Inlaying ZIF-derived Co3S4 hollow nanocages on intertwined polypyrrole tubes conductive networks for high-performance supercapacitors

Zeolitic imidazolate framework-67-derived chalcogenides as electrode materials for supercapacitors

With the rapid development of new energy technologies, hybrid supercapacitors have received widespread attention owing to their advantages of high power density, fast charging/discharging rate and long cycle life. In this case, the selection and design of electrode materials are the key to improving the energy storage performance of supercapacitors. Herein, zeolitic imidazolate framework-67 (ZIF-67) is presented as a good candidate material for the fabrication of supercapacitor electrodes because of its controllable pore size, constant cavity size and large specific area. Moreover, pristine ZIF-67 and ZIF-67-derived porous carbon have shown exemplary performances in supercapacitors. However, they belong to the class of electric double layer capacitor materials and have a lower magnitude of energy storage compared with pseudocapacitor materials. Therefore, to improve the energy density of hybrid supercapacitors, other ZIF-67 derivatives need to be explored, especially chalcogenides. This review mainly reports the application of ZIF-67-derived transition metal chalcogenides (TMCs, C including Oxide, Sulfide, Selenide, Telluride) in supercapacitors. Moreover, the strategies for the preparation of ZIF-67-derived TMCs and their electrochemical performance in supercapacitors are further discussed. Finally, the remaining challenges and future perspectives are highlighted.

Construction of layered micro-/nano-structured MoNiCo-S cathode and broad bean shell derived carbon anode for hybrid supercapacitors

Transition metal sulfides, despite their abundance of electrochemically active sites, often demonstrate inadequate rate performance and mechanical stability. The development of a multi-dimensional hierarchical architecture has proven to be an effective approach to address the limitations associated with sulfides. In the present study, MoNiCo-S nanorods featuring hierarchical micro-/nano-structures were successfully synthesized through a straightforward methodology that involved "in situ growth-etching-vulcanization". The one-dimensional nanostructure CoMoO4 served as both the substrate and metal source for the in-situ growth of ZIF-67. Subsequently, Lewis acid was introduced to facilitate the formation of hydroxides, ultimately leading to the synthesis of sulfides via ion exchange with sulfur ions. Due to its rational design and element composition, MoNiCo-S exhibited excellent capacitance (3125.1 F/g at 1 A/g) and cycling stability (capacitance retention rate of 72.9 % over 5,000 cycles). In addition, the broad bean shell derived carbon (KBBC), prepared through a carbonization and activation process, demonstrated a specific capacitance of 295.0 F/g and a cyclic capacitance retention of 99.6 %. The assembled MoNiCo-S//KBBC asymmetric supercapacitor devices achieves a high energy density of 78.5 Wh kg-1 at a power density of 1004.3 W kg-1. After 10,000 cycles, the device exhibited a capacitance retention rate of 107.9 %, indicating excellent cycling stability. This research contributes significantly to the advancement of sulfide materials in the context of performance optimization design.

Functional metal-organic frameworks derived electrode materials for electrochemical energy storage: a review

Pristine metal-organic frameworks (MOFs) are built through self-assembly of electron rich organic linkers and electron deficient metal nodes via coordinate bond. Due to the unique properties of MOFs like highly tunable frameworks, huge specific surface areas, flexible chemical composition, flexible structures and a large volume of pores, they are being used to design the electrode materials for electrochemical energy storage devices. As per the literature, MOFs (including manganese, nickel, copper, and cobalt-based zeolitic imidazolate frameworks (ZIFs), University of Oslo (UiO) MOFs, Hong Kong University of Science and Technology (HKUST) MOFs and isoreticular MOFs (IRMOFs)) have attracted much attention in the field of supercapacitors (SCs)/batteries. According to their dimensionality such as 1D, 2D and 3D, pristine MOFs are mainly used as SC materials. Highly porous materials and their composites are capable for intercalation of metal ions (Na+/Li+). Moreover, the supramolecular features (π⋯π, C-H⋯π, hydrogen bond interactions) of redox stable MOFs provide better insight for electrochemical stability. So, this review provides an in-depth analysis of pure MOFs and MOF derived composites (MOF composites and MOF derived porous carbon) as electrode materials and also discusses their metal ion charge storage mechanism. Finally, we provide our perspectives on the current issues and future opportunities for supercapacitor materials.

Porous Structure Fibers Based on Multi-Element Heterogeneous Components for Optimized Electromagnetic Wave Absorption and Self-Anticorrosion Performance

The excellent performance of electromagnetic wave absorbers primarily depends on the coordination among components and the rational design of the structure. In this study, a series of porous fibers with carbon nanotubes uniformly distributed in the shape of pine leaves are prepared through electrospinning technique, one-pot hydrothermal synthesis, and high-temperature catalysis method. The impedance matching of the nanofibers with a porous structure is optimized by incorporating melamine into the spinning solution, as it undergoes gas decomposition during high-temperature calcination. Moreover, the electronic structure can be modulated by controlling the NH4F content in the hydrothermal synthesis process. Ultimately, the Ni/Co/CrN/CNTs-CF specimen (P3C NiCrN12) exhibited superior performance, while achieving a minimum reflection loss (RLmin) of -56.18 dB at a thickness of 2.2 mm and a maximum absorption bandwidth (EABmax) of 5.76 GHz at a thickness of 2.1 mm. This study presents an innovative approach to fabricating lightweight, thin materials with exceptional absorption properties and wide bandwidth by optimizing the three key factors influencing electromagnetic wave absorption performance.

Unveiling the scope and perspectives of MOF-derived materials for cutting-edge applications

Although synthesis and design of MOFs are crucial factors to the successful implementation of targeted applications, there is still lack of knowledge among researchers about the synthesis of MOFs and their derived composites for practical applications. For example, many researchers manipulate study results, and it has become quite difficult to quit this habit specifically among the young researchers Undoubtedly, MOFs have become an excellent class of compounds but there are many challenges associated with their improvement to attain diverse applications. It has been noted that MOF-derived materials have gained considerable interest owing to their unique chemical properties. These compounds have exhibited excellent potential in various sectors such as energy, catalysis, sensing and environmental applications. It is worth mentioning that most of the researchers rely on commercially available MOFs for use as precursor supports, but it is an unethical and wrong practice because it prevents the exploration of the hidden diversity of similar materials. The reported studies have significant gaps and flaws, they do not have enough details about the exact parameters used for the synthesis of MOFs and their derived materials. For example, many young researchers claim that MOF-based materials cannot be synthesized as per the reported instructions for large-scale implementation. In this regard, current article provides a comprehensive review of the most recent advancements in the design of MOF-derived materials. The methodologies and applications have been evaluated together with their advantages and drawbacks. Additionally, this review suggests important precautions and solutions to overcome the drawbacks associated with their preparation. Applications of MOF-derived materials in the fields of energy, catalysis, sensing and environment have been discussed. No doubt, these materials have become excellent class but there are still many challenges ahead to specify it for the targeted applications.

Binder-Free MOF-Based and MOF-Derived Nanoarrays for Flexible Electrochemical Energy Storage: Progress and Perspectives

The fast development of Internet of Things and the rapid advent of next-generation versatile wearable electronics require cost-effective and highly-efficient electroactive materials for flexible electrochemical energy storage devices. Among various electroactive materials, binder-free nanostructured arrays have attracted widespread attention. Featured with growing on a conductive and flexible substrate without using inactive and insulating binders, binder-free 3D nanoarray electrodes facilitate fast electron/ion transportation and rapid reaction kinetics with more exposed active sites, maintain structure integrity of electrodes even under bending or twisted conditions, readily release generated joule heat during charge/discharge cycles and achieve enhanced gravimetric capacity of the whole device. Binder-free metal-organic framework (MOF) nanoarrays and/or MOF-derived nanoarrays with high surface area and unique porous structure have emerged with great potential in energy storage field and been extensively exploited in recent years. In this review, common substrates used for binder-free nanoarrays are compared and discussed. Various MOF-based and MOF-derived nanoarrays, including metal oxides, sulfides, selenides, nitrides, phosphides and nitrogen-doped carbons, are surveyed and their electrochemical performance along with their applications in flexible energy storage are analyzed and overviewed. In addition, key technical issues and outlooks on future development of MOF-based and MOF-derived nanoarrays toward flexible energy storage are also offered.

A heterostructure of NiMn-LDH nanosheets assembled on ZIF-L-derived ZnCoS hollow nanosheets with a built-in electric field enables boosted electrochemical energy storage

Supercapacitors (SCs) have emerged as an efficient technology toward the utilization of renewable energy, which demands high-performance electrode materials. Transition-metal sulfides (TMSs) and layered double hydroxides (LDHs) rich in active sites and valence states are very promising electrode materials, but they still suffer from inherent defects, such as low electric conductivity, sluggish reaction kinetics and large volume change during electrochemical reactions. In this work, NiMn-LDH nanosheets are assembled on the surfaces of ZnCoS hollow nanosheet arrays derived from a zeolitic imidazolate framework-L (ZIF-L) to form a ZnCoS@NiMn-LDH heterostructure (ZCS@LDH) with a built-in electric field. The unique structure gives rise to abundant exposed active sites and improved ion diffusion. More importantly, the built-in electric field can enhance conductivity and charge transfer by modulating the electronic structures. With these merits, the optimal ZCS@LDH-6 electrode displays outstanding specific capacitance (2102.2 F g-1 at 1 A g-1) and remarkable rate performance (68.1% at 10 A g-1). The assembled asymmetric supercapacitor (ASC) using the ZCS@LDH-6 electrode shows high energy storage capacity (41.7 W h kg-1 at 850.0 W kg-1), satisfactory cycle life (92.2% capacitance retention after 10 000 cycles) and high coulombic efficiency (95.8%). This work will shed light on designing high-performance electrode materials via heterostructure and morphology engineering.

MOF-derived NiCo-LDH Nanocages on CuO Nanorod Arrays for Robust and High Energy Density Asymmetric Supercapacitors

Layered double hydroxide (LDH) is widely explored in supercapacitors on account of its high capacity, adjustable composition and easy synthesis process. Unfortunately, solitary LDH still has great limitations as an electrode material due to its shortcomings, such as poor conductivity and easy agglomeration. Herein, nanoflakes assembled NiCo-LDH hollow nanocages derived from a metal-organic framework (MOF) precursor are strung by CuO nanorods formed from etching and oxidation of copper foam (CF), forming hierarchical CuO@NiCo-LDH heterostructures. The as-synthesized CuO@NiCo-LDH/CF shows a large capacitance (5607 mF cm^-2 at 1 mA cm^-2 ), superior rate performance (88.3 % retention at 10 mA cm^-2 ) and impressive cycling durability (93.1 % capacitance is retained after 5000 cycles), which is significantly superior to control CuO/CF, CuO@ZIF-67/CF, NiCo-LDH/CF and Cu(OH)₂ @NiCo-LDH/CF electrodes. Besides, an asymmetrical supercapacitor consists of CuO@NiCo-LDH/CF and activated carbon displays a maximum energy density of 47.3 Wh kg^-1 , and its capacitance only declines by 6.8 % after 10000 cycles, demonstrating remarkable cycling durability. The advantages of highly conductive and robust CuO nanorods, MOF-derived hollow structure and the core-shell heterostructure contribute to the outstanding electrochemical performance. This synthesis strategy can be extended to design various core-shell heterostructures adopted in versatile electrochemical energy storage applications.

High-performance pseudocapacitive removal of cadmium via synergistic valence conversion in perovskite-type FeMnO3

Cadmium pollution is a serious threat for the global drink water and natural environment. Herein, a poly-pyrrole coated dual-metal perovskite-type oxide FeMnO₃ (PFMO@PPy) was developed firstly as pseudocapacitive cathode for the reversible capture and release of cadmium ions by asymmetry pseudocapacitive deionization (APCDI) technology, extending the library of CDI electrodes. Our work highlighted several points: (i) PFMO@PPy achieved a maximum Cd-removal capacity of 144.6 mg g^-1, and maintained the retention rate of 93.4% after 15-cycle CDI process for up to 150 h, far beyond other previous work. (ii) PFMO@PPy showed the superior removal ratio (~90%) under different real water environments such as tap water, lake water and the groundwater. (iii) The superior Cd(II) electrosorption and desorption behavior is ascribed to the reversible synergistic valence conversion (Fe³⁺/Fe⁰ and Mn³⁺/Mn²⁺), which is confirmed by ex-situ XPS measurement and electrochemical tests. (iv) DFT calculations confirmed the synergistic effect from Mn and Fe elements in perovskite-type bimetallic oxide FeMnO₃. This study paves a new way for promising future applications of perovskite-type oxides containing dual Faradic redox-activity for wastewater treatment and environmental remediation.

Doping-driven electronic structure and conductivity modification of nickel sulfide

The lack of electrical conductivity limits the electrochemical kinetic rate of the electrode material, resulting in the inability to reach its theoretical capacity. A facile method is adopted to improve the intrinsic conductivity of binary NiS₂/Ni₃S₄ hybrid nickel sulfide, with the doping of transition metal atoms Co, Mn and Ag. Through the introduction of heteroatoms, the electronic structure of the electrode material is modified and the electrical conductivity is significantly improved, thus enhancing its electrochemical performance. The improvement of conductivity is attributed to the formation of intermediate bands of transition metals and the redistribution of electrons, and the result is demonstrated by experimental and density functional theory (DFT) calculations. As a result, the NiS₂/Ni₃S₄ hybrid nickel sulfide after 0.5% amount of Co-doping reaches the highest specific capacitance of 2874 F g^-1 at 1 A g^-1, increasing specific capacitance of 653 F g^-1 as 29.4% of the specific capacitance of non-doped nickel sulfide. The Co doped nickel sulfide also exhibits remarkable cycling stability compared with non-doped nickel sulfide. The assembled 2% Co-doped nickel sulfide//rGO, 0.5% Mn-doped nickel sulfide//rGO and 0.5% Ag-doped nickel sulfide//rGO asymmetric supercapacitors show a specific energy density of 36.6, 36.1 and 36.0 W h kg^-1 at a power density of 800 W kg^-1. This study provides a useful insight into the fabrication of high performance pseudocapacitive materials.

Honeycomb-like biomass carbon with planted CoNi3 alloys to form hierarchical composites for high-performance supercapacitors

It is a significant challenge to combine a large pseudocapacitive material with conductive honeycomb-like carbon frameworks for long-term stable supercapacitors. Herein, hierarchical composite materials are manufactured by using biomass carbon, ZIF-67, and a mild pore former (Ni(CH₃COO)₂) to generate alloy-type CoNi₃ nanoparticles planted into conductive honeycomb-like carbon frameworks (C@ZIF-67-T). Meanwhile, the effect of carbonization temperature on the honeycomb-like pore size and the structure of composite materials is systematically investigated. As the honeycomb-like carbon skeleton structure guarantees good ionic and electronic conductivities and a large contact area, whereas the alloy nanoparticles provide a rich redox reaction for Faradaic capacitance. Therefore, the as-obtained C@ZIF-67-600 electrode presents a remarkable specific capacitance of 1044.8 F · g^-1 at 1.0 A · g^-1 and an ultra-long cycling stability with 30,000 cycles at 5.0 A · g^-1 in a three-electrode system. In addition, the assembled C@ZIF-67-600//activated carbon asymmetrical supercapacitor exhibit a high specific capacitance of 274.4F · g^-1 at 1.0 A · g^-1 and a long-term stable lifespan with a capacitance retention of 87% after 20,000 cycles at 5.0 A · g^-1. Besides, the asymmetrical supercapacitor also presents a maximum energy density of 85.13 Wh · kg^-1 at a power density of 750 W · kg^-1. Such superior electrochemical performance demonstrate that the designed electrode material provides a promising energy storage application.

MOF-derived hierarchical core-shell hollow Co3S4@NiCo2O4 nanosheet arrays for asymmetric supercapacitors

Transition metal sulfides (TMSs) have been widely explored as electrode materials for supercapacitors (SCs). Nevertheless, the application of single TMS is limited due to its lattice expansion and dissolution in...

Boosting energy storage performance of MOF-derived Co3S4 arrays via sulfur vacancy and surface engineering

Hierarchical Co3S4 hollow nanosheet arrays are prepared through a MOF-engaged strategy followed by room-temperature NaBH4 treatment, resulting in simultaneous regulation of sulfur vacancy and surface morphology. The obtained electrode exhibits...

Design of trimetallic sulfide hollow nanocages from metal-organic frameworks as electrode materials for supercapacitors

Transition metal sulfides (TMSs) are the most used electrode materials for supercapacitors (SCs). However, they still suffer from unsatisfactory electrochemical properties. Designing a hollow mixed TMS nanostructure with a well-defined chemical composition and shape is an effective strategy to tackle this issue, yet remains challenging. Herein, using a bimetallic zeolitic imidazolate framework (Zn-Co-ZIF) with various Zn/Co ratios as the template, a series of trimetallic sulfide (Ni-Zn-Co-S) hollow nanocages were successfully prepared by sequential nickel nitrate etching, co-precipitation and vulcanization. As an electrode material for a three-electrode SC in an aqueous alkaline electrolyte, the Ni-Zn-Co-S-0.25 electrode achieves an ultra-high specific capacitance of 1930.9 at 1 A g^-1 with a good rate performance (64.5% at 10 A g^-1). In order to further prove the advantage of the as-prepared Ni-Zn-Co-S-0.25 material, it was assembled into an asymmetric energy storage device using an activated carbon (AC) anode. The Ni-Zn-Co-S-0.25//AC cell exhibits an outstanding energy storage capability (32.8 W h kg^-1 at 864.8 W kg^-1) with a splendid cyclic life (retaining ∼92.2% of the initial capacitance after 10 000 cycles). The excellent electrochemical performance of Ni-Zn-Co-S-0.25 is ascribed to the merits of the trimetallic sulfide hollow nanocage i.e., good electronic conductivity, a large active surface area, fast charge transfer, rich redox reactions and the synergic effect of different metal ions.

Mechanistic Insight into the Synergetic Interaction of Ammonia Borane and Water on ZIF-67-Derived Co@Porous Carbon for Controlled Generation of Dihydrogen

Regarding dihydrogen as a clean and renewable energy source, ammonia borane (NH₃BH₃, AB) was considered as a chemical H₂-storage and H₂-delivery material due to its high storage capacity of dihydrogen (19.6 wt %) and stability at room temperature. To advance the development of efficient and recyclable catalysts for hydrolytic dehydrogenation of AB with parallel insight into the reaction mechanism, herein, ZIF-67-derived fcc-Co@porous carbon nano/microparticles (cZIF-67_nm/cZIF-67_μm) were explored to promote catalytic dehydrogenation of AB and generation of H_2(g). According to kinetic and computational studies, zero-order dependence on the concentration of AB, first-order dependence on the concentration of cZIF-67_nm (or cZIF-67_μm), and a kinetic isotope effect value of 2.45 (or 2.64) for H₂O/D₂O identify the Co-catalyzed cleavage of the H-OH bond, instead of the H-BH₂NH₃ bond, as the rate-determining step in the hydrolytic dehydrogenation of AB. Despite the absent evolution of H_2(g) in the reaction of cZIF-67 and AB in the organic solvents (i.e., THF or CH₃OH) or in the reaction of cZIF-67 and water, Co-mediated activation of AB and formation of a Co-H intermediate were evidenced by theoretical calculation, infrared spectroscopy in combination with an isotope-labeling experiment, and reactivity study toward CO₂-to-formate/H₂O-to-H₂ conversion. Moreover, the computational study discovers a synergistic interaction between AB and the water cluster (H₂O)₉ on fcc-Co, which shifts the splitting of water into an exergonic process and lowers the thermodynamic barrier for the generation and desorption of H_2(g) from the Co-H intermediates. With the kinetic and mechanistic study of ZIF-67-derived Co@porous carbon for catalytic hydrolysis of AB, the spatiotemporal control on the generation of H_2(g) for the treatment of inflammatory diseases will be further investigated in the near future.

Recent advances in metal-organic framework-based electrode materials for supercapacitors

Exploring porous electrode materials with designed micro/nano-structures is an effective way to realize high-performance supercapacitors (SCs). A metal-organic framework (MOF) is a porous crystalline material with a periodic structure formed by coordination of metal ions/clusters and organic ligands. Due to the excellent properties (e.g., large specific surface area, high porosity and tailorable structure), MOFs have been widely used in diverse applications. This Frontier article highlights the recent progress in the synthesis of MOF-based micro/nano-structured electrode materials including pristine MOFs, MOF composites and MOF derivatives, and their application in SCs. Furthermore, the challenges of MOF-based electrode materials and possible solutions are also discussed.

Assembly of Copolymer and Metal-Organic Framework HKUST-1 to Form Cu2-xS/CNFs Intertwining Network for Efficient Electrocatalytic Hydrogen Evolution

The construction of complex intertwined networks that provide fast transport pathways for ions/electrons is very important for electrochemical systems such as water splitting, but a challenge. Herein, a three dimensional (3-D) intertwined network of Cu2-xS/CNFs (x = 0 or 0.04) has been synthesized through the morphology-preserved thermal transformation of the intertwined PEG-b-P4VP/ HKUST-1 hybrid networks. The strong interaction between PEG chains and Cu2+ is the key to the successful assembly of PEG-b-P4VP nanofibers and HKUST-1, which inhibits the HKUST-1 to form individual crystalline particles. The obtained Cu2-xS/CNFs composites possess several merits, such as highly exposed active sites, high-speed electronic transmission pathways, open pore structure, etc. Therefore, the 3-D intertwined hierarchical network of Cu2-xS/CNFs displays an excellent electrocatalytic activity for HER, with a low overpotential (η) of 276 mV to reach current densities of 10 mA cm-2, and a smaller Tafel slope of 59 mV dec-1 in alkaline solution.

Polypyrrole-Based Metal Nanocomposite Electrode Materials for High-Performance Supercapacitors

Metallic nanostructures (MNs) and metal-organic frameworks (MOFs) play a pivotal role by articulating their significance in high-performance supercapacitors along with conducting polymers (CPs). The interaction and synergistic pseudocapacitive effect of MNs with CPs have contributed to enhance the specific capacitance and cyclic stability. Among various conjugated heterocyclic CPs, polypyrrole (PPy) (prevalently knows as “synthetic metal”) is exclusively studied because of its excellent physicochemical properties, ease of preparation, flexibility in surface modifications, and unique molecular structure–property relationships. Numerous researchers attempted to improve the low electronic conductivity of MNs and MOFs, by incorporating conducting PPy and/or used decoration strategy. This was succeeded by fine-tuning this objective, which managed to get outstanding supercapacitive performances. This brief technical note epitomizes various PPy-based metallic hybrid materials with different nano-architectures, emphasizing its technical implications in fabricating high-performance electrode material for supercapacitor applications.

In situ synthesis of nitrogen site activated cobalt sulfide@N, S dual-doped carbon composite for a high-performance asymmetric supercapacitor

Cobalt sulfides with high theoretical capacity are considered as potential electrodes for supercapacitors (SCs). However, the insufficient reactive sites and low electrical conductivity of bulky cobalt sulfides restrict their applications. Here, we proposed an efficient approach for in situ formation of nitrogen site activated cobalt sulfide@N, S dual-doped carbon composite (CS@NSC) by vulcanizing the cobalt-glutamine complex (CG) precursor in a tube furnace. The effects of the molecular structure and calcination temperature of CG precursors on the morphology, structure and electrochemical performance of CS@NSC were studied. The designed CS@NSC-2 exhibited a specific capacity of 593 C g^-1 at the current density of 1 A g^-1 and good cyclic stability with 88.7% retention after 2000 cycles. Moreover, an asymmetric supercapacitor (ASC) was fabricated by CS@NSC-2 (positive electrode) and activated carbon (AC) (negative electrode), which delivered ultra-high energy density of 67.8 Wh kg^-1 at a power density of 400 W kg^-1 and possessed 83.1% capacitance retention after 5000 cycles. The eco-friendly method was also suitable for synthesizing nickel sulfide. This work may provide an innovative horizon for the in situ formation of active sites in electrode materials.