Synergistic degradation of dentin by cyclic stress and buffer agitation

Degradation in the fatigue crack growth resistance of human dentin by lactic acid

The oral cavity frequently undergoes localized changes in chemistry and level of acidity, which threatens the integrity of the restorative material and supporting hard tissue. The focus of this study was to evaluate the changes in fatigue crack growth resistance of dentin and toughening mechanisms caused by lactic acid exposure. Compact tension specimens of human dentin were prepared from unrestored molars and subjected to Mode I opening mode cyclic loads. Fatigue crack growth was achieved in samples from mid- and outer-coronal dentin immersed in either a lactic acid solution or neutral conditions. An additional evaluation of the influence of sealing the lumens by dental adhesive was also conducted. A hybrid analysis combining experimental results and finite element modeling quantified the contribution of the toughening mechanisms for both environments. The fatigue crack growth responses showed that exposure to lactic acid caused a significant reduction (p≤0.05) of the stress intensity threshold for cyclic crack extension, and a significant increase (p≤0.05) in the incremental fatigue crack growth rate for both regions of coronal dentin. Sealing the lumens had negligible influence on the fatigue resistance. The hybrid analysis showed that the acidic solution was most detrimental to the extrinsic toughening mechanisms, and the magnitude of crack closure stresses operating in the crack wake. Exposing dentin to acidic environments contributes to the development of caries, but it also increases the chance of tooth fractures via fatigue-related failure and at lower mastication forces.

Designing Multiagent Dental Materials for Enhanced Resistance to Biofilm Damage at the Bonded Interface

The oral environment is considered to be an asperous environment for restored tooth structure. Recurrent dental caries is a common cause of failure of tooth-colored restorations. Bacterial acids, microleakage, and cyclic stresses can lead to deterioration of the polymeric resin-tooth bonded interface. Research on the incorporation of cutting-edge anticaries agents for the design of new, long-lasting, bioactive resin-based dental materials is demanding and provoking work. Released antibacterial agents such as silver nanoparticles (NAg), nonreleased antibacterial macromolecules (DMAHDM, dimethylaminohexadecyl methacrylate), and released acid neutralizer amorphous calcium phosphate nanoparticles (NACP) have shown potential as individual and dual anticaries approaches. In this study, these agents were synthesized, and a prospective combination was incorporated into all the dental materials required to perform a composite restoration: dental primer, adhesive, and composite. We focused on combining different dental materials loaded with multiagents to improve the durability of the complex dental bonding interface. A combined effect of bacterial acid attack and fatigue on the bonding interface simulated the harsh oral environment. Human saliva-derived oral biofilm was grown on each sample prior to the cyclic loading. The oral biofilm viability during the fatigue performance was monitored by the live-dead assay. Damage of the samples that developed during the test was quantified from the fatigue life distributions. Results indicate that the resultant multiagent dental composite materials were able to reduce the acidic impact of the oral biofilm, thereby improving the strength and resistance to fatigue failure of the dentin-resin bonded interface. In summary, this study shows that dental restorative materials containing multiple therapeutic agents of different chemical characteristics can be beneficial toward improving resistance to mechanical and acidic challenges in oral environments.