One-pot green synthesis of polymeric nanocomposite: Biodegradation studies and application in sorption-degradation of organic pollutants

Removal of As(V) from aqueous solution using modified Fe3O4 nanoparticles

The removal of arsenic contamination from the aqueous environment is of great importance in the conservation of the Earth's water resources, and surfactants are a promising material used to modify magnetic nanoparticles to improve adsorption properties. Therefore, it is important to develop efficient and selective adsorbents for arsenic. Surface modification of Fe₃O₄ was carried out using anionic, cationic and zwitterionic surfactants to obtain composite Fe₃O₄@SDS, Fe₃O₄@CTAB, Fe₃O₄@SNC 16 and Fe₃O₄@NPC 16 (collectively referred to as Fe₃O₄@surfactants). The synthesized composite Fe₃O₄@surfactants magnetic nanoparticles were characterized by XRD, TEM and FTIR. The As(V) removal characteristics of the composite magnetic nanoparticles from the aqueous solution were evaluated by adsorption batch experiments which indicated the possibility of effective application of the surfactant-modified Fe₃O₄ magnetic nanoparticles for the removal of As(V) from aqueous solution. The adsorption equilibrium of the composites was reached in 30 min and the kinetic data followed the pseudo-second-order model. Langmuir equation could represent the adsorption isotherm data very well. Moreover, under the identical conditions, Fe₃O₄@CTAB showed maximum capacity of adsorption for As(V) (55.671 mg g^-1), with its removal efficiency being much higher than that of the other composites. In addition, the Fe₃O₄@surfactants composite magnetic nanoparticles retained 93.5% of its initial arsenic removal efficiency even after re-using it five times. The mechanism of arsenic adsorption by Fe₃O₄@surfactants composite magnetic nanoparticles was proved to be complexation via electrostatic attraction, which was mainly innersphere in nature.

DOE-based synthesis of gellan gum-acrylic acid-based biodegradable hydrogels: screening of significant process variables and in situ field studies

The current study uses the free radical graft copolymerization of acrylic acid as a monomer, N,N-methylene-bis-(acrylamide) as a crosslinker and ammonium persulfate as an initiator to synthesise GG-cl-poly(AA) hydrogels based on gellan gum utilising response surface methodology (RSM). A full factorial design was used to obtain the greatest percent swelling (P_s), and key process variables were determined using the Pareto chart. To make the procedure cost-effective, a multiple regression model employing ANOVA projected a linear model with a maximum percentage swelling of 556 at the lowest concentration of all three studied factors. As a result, the sequential experimental design was successful in obtaining two-fold increases in the percentage swelling in a systematic way. An RSM-based central composite design was used to optimize the percentage swelling of the three most important synthesis parameters: initiator concentration, monomer concentration, and crosslinker concentration. The best process conditions are 7.3 mM L⁻¹ initiator, 44 μM L⁻¹ monomer, and 21.6 mM L⁻¹ crosslinker. The effective synthesis of GG-cl-poly(AA) was validated by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction, field emission scanning electron microscopy (FE-SEM), and ¹H-nuclear magnetic resonance. The swelling behavior of GG-cl-poly(AA) in water and saline solutions, as well as its water retention capability, was investigated. In comparison to distilled water, the swelling potential of optimized hydrogel was shown to be significantly reduced in saline solutions. The addition of GG-cl-poly(AA) significantly improved the moisture properties of plant growth media (clay, sandy, and clay–soil combination), implying that it has great potential in moisture stress agriculture. GG-cl-poly(AA) biodegradation was studied by soil burial and vermicomposting methods. The composting approach showed 89.95% deterioration after 22 days, while the soil burial method showed 86.71% degradation after 22 days. The synthesized hydrogel may be beneficial for agricultural applications because of its considerable degradation behaviour, strong water retention capacity, low cost, and environmental friendliness.

We use free radical graft copolymerization of acrylic acid as a monomer, N,N-methylene-bis-(acrylamide) as a crosslinker and ammonium persulfate as an initiator to synthesise GG-cl-poly(AA) hydrogels based on gellan gum utilising response surface methodology.

Facile fabrication and application of poly(ortho-phenetidine) nanocomposite coating for solid-phase microextraction of carcinogenic polycyclic aromatic hydrocarbons from wastewaters

The waters and wastewaters around industrial areas are heavily polluted and have adverse effects on the ecosystems. The present study is mainly focused on the electropolymerization of ortho-phenetidine and co-deposited on a steel wire along with graphene oxide nanosheets as a novel coating for solid-phase microextraction of polycyclic aromatic hydrocarbons (PAHs) from aqueous media prior to gas chromatography-mass spectrometry. PAHs are composed of multiple aromatic rings which have been linked to skin, lung, bladder and liver. Cancer is a primary human health risk of exposure to PAHs. To obtain a firm and stable coating, several empirical factors relevant to the electrochemical process were investigated. Characterization for chemical structure and surface morphology of the synthesized nanocomposite was conducted with FT-IR spectroscopy and FE-SEM, respectively. XRD and TGA were applied to study the other properties of the nanocomposite. Some essential items involved in microextraction process were also checked in details. Under optimized case, validation parameters were assessed. Wide linearity (0.005-5.0 ng mL^-1), low detection limits (0.4-4.3 pg mL^-1) and good repeatability (3.6-9.5%) and reproducibility (7.6-11.8%) were achieved. The developed method was utilized to analyze contaminated real samples such as wastewater samples from coal processing industries and agricultural water samples collected from the vicinity of the industry in different seasons and high recoveries were obtained, finally.

Synergic effect of Guggul gum based hydrogel nanocomposite: An approach towards adsorption-photocatalysis of Magenta-O

The article is related to sunlight and UV-visible mineralization of harmful magenta-O (FB) dye. The nanocomposite used is a cross linked network of acrylic acid synthesized inside poly(acrylamide) grafted Guggul gum in the presence of UV-visible respondent bismuth ferrite nanoparticles. The synthesis of poly(acrylamide) grafted Guggul gum (Sample I) and synthesizing a crosslinked network inside it (Sample II) involved a two-step synthesis for optimizing various reaction parameters. The maximum % water uptake obtained for polymeric samples I and II was calculated as 1227.78% and 387.97%, respectively. Average particle size of bismuth ferrite nanoparticles was 47.34 nm. The nanocomposite could maximum uptake-mineralize FB dye as 97.3% and 98.8% under sunlight and photochemical reactor, respectively for 500 mg nanocomposite dose in 10 mg/L concentrated FB solution. Dye uptake occurs through ionic interactions. However, mineralization is a consequence of advanced oxidation process involving free radical species (OH and O₂^-.). The overall process of uptake-mineralization resembled second order kinetics and Langmuir theorem (monolayer adsorption). Intraparticle diffusion model gave an idea about the multistep (three steps) process of adsorption. Physico-chemical properties of FB dye got changed after mineralization except for the pH. The maximum uptake-mineralization was observed to be 76.2% after consecutive reuse of the nanocomposite hydrogel for five cycles.