Surface properties of alternated aliphatic polyketones

Rapid Transformation in Wetting Properties of PTFE Membrane Using Plasma Treatment

In this paper, we describe the surface modification of polytetrafluoroethylene (PTFE) through the plasma treatment process. Several parameters including different active gases, RF power, distance between the plasma source and sample, and plasma duration were optimized to reduce the hydrophobic nature of PTFE. Three different active gases were used (i.e., N2, O2, and (Ar+H2)); N2 was effective to reduce the hydrophobicity of PTFE within a shorter plasma duration of 2 min. Several surface characterizations including ATR-FTIR, water contact angle, FE-SEM, and XPS were utilized to verify the neat and modified PTFE surface after plasma treatment. The plasma treatment using N2 as an active gas improved the wettability of the PTFE membrane, showing a water contact angle of 109.5° when compared with the neat PTFE (141.9°). The SEM images of plasma-treated PTFE showed greater modifications on the surface indicating non-uniform fiber alignment and torn fibers at several places. The obtained results confirm the fact that plasma treatment is an effective way to modify the PTFE surface without altering its bulk property.

High Density Polyethylenes Bearing Isolated In-Chain Carbonyls*

Polyethylene materials are highly important polymers which are produced in the largest volume among all plastics. Due to the chemical inert property of saturated carbon-carbon bonds, the degradation of polyethylene is extremely challenging, which prevents them from efficient chemical recycling. Installing functional groups in the main chain of polyethylenes may facilitate the degradation and following chemical recycling of polyethylene materials. Here we report a highly selective approach for the synthesis of high density polyethylenes bearing low content isolated in-chain carbonyls. Linear high-molecular weight polyethylene chains are synthesized via the palladium catalyzed copolymerization of ethylene with metal carbonyls. Different from traditional ethylene/CO copolymerization reactions, excellent non-alternating selectivity has been achieved. While the properties of polyethylene have been retained in the copolymer, faster degradation compared with that of polyethylene was observed upon UV light irradiation. The synthesized materials may therefore serve as more environmentally friendly alternative plastics than traditional polyethylene materials.

The microstructure and melt properties of CO–ethylene copolymers with remarkably low CO content

Unique structure–property relationships were revealed for non-alternating polyketones obtained with unprecedented efficiency by a new protocol for the palladium-catalysed copolymerisation of CO and ethylene.