Ternary Zinc Antimonides Unlocked Using Hydride Synthesis

Advancing Heteroanionicity in Zintl Phases: Crystal Structures, Thermoelectric and Magnetic Properties of Two Quaternary Semiconducting Arsenide Oxides, Eu8Zn2As6O and Eu14Zn5As12O

Two novel quaternary oxyarsenides, Eu8Zn2As6O and Eu14Zn5As12O, were synthesized through metal flux reactions, and their crystal structures were established by single-crystal X-ray diffraction methods. Eu8Zn2As6O crystallizes in the orthorhombic space group Pbca, featuring polyanionic ribbons composed of corner-shared triangular [ZnAs3] units, running along the [100] direction. The structure of Eu14Zn5As12O crystallizes in the monoclinic space group P2/m and its anionic substructure can be described as an infinite "ribbonlike" chain comprised of [ZnAs3] trigonal-planar units, although the structural complexity here is greater and also amplified by disorder on multiple crystallographic positions. In both structures, the O2- anion occupies an octahedral void with six neighboring Eu2+ cations. Formal electron counting, electronic structure calculations, and transport properties reveal the charge-balanced semiconducting nature of these heteroanionic Zintl phases. High-temperature thermoelectric transport properties measurements on Eu14Zn5As12O reveal relatively high resistivity (ρ500K = 8 Ω·cm) and Seebeck coefficient values (S500K = 220 μV K-1), along with a low concentration and mobility of holes as the dominant charge-carriers (n500K = 8.0 × 1017 cm-3, μ500K = 6.4 cm2/V s). Magnetic studies indicate the presence of divalent Eu2+ species in Eu14Zn5As12O and complex magnetic ordering, with two transitions observed at T1 = 21.6 K and T2 = 9 K.

How to Look for Compounds: Predictive Screening and in situ Studies in Na-Zn-Bi System

Here, the combination of theoretical computations followed by rapid experimental screening and in situ diffraction studies is demonstrated as a powerful strategy for novel compounds discovery. When applied for the previously “empty” Na−Zn−Bi system, such an approach led to four novel phases. The compositional space of this system was rapidly screened via the hydride route method and the theoretically predicted NaZnBi (PbClF type, P4/nmm) and Na₁₁Zn₂Bi₅ (Na₁₁Cd₂Sb₅ type, P1‾ ) phases were successfully synthesized, while other computationally generated compounds on the list were rejected. In addition, single crystal X‐ray diffraction studies of NaZnBi indicate minor deviations from the stoichiometric 1 : 1 : 1 molar ratio. As a result, two isostructural (PbClF type, P4/nmm) Zn‐deficient phases with similar compositions, but distinctly different unit cell parameters were discovered. The vacancies on Zn sites and unit cell expansion were rationalized from bonding analysis using electronic structure calculations on stoichiometric “NaZnBi”. In‐situ synchrotron powder X‐ray diffraction studies shed light on complex equilibria in the Na−Zn−Bi system at elevated temperatures. In particular, the high‐temperature polymorph HT‐Na₃Bi (BiF₃ type, Fm3‾m) was obtained as a product of Na₁₁Zn₂Bi₅ decomposition above 611 K. HT‐Na₃Bi cannot be stabilized at room temperature by quenching, and this type of structure was earlier observed in the high‐pressure polymorph HP‐Na₃Bi above 0.5 GPa. The aforementioned approach of predictive synthesis can be extended to other multinary systems.