Scalable Fabrication of Efficient NiCo2S4 Counter Electrodes for Dye-sensitized Solar Cells Using a Facile Solution Approach

Nanograss-Assembled NiCo2S4 as an Efficient Platinum-Free Counter Electrode for Dye-Sensitized Solar Cell

Dye-sensitized solar cells (DSSCs) are often viewed as the potential future of photovoltaic systems and have garnered significant attention in solar energy research. In this groundbreaking research, we introduced a novel solvothermal method to fabricate a unique "grass-like" pattern on fluorine-doped tin oxide glass (FTO), specifically designed for use as a counter electrode in dye-sensitized solar cell (DSSC) assemblies. Through rigorous structural and morphological evaluations, we ascertained the successful deposition of nickel cobalt sulfide (NCS) on the FTO surface, exhibiting the desired grass-like morphology. Electrocatalytic performance assessment of the developed NCS-1 showed results that intriguingly rivaled those of the acclaimed platinum catalyst, especially during the conversion of I3 to I- as observed through cyclic voltammetry. Remarkably, when integrated into a solar cell assembly, both NCS-1 and NCS-2 electrodes exhibited encouraging power conversion efficiencies of 6.60% and 6.29%, respectively. These results become particularly noteworthy when compared to the 7.19% efficiency of a conventional Pt-based electrode under similar testing conditions. Central to the performance of the NCS-1 and NCS-2 electrodes is their unique thin and sharp grass-like morphology. This structure, vividly showcased through scanning electron microscopy, provides a vast surface area and an abundance of catalytic sites, pivotal for the catalytic reactions involving the electrolytes in DSSCs. In summation, given their innovative synthesis approach, affordability, and remarkable electrocatalytic attributes, the newly developed NCS counter electrodes stand out as potent contenders in future dye-sensitized solar cell applications.

Ti Porous Film-Supported NiCo₂S₄ Nanotubes Counter Electrode for Quantum-Dot-Sensitized Solar Cells

In this paper, a novel Ti porous film-supported NiCo₂S₄ nanotube was fabricated by the acid etching and two-step hydrothermal method and then used as a counter electrode in a CdS/CdSe quantum-dot-sensitized solar cell. Measurements of the cyclic voltammetry, Tafel polarization curves, and electrochemical impedance spectroscopy of the symmetric cells revealed that compared with the conventional FTO (fluorine doped tin oxide)/Pt counter electrode, Ti porous film-supported NiCo₂S₄ nanotubes counter electrode exhibited greater electrocatalytic activity toward polysulfide electrolyte and lower charge-transfer resistance at the interface between electrolyte and counter electrode, which remarkably improved the fill factor, short-circuit current density, and power conversion efficiency of the quantum-dot-sensitized solar cell. Under illumination of one sun (100 mW/cm²), the quantum-dot-sensitized solar cell based on Ti porous film-supported NiCo₂S₄ nanotubes counter electrode achieved a power conversion efficiency of 3.14%, which is superior to the cell based on FTO/Pt counter electrode (1.3%).

Growth of hierarchical TiO2 flower-like microspheres/oriented nanosheet arrays on a titanium mesh for flexible dye-sensitized solar cells

A triple-layer TiO₂ (TiO₂-TL) structure was synthesized with an over-layer composed of TiO₂ flower-like microspheres (MSs), a middle layer of nanosheet arrays (NSAs) and an under-layer of compact film (CF) on a titanium (Ti) mesh substrate using a one-step hydrothermal route and used to make a series of flexible dye-sensitized solar cells (DSSCs).

Chemical synthesis of hierarchical NiCo2S4 nanosheets like nanostructure on flexible foil for a high performance supercapacitor

In this study, hierarchical interconnected nickel cobalt sulfide (NiCo₂S₄) nanosheets were effectively deposited on a flexible stainless steel foil by the chemical bath deposition method (CBD) for high-performance supercapacitor applications. The resulting NiCo₂S₄ sample was characterized by X-ray powder diffraction (XRD), field emission scanning electron microscopy (FE-SEM), high-resolution transmission electron microscopy (HR-TEM), and electrochemical measurements. XRD and X-ray photoelectron spectroscopy (XPS) results confirmed the formation of the ternary NiCo₂S₄ sample with a pure cubic phase. FE-SEM and HR-TEM revealed that the entire foil surface was fully covered with the interconnected nanosheets like surface morphology. The NiCo₂S₄ nanosheets demonstrated impressive electrochemical characteristics with a specific capacitance of 1155 F g⁻¹ at 10 mV s⁻¹ and superior cycling stability (95% capacity after 2000 cycles). These electrochemical characteristics could be attributed to the higher active area and higher conductivity of the sample. The results demonstrated that the interconnected NiCo₂S₄ nanosheets are promising as electrodes for supercapacitor and energy storage applications.