Improved bond performances of self-etch adhesives to enamel through increased MDP-Ca salt formation via phosphoric acid pre-etching

Effects of 10-MDP calcium salt on osteoblasts and fibroblasts

OBJECTIVE

10-methacryloyloxidecyl dihydrogen phosphate monomer (10-MDP) is commonly used as a bonding monomer in universal adhesives. Adhesives that contain this monomer can directly contact the surrounding periodontium due to the chemical binding of 10-MDP with hydroxyapatite in hard tissue to form calcium salts. However, the effect of these calcium salts on the periodontium in the case of subgingival fillings remains poorly understood. The objective of this study was to investigate effects of 10-MDP calcium salts on osteoblasts and fibroblasts in the periodontal tissues.

METHODS

This study investigated the effects of different concentrations of 10-MDP calcium salts on the migration, proliferation, and differentiation of osteoblasts (MC3T3-E1) and fibroblasts (L929); additionally, the effect on apoptosis and matrix metalloproteinases (MMPs) expression in these cells was evaluated. Cell proliferation assay, alkaline phosphatase (ALP) activity assay, Western blotting, and quantitative real-time polymerase chain reaction were performed to determine the effects.

RESULTS

The 10-MDP calcium salts (within a concentration of 0.5 mg/mL) showed no cytotoxicity and did not seem to influence the apoptosis, mitochondrial membrane potential, and reactive oxygen species (ROS) levels in the cells. However, they had an inhibitory effect on the secretion of MMP2 and MMP9 in the osteoblasts and fibroblasts. The ALP activity assay and Alizarin Red staining did not reveal any significant effects of the 10-MDP calcium salts on osteoblast differentiation.

SIGNIFICANCE

These results suggest that applying 10-MDP-containing adhesives to subgingival fillings may be safe and beneficial for the periodontal tissues.

Hydroxyapatite-based dental inserts: Microstructure, mechanical properties, bonding efficiency and fracture resistance of molars with occlusal restorations

This study aimed to (1) comparatively analyze properties of Sr- and Mg-substituted hydroxyapatite (HAP)-based dental inserts; (2) evaluate insert bonding to restorative materials, and (3) evaluate the effect of doped HAP inserts on fracture resistance (FR) of human molars with large occlusal restorations. By ion-doping with Sr or Mg, 3 insert types were obtained and characterized using XRD, SEM, Vickers hardness and fracture toughness. Shear bond strength (SBS) was determined between acid etched or unetched inserts and following materials: Maxcem cement (Kerr); Filtek Z250 (3M) bonded with Single Bond Universal (SBU; 3M) or Clearfil Universal (Cf; Kuraray). Modified Class I cavities were prepared in 16 intact molars and restored using insert + composite or composite only (control) (n = 8/group). FR of restored molars was determined by static load until fracture upon thermal cycling. Fracture toughness was similar between Sr/Mg-doped inserts (0.94-1.04 MPam-1/2 p = .429). Mg-doped inserts showed greater hardness (range 4.78-5.15 GPa) than Sr6 inserts (3.74 ± 0.31 GPa; p < .05). SBS for SBU and Cf adhesives (range 7.19-15.93 MPa) was higher than for Maxcem (range 3.07-5.95 MPa) (p < .05). There was no significant difference in FR between molars restored with insert-containing and control restorations (3.00 ± 0.30 kN and 3.22 ± 0.42 kN, respectively; p > .05). HAP-based inserts doped with Mg/Sr had different composition and mechanical properties. Adhesive bonding to inserts resulted in greater bond strength than cementation, which may be improved by insert acid-etching. Ion-doped HAP inserts did not affect FR of restored molars. In conclusion, HAP-based dental inserts may potentially replace dentin in large cavities, without affecting fracture resistance of restored teeth.

A randomized clinical study of the performance of self-etching adhesives containing HEMA and 10-MDP on non-carious cervical lesions: A 2-year follow-up study

OBJECTIVE

To evaluate the association of HEMA and 10-MDP in the clinical performance of self-etching adhesives in the restoration of NCCLs during 2-years.

MATERIALS AND METHODS

60 restorations were performed in 17 volunteers and randomized into three groups: G1 (n = 20) - Prime and Bond Universal (10-MDP); G2 (n = 20) - Optibond All-in-One (HEMA); and G3 (n = 20) - Clearfil SE (10-MDP and HEMA). No cavity preparation was performed. After 2 years, the restorations were evaluated using the modified USPHS criteria for retention, marginal adaptation/ staining, postoperative sensitivity and secondary caries. The results were analyzed using Fisher's exact test and Kruskal-Wallis test.

RESULTS

All groups showed 100% retention rate, except G1, who lost two restorations (p > 0.05). Regarding marginal adaptation, G1 showed greater deficiency, as only eight restorations (40%) remained intact (p < 0.05). Regarding marginal staining, G1 and G2 showed higher rate, as only 12 restorations (65%) in each one were free of staining (p < 0.05). All groups showed similar results for postoperative sensitivity and secondary caries (p > 0.05).

CONCLUSION

The association of HEMA and 10-MDP monomers in the self-etching adhesives did not influence the clinical performance of the NCCL restorations with respect to retention, postoperative sensitivity, and incidence of secondary caries. However, positively influenced the marginal adaptation and marginal staining at the 2-year follow-up.

CLINICAL SIGNIFICANCE

The association of HEMA and 10-MDP monomers in the self-etching adhesives positively influence the clinical performance of the NCCL restorations with respect to marginal adaptation and marginal staining.

Evaluation of Infiltrant Application in the Course of Root Cementum Caries with Different Methods of Surface Preparation—An In Vitro Study

The aim of this study is to evaluate the depth of penetration of an experimental preparation with the characteristics of a dental infiltrant into the decalcified root cementum tissue and observation of the root cementum tissue subjected to a single and repeated twice hydrochloric acid etching process. The study material consisted of 20 human teeth (the study group—12 demineralised teeth, the control group—8 teeth). A commercially available Icon preparation and an experimental preparation were used for the study with addition 2% of YF3 (yttrium trifluoride) added as an indicator to facilitate microscopic observation. Each tooth was divided into two zones, blue (Icon) and red (experimental preparation). The teeth were divided into two subgroups—in the first subgroup, the etching preparation was applied once, in the second subgroup twice, and at the end the teeth were infiltrated with the experimental preparation and the Icon preparation. The study of tooth longitudinal section morphology and chemical composition was performed with the use of a Hitachi S-3400N scanning electron microscope. Microscopic observations show that the applied YF3 tracer in most cases agglomerates and remains in the form of conglomerates on the surface of the root cementum. Single particles of YF3 are visible, penetrating through the cementum tissues into the root dentine structure. The degree of tissue infiltration with the resin (depth of penetration into decalcified tissues) is visible at a depth of approx. 80–120 μm. In the test group subjected to a single etching process, good penetration of both resins was noticeable, however, excessive erosion of the root surface was evident in several of the specimens—indicating that damage occurred as a result of the etching process. In the test group subjected to two etching processes, excessive erosion of the cementum is visible in each deposit.