites and self etch adhesives, eliminating the need for separate bond application that simplifies direct restorative procedure. The evolution of self adhering materials could open new horizons for pediatric dentistry.

Nanoleakage Evaluation of Posterior Teeth Restored with Low Shrinkable Resin Composite- An invitro Study

INTRODUCTION

The effect of nanoleakage on the integrity of resin-dentin bond has been in interest for long-term adhesion.

AIM

This study evaluated the nanoleakage in premolar teeth restored with low shrinkable resin composite.

MATERIALS AND METHODS

A total of 40 human premolars were used for nanoleakage evaluation in this study. Each group was divided into four equal groups; Group A: using silorane with its adhesive system. Group B: using silorane with G-bond. Group C: using Filtek supreme composite with G-bond. Group D: using Filtek supreme composite with AdheSE adhesive. Nanoleakage analysed using Scaning Electron Microscope (SEM) and Energy Dispersive X-Ray Spectrometery (EDX).

RESULTS

The amount of silver present in hybrid layer depend on the adhesive used; this indicated different nanoleakage expressions in different adhesive systems. Filtek Z350 composite with G-bond showed clear silver uptake in both the adhesive and hybrid layer. Low shrinkable resin composite (silorane) with its adhesive system showed less silver penetration and slight silver peak on the elemental energy spectroscopy of energy dispersive X-Ray spectrometry (EDS) as compared to other samples.

CONCLUSION

Adhesives used between different groups, influence the location and degree of nanoleakage. There is difference in nanoleakage patterns between two-step and one-step adhesives and also among the one-step adhesives themselves.

Effect of Storage Time on Bond Strength and Nanoleakage Expression of Universal Adhesives Bonded to Dentin and Etched Enamel

PURPOSE

To investigate bond strength and nanoleakage expression of universal adhesives (UA) bonded to dentin and etched enamel.

METHODS

Extracted human third molars were sectioned and ground to obtain flat surfaces of dentin (n = 36) and enamel (n = 48). Dentin and etched enamel surfaces were bonded with one of two UAs, All-Bond Universal (ABU) or Scotchbond Universal (SBU); or a two-step self-etching adhesive, Clearfil SE Bond (CSEB). A hydrophobic bonding resin, Adper Scotchbond Multi-Purpose Bond (ASMP Bond) was applied only on etched enamel. Following each bonding procedure, resin composite blocks were built up incrementally. The specimens were sectioned and subjected to microtensile bond strength (MTBS) testing after 24 hours or one year water storage, or immersed into ammoniacal silver nitrate solution after aging with 10,000 thermocycles and observed using scanning electron microscopy. The percentage distribution of silver particles at the adhesive/tooth interface was calculated using digital image-analysis software.

RESULTS

The MTBS (CSEB = SBU > ABU, for dentin; and CSEB > ABU = SBU = ASMP Bond, for etched enamel) differed significantly between the adhesives after 24 hours. After one year, MTBS values were reduced significantly within the same adhesive for both substrates (analysis of variance, Bonferroni post hoc, p<0.05), and no significant differences were found among the adhesives for etched enamel. Silver particles could be detected within the adhesive/dentin interface of all specimens tested. Kruskal-Wallis mean ranks for nanoleakage in ABU, SBU, and CSEB were 16.9, 18.5 and 11, respectively (p>0.05).

CONCLUSIONS

In the short term, MTBS values were material and dental-substrate dependent. After aging, a decrease in bonding effectiveness was observed in all materials, with nanoleakage at the adhesive/dentin interface. The bonding of the UAs was equal or inferior to that of the conventional restorative systems when applied to either substrate and after either storage period.

Nanotechnology in dentistry: prevention, diagnosis, and therapy

Nanotechnology has rapidly expanded into all areas of science; it offers significant alternative ways to solve scientific and medical questions and problems. In dentistry, nanotechnology has been exploited in the development of restorative materials with some significant success. This review discusses nanointerfaces that could compromise the longevity of dental restorations, and how nanotechnolgy has been employed to modify them for providing long-term successful restorations. It also focuses on some challenging areas in dentistry, eg, oral biofilm and cancers, and how nanotechnology overcomes these challenges. The recent advances in nanodentistry and innovations in oral health-related diagnostic, preventive, and therapeutic methods required to maintain and obtain perfect oral health, have been discussed. The recent advances in nanotechnology could hold promise in bringing a paradigm shift in dental field. Although there are numerous complex therapies being developed to treat many diseases, their clinical use requires careful consideration of the expense of synthesis and implementation.

Influence of a hydrophobic resin coating on the immediate and 6-month dentin bonding of three universal adhesives

OBJECTIVE

To test the influence of a hydrophobic resin coating (HC) on the immediate (24h) and 6-month (6m) microtensile dentin bond strengths (μTBS) and nanoleakage (NL) of three universal adhesives applied in self-etch (SE) or in etch-and-rinse (ER) mode.

METHODS

Sixty caries-free extracted third molars were assigned to 12 experimental groups resulting from the combination of the factors "adhesive system" (Scotchbond Universal Adhesive [SBU], 3M ESPE; All-Bond Universal [ABU], Bisco Inc.; and G-Bond Plus [GBP], GC Corporation); "adhesive strategy" (SE or ER); "hydrophobic resin coating" [HC] (with or without Heliobond, Ivoclar Vivadent); and "storage time" (24h or 6m). Specimens were prepared for μTBS testing - (24h) half of the beams were immediately tested under tension; and (6m) the other half was stored in distilled water (37°C) for 6m prior to testing. For each tooth, two beams were randomly selected for NL evaluation for both evaluation times. Data were analyzed for each adhesive system using three-way ANOVA and Tukey's post-hoc test (α=0.05).

RESULTS

μTBS: (24h): In SE mode, HC resulted in statistically greater mean μTBS for all adhesives. (6m): When HC was not used the mean μTBS for SBU/ER, ABU/ER, GBP/ER and SBU/SE decreased significantly. NL: (24h): SBU/ER, ABU/ER and GBP/SE resulted in a significant reduction in NL when HC was applied. (6m): No significant reduction was observed for SBU/ER or for SBU/SE regardless of the use of HC.

SIGNIFICANCE

The application of a hydrophobic resin coating improved the 24h and the 6m performances of all three adhesives systems in SE mode.

Morphological and chemical comparative analysis of the human and bovine dentin-adhesive layer

Micro energy-dispersive X-ray fluorescence spectrometry (µ-EDXRF) and scanning electron microscopy (SEM) were used to evaluate dentin treated with an etch and rinse adhesive (ER) and a self-etch adhesive (SE). Ten human molars (H) and ten bovine anterior teeth (B) were prepared (exposure of dentin and divided in the middle) and allocated into two different adhesion strategy groups per substrate (n=40). µ-EDXRF data and SEM images were obtained before and after treatment. Untreated dentin of both substrates did not differ in terms of Ca (p<0.1503), P (p<0.2986) or Ca/P ratio (p<0.1400). H-SE and B-SE specimens showed reduced P content (p<0.0001; p<0.0002), while H-ER and B-ER specimens showed reduced Ca and P content (p<0.0001; p<0.0001) when compared with untreated specimens. The Ca/P ratio was significantly higher in H-ER and B-ER specimens than in H-SE and B-SE specimens (p<0.0001; p<0.0080). Untreated dentin showed a homogeneous elemental distribution. However, after adhesive treatments, the surface of the dentin showed an irregular demineralization pattern. The resin tags and adhesive layer were shorter in bovine specimens than in human specimens due to morphological differences.

Randomized clinical trial of four adhesion strategies in posterior restorations-18-month results

PURPOSE

To evaluate the 18-month clinical performance of four adhesive strategies in posterior composite restorations placed in private practice.

MATERIALS AND METHODS

Upon approval by an institutional review board, 144 restorations were inserted in 45 subjects (average age = 32.6) to treat caries lesions or to replace existing restorations in vital molars and premolars. The adhesives OptiBond FL (three-step etch-and-rinse), OptiBond SOLO Plus (two-step etch-and-rinse), OptiBond XTR (two-step self-etch), and OptiBond All-in One (one-step self-etch) were applied as per manufacturer's (Kerr Co.) instructions followed by a nanofilled resin composite (Filtek Z350XT, 3M ESPE) under rubber dam isolation. Restorations were evaluated at baseline and at 18 months using United States Public Health Service (USPHS)-modified criteria and high-resolution digital photographs. Statistical analyses included the McNemar and the Mann-Whitney non-parametric tests (p < 0.05).

RESULTS

A total of 137 restorations were evaluated after 18 months. The number of alfa ratings did not change significantly from baseline to 18 months for any of the adhesion strategies. When the 18-month evaluation criteria were pooled by pairs of adhesives, none of the adhesives resulted in a significantly different number of alfa ratings for any of the criteria compared with the other adhesives.

CONCLUSION

Bonding strategy did not influence the clinical performance of posterior composite restorations under the clinical conditions used in this study.

CLINICAL SIGNIFICANCE

When used in ideal clinical conditions, the composition of current dentin adhesives may be more clinically relevant than their adhesion strategy.

Fracture strength and nanoleakage of weakened roots reconstructed using relined glass fiber-reinforced dowels combined with a novel prefabricated core system

PURPOSE

The aim of this study was to evaluate fracture strength and nanoleakage of endodontically treated weakened teeth after being restored with relined glass fiber-reinforced dowels and two types of cores.

MATERIALS AND METHODS

Sixty sound human decoronated and endodontically treated teeth were embedded in epoxy resin blocks, then divided into three groups (n = 20) according to the method of root reconstruction. Group 1 (control): nonweakened roots were restored with glass fiber-reinforced dowels (UNIC); group 2: weakened roots restored with glass fiber-reinforced dowels relined with composite resin; group 3: weakened roots restored with glass fiber-reinforced dowels and a thick layer of luting cement. Dowels were cemented using Corposit, a dual-cured adhesive resin cement, then each group was assigned into two subgroups (n = 10) according to the type of core used; subgroup a: custom-made core using the same luting cement, subgroup b: prefabricated glass fiber-reinforced core (UNIC). Half the specimens of each subgroup were individually mounted at 45° angles and statically compressed until fracture at a 0.5 mm/min crosshead speed with a 5 kN load cell. The type of failure was assessed using a magnification lens. The other half of the specimens were removed from the block, placed in silver nitrate solution for 24 hours followed by photo developer for 8 hours, then examined using environmental scanning electron microscope/energy dispersive analytical X-ray for nanoleakage evaluation. Data were statistically analyzed.

RESULTS

The nonweakened group recorded the highest fracture strength values. The composite relined group showed significantly higher fracture strength values than the cement group. The prefabricated core yielded higher fracture strength values than the custom-made core. All groups showed a degree of nanoleakage, with higher scores recorded for the composite group.

CONCLUSIONS

The fracture resistance of wide root canals can be improved by using glass fiber-reinforced dowels relined with composite resin as an alternative to increasing the thickness of luting cement; however, the percentage nanoleakage would increase. On the other hand, the recently introduced prefabricated glass fiber-reinforced core can be considered a promising technique, but further investigations are necessary.

Effect of the application time of phosphoric acid and self-etch adhesive systems to sclerotic dentin

Objectives:

To evaluate the effect of application time on the resin-dentin bond strength (µTBS) and etching pattern of adhesive systems applied on sclerotic dentine.

Material and Methods:

A total of forty-two bovine incisors had their roots removed. The 1-step self-etch GO (SDI), the 2-step self-etch Adper SE Bond (3MESPE) and the 35% phosphoric acid (3MESPE) from the 2-step etch-and-rinse Adper Single Bond 2 (3MESPE) were applied on the bovine incisal surfaces according to the manufacturer's instructions or duplicating the recommended conditioning time. After adhesive application, thirty teeth were restored with composite resin, stored for 24 h in distilled water at 37º C, and sectioned into resin-dentin bonded sticks (0.8 mm²⁾ and tested according to the µTBS at 0.5 mm/min. The etching pattern of the remaining twelve teeth (n=4 for each material) was examined under scanning electron microscopy. Each tooth was divided into a buccal-to-lingual direction into three thirds, and each third randomly assigned to the groups: control (no treatment), according to the manufacturers' instructions and duplicating the recommended application time. The µTBS and the relative percentage of the tubule area opening were evaluated by two-way repeated measures ANOVA and Tukey's tests (α=0.05).

Results:

The duplication of the conditioning time favored only the GO adhesive (p<0.05). Both application methods significantly increased the tubule area opening (p<0.05) compared to the controls.

Conclusions:

The efficacy of duplicating the conditioning time was only effective for the 1-step self-etch adhesive system tested.

Effect of a chlorhexidine-containing adhesive on dentin bond strength stability

PURPOSE

The present study aimed to investigate a novel adhesive system containing 0.2% chlorhexidine digluconate (CHX) for its ability to improve the stability of the adhesive interface compared with the use of 2% CHX as a therapeutic primer. Furthermore, the study aimed to confirm the inhibitory properties of these CHX concentrations (0.2% and 2.0%) on dentin matrix metalloproteinase activity by gelatin zymography.

METHODS

Superficial dentin substrate for bonding was obtained from 120 non-carious human molars. A conventional adhesive Peak LC Bond and a CHX-containing adhesive Peak Universal Bond were used either in combination with 35% phosphoric acid (etch-and-rinse approach) or with self-etching primer (self-etch approach) for evaluation of the variables CHX treatment (2.0% therapeutic primer and 0.2% adhesive), adhesive approach (etch-and-rinse and self-etch), and storage time (24 hours and six months). A bonding jig was used to fabricate composite cylinders, which were stored for either 24 hours or six months, after which shear bond strength (SBS) was evaluated using a notched-edge testing device. A three-way analysis of variance and a Student t-test with a significance level of p<0.05 were used to analyze the data. Extracts from concentrated demineralized human dentin powder were subjected to sodium dodecyl sulfate polyacrylamide gel electrophoresis and incubated in the presence of 0.2% and 2.0% CHX.

RESULTS

No significant effect of CHX treatment, adhesive approach, storage time variables, or their interactions on mean SBS was demonstrated (p<0.05). No significant difference between the control and the CHX-treated groups was detected for either adhesive technique at 24 hours or six months (p<0.05). No significant variation in mean SBS was detected after six months of storage (p<0.05). Zymographic analysis revealed bands of enzymatic activity for the group demineralized with phosphoric acid and complete inhibition of gelatinolytic activity for the groups treated with 0.2% and 2.0% CHX.

CONCLUSIONS

CHX demonstrated inhibition of dentin proteolytic activity. However, when CHX was incorporated into a commercially available adhesive or used as a therapeutic primer, no difference in bond strength was observed at baseline or after six months of storage relative to the control group without CHX.

Interfacial Nanoleakage and Bonding of Self-Adhesive Systems Cured with a Modified-Layering Technique to Dentin of Weakened Roots

Objective

The purpose of the study was to evaluate the nanoleakage and bond strength of different self adhesive systems cured with a modified-layering technique (MLT) to dentin of weakened roots.

Methods

Twenty-one maxillary incisors were decoronated and then root canals were instrumented and obturated with the cold lateral compaction technique. Weakened roots were simulated by flaring root canals until only 1 mm dentin thickness remained. Teeth were distributed into three groups. The canals were backfilled with Vertise Flow (VF group), a self-adhering system, following a modified-layering technique using two light-transmitting posts, sizes 6 and 3. DT Light Post size 2 was cemented using the same material. Remaining roots were prepared and cured in the same way as the VF group. However, in the TS/MF group, Clearfil Tri-S Bond (TS) adhesive and Clearfil Majesty Flow (MF) composite were used, while in the ED/PF group, ED primer II (ED)/Panavia F2.0 (PF) were used. After one week of storage, each root was sectioned to obtain six slices (two slices from each root third: coronal, middle and apical) of 0.9 ± 0.1 mm thickness. Interfacial nanoleakage expression was analyzed using a field emission scanning electron microscope (FEG-SEM), and the micro push-out bond strength (μPOBS) was measured at different root regions. Modes of failure were also determined using SEM. Data were statistically analyzed using two-way analysis of variance with repeated measures and Tukey post hoc test (p≤0.05).

Results

With MLT, all adhesive systems showed nanoleakage. For μPOBS, there was a statistically significant effect for adhesive systems (p&lt;0.001) but not for root region (p&lt;0.64) or for their interaction (p=0.99). Tukey post hoc test revealed that the bond strength of the VF group was significantly higher than the TS/MF and ED/PF groups for all root regions.

Conclusion

All of the tested self-adhesive systems cured using MLT had slight nanoleakage and were not sensitive to root regional differences. Self-adhering systems had higher bond strength than self-etch adhesives.

Strategies to prevent hydrolytic degradation of the hybrid layer-A review

OBJECTIVE

Endogenous dentin collagenolytic enzymes, matrix metalloproteinases (MMPs) and cysteine cathepsins, are responsible for the time-dependent hydrolysis of collagen matrix of hybrid layers. As collagen matrix integrity is essential for the preservation of long-term dentin bond strength, inhibition of endogenous dentin proteases is necessary for durable resin-bonded restorations.

METHODS

Several tentative approaches to prevent enzyme function have been proposed. Some of them have already demonstrated clinical efficacy, while others need to be researched further before clinical protocols can be proposed. This review will examine both the principles and outcomes of techniques to prevent collagen hydrolysis in dentin-resin interfaces.

RESULTS

Chlorhexidine, a general inhibitor of MMPs and cysteine cathepsins, is the most tested method. In general, these experiments have shown that enzyme inhibition is a promising approach to improve hybrid layer preservation and bond strength durability. Other enzyme inhibitors, e.g. enzyme-inhibiting monomers, may be considered promising alternatives that would allow more simple clinical application than chlorhexidine. Cross-linking collagen and/or dentin matrix-bound enzymes could render hybrid layer organic matrices resistant to degradation. Alternatively, complete removal of water from the hybrid layer with ethanol wet bonding or biomimetic remineralization should eliminate hydrolysis of both collagen and resin components.

SIGNIFICANCE

Understanding the function of the enzymes responsible for the hydrolysis of hybrid layer collagen has prompted several innovative approaches to retain hybrid layer integrity and strong dentin bonding. The ultimate goal, prevention of collagen matrix degradation with clinically applicable techniques and commercially available materials may be achievable in several ways.

Overview of Clinical Alternatives to Minimize the Degradation of the Resin-dentin Bonds

The incorporation of hydrophilic and acidic resin monomers substantially improved the initial bonding of contemporary etch-and-rinse (ER) and self-etch (SE) adhesives to intrinsically wet dental substrates, providing quite favorable immediate results, regardless of the bonding approach used. However, in the long term, the bonding effectiveness of most simplified ER and SE adhesives drop dramatically. This review examines the fundamental processes that are responsible for the aging mechanisms involved in the degradation of the resin-bonded interfaces and some possible clinical approaches that have been effective in minimizing or even preventing the degradation of the adhesive interfaces produced with simplified adhesives. The incorporation of some of the feasible approaches - described in this review - may improve the quality of the adhesive restorations performed in clinical practice, while manufacturers develop bonding materials that are less susceptible to the aging mechanisms present in the oral environment.

Bond strength of self-adhesive resin cements to dentin after antibacterial and chelating solution treatment

OBJECTIVE

The aim of this study was to evaluate the effect of tetracycline HCl, 1-hydroxyethylidene-1, 1-bisphosphonate (HEBP) and chlorhexidine digluconate (CHX) on micro push-out (µ-PO) bond strengths of two self-adhesive resin cements on dentin.

MATERIALS AND METHODS

Sixty discs of 1.25 mm thickness (middle dentin) were prepared from human molars perpendicular to the tooth axis. Two standardized occlusal cavities of 2.20 mm occlusal diameter and 1.25 mm cervical diameter were prepared in each disc. The cavities were divided into three groups in accordance with the surface treatment (50 mg/ml tetracycline HCl, 18% HEBP and 2% CHX solutions). Following the treatment of the discs for 5 min, cavities were filled with two different self-adhesive resin cements (Clearfil(™) SA Cement and RelyX(™) Unicem). After light polymerization of cements, µ-PO bond strength tests were performed. Failure modes were examined and dentin morphologic assessments were done. Statistical significance was determined by a multivariate analysis of variance (MANOVA) followed by Tukey's post-hoc test (p < 0.05). Additionally, a paired-samples T-test was used to compare the µ-PO bond strengths of self-adhesive resin cements (p < 0.05).

RESULTS

Paired-samples T-test revealed that there was no significant difference between tested self-adhesive resin cements (p = 0.612). No significant two-factor interaction was observed between Clearfil(™) SA Cement and chemical agents (p = 0.457). Similarly, tetracycline HCl and CHX did not have a significant effect on the bond strength of RelyX(™) Unicem (p > 0.05). However, HEBP significantly decreased the bond strength of RelyX(™) Unicem when compared to the control (p < 0.05). Conclusion. The tetracycline HCl and CHX solutions do not have beneficial effects on µ-PO bond strengths of self-adhesive resin cements. Additionally, the results of this study do not justify the use of self-adhesive resin cements, following HEBP treatment of dentin.

CLINICAL SIGNIFICANCE

The application of topical HEBP solution treatment to dentin could have adverse effects on the µ-PO bond strengths of RelyX(™) Unicem.

Two-year interfacial bond durability and nanoleakage of repaired silorane-based resin composite

OBJECTIVES

To investigate the effect of silane primer application, intermediate adhesive agent/repair composite, and storage period on the interfacial microtensile bond strength (μTBS) of repaired silorane-based resin composite compared with unrepaired composites and on the nanoleakage.

METHODS

Forty-eight 1-month-old substrate specimens from Filtek P90 were roughened, etched, and distributed over two groups (n=24) based on receiving silane (Clearfil Ceramic Primer) or not. Then, half of the specimens (n=12) were repaired with P90 System Adhesive/Filtek P90 and the other half with Adper Scotchbond Multipurpose adhesive/Filtek Z250 resin composite. Within each repair category, repaired specimens were stored in artificial saliva at 37°C for either 24 hours (n=6) or two years before being serially sectioned into sticks (0.6 ± 0.01 mm(2)). From each specimen, two sticks were prepared for nanoleakage determination and four sticks were used for μTBS testing. Additional unrepaired specimens from each composite (n=12) were made to determine the cohesive strength at 24 hours and two years. Mean μTBS were calculated and statistically analyzed. Modes of failure were also determined.

RESULTS

General linear model analysis revealed no significant effect for the silane priming, intermediate adhesive agent/repair composite, and storage period or for their interactions on the μTBS values of the repaired specimens. There was no significant difference between the cohesive strength of Filtek P90 and Filtek Z250; both were significantly higher than all repaired categories. At 24 hours, nanoleakage was not detected when silorane-based composite was repaired with the same material. However, after two years, all repair categories showed nanoleakage.

CONCLUSIONS

Silane application has no effect on μTBS and nanoleakage. Durability of the interfacial bond of repaired silorane-based resin composite appeared successful regardless of the chemistry of the intermediate adhesive agent/composite used for repair. However, nanoleakage was detected early when a different repair intermediate adhesive agent/composite was used.

Nanoleakage in primary teeth prepared by laser irradiation or bur

The aim of this in vitro study was to analyze hybrid layer and nanoleakage of composite resin restorations in cavities prepared by either Er,Cr:YSGG laser or bur, followed by acid etching in primary teeth. Ten extracted primary molar teeth were randomly allocated into two groups consisting of ten cavities according to surface treatment regimen: Er,Cr:YSGG laser + acid etching(group 1) and bur + acid etching(group 2). Restorations of all samples were completed. Then, teeth were sectioned and immersed to ammoniacal silver nitrate solution. After polishing, hybrid layer thicknesses were examined under scanning electron microscopy (SEM) and ion analysis was carried out with SEM/energy dispersive X-ray spectroscopy preparation in terms of nanoleakage. Hybrid layer thickness and the amount of silver ions were assessed for the acid-etched groups. The collected data were analyzed with independent sample t test and Spearman's rank correlation. In groups 1 and 2, the mean hybrid layer thicknesses were 4.25 ± 1.41 and 5.24 ± 1.07 μm and the silver ion percentages were 10.97 ± 13.81 and 22.79 ± 21.62 %, respectively. Although no significant correlation was observed between the increase of hybrid layer thickness and the amount of silver ions, more silver ions were observed in group 2 (p < 0.05). According to the results of this study, acid-etched cavities prepared with laser promoted better results when compared to the acid-etched cavities prepared with bur.

Comparison of microleakage of composite restorations using fifth and sixth generation dentin bonding agent: an in vivo study

INTRODUCTION

The success of bonded restorations depends on effective bonding between restorative materials and tooth structure, and it prevents microleakage. New dentin bonding systems have been introduced which promotes this concept. The aim of this study was to compare the amount of microleakage between 'single bond' vs 'Prompt L-Pop' during different time periods.

MATERIALS AND METHODS

In this clinical trial study, 60 nonretentive class five cavities were prepared on buccal surfaces of human premolars which were scheduled to be removed for orthodontic purposes. The cavities were restored using two different bonding agents; fifth generation (Single Bond) and sixth generation (Prompt L-Pop) and then filled with resin composite (Filtek Z-250). The samples in both groups were extracted after placing the restoration in three periods of time: Immediately, 1 week and 6 months postplacement. Specimens were sealed with two layers of nail varnish except for 1 mm around restoration and immersed in a silver nitrate solution for 24 hours. The teeth were then sectioned longitudinally and the degree of microleakage was determined by stereomicroscope based on standard usual criteria.

RESULTS

Single bond showed more leakage at dentin margin than enamel margin in all three extraction periods and differences were significant among three groups (p < 0.05). In samples which were restored with Prompt L-Pop only in groups of 6 months there were significant differences between enamel and dentin margins. At enamel margin there were no significant differences between microleakage of groups according to the passage of time (p > 0.05).

CONCLUSION

The results of this study using two different bonding systems, indicate that adhesion to enamel was more valuable than dentin and perhaps systems that include self-etching primers are less sensitive to remaining moisture on dentin and they are less affected during different time periods.