Variable-temperature Fourier-transform infrared studies of poly(l-lactic acid) in different states of order: A 2DCOS and PCMW2D analysis

Effects of montmorillonite (MMT) on the crystallization behavior of poly(L-lactic acid) (PLLA) by variable-temperature FTIR coupled with difference spectrometry, PCMW2D and 2DCOS analyses

Effects of montmorillonite (MMT) on the crystallization behavior of poly(L-lactic acid) (PLLA) were investigated by variable-temperature FTIR spectroscopy. The variations of carbonyl band (1800-1720 cm^-1) of different PLLA/MMT nanocomposites were focused due to its strong intensity and the involved abundant structure information. Difference spectrometry was used to evaluate the structural variations of PLLA after introducing MMT, and perturbation correlation moving window two-dimensional analysis (PCMW2D) split the temperature range into two sub-regions, i.e., 32-116 ℃ and 116-152 ℃, on the basis of the spectral variation. Two-dimensional correlation spectroscopy (2DCOS) was further applied to such sub-regions in order to find the change order between varied PLLA polymorphs. The results showed that less addition of MMT (≤3%) would lead to a well-exfoliated structure, which not only had no nucleation effect for PLLA, but also delayed the cold crystallization to a higher temperature compared with the one of pure PLLA. However, a higher addition of MMT (≥5%) would lead to an intercalated structure, which acted as a nucleating agent and thus advanced the cold crystallization to a lower temperature. Nevertheless, the introduction of MMT cannot affect the phase transition order between the amorphous, the intermediate, the α'- and the α'-PLLAs based on 2DCOS results.

Isothermal crystalline polymorphs of poly(l-lactic acid) by FTIR coupled with two-dimensional correlation spectroscopy and perturbation-correlation moving-window two-dimensional analysis

The evolutions of the crystalline polymorphs of poly(l-lactic acid) (PLLA) at 85 °C and 145 °C were respectively studied by Fourier transform infrared (FTIR) spectroscopy coupled with two-dimensional correlation spectroscopy (2DCOS) and perturbation-correlation moving-window two-dimensional (PCMW2D) analysis in the carbonyl stretching band region (1820-1720 cm^-1). The perturbation region was divided into a few sub-regions by PCMW2D based on the spectral variations. Further 2DCOS analyses were implemented on these sub-regions. Four stages were identified for crystallization at 85 °C, in which the transformation of amorphous PLLA to α'-PLLA was found in the initial stage (0-30 min), while some of α'-PLLA was also changed to α-PLLA in the growth stage (30-150 min). For isothermal crystallization at 145 °C, the amorphous and the intermediate PLLAs were first changed to the crystalline forms in the initial period (0-30 min), then alternate changes between α-, α'- and intermediate phases occurred in the other periods with the extension of crystallization.

Soy Protein Isolate and Glycerol Hydrogen Bonding Using Two-Dimensional Correlation (2D-COS) Attenuated Total Reflection Fourier Transform Infrared (ATR FT-IR) Spectroscopy

It is a trend to substitute bioplastics for petroleum-based plastics in food packaging. Glycerol-plasticized soy protein isolate (SPI) is promising as a replacement for traditional petroleum-based plastics. Hydrogen bonding (H-bonding) plays a key role in plasticization of SPI film. However, few publications are concerned with the interactions of SPI and glycerol at the molecular level. In this paper, attenuated total reflection Fourier transform infrared (ATR FT-IR) spectroscopy was applied to investigate the effect of H-bonding on the secondary structures of glycerol-plasticized SPI films and thus on the plasticization. An "S" profile of the H-bonding between SPI and glycerol with an abrupt jump in the glycerol range of 10-30% was achieved. For more in-depth investigation of the H-bonding, two-dimensional correlation spectroscopy (2D-COS) and perturbation-correlation moving-window two-dimensional (PCMW2D) analyses were applied to the amide I and II bands of SPI films spectra series. The conformation change sequences under the effect of H-bonding were revealed. When glycerol was involved, it entered into the β-sheet and the H-bonds of the SPI peptide backbone (C = O···H-N-) were replaced by the new H-bonds between SPI and glycerol (C = O···H-O-). The transformations of parallel β-sheet to β-turn in the range of 0-20% and anti-parallel β-sheet to β-turn in the range of 20-35% were obtained. In the 35-60% concentration range, the β-sheet was first changed to a transition state conformation, then together with the β-turn, to the random coil. The 2D-COS results clearly suggest that the conformations of SPI gradually change from the ordered to the less ordered and disordered, which significantly improve the plasticity of SPI film.