Temperature-dependent adsorption and adsorption hysteresis of a thermoresponsive diblock copolymer

Poly(2-isopropyl-2-oxazoline)-b-poly(lactide) (PiPOx-b-PLA) Nanoparticles in Water: Interblock van der Waals Attraction Opposes Amphiphilic Phase Separation

Poly(2-isopropyl-2-oxazoline)-b-poly(lactide) (PiPOx-b-PLA) diblock copolymers comprise two miscible blocks: the hydrophilic and thermosensitive PiPOx and the hydrophobic PLA, a biocompatible and biodegradable polyester. They self-assemble in water, forming stable dispersions of nanoparticles with hydrodynamic radii (R h) ranging from ∼18 to 60 nm, depending on their molar mass, the relative size of the two blocks, and the configuration of the lactide unit. Evidence from 1H nuclear magnetic resonance spectroscopy, light scattering, small-angle neutron scattering, and cryo-transmission electron microscopy indicates that the nanoparticles do not adopt the typical core-shell morphology. Aqueous nanoparticle dispersions heated from 20 to 80 °C were monitored by turbidimetry and microcalorimetry. Nanoparticles of copolymers containing a poly(dl-lactide) block coagulated irreversibly upon heating to 50 °C, forming particles of various shapes (R h ∼ 200-500 nm). Dispersions of PiPOx-b-poly(l-lactide) coagulated to a lesser extent or remained stable upon heating. From the entire experimental evidence, we conclude that PiPOx-b-PLA nanoparticles consist of a core of PLA/PiPOx chains associated via dipole-dipole interactions of the PLA and PiPOx carbonyl groups. The core is surrounded by tethered PiPOx loops and tails responsible for the colloidal stability of the nanoparticles in water. While the core of all nanoparticles studied contains associated PiPOx and PLA blocks, fine details of the nanoparticles morphology vary predictably with the size and composition of the copolymers, yielding particles of distinctive thermosensitivity in aqueous dispersions.

Thermoresponsive Pentablock Copolymer on Silica: Temperature Effects on Adsorption, Surface Forces, and Friction

The adsorption of hydrophilic or amphiphilic multiblock copolymers provides a powerful means to produce well-defined "smart" surfaces, especially if one or several blocks are sensitive to external stimuli. We focus here on an A-B-A-B-A copolymer, where A is a cationic poly((3-acrylamido-propyl)-trimethylammonium chloride) (PAMPTMA) block containing 15 (end blocks) or 30 (middle block) repeat units and B is a neutral thermosensitive water-soluble poly(2-isopropyl-2-oxazoline) (PIPOZ) block with 50 repeat units. X-ray reflectivity and quartz crystal microbalance with dissipation monitoring were employed to study the adsorption of PAMPTMA₁₅-PIPOZ₅₀-PAMPTMA₃₀-PIPOZ₅₀-PAMPTMA₁₅ on silica surfaces. The latter technique was employed at different temperatures up to 50 °C. Surface forces and friction between the two silica surfaces across aqueous pentablock copolymer solutions at different temperatures were determined with the atomic force microscopy colloidal probe force and friction measurements. The cationic pentablock copolymer was found to have a high affinity to the negatively charged silica surface, leading to a thin (2 nm) and rigid adsorbed layer. A steric force was encountered at a separation of around 3 nm from hard wall contact. A capillary condensation of a polymer-rich phase was observed at the cloud point of the solution. The friction forces were evaluated using Amontons' rule modified with an adhesion term.

Thermoresponsive poly(2-oxazoline)s, polypeptoids, and polypeptides

Recent advances in thermoresponsive poly(2-oxazoline)s, polypeptoids, and polypeptides, with a specific focus on structure–property relationships, self-assembly, and applications, are reviewed.

Tethered poly(2-isopropyl-2-oxazoline) chains: temperature effects on layer structure and interactions probed by AFM experiments and modeling

Thermoresponsive polymer layers on silica surfaces have been obtained by utilizing electrostatically driven adsorption of a cationic-nonionic diblock copolymer. The cationic block provides strong anchoring to the surface for the nonionic block of poly(2-isopropyl-2-oxazoline), referred to as PIPOZ. The PIPOZ chain interacts favorably with water at low temperatures, but above 46 °C aqueous solutions of PIPOZ phase separate as water becomes a poor solvent for the polymer. We explore how a change in solvent condition affects interactions between such adsorbed layers and report temperature effects on both normal forces and friction forces. To gain further insight, we utilize self-consistent lattice mean-field theory to follow how changes in temperature affect the polymer segment density distributions and to calculate surface force curves. We find that with worsening of the solvent condition an attraction develops between the adsorbed PIPOZ layers, and this observation is in good agreement with predictions of the mean-field theory. The modeling also demonstrates that the segment density profile and the degree of chain interpenetration under a given load between two PIPOZ-coated surfaces rise significantly with increasing temperature.