Translucency and mechanical behavior of partially stabilized monolithic zirconia after staining, finishing procedures and artificial aging

Effect of Staining, Glazing and Polishing on the Survival Probability of Monolithic Zirconia Crowns

OBJECTIVE

The purpose of this in vitro study was to evaluate the effect of staining, glazing, and polishing on the survival probability of monolithic crowns manufactured with preshaded stabilized zirconia with 5 mol% of yttrium oxide (5Y-TZP).

MATERIALS AND METHODS

Monolithic crowns in the shape of an upper canine (1.5 mm of thickness) were manufactured by CAD/CAM, adhesively cemented on metallic foundation, and divided into 6 groups (n = 21): C (control), S (staining), G (glazing), P (polishing), SG (staining and glazing), and SP (staining and polishing). The survival probability was determined by step-stress accelerated life testing with a load applied to the palatine concavity of the crown. First, the specimens were subjected to a single-load to fracture test (SLF) and next to the fatigue test (5 Hz, thermocycling immersed in water varying 5-55°C), including the light (n = 9), moderate (n = 6), and aggressive (n = 3) loading profiles (load ranged between 20% and 60% of SLF). The survival probability was calculated considering the cycles for failure (CFF) and fatigue failure load (FFL) and illustrated using a Kaplan-Meier graph. The comparison among groups was performed using a Log-Rank test (α = 0.05).

RESULTS

The mean value of SLF was 586.7 N. There was no difference among groups in survival probability, considering CFF and FFL.

CONCLUSION

Staining, glazing, and polishing can be performed safely without damaging the mechanical behavior of 5Y-TZP monolithic crowns.

CLINICAL SIGNIFICANCE

Staining is used to characterize and improve the esthetic of zirconia monolithic crowns. It can be used to reproduce the color gradient in the cervical region of the crown and pigmented grooves. This study showed that staining, glazing, and polishing did not affect the survival probability and the use of finishing procedures (glazing or polishing) after staining did not improve the survival probability of zirconia monolithic crowns.

In Vitro Wear of Human Enamel Against Monolithic Zirconia After Staining, Glazing and Polishing Treatments

OBJECTIVE

To evaluate the effect of staining, glazing, and polishing of stabilized zirconia with 5 mol% of yttrium oxide (5Y-TZP) on the wear behavior of opposing tooth enamel.

MATERIALS AND METHODS

The plane specimens of 5Y-TZP were divided into 6 groups (n = 10), according to surface treatment: as sintered, staining, glazing, polishing, staining followed by glazing, and staining followed by polishing, and positioned against tooth enamel during the two-body wear test (20 N, 2 Hz, until completing 300,000 cycles). The wear rates of tooth enamel were evaluated using a profile projector and a digital pachymeter as a measure of vertical height loss. The data were analyzed by one-way ANOVA and a Tukey post hoc test (α = 0.05).

RESULTS

Polishing reduced the vertical height loss (p < 0.001) while there was no difference among other groups.

CONCLUSION

Polishing is recommended as a finishing procedure to reduce the wear rates of tooth enamel, and finishing procedures (glazing or polishing) performed after staining did not affect the vertical height loss of tooth enamel.

CLINICAL SIGNIFICANCE

Polishing is the recommended finishing procedure for preshaded 5Y-TZP to reduce the wear rates of opposing tooth enamel. Staining is applied to the occlusal surface to reproduce the pigmented groove appearance, and glazing or polishing performed after staining did not affect the wear rates of opposing tooth enamel.

In Vitro Evaluation of Speed Sintering and Glazing Effects on the Flexural Strength and Microstructure of Highly Translucent Multilayered 5 mol% Yttria-Stabilized Zirconia

This study aimed to investigate the impact of speed sintering and glazing on the flexural strength and microstructure of multilayered 5 mol% yttria-stabilized (5Y-) zirconia, which remains unknown. Bar-shaped specimens (N = 600) were fabricated from 5Y-zirconia (FX; Ceramill Zolid FX ML, ST; Katana STML) by cutting, polishing, sintering (conventional and speed sintering), and then glazing. A flexural strength test (n = 30/group), field emission scanning electron microscopy (FE-SEM) observation (n = 2/group), and an X-ray diffraction (XRD) study with Rietveld refinement (n = 1/group) were performed. The flexural strength was analyzed using three-way ANOVA and a post hoc Scheffé test. The grain size was analyzed using the Kruskal-Wallis H test and Bonferroni-Dunn post hoc test. Flexural strength slightly decreased in the nonglazed FX after speed sintering (p < 0.05). Glazing with and without glazing paste did not affect flexural strength at both sintering speeds (p > 0.05). Speed sintering and glazing minimally changed the Weibull modulus and phase fraction, and did not affect grain size (p > 0.05). ST had a larger grain size and lower tetragonal phase content than FX and had a lower flexural strength than FX in most groups (p < 0.05). Overall, the multilayered 5Y-zirconia is considered suitable for dental application using speed sintering and glazing.

Fracture characteristics and translucency of multilayer monolithic zirconia crowns of various thicknesses

OBJECTIVES

Multilayer monolithic zirconia (M-Zr) crowns can be engineered to achieve gradational translucency and color intensity. However, this modification may compromise the mechanical strength, raising concerns regarding the ability of M-Zr crowns to withstand occlusal stresses. The effects of M-Zr crown thickness on translucency and ability to endure occlusal forces were investigated at different tooth positions (incisors, premolars, and molars). The objective was to determine the minimal thickness of M-Zr crowns used in tooth preparation to meet aesthetic and functional demands.

METHODS

M-Zr samples (Vita A1) with four thicknesses (0.5, 1.0, 1.5, and 2.0 mm) were prepared and subjected to translucency testing using a digital colorimeter by 3-third and 9-square division methods. Crown-shaped M-Zr samples with three thicknesses (1.0, 1.5, and 2.0 mm) and three tooth positions (incisor, premolar, and molar) were digitally designed, and 2.0 mm metal abutments were fabricated. The samples were bonded to the abutments; their fracture characteristics were evaluated using a universal testing machine, and their fracture surfaces examined using an optical microscope. Statistical analyses included the Shapiro-Wilk test, Pearson correlation, and one-way and two-way ANOVA with a post hoc Tukey HSD test (α = 0.05).

RESULTS

Color analysis results revealed a significant negative correlation between thickness and translucency (r < -0.96, P < 0.01), with the highest values in the incisal region. Cross-sectional profiles confirmed the uniform thickness and morphology of the digitally designed M-Zr crowns. The results of fracture strength analysis showed position-dependent variability, a strong positive correlation with thickness (r > 0.96, P < 0.01), and fracture strengths consistently exceeding 1200 N across all tooth positions. Fracture patterns indicated that thinner crowns at the incisors and molars were more prone to cracking, whereas those at the premolars demonstrated significantly higher strength (4872.51 N, P < 0.05), only with crack or even no fracture occurring at 2.0 mm.

CONCLUSIONS

Thickness significantly influenced both the translucency and fracture strength of M-Zr, with the tooth position playing an additional role, albeit to a lesser extent. Although thinner crowns exhibited lower strength at each tooth position, even at a thickness of 1.0 mm, fracture strength exceeding 1200 N was maintained, surpassing the typical occlusal forces. Thus, it can be asserted that M-Zr crowns with a minimum thickness of 1.0 mm can meet both aesthetic and functional requirements.

Optimized 3D printed zirconia-reinforced leucite with antibacterial coating for dental applications

OBJECTIVES

This study aims to produce by robocasting leucite/zirconia pieces with suitable mechanical and tribological performance, convenient aesthetics, and antibacterial properties to be used in dental crown replacement.

METHODS

Leucite pastes reinforced with 12.5%, 25%, and 37.5% wt. ZrO2 nanoparticles were prepared and used to print samples that after sintering were characterized in terms of density, shrinkage, morphology, porosity, mechanical and tribological properties and translucency. A coating of silver diamine fluoride (SDF) and potassium iodide (KI) was applied over the most promising material. The material's antibacterial activity and cytotoxicity were assessed.

RESULTS

It was found that the increase of ZrO2 reinforcement up to 25% enhanced both microhardness and fracture toughness of the sintered composite. However, for a superior content of ZrO2, the increase of the porosity negatively affected the mechanical behaviour of the composite. Moreover, the composite with 25% ZrO2 exhibited neglectable wear in chewing simulator tests and induced the lowest wear on the antagonist dental cusps. Although this composite exhibited lower translucency than human teeth, it was three times higher than the ZrO2 glazed material. Coating this composite material with SDF+KI conferred antibacterial properties without inducing cytotoxicity.

SIGNIFICANCE

Robocasting of leucite reinforced with 25% ZrO2 led to best results. The obtained material revealed superior optical properties and tribomechanical behaviour compared to glazed ZrO2 (that is a common option in dental practice). Moreover, the application of SDF+KI coating impaired S. aureus proliferation, which anticipates its potential benefit for preventing pathogenic bacterial complications associated with prosthetic crown placement.

The Effect of Restoration Thickness on the Fracture Resistance of 5 mol% Yttria-Containing Zirconia Crowns

BACKGROUND

To determine what thickness of 5 mol% yttria zirconia (5Y-Z) translucent crowns cemented with different cements and surface treatments would have equivalent fracture resistance as 3 mol% yttria (3Y-Z) crowns.

METHODS

The study included 0.8 mm, 1.0 mm, and 1.2 mm thickness 5Y-Z (Katana UTML) crowns and 0.5 and 1.0 mm thickness 3Y-Z (Katana HT) crowns as controls. The 5Y-Z crowns were divided among three treatment subgroups (n = 10/subgroup): (1) cemented using RMGIC (Rely X Luting Cement), (2) alumina particle-abraded then luted with the same cement, (3) alumina particle-abraded and cemented using a resin cement (Panavia SA Cement Universal). The 3Y-Z controls were alumina particle-abraded then cemented with RMGIC. The specimens were then loaded in compression at 30° until failure.

RESULTS

All 5Y-Z crowns (regardless of thickness or surface treatment) had a similar to or higher fracture force than the 0.5 mm 3Y-Z crowns. Only the 1.2 mm 5Y-Z crowns with resin cement showed significantly similar fracture force to the 1 mm 3Y-Z crowns.

CONCLUSION

In order to achieve a similar fracture resistance to 0.5 mm 3Y-Z crowns cemented with RMGIC, 5Y-Z crowns may be as thin as 0.8 mm. To achieve a similar fracture resistance to 1.0 mm 3Y-Z crowns cemented with RMGIC, 5Y-Z crowns must be 1.2 mm and bonded with resin cement.

Translucent Zirconia in Fixed Prosthodontics-An Integrative Overview

Over the past two decades, dental ceramics have experienced rapid advances in science and technology, becoming the fastest-growing field of dental materials. This review emphasizes the significant impact of translucent zirconia in fixed prosthodontics, merging aesthetics with strength, and highlights its versatility from single crowns to complex bridgework facilitated by digital manufacturing advancements. The unique light-conducting properties of translucent zirconia offer a natural dental appearance, though with considerations regarding strength trade-offs compared to its traditional, opaque counterpart. The analysis extends to the mechanical attributes of the material, noting its commendable fracture resistance and durability, even under simulated physiological conditions. Various zirconia types (3Y-TZP, 4Y-TZP, 5Y-TZP) display a range of strengths influenced by factors like yttria content and manufacturing processes. The study also explores adhesive strategies, underlining the importance of surface treatments and modern adhesives in achieving long-lasting bonds. In the realm of implant-supported restorations, translucent zirconia stands out for its precision, reliability, and aesthetic adaptability, proving suitable for comprehensive dental restorations. Despite its established benefits, the review calls for ongoing research to further refine the material's properties and adhesive protocols and to solidify its applicability through long-term clinical evaluations, ensuring its sustainable future in dental restorative applications.

Effect of Finishing Protocols on the Surface Roughness and Fatigue Strength of a High-Translucent Zirconia

Purpose

In case of need for esthetical improvement of zirconia restorations, an individualization using extrinsic staining can be applied. This study aimed to evaluate the surface roughness and fatigue strength (survival) of high-translucency zirconia (3Y-TZP, YZ®HT, Vita Zanhfabrik) with extrinsic characterization and/or glaze.

Methods

Sixty (60) zirconia discs (12 × 1.2 mm) were obtained, sintered, and randomly distributed among three groups (n = 20) according to the surface finishing protocol: C (control), C + G (extrinsic characterization followed by a glaze layer), and G (glaze layer). The surface roughness (Ra) was analyzed with a contact profilometer. Subsequently, the specimens were subjected to a fatigue load profile starting at 120 N during 20,000 cycles at 4 Hz frequency, with a 5% increase at each step until failure. The failed specimens were evaluated under a stereomicroscope. Surface roughness analysis was evaluated by using one-way ANOVA and post hoc Tukey tests (95%); while fatigue survival probability was analyzed with Kaplan-Meier and Mantel-Cox (log- rank, 95%).

Results

One-way ANOVA revealed that surface roughness was affected by the finishing protocol, where C + G showed the highest mean value (0.46 ± 0.18 µm)A followed by G (0.30 ± 0.10 µm)B, and C (0.19 ± 0.02 µm)C. While for fatigue strength, the G protocol presented a higher mean value (243.00, and 222.36-263.63)A, followed by C + G (192.75 and 186.61-198.88)B and C (172.50 and 159.43-185.56)C.

Conclusion

Surface finishing protocols modify the surface roughness and fatigue strength of high-translucent zirconia. Regardless of the surface roughness, both glazing protocols improved the ceramic fatigue strength, favoring the restoration's long-term survival.