Adsorption of acetone and toluene by N-functionalized porous carbon derived from ZIF-8

Design of bifunctional nitrogen-doped biochar with adsorption and catalytic oxidation capabilities for enhanced toluene emission control

Volatile organic compounds (VOCs), such as toluene, are hazardous air pollutants that pose significant health and environmental risks. This study addresses remediation of toluene by developing a bifunctional nitrogen-doped biochar (NDB) activated with sodium hydroxide (NaOH), aimed at reducing toluene emissions through both adsorption and catalytic oxidation. A series of NDB samples were prepared via NaOH activation and pyrolysis at varying temperatures to optimize their adsorption capacity and catalytic performance. The results demonstrated that NaOH-activated NDB exhibits substantial mesopore volumes and excellent surface area, with adsorption performance highly dependent on surface area and catalytic performance strongly influenced by nitrogen species. The dynamic adsorption tests revealed that BUN-900 achieved an outstanding toluene adsorption capacity of 422.25 mg/g, attributed to its high specific surface area of 1321.72 m2/g. In contrast, BU-800 showed complete toluene conversion at 450 °C via catalytic oxidation, attributed to the presence of pyridinic-N species. Interestingly, while the sample with the best adsorption performance had the lowest catalytic oxidation performance, the sample with the best catalytic performance exhibited the lowest adsorption capacity. This study demonstrates that NaOH activation and nitrogen doping can significantly enhance the bifunctional properties of biochar, positioning it as a promising, sustainable material for VOC control through combined adsorption and catalytic oxidation.

Defective UiO-66 metal-organic gels for optimizing gaseous toluene capture

Developing high-performance sorbents for volatile organic compounds (VOCs) is urgently required for environmental cleaning and personnel protection. Zirconium-based metal-organic frameworks (Zr-MOFs) have been deemed attractive candidates for gaseous toluene capture due to their superior stability and high adsorption capacity. However, the practical application of powdered Zr-MOFs is hindered by inherent limitations. Here, we report a series of defective UiO-66 metal-organic gels (G66-X) with variable missing linker deficiency by altering the modulator concentration. The defect concentration of the adsorbents has a significant impact on the porosity and gaseous toluene adsorption capacity. Dynamic breakthrough results reveal that G66-9 demonstrates optimal breakthrough time of 336 min/g and uptake amount of 334 mg/g, outperforming those of many other typical toluene adsorbents. The breakthrough times and the uptake capacities dramatically decrease with the increase of adsorption temperature. An outstanding regeneration performance of adsorbents can almost maintain even after five adsorption-desorption cycles.

Nitrogen-Doped Porous Carbon from Biomass with Efficient Toluene Adsorption and Superior Catalytic Performance

The chemical composition and surface groups of the carbon support affect the adsorption capacity of toluene. To investigate the effect of catalyst substrate on the catalytic performance, two different plant biomasses, banana peel and sugarcane peel, were used as carbon precursors to prepare porous carbon catalyst supports (Cba, Csu, respectively) by a chemical activation method. After decorating PtCo₃ nanoparticles onto both carbon supports (Cba, Csu), the PtCo₃-su catalyst demonstrated better catalytic performance for toluene oxidation (T₁₀₀ = 237 °C) at a high space velocity of 12,000 h^-1. The Csu support possessed a stronger adsorption capacity of toluene (542 mg g^-1), resulting from the synergistic effect of micropore volume and nitrogen-containing functional groups, which led to the PtCo₃-su catalyst exhibiting a better catalytic performance. Moreover, the PtCo₃-su catalyst also showed excellent stability, good water resistance properties, and high recyclability, which can be used as a promising candidate for practical toluene catalytic combustion.

Preparation and Adsorption Performance Study of Graphene Quantum Dots@ZIF-8 Composites for Highly Efficient Removal of Volatile Organic Compounds

Based on the large specific surface area and excellent adsorption potential of graphene quantum dots (GQDs) and zeolitic imidazolate framework-8 (ZIF-8) materials, a GQDs@ZIF-8 composite was constructed to achieve optimal matching of the microstructure and to acquire efficient adsorption of volatile organic compounds (VOCs). GQDs and ZIF-8 were synthesized and then compounded by the solution co-deposition method to obtain GQDs@ZIF-8 composites. GQDs were uniformly decorated on the surface of the ZIF-8 metal-organic framework (MOF), effectively restraining the agglomeration, improving the thermal stability of ZIF-8 and forming abundant active sites. Thus, the VOC removal percentage and adsorption capacity of the GQDs@ZIF-8 composites were significantly improved. Toluene and ethyl acetate were chosen as simulated VOC pollutants to test the adsorption performance of the composites. The results showed that, after the addition of GQDs, the adsorption property of GQDs@ZIF-8 composites for toluene and ethyl acetate was obviously improved, with maximum adsorption capacities of 552.31 mg/g and 1408.59 mg/g, respectively, and maximum removal percentages of 80.25% and 93.78%, respectively, revealing extremely high adsorption performance. Compared with raw ZIF-8, the maximum adsorption capacities of the composites for toluene and ethyl acetate were increased by 53.82 mg/g and 104.56 mg/g, respectively. The kinetics and isotherm study revealed that the adsorption processes were in accordance with the pseudo-first-order kinetic model and the Freundlich isotherm model. The thermodynamic results indicated that the adsorption process of the GQDs@ZIF-8 composites was a spontaneous, endothermic and entropy increase process. This study provides a new way to explore MOF-based adsorption materials with high adsorption capacity which have broad application prospects in VOC removal fields.